内氧化法制备Al2O3/Cu复合材料的再结晶

利用内氧化法制备了Al2O3/Cu复合材料,研究了该材料在不同冷拔变形量和Al2O3含量下,其硬度值随退火温度变化的规律,并进行了显微组织结构分析。结果表明:采用内氧化法制备的Al2O3/Cu复合材料,在铜基体中弥散分布着纳米级的Al2O3颗粒;经900℃×1h退火后,其硬度可保持室温的87%以上;其再结晶温度高达1000℃;变形量和Al2O3含量增加均使硬度提高,但对软化和再结晶温度影响不大。     

内氧化法制备Al2O3／Cu复合材料的再结晶行为

以Cu2O为氧化剂，采用Cu-Al合金粉末内氧化及后续的粉末冶金法制备了Al2O3／Cu复合材料。并将不同Al2O3含量的试样进行不同变形量的冷拔处理，在氮气保护下进行高温退火处理(700℃～1050℃，1h)。研究了硬度随退火温度的变化规律，观察了显微组织。结果表明：在铜基体中弥散分布着纳米级的Al2O3颗粒：经900℃，1h退火后Al2O3／Cu复合材料的硬度可保持室温的87％以上；其再结晶温度高达1000℃；变形量和Al2O3含量增加均使硬度提高，但对软化和再结晶温度影响不大。     

添加剂对新型AgTiB2触头材料微结构和性能的影响

采用高能球磨和粉末冶金法制备了含不同添加剂的AgTiB2触头材料,系统研究了WO3、Al、Bi2O3以及WO3+Bi2O3、WO3+Al复合添加对AgTiB2材料微结构和性能的影响。采用扫描电子显微镜(SEM)和能谱仪(EDS)分析了AgTiB2复合粉末形貌和AgTiB2复合材料的组织,并对硬度和导电率进行测试。结果表明:WO3、Al+WO3与Bi2O3+WO3添加有助于提高AgTiB2复合材料致密度;与未添加的相比,单独添加WO3和复合添加Al+WO3的AgTiB2材料的硬度和导电率都有不同程度的增加,硬度分别为1253和1022 MPa,导电率分别为78.62%IACS和14.91%IACS;与未添加的相比,复合添加Bi2O3+WO3的AgTiB2材料硬度和导电率分别为786 MPa和16.12%IACS。     

Al2O3弥散强化铜基复合材料的制备及物理性能的研究

采用硝酸盐分解法制备Al2O3弥散强化铜基复合材料，通过测试材料的硬度、抗软化温度和电导率，研究了Al2O3增强相对材料性能的影响。结果表明，Al2O3颗粒弥散分布在铜基体上，制备的Al2O3弥散强化铜基复合材料的强度、硬度、软化温度等远高于纯铜，具有良好的高温性能，当Al2O3含量为1．0％时，复合材料的软化温度在800℃以上、硬度达到125HB。     

原位热压合成Ti3AlC2/Al2O3复合材料的研究

以Ti,Al,TiC,TiO2粉末为原料,采用原位热压合成法制备了Ti3AlC2/Al2O3复合材料。主要考察不同Al2O3含量对复合材料性能的影响。在1400℃,30MPa压力,保温2h条件下烧结制得致密的Ti3AlC2/Al2O3块体材料。采用XRD分析了不同Al2O3含量的复合材料的相组成。用SEM观察组织结构特征。测量了维氏硬度和电导率同Al2O3含量的关系曲线。研究结果表明,Al2O3的加入可大幅度提高复合材的硬度。Ti3AlC2/25%Al2O3的维氏硬度可达8.7GPa。虽然添加Al2O3后复合材料的电导率有所下降,但Al2O3对复合材料强度和硬度的增加有显著的贡献。Ti3Al2C2/Al2O3乃不失为一种性能良好的高温结材材料。     

内氧化制备Cu/Al2O3弥散强化铜的组织性能研究

实验用Cu2O粉作氧化剂,采用简化的内氧化法工艺,在900℃下使Cu-Al合金薄平板内氧化,获得Cu/Al2O3复合材料。研究不同氧化时间(3、6、10 h)下的Cu/Al2O3复合材料的组织特征及性能。研究表明:复合层中Al2O3颗粒呈弥散状分布;复合层表面和内部的晶粒大小明显不同,由于表面Al2O3析出较早,阻止晶粒的充分长大;表面晶粒较小,表面硬度随时间延长而升高。     

反应热压法制备Al2O3/NiCrAl复合材料及功能梯度材料

采用NiO、Al和Cr粉末反应热压制备了Al2O3/NiCrAl复合材料,NiCrAl合金由NiO还原出来的Ni与添加的Cr和Al反应形成.制备了不同Al2O3含量的Al2O3/NiCrAl复合材料,并以Al2O3体积分数分别为25%、52.2%和75%的Al2O3/NiCrAl复合材料为过渡层制备了Y稳定氧化锆(YSZ)到NiCrAl合金的功能梯度材料.X射线衍射分析、金相观察、硬度测量和热循环冲击实验结果表明:用该方法制备的复合材料由Al2O3陶瓷相和(Ni,Cr,Al)固溶体组成,而Al2O3颗粒由NiO与Al原位反应形成,尺寸细小,呈弥散分布.该功能梯度材料经从室温到1 000℃空气中10次热循环后未发现有裂纹,表明该方法制备的材料陶瓷相与合金相有良好的相容性、较高的结合强度、良好的耐高温抗氧化及热循环冲击性能.     

Cu-Al合金平板内氧化组织性能研究

采用简化的内氧化工艺制备了Al2O3/Cu复合材料,研究不同内氧化时间(3～10h)及不同变形量(20%～80%)下的Al2O3/Cu复合材料的显微硬度和导电率,并对其显微组织进行了分析。结果表明:内氧化法制备的Al2O3/Cu复合材料中弥散分布着纳米级的Al2O3颗粒;复合材料的表面和内部的晶粒大小明显不同,表面晶粒较小(粒径10～30μm);冷加工变形量越大,Al2O3颗粒与位错的缠结越严重;经900℃内氧化制备的Al2O3/Cu复合材料具有良好的导电率和显微硬度。     

激光熔覆纳米Al_2O_3等离子喷涂陶瓷涂层

采用X射线衍射仪、扫描电镜和显微硬度计研究了45#钢表面激光熔覆纳米Al2O3改性Al2O3 13%TiO2(质量分数)陶瓷涂层的相组成、微观结构和显微硬度,同时对涂层的磨损特性进行了考察。结果表明,激光重熔区亚稳相γ Al2O3转变成稳定相α Al2O3,熔覆层由粗颗粒α Al2O3和TiO2以及纳米α Al2O颗粒组成,在激光的作用下,等离子喷涂层的片层状结构得以消除;纳米Al2O3颗粒仍然保持在纳米尺度,填充在涂层的大颗粒之间,使涂层致密化程度得以提高,因此纳米Al2O3改性涂层的显微硬度较高,且其耐磨性能明显优于等离子喷涂层。     

纳米Al2O3颗粒含量对Ni-Co基纳米复合电刷镀层的组织和性能影响

采用电刷镀技术制备了不同Al2O3颗粒含量的合金纳米复合电刷镀层,采用扫描电镜、硬度测试仪和摩擦磨损试验机测试了纳米Al2O3颗粒含量对镀层的组织和性能的影响。结果表明,随着镀液中纳米Al2O3颗粒含量的增加,电刷镀层沉积速度降低、表面形貌平整,显微硬度先提高而后减低,磨痕深度先减小后增大,摩擦系数先减小后增大。当镀液中纳米Al2O3含量为20g/L时,镀层具有最优的组织和性能。     

Synthesis and characterization of Li_(1.3)Al_(0.3)Ti_(1.7)(PO_4)_3-coated LiMn_2O_4 by wet chemical route

Li1.3Al0.3Ti1.7(PO4)3-coated LiMn2O4 was prepared by wet chemical route. The phase,surface morphology,and electrochemical properties of the prepared powders were characterized by X-ray diffraction,scanning electron micrograph,and galvanostatic charge-discharge experiments. Li1.3Al0.3Ti1.7(PO4)3-coated LiMn2O4 has similar X-ray diffraction patterns as LiMn2O4. The corner and border of Li1.3Al0.3Ti1.7(PO4)3-coated LiMn2O4 particles are not as clear as the uncoated one. The two powders show similar values of l...     

亚微米Al2O3颗粒表面稀土改性及其对6061Al复合材料时效行为的影响

采用液相包裹法对亚微米Al2O3颗粒进行稀土表面改性，用挤压铸造法制备表面经稀土改性的Al2O3p／6061Al复合材料．对颗粒表面经稀土改性前后增强6061Al复合材料在不同温度下的时效析出行为进行分析研究．结果表明：改性后的亚微米Al2O3粉体颗粒表面Y2O3包裹均匀，其增强的复合材料在不同时效阶段的硬度值均较改性前有明显提高．且随着时效温度的升高，Mg2Si析出过程加快，时效峰提前，呈现出硬度值变小的趋势，透射电镜观察表明，表面改性颗粒增强的复合材料基体中存在一定量的位错和析出相；而改性前复合材料却呈现出位错和析出相极其稀少的组织特征．分析了改性前后复合材料时效组织形成的原因。     

Al-Si/Al_2O_3 in situ composite prepared by displacement reaction of CuO/Al system

Al2O3 particle-reinforced ZL109 composite was prepared by in situ reaction between CuO and Al.The microstructure was observed by means of OM,SEM and TEM.The Al2O3 particles in sub-micron sizes distribute uniformly in the matrix,and the Cu displaced from the in situ reaction forms net-like alloy phases with other alloy elements.The hardness and the tensile strength of the composites at room temperature have a slight increase as compared to that of the matrix.However,the tensile strength at 350 ℃ has reached 90.23 MPa,or 16.92 MPa higher than that of the matrix.The mechanism of the reaction in the CuO/Al system was studied by using of differential scanning calorimetry(DSC) and thermodynamic calculation.The reaction between CuO and Al involves two steps.First,CuO reacts with Al to form Cu2O and Al2O3 at the melting temperature of the matrix alloy,and second,Cu2O reacts with Al to form Cu and Al2O3 at a higher temperature.At ZL109 casting temperature of 750-780 ℃,the second step can also take place because of the effect of exothermic reaction of the first step.     

等离子喷涂 NiCoCrAlY / Al2 O3 涂层的制备及摩擦性能研究

目的制备等离子喷涂NiCoCrAlY/Al2O3高温固体润滑耐磨涂层,并研究该涂层的摩擦性能和磨损机理。方法采用喷雾造粒、化工冶金包覆和固相合金化技术制备NiCoCrAlY/Al2O3复合粉体,用等离子喷涂技术在45#钢表面制备NiCoCrAlY/Al2O3复合涂层。用SEM和XRD等手段分析粉体和涂层的显微结构和物相组成,研究涂层从室温到800℃的摩擦磨损性能,探讨NiCoCrAlY/Al2O3复合涂层在室温和高温下的磨损机理。结果 Al2O3颗粒表面均匀包覆着一层致密的NiCoCrAlY合金,包覆层厚度大约为3~5μm;等离子喷涂NiCoCrAlY/Al2O3复合涂层呈典型的层状结构,涂层各层间结合良好,涂层中孔隙率约为2.84%,主晶相为Ni Cr Al合金相和Al2O3相。涂层的摩擦系数随温度的升高逐渐降低,在室温下约为0.64,800℃时在0.4以下。高温下,金属氧化物的形成是摩擦系数降低的主要原因。涂层的磨损率随温度的升高先升高后降低。涂层在低温下为脆性断裂和磨粒磨损,高温下为氧化磨损、磨粒磨损、塑性变形和金属氧化物的转移。结论等离子喷涂NiCoCrAlY/Al2O3复合涂层是一种性能优良的高温固体润滑耐磨涂层。     

Al2O3/Cu复合材料强化机理研究

采用内氧化法制备了Al2O3／Cu复合材料，进行了高温电子拉伸实验，并通过微观组织观察，分析了该复合材料的强化机理。拉伸实验结果显示：Al2O3／Cu复合材料不仅室温强度很高，而且高温时仍保持较高的强度。微观组织观察分析表明：细小的Al2O3颗粒的弥散分布是该复合材料具有高强度的主要原因，表现在：Al2O3颗粒存在能够抑制Cu基再结晶的进行；Al2O3颗粒的存在阻碍晶界亚晶界运动，从而阻碍晶粒长大；Al2O3颗粒的阻碍位错运动，增加位错密度；Al2O3颗粒的存在提高材料的蠕变抗力。     

Effect of Al powder and silica sol on the structure and mechanical properties of Al_2O_3-ZrO_2 foams

Polymeric sponge replication method is one of the common ways for ceramic foam production. The existence of central triangular voids in the struts results in a decrease of mechanical properties limiting their applications. To remove this defect, some additives consisting of Al powder particles and silica sol are added to ceramic slurries consisting of Al2O3 and ZrO2 (partially stabilized zirconia). With increasing temperature for pyrolyzing and sintering of raw materials, first the Al powder and then the gl...     

特征喷涂参数对等离子喷涂纳米 Al2 O3 -13%TiO2涂层微观结构及耐磨性能的影响

目的研究等离子喷涂纳米Al2O3-13%TiO2的特征喷涂参数(CPSP)对涂层微观结构及耐磨性能的影响,探索更合理的等离子喷涂工艺参数。方法采用等离子喷涂,在Q235钢表面制备过渡层为NiCrAl、陶瓷层为纳米Al2O3-13%TiO2的涂层系统。对涂层试样进行高温和常温磨损性能测试,并对比分析喷涂粉末、涂层的微观结构和相组成。结果纳米涂层为微观双模结构,由部分熔化区和完全熔化区组成,存在裂纹、孔隙等缺陷,其主要物相为α-Al2O3,γ-Al2O3和rutile-TiO2。纳米涂层磨损失效的主要原因是内部板条的分层剥落和涂层表面材料的塑性变形切削。结论随着CPSP的增大,纳米涂层的耐磨性能增强,且高温磨损性能较室温磨损性能为差。纳米Al2O3-13%TiO2涂层微观结构中部分熔化区结构和纳米晶粒的存在显著提高了涂层的耐磨性。     

基于包混和复合添加工艺的多孔碳化硅陶瓷的制备和性能

采用包混工艺合成核-壳结构的硅-树脂先驱体粉体,引入Al2O3-SiO2-Y2O3复合添加剂,通过成型、炭化和烧结工艺制备多孔碳化硅陶瓷。分析多孔碳化硅陶瓷样品的物相、形貌、孔隙率、热导率、热膨胀系数和抗热震性能。结果表明：复合添加能够在较低的温度下制得多孔碳化硅陶瓷;陶瓷样品的晶粒较小,明显增强了多孔碳化硅陶瓷的导热性能;复合添加提高了碳化硅陶瓷的抗热震性能,添加Al2O3-SiO2-Y2O3并且在1650℃下烧结制备的多孔碳化硅陶瓷经过30次热震后的抗弯强度损失率为6.5%;陶瓷样品的孔壁更加光滑,孔分布更均匀;复合添加对多孔碳化硅陶瓷热膨胀系数的影响较小。     

用高岭土合成Sialon粉末的无压烧结

概述了Ｓｉａｌｏｎ陶瓷材料制备方面的研究。以高岭土为主要原料,采用碳热还原氮化法合成的Ｓｉａｌｏｎ粉末为主要原料,分别添加Ｙ２Ｏ３Ａｌ２Ｏ３系与Ａｌ２Ｏ３ＭｇＯ系两种烧结助剂后进行充分混合,混合物粉末在钢模中冷压成两种压坯试样ａ和ｂ,然后在Ｎ２气氛中进行无压烧结。对烧成温度与烧结体体积密度的关系,烧结助剂的作用以及Ｓｉａｌｏｎ粉末无压烧结致密化过程进行了重点讨论。实验结果表明,分别添加１０％Ｙ２Ｏ３５％Ａｌ２Ｏ３和１０％Ａｌ２Ｏ３５％ＭｇＯ（均为质量分数,％）两种烧结助剂的试样ａ和ｂ分别在１６２０℃和１５９０℃烧成温度下,获得了致密的Ｓｉａｌｏｎ陶瓷材料。并且建立了Ｓｉａｌｏｎ粉末无压烧结致密化模型,即ｌｇ（ΔＶ／Ｖ０）∝ｌｇｔ,其致密化过程分为颗粒重排与溶解析出两个阶段,且扩散为全过程的控制性步骤。     

CuO颗粒粒度对Al-CuO体系合成Al2O（3p）-Al复合材料反应温度和显微组织的影响

在80%Al-20%CuO（质量分数）体系中,通过原位反应法制备Al2O3p-Al复合材料。采用不同方法研究CuO颗粒粒度对复合材料合成温度和显微组织的影响。结果表明,Cu O颗粒粒度对Al-CuO体系的完全反应温度有显著影响：含有粒度小于6μm CuO颗粒样品的完全反应温度比含有粒度小于100μm CuO颗粒样品的完全反应温度低200°C。当反应温度低于某一临界值时,原位Al2O3颗粒和Al基体之间不能完全结合;当温度高于某一临界值时,原位Al2O3颗粒的形貌从棒状转变成近球形。这两个临界温度受Cu O颗粒粒度的影响：含有粒度小于6μm Cu O颗粒样品的临界温度比含有小于100μm CuO颗粒样品的临界温度低100℃。