Effect of PyC interface phase on the cyclic ablation resistance and flexural properties of two-dimensional Cf/HfC composites

Composites based on hafnium carbide and reinforced with continuous naked carbon fiber with and without PyC interface were prepared at low temperature by precursor infiltration and pyrolysis and chemical vapor deposition method. The microstructure, mechanical property, cyclic ablation and fiber bundle push-in tests of the composites were investigated. The results show that after three times ablation cycles, the bending strength of samples without PyC interface decreased by 63.6 %; the bending strength of samples with PyC interface only decreased by 37.8 %. The force displacement curve of the samples with PyC interface presented a well pseudoplastic deformation state. The mechanical behavior difference of two kinds of composites was due to crucial function of PyC interface phase including protection of fiber and weakening of fiber/matrix interface.     

Pricing and personal data collection strategies of online platforms in the face of privacy concerns

Electronic Commerce Research - We consider a platform providing free content for users and earning profit from the sale of advertising. The platform can collect and analyze personal data to...     

Revealing cracking and breakage behaviours of gibbsite particles

Mitigating gibbsite particle cracking and breakage during industrial alumina production can increase the quality of smelter grade alumina product by reducing the ultrafine particle content. Therefore, it is essential to investigate the particle cracking during static calcination and the breakage of calcined gibbsite particles under external force. In this work, we investigated the impact of the calcination ramping rate and the crystallite size on gibbsite particle cracking during static calcination. A slow ramping rate and a large pristine crystallite size tend to increase particle cracking. Apart from the study of particle cracking behaviour, we also investigated the breakage of calcined gibbsite particle under external force. Cracks on the particle surface can initiate breakage within the crystallite and along the grain boundary under external force. The breakage within crystallite occurs as the cleavage of the crystallite, while the breakage along the grain boundary leads to the shedding of a whole crystallite. We further explored the factors influencing the strength of calcined gibbsite particles. With increasing calcination temperature, the strength of particle increases when gibbsite converts to boehmite, and then decreases when boehmite converts into amorphous alumina. Particles containing smaller crystallites and calcined with fast ramping rates exhibit higher resistance to breakage.     

9000m顶部驱动钻井装置结构选型研究

为大幅提高钻井效率,针对9 000 m钻井深度对顶驱的设计要求,通过比较顶驱装置关键部分几种典型的结构,提出适合该型号顶部驱动钻井装置的最优结构形式,为后续9 000 m钻井深度顶部驱动钻井装置的研究提供指导和借鉴。     

Polyethylene oxide-polypropylene oxide -polyethylene oxide derived porous carbon materials with different molecular weights as ORR catalyst in alkaline electrolytes

Polyethylene oxide (PEO)-polypropylene oxide (PPO)-polyethylene oxide block copolymer having different molecular weights are used as precursors of carbon materials to prepare Hollow -Derivatives carbon material as an electrocatalyst through block copolymer self-assembly. The composition and microstructure of the prepared catalysts are shown by Raman spectroscopy, X-ray diffraction (XRD), Test of nitrogen adsorption and desorption curves, High resolution transmission electron microscopy (HR-TEM) and scanning electron microscopy (HR-SEM). Oxygen was passed into alkaline electrolyte solution until the solution reached saturation state. With molecular weight increasing, the obtained sample gradually changed from block to hollow and spherical. When the molecular weight was 12600 g mol^?1, the evenly hollow carbon nanocages was acquired (C-12600). In O₂ saturated alkaline electrolyte (0.1 M KOH solution), C-12600's limited current density，half-wave potential and initial potential are 5.23 mA cm^?2@0.4 V, 0.72 V and 0.81 V, respectively. And most important is that half-wave potential and onset potential have barely change after 2000 cycles of cyclic voltammetry. As a result, the porous carbon materials exhibited excellent electrocatalytic activity while maintaining high stability in alkaline KOH solution.