磨料有序排布电镀砂轮的制备及其把持力研究

为解决电镀砂轮磨削加工中容屑空间不足的问题，采用点胶微粘接的方法制备了磨料有序排布的电镀砂轮，分析了磨料粘接效果和镀层力学性能。通过SEM分析了磨料/镀层/导电胶的结合界面，并进行了干磨削试验。研究结果表明，直径约为磨料粒径40%的胶点可粘接住磨料，单个胶点上粘接多颗磨料的占比小于6%；双脉冲电镀工艺制备的镀层显微硬度大于500HV，表层残余应力小于100MPa，磨料/镀层/导电胶之间的界面贴合紧密，无明显缺陷；砂轮在磨削时没有出现磨料脱落现象。     

铜离子掺杂对高铁低钙水泥熟料性能的影响

基于C4AF可以提高水泥基材料的抗蚀性,以高铁低钙水泥熟料为研究对象,掺入不同含量的CuO,通过对熟料及其水化产物进行X射线衍射(XRD)、水化热、抗压强度、非蒸发水含量和固化氯离子能力等测试,探究Cu2+对高铁低钙水泥熟料水化性能与氯离子吸附固化能力的影响.结果发现,适量CuO的掺入促进了高铁低钙水泥熟料中C4AF的生成,降低了熟料液相的粘度,有利于C3S的晶粒生长,有利于提高高铁低钙水泥熟料的水化活性和固化氯离子能力,最佳掺量为0.2 wt％.     

Highly active sites of low spin FeⅡN4species:The identification and the ORR performance

Over recent years,catalytic materials of Fe-N-C species have been recognized being active for oxygen reduction reaction(ORR).However,the identification of active site remains challenging as it generally involves a pyrolysis process and mixed components being obtained.Herein Fe₃C/C and Fe₂N/C samples were synthesized by temperature programmed reduction of Fe precursors in 15%CH₄/H₂and pure NH₃,respectively.By acid leaching of Fe₂N/C sample,only single sites of FeN₄species were presented,providing an ideal model for identification of catalytic functions of the single sites of FeN₄in ORR.A correlation was conducted between the concentration of Fe^ⅡN₄in low spin state by Mossbauer spectra and the kinetic current density at 0.8 V in alkaline media,and such a structure-performance correlation assures the catalytic roles of low spin Fe^ⅡN₄ species as highly active sites for the ORR.     

The formation of fibrous structure of polyamide 6 induced by the three-step forming process and its prominent reinforcement in nitrile rubber

Nitrile rubber (NBR) blends with excellent performance have always been a hot research topic in petroleum field. Due to the excellent performance and compatibility of polyamide 6 (PA6), it provides an opportunity for the preparation of high-performance NBR/PA6 blends. In this article, NBR/PA6 blends were prepared by the three-step molding process. Experimentally, it was found that PA6 has a prominent reinforcement effect in NBR matrix. The variation of this mechanical property was investigated from different aspects of the crystal structure, crystallinities, phase morphology, and so on. It can be cleared that the formation of fibrous structure of PA6 phase is the main factor for reinforcement of the polymer blends. Meanwhile, the formation mechanism of the special phase structure induced by the three-step process is deeply expounded and its structural evolution schematic is established. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47472.     

Evaluation of bismuth doped La2-xBixNiO4+δ (x = 0, 0.02 and 0.04) as cathode materials for solid oxide fuel cells

Bismuth doped La_2-xBi_xNiO_4+δ (x = 0, 0.02 and 0.04) oxides are investigated as SOFC cathodes. The effects of Bi doping on the phase structure, thermal expansion, electrical conduction behavior as well as electrochemical performance are studied. All the samples exist as a tetragonal Ruddlesden-Popper structure. Bi-doped LBNO-0.02 and LBNO-0.04 have good chemical and thermal compatibility with LSGM electrolyte. The average TEC over 20–900°С was 13.4 × 10^?6 and 14.2 × 10^?6 K^?1 for LBNO-0.02 and LBNO-0.04, respectively. The electrical conductivity was decreasing with the rise of Bi doping content. EIS measurement indicates Bi doping can decrease the ASR values. At 750 °C, the obtained ASR for LBNO-0.04 is 0.18 Ωcm², which is 56% lower than that of the sample without Bi doping, suggesting Bi doping is beneficial to the electrochemical catalytic activity of LBNO cathodes.     

Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.     

Amine-containing olefin copolymer with CO2-switchable oil absorption and desorption

Global decrease in crude oil resources and frequent crude oil leaks cause the energy crisis and ecological pollution. The absorption and release of leaked crude oil through absorption materials are a necessary process for environmental protection and recycling. In this article, a CO₂-responsive olefin copolymer was obtained by copolymerization of styrene and an amine-containing olefin monomer. The structure of resultant copolymer was characterized by FTIR; thermal properties and CO₂-responsive morphology changes were determined by DSC/TGA and SEM, respectively. Copolymers had certain absorption capacity for toluene with absorption rate up to 180.0%. The absorbed toluene could be released upon CO₂ stimulation with desorption rate up to 84.6%. The CO₂-responsive copolymer could be regenerated through a simple heating process and showed stable absorption–desorption performance even after being recycled for 4 times. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47439.