Fabrication of barium titanate ceramics via digital light processing 3D printing by using high refractive index monomer

A digital light processing (DLP) technology has been developed for 3D printing lead-free barium titanate (BTO) piezoelectric ceramics. By comparing the curing and rheological properties of slurries with different photosensitive monomer, a high refractive index monomer acryloyl morpholine (ACMO) was chosen, and a design and preparation method of BTO slurry with high solid content, low viscosity and high curing ability was proposed. By further selecting the printing parameters, the single-layer exposure time was reduced and the forming efficiency has been greatly improved. Sintered specimens were obtained after a nitrogen-air double-step debinding and furnace sintering process, and the BTO ceramics fabricated with 80 wt% slurry shows the highest relative density (95.32 %) and piezoelectric constant (168.1 pC/N). Furthermore, complex-structured BTO ceramics were prepared, impregnated by epoxy resin and finally assembly made into hydrophones, which has significance for the future design and manufacture of piezoelectric ceramic-based composites that used in functional devices.     

High-temperature oxidation behavior of monolithic Zr3[Al(Si)]4C6 and its composite incorporating 30vol% ZrB2-SiC: Providing a basis for broadening the service temperature

To provide a basis for the high-temperature oxidation of ultra-high temperature ceramics (UHTCs), the oxidation behavior of Zr₃[Al(Si)]₄C₆ and a novel Zr₃[Al(Si)]₄C₆-ZrB₂-SiC composite at 1500 °C were investigated for the first time. From the calculation results, the oxidation kinetics of the two specimens follow the oxidation dynamic parabolic law. Zr₃[Al(Si)]₄C₆ exhibited a thinner oxide scale and lower oxidation rate than those of the composite under the same conditions. The oxide scale of Zr₃[Al(Si)]₄C₆ exhibited a two-layer structure, while that of the composite exhibited a three-layer structure. Owing to the volatilization of B₂O₃ and the active oxidation of SiC, a porous oxide layer formed in the oxide scale of the composite, resulting in the degradation of its oxidation performance. Furthermore, the cracks and defects in the oxide scale of the composite indicate that the reliability of the oxide scale was poor. The results support the service temperature of the obtained ceramics.     

A cheating immune (k, n) visual cryptography scheme by using the rotation of shares

Multimedia Tools and Applications - Since Noar and Shamir introduced visual cryptography scheme (VCS), the cheating problem of VCS has absorbed much attention of scholars. The current researches on...     

掺钪AlN材料特性及HBAR器件性能研究

该文基于掺钪AlN薄膜制备了高次谐波体声波谐振器(HBAR),研究了钪(Sc)掺杂浓度对AlN压电薄膜材料特性及器件性能的影响。研究表明,当掺入Sc的摩尔分数从0增加到25%时,压电应力系数e₃₃增加、刚度 下降,导致Al₁-_xSc_xN压电薄膜的机电耦合系数 从5.6%提升至15.8%,从而使HBAR器件的有效机电耦合系数 提升了3倍。同时,当Sc掺杂摩尔分数达25%时,Al₁-_xSc_xN(x为Sc掺杂摩尔分数)压电薄膜的声速下降13%,声学损耗提高,导致HBAR器件的谐振频率和品质因数降低。     

Facile synthesis of MgO–Mg2SiO4 composite ceramics with high strength and low thermal conductivity

The recycling of solid waste is a win-win solution for humans and nature. For this purpose, magnesite tailings and silicon kerf waste were employed to prepare MgO–Mg₂SiO₄ composite ceramics by solid-state reaction synthesis in the present work. Then, effects of sintering temperature and raw material ratio on as-prepared ceramics were systematically studied. As-prepared ceramics showed improvement in their relative density (from 47.55%–68.12% to 90.96%–95.25%) and cold compressive strength (from 7.34–118.66 MPa to 303.39–546.65 MPa) with the increase in sintering temperature from 1300 to 1600 °C. In addition, it was found that Si promoted synthesis process of Mg₂SiO₄ phase through transient liquid phase sintering and Fe₂O₃ accelerated sintering process through activation sintering. Consequently, the presence of Mg₂SiO₄ phase effectively improved the density and strength of MgO–Mg₂SiO₄ composite ceramic, while reducing its thermal conductivity. This work provides a potential reutilization strategy for magnesite tailings, and as-prepared products are expected to be applied in fields of construction, metallurgy, and chemical industry.     

Effects of (Li0.5Sm0.5)/W co-substitution and sintering temperature on the structure and electrical properties of ultrahigh Curie temperature piezoceramics,Ca0.92(Li0.5Sm0.5)0.08Bi2Nb2-xWxO9

With co-substitution of (Li_0.5Sm_0.5) at A site and W at B site, the electrical properties of modified Ca_0.92(Li_0.5Sm_0.5)_0.08Bi₂Nb_2-xW_xO₉ [(CLS)BN-xW, x = 0, 0.015 and 0.03] piezoceramics with ultrahigh Curie temperature (T_C) of > 930 °C were enhanced dramatically. The increased resistivity induced by the co-substitution ensure them to be polarized under an enough high field. Combined with the increase of spontaneous ferroelectric polarization (P_S), the significant enhancements in the piezoelectric, dielectric and ferroelectric properties can be obtained in the composition x = 0.015. Furthermore, the piezoelectric activity (d₃₃) and bulk resistivity (ρ_b) of (CLS)BN-0.015 W can be further enhanced at an appropriate sintering temperature. This optimum composition sintered at 1170 °C shows ultrahigh T_C of ～948 °C, d₃₃ of ～17.3 pC/N and ρ_b of ～6.9 MΩ cm at 600 °C, which are comparable to those of the reported high-temperature Aurivillius piezoceramics with T_C > 850 °C.     

Microstructure and electric properties of Pr-doped Pb(Zr0.52Ti0.48)O3 ceramics

Improving the piezoelectric activity of lead zirconate titanate (PZT) ceramics is of great importance for practical applications. In this study, the influence of Pr³⁺ doping on the ferroelectric phase composition, microstructure, and electric properties on the A-site of (Pb_1-1.5xPr_x)(Zr_0.52Ti_0.48)O₃ is extensively investigated. A dense and fine microstructural sample is obtained with the introduction of Pr³⁺. The results show that the morphotropic phase boundary (MPB) moves to the rhombohedral phase region. The rhombohedral and tetragonal phases exhibit an ideal coexistence in the 4 mol.% Pr³⁺ doped (PPZT4) samples. Lead vacancy and the reduction of the potential energy barrier are considered to be the key mechanisms for donor doping, which is upheld by the Pr³⁺ doping. Combining the I-E hysteresis loops with the P-E hysteresis loops, it becomes apparent that both contribution maximums of the domain switching and residual polarisation are in PPZT4. Moreover, the thermal aging resistance of PZT is improved by doping, and the temperature stability is optimised from 83% in PZT to 96% in PPZT4. Hence, an appropriate amount of Pr³⁺ doping can effectively improve the piezoelectric activity of PZT ceramics in the MPB area and optimise the performance stability of the material under application temperatures.     

Rheological phase reaction synthesis and electrochemical performance of LiFe2/3Mn1/3PO4/C cathode for lithium-ion batteries

LiFe_2/3Mn_1/3PO₄/C composite was prepared by the rheological phase reaction using LiH₂PO₄, Li₂CO₃, FePO₄, Mn(Ac)₂·4H₂O and ascorbic acid as starting materials. The crystal structure and morphology of as-synthesized sample were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The analysis of XRD results showed that the obtained sample was single-phase with orthorhombic olivine-type structure (Pnma space group). SEM micrographs revealed that the sample was aggregates, with an irregular morphology. The initial discharge capacity was 166.9, 149.1, 139.6, 112.8, 82.93 mAh g^??1 at the rate of 0.1, 0.5, 1, 2, and 10 C, respectively. And when the rate was 0.1, 0.5, 1, 2, and 10 C, the capacity retention was 92.2%, 90%, 92.9%, 97.6%, 91.5% after 50, 100, 200, 200, 500 cycles, respectively.