Garzan oil field is located at the south east of Turkey. It is a mature oil field and the reservoir is fractured carbonate reservoir. After producing about 1% original oil in place (OOIP) reservoir pressure started to decline. Waterflooding was started in order to support reservoir pressure and also to enhance oil production in 1960. Waterflooding improved the oil recovery but after years of flooding water breakthrough at the production wells was observed. This increased the water/oil ratio at the production wells. In order to enhance oil recovery again different techniques were investigated. Chemical enhanced oil recovery (EOR) methods are gaining attention all over the world for oil recovery. Surfactant injection is an effective way for interfacial tension (IFT) reduction and wettability reversal. In this study, 31 different types of chemicals were studied to specify the effects on oil production. This paper presents solubility of surfactants in brine, IFT and contact angle measurements, imbibition tests, and lastly core flooding experiments. Most of the chemicals were incompatible with Garzan formation water, which has high divalent ion concentration. In this case, the usage of 2-propanol as co-surfactant yielded successful results for stability of the selected chemical solutions. The results of the wettability test indicated that both tested cationic and anionic surfactants altered the wettability of the carbonate rock from oil-wet to intermediate-wet. The maximum oil recovery by imbibition test was reached when core was exposed 1-ethly ionic liquid after imbibition in formation water. Also, after core flooding test, it is concluded that considerable amount of oil can be recovered from Garzan reservoir by waterflooding alone if adverse effects of natural fractures could be eliminated.     

Modulation of electrical transport in calcium cobaltite ceramics and thick films through microstructure control and doping

Ca₃Co₄O₉ is a promising p-type thermoelectric oxide material having intrinsically low thermal conductivity. With low cost and opportunities for automatic large scale production, thick film technologies offer considerable potential for a new generation of micro-sized thermoelectric coolers or generators. Here, based on the chemical composition optimized by traditional solid state reaction for bulk samples, we present a viable approach to modulating the electrical transport properties of screen-printed calcium cobaltite thick films through control of the microstructural evolution by optimized heat-treatment. XRD and TEM analysis confirmed the formation of high-quality calcium cobaltite grains. By creating 2.0 at% cobalt deficiency in Ca_2.7Bi_0.3Co₄O_9+δ, the pressureless sintered ceramics reached the highest power factor of 98.0 μWm^?1 K^-2 at 823 K, through enhancement of electrical conductivity by reduction of poorly conducting secondary phases. Subsequently, textured thick films of Ca_2.7Bi_0.3Co_3.92O_9+δ were efficiently tailored by controlling the sintering temperature and holding time. Optimized Ca_2.7Bi_0.3Co_3.92O_9+δ thick films sintered at 1203 K for 8 h exhibited the maximum power factor of 55.5 μWm^?1 K^-2 at 673 K through microstructure control.     

Diluted chemical bath deposition of CdZnS as prospective buffer layer in CIGS solar cell

In this study, dilute chemical bath deposition technique has been used to deposit CdZnS thin films on soda-lime glass substrates. The structural, morphological, optoelectronic properties of as-grown films have been investigated as a function of different Zn²⁺ precursor concentrations. The X-ray diffractogram of CdS thin-film reveals a peak corresponding to (002) plane with wurtzite structure, and the peak shift has been observed with the increase of the Zn²⁺ concentration upon formation of CdZnS thin film. From morphological studies, it has been revealed that the diluted chemical bath deposition technique provides homogeneous distribution of film on the substrate even at a lower concentration of Zn²⁺. Optical characterization has shown that the transparency of the film is influenced by Zn²⁺ concentration and when the Zn²⁺ concentration is varied from 0 M to 0.0256 M, bandgap values of resulting films range from 2.42 eV to 3.90 eV while. Furthermore, electrical properties have shown that with increasing zinc concentration the resistivity of the film increases. Finally, numerical simulation validates and suggests that CdZnS buffer layer with composition of 0.0032 M Zn²⁺ concentration would be a promising candidate in CIGS solar cell.     

近源成藏——来自鄂尔多斯盆地延长组湖盆东部“边缘”延长组6段原油的地球化学证据

延安以东和以北的鄂尔多斯盆地东北部地区曾被认为位处三叠纪延长组7段（长7段）沉积期古湖盆的"边缘"，一些学者认为该区延长组烃源岩不发育，因而其油藏原油系湖盆中心生成的原油经长距离侧向运移而来；但也有研究认为，包括盆地边缘在内的整个鄂尔多斯盆地致密油藏均为近源成藏。为明确盆地东部地区延长组原油来源，对三叠纪湖盆"东缘"七里村油田的主力油层延长组6段（长6段）原油开展了原油地球化学和油源对比研究。七里村油田长6段原油具有高饱和烃、高饱芳比、低非烃和低沥青质的特征，正构烷烃呈前高单峰型，主峰碳为C₁₉，生物标志化合物分析显示长6段原油为同源成熟原油，生油母质以藻类等低等水生生物为主，混有陆源高等植物，母源沉积环境为偏还原性的淡水湖泊。七里村油田长6段原油与本地区长7段黑色泥页岩和暗色泥岩2种烃源岩均具有明显亲缘关系，而与志丹、富县等湖盆中心地区的长7段烃源岩在族组成、生物标志化合物和稳定碳同位素特征上均存在明显区别。综合分析认为七里村油田长6段原油并非湖盆中心长7段优质烃源岩所生油气经长距离运移而来，而主要为原位长7段烃源岩生成的原油经垂向运移和短距离侧向运移在长6段等储层中聚集成藏，属于近源成藏。     

Large domain-wall currents in epitaxial Au/BiFeO3/SrRuO3 thin-film capacitors with modulated oxygen vacancy and wall densities

Large domain wall (DW) conductivity in an insulating ferroelectric plays an important role in the future nanosensors and nonvolatile memories. However, the wall current was usually too small to drive high-speed memory circuits and other agile nanodevices requiring high output-powers. Here, a large domain-wall current of 67.8 μA in a high on/off ratio of ~4460 was observed in an epitaxial Au/BiFeO₃/SrRuO₃ thin-film capacitor with the minimized oxygen vacancy concentration. The studies from read current-write voltage hysteresis loops and piezo-response force microscope images consistently showed remaining of partially unswitched domains after application of an opposite poling voltage that increased domain wall density and wall current greatly. A theoretical model was proposed to explain the large wall current. According to this model, the domain reversal occurs with the appearance of head-to-head and tail-to-tail 180° domain walls (DWs), resulting in the formation of highly conductive wall paths. As the applied voltage increased, the domain-wall number increased to enhance the on-state current, in agreement with the measurements of current-voltage curves. This work paves a way to modulate DW currents within epitaxial Au/BiFeO₃/SrRuO₃ thin-film capacitors through the optimization of both oxygen vacancy and domain wall densities to achieve large output powers of modern domain-wall nanodevices.     

Photophysical investigation of the formation of defect levels in P doped ZnO thin films

Zinc oxide (ZnO) offers a major disadvantage of asymmetry doping in terms of reliability, stability, and reproducibility of p-type doping, which is the main hindrance in realization of optoelectronic devices. The problem is even more complicated due to formation of various native defects in unintentionally doped n-type ZnO. The realization of p-type conductivity in doped ZnO requires an in-depth understanding of the formation of an effective shallow acceptor, as well as donor-acceptor compensation. Photophysical properties such as photoconductivity along with photoluminescence (PL) studies have unprecedentedly and effectively been utilized in this work to monitor the evolution of various in-gap defects. Phosphorus (P) doped ZnO thin films have been grown by RF magnetron sputtering under various Ar to O₂ gas ratios to investigate the effect of O₂ on the donor-acceptor compensation by comprehensive photoconductivity measurements supported by the PL studies. Initial elemental analyses indicate presence of abundant zinc vacancies (V_Zn) in O-rich ambience. The results predict that P sits in the zinc (Zn) site rather than the oxygen (O) site causing the formation of P_Zn–2V_Zn acceptor-like defects, which compensates the donor defects in P doped ZnO films. Photocurrent spectra uniquely reveal presence of more oxygen vacancies (V_O) defects states in lower O₂ flow, which gets compensated with an increase in the O₂ flow. Successive photocurrent transients indicate probable presence of more V_O in the films grown with lower O₂ flow and more V_Zn in higher O₂ flow. Overall the photosensitivity measurements clearly present that O-rich ambience expedites the formation of acceptor defects which are compensated, thereby lowering the dark current and enhancing the ultraviolet photosensitivity.     

Agronomic performance of high oleic,low linolenic soybean in Tennessee

Soybean oil hydrogenation alters the linolenic acid molecule to prevent the oil from becoming rancid, however, health reports have indicated trans-fat caused by hydrogenation, is not generally regarded as safe. Typical soybeans contain approximately 80 g kg⁻¹ to 120 g kg⁻¹ linolenic acid and 240 g kg⁻¹ of oleic acid. In an effort to accommodate the need for high-quality oil, the United Soybean Board introduced an industry standard for a high oleic acid greater than 750 g kg⁻¹ and linolenic acid less than 30 g kg⁻¹ oil. By combing mutations in the soybean plant at four loci, FAD2-1A and FAD2-1B, oleate desaturase genes and FAD3A and FAD3C, linoleate desaturase genes, and seed oil will not require hydrogenation to prevent oxidation and produce high-quality oil. In 2017 and 2018, a study comparing four near-isogenic lines across multiple Tennessee locations was performed to identify agronomic traits associated with mutations in FAD3A and FAD3C loci, while holding FAD2-1A and FAD2-1B constant in the mutant (high oleic) state. Soybean lines were assessed for yield and oil quality based on mutations at FAD2-1 and FAD3 loci. Variations of wild-type and mutant genotypes were compared at FAD3A and FAD3C loci. Analysis using a generalized linear mixed model in SAS 9.4, indicated no yield drag or other negative agronomic traits associated with the high oleic and low linolenic acid genotype. All four mutations of fad2-1A, fad2-1B, fad3A, and fad3C were determined as necessary to produce a soybean with the new industry standard (>750 g kg⁻¹ oleic and <30 g kg⁻¹ linolenic acid) in a maturity group-IV-Late cultivar for Tennessee growers.