The PbCl_xS_1-x and Pb_1-xBi_xS (x? =?0–0.05) bulks were fabricated with a facile method of hydrothermal synthesis and microwave sintering, and the effect of anionic and cationic donors on the thermoelectric performance of PbS was investigated. Although Cl^? and Bi³⁺ both effectively improved the thermoelectric properties of n-type PbS, more excellent thermoelectric performance was obtained from Cl^? doped samples because of higher electrical property and lower thermal conductivity at higher temperature (T? >?600?K). The thermoelectric figure of merit (ZT) reaches 1.04 for PbCl_0.015S_0.985 at 800?K and increases with temperature increasing without sign of saturation, which is probably the highest value ever reported for single-phase polycrystalline n-type PbS. The results also indicate that the hydrothermal synthesis and microwave sintering can realize anion doping as well as cation doping for n-type PbS at low cost, and PbS should be a robust alternative for PbTe thermoelectric materials.     

Microstructures and mechanical properties of B4C-TiB2-SiC composites fabricated by ball milling and hot pressing

B₄C-TiB₂-SiC composites were fabricated via hot pressing using ball milled B₄C, TiB₂, and SiC powder mixtures as the starting materials. The impact of ball milling on the densification behaviors, mechanical properties, and microstructures of the ceramic composites were investigated. The results showed that the refinement of the powder mixtures and the removal of the oxide impurities played an important role in the improvement of densification and properties. Moreover, the formation of the liquid phases during the sintering was deemed beneficial for densification. The typical values of relative density, hardness, bending strength, and fracture toughness of the composites reached 99.20%, 32.84?GPa, 858?MPa and 8.21?MPa?m^1/2, respectively. Crack deflection, crack bridging, crack branching, and microcracking were considered to be the potential toughening mechanisms in the composites. Furthermore, numerous nano-sized intergranular/intragranular phases and twin structures were observed in the B₄C-TiB₂-SiC composite.     

钛基Ce掺杂SnO_2-RuO_2电极的制备及其对焦化废水的电解处理

采用溶胶-凝胶法制备了经稀土元素Ce掺杂改性的Ti/RuO_2-SnO_2-Ce电极,利用SEM、XRD、EDS等分析方法对电极表面的形貌、物相和涂层成分进行了表征,利用CV曲线、LSV曲线等检测手段对电极的电化学性能进行了测试。以Ti/RuO_2-SnO_2-Ce电极为阳极,钛板为阴极,构建电化学氧化反应装置,并采用其对焦化废水进行电解处理。结果表明,Ti/RuO_2-SnO_2电极经稀土Ce改性后极板表面活性位点数量明显增大,金属涂层的结晶化程度明显增强,电极的催化氧化活性显著提高。室温条件下,保持pH值为7.83,在电流密度为30mA/cm~2,电解时间为30min时,焦化废水经电解处理后COD去除率可达91.63%,TOC去除率可达66.22%,UV254值下降到0.921。     

600MW超临界CFB机组深度调峰运行技术

经通过分析超临界CFB机组在深度调峰方面的优势,结合600MW超临界CFB机组的实际运行工况,提出机组在深度调峰前应开展的试验工作。研究600MW超临界CFB机组的深度调峰过程,从汽机、锅炉、电气等方面提出有效的技术措施,解决深度调峰可能带来的锅炉流化不良、环保参数控制困难等问题。通过在600MW超临界CFB机组上应用,机组在30%负荷深度调峰运行,工况稳定,各项参数正常,取得了较好效果。     

潮流能水平轴水轮机在剪切来流下的水动力分析

采用基于计算流体力学方法的全尺度数值模拟计算,建立了适用于潮流能水轮机模拟的剪切来流环境,通过数值计算结果,对潮流能水轮机随时间变化的宏观力和流场特征进行了系统分析,探索水轮机在复杂工况下的水动力特性规律。结果表明,水轮机整个叶轮的总体平均受力在剪切流工况中未受到明显影响; 单个叶片的瞬态轴向力系数和瞬态轴向扭矩系数在旋转周期内出现了明显的周期性变化,且周期性变化幅值随转速增大而增大; 非定常的瞬时轴向扭矩和力的周期性振荡容易引起单个叶片的结构性振动,可能对水轮机的机械结构造成影响。     

某低品位铜铅锌多金属硫化矿选矿工艺研究

某低品位铜铅锌多金属硫化矿的原矿品位分别为Cu 0.47%、Pb 1.236%和Zn 0.891%。矿石中铜铅锌有用矿物的嵌布粒度较细且共生关系较复杂。试验着重探讨了磨矿细度、浮选捕收剂和调整剂的优化,在解决矿物有效解离的前提下,提高铜铅锌浮选分离的选择性。当原矿磨矿细度为-0.074mm占80%时,采用乙硫氮作捕收剂,石灰、硫酸锌和亚硫酸钠作调整剂,粗选获得的铜铅混合粗精矿再磨至-0.043mm占81.31%后,经两次精选获得铜铅混合精矿。铜铅混合精矿采用活性炭脱药,亚硫酸钠和CMC组合抑铅,Z200浮选铜,实现了铜铅分离。铜铅混合浮选尾矿,采用硫酸铜活化,丁基黄药作捕收剂,浮选获得锌精矿。最终浮选指标为:铜精矿的铜品位27.26%,铜回收率80.62%;铅精矿的铅品位59.35%,铅回收率85.20%;锌精矿的锌品位41.14%,锌回收率为82.74%。为该低品位铜铅锌多金属硫化矿资源的开发利用提供了可行的技术方案。     

Single copper sites dispersed on hierarchically porous carbon for improving oxygen reduction reaction towards zinc-air battery

The demand for high-performance non-precious-metal electrocatalysts to replace the noble metal-based catalysts for oxygen reduction reaction(ORR)is intensively increasing.Herein,single-atomic copper sites supported on N-doped three-dimensional hierarchically porous carbon catalyst(Cu₁/NC)was prepared by coordination pyrolysis strategy.Remarkably,the Cu₁/NC-900 catalyst not only exhibits excellent ORR performance with a half-wave potential of 0.894 V(vs.RHE)in alkaline media,outperforming those of commercial Pt/C(0.851 V)and Cu nanoparticles anchored on N-doped porous carbon(CuNPs/NC-900),but also demonstrates high stability and methanol tolerance.Moreover,the Cu₁/NC-900 based Zn-air battery exhibits higher power density,rechargeability and cyclic stability than the one based on Pt/C.Both experimental and theoretical investigations demonstrated that the excellent performance of the as-obtained Cu₁/NC-900 could be attributed to the synergistic effect between copper coordinated by three N atoms active sites and the neighbouring carbon defect,resulting in elevated Cu d-band centers of Cu atoms and facilitating intermediate desorption for ORR process.This study may lead towards the development of highly efficient non-noble metal catalysts for applications in electrochemical energy conversion.     

饱和尾粉砂动孔隙水压力发展特性试验研究

采用动三轴仪对内蒙古某尾矿库尾粉砂进行了动强度试验,研究了围压、相对密实度及固结比对动荷载作用下尾粉砂中孔隙水压力发展特性的影响。研究结果表明,随着固结比、相对密实度、围压的增大,动荷载作用下饱和尾粉砂孔压增长曲线形状由陡峭转变为平缓。随着围压及固结比增大,试样动力破坏形式从以孔压值为主要表征指标的液化破坏,转化为以动剪应变为主要破坏形式的软化破坏。动荷载作用下发生液化破坏的饱和尾粉砂孔压增长过程分可为初始增长阶段、稳定增长阶段和快速增长至破坏阶段,孔压增长曲线表现为明显的反S型,本文采用双对数函数对该试验孔压增长曲线进行拟合,结果表明该模型可以较好地模拟尾粉砂在动荷载作用下的孔压发展规律。     

改善硫精矿浓密机溢流跑浑试验研究

本文旨在改善某选厂硫精矿浓密机溢流跑浑问题,对生产现场进行勘察和分析,分析浓密机溢流跑浑的原因,并开展原矿配比和沉降试验研究。对采场原矿矿样和硫精矿矿浆进行系统的试验研究,分别采用不同沉降方案进行条件试验,考察絮凝剂种类、絮凝剂用量、pH调整剂用量、不同药剂之间的配比等条件对沉降的影响,确定合适的原矿配比及合理药剂制度,有效地控制金属在溢流中的损失,充分获取现有产品的蕴含价值。