Hydraulic fracturing with slickwater is a field-proven stimulation technology used in tight reservoirs. Because of the high pumping rate associated with slickwater fracturing, drag reduction (DR) is critical in minimizing pressure drop and the success of oilfield operations. In this paper, a new type of drag reducer (SPR) was synthesized with acrylamide and 12-allyloxydodecyl acid sodium, and its drag reduction performance was evaluated. The results showed that the new drag reducer features low molecular weight, fast-dissolving rate and low interfacial tension. The algorithm of estimating the drag reduction rate of non-Newtonian fluid SPR was proposed and validated. Empirical or semianalytical models for estimating the friction ratio (σ) or friction factor (λ or f) were used to simulate the turbulence behavior of the SPR drag reducer under different Reynolds numbers (Re). The modified Virk's correlation could accurately model the turbulent behavior of the SPR drag reducer. A unified calculation formula was established in this study for different pipe diameters.     

煤矸石粉/聚酯纤维沥青混合料盐冻损伤研究EI北大核心CSCD

针对煤矸石粉替代率50%、聚酯纤维掺量0.4%的沥青混合料,开展盐冻耦合作用(NaCl溶液质量分数为0%、7.0%、13.0%、26.5%,冻融循环次数为0、2、4、6、8)下的半圆弯曲(SCB)试验,分析了盐冻耦合作用对SCB试件内部损伤劣化过程的影响.结果表明:NaCl溶液质量分数为13.0%、冻融循环为8次时,盐冻耦合作用对沥青混合料的侵蚀破坏作用最强,试件内部损伤最严重;在煤矸石粉与矿粉质量比为1∶1、聚酯纤维掺量为0.4%的条件下,沥青混合料能够形成高黏性、致密、厚实的沥青膜以及由纤维形成的三维网状结构,从而显著降低盐冻侵蚀对沥青混合料的损伤.通过Poly2D模型对SCB试件的极限拉应力损伤量进行拟合,拟合系数为0.944.     

Optical design of the Lyman alpha based beam emission spectroscopy(LAB)diagnostic on the HL-2A tokamak

In this article, we present the optical design of a novel diagnostic on the HL-2 A tokamak, i.e. the20-channel edge Lyman-alpha beam emission spectroscopy, which is a promising solution for edge density turbulence research on tokamaks, as it offers the possibility of density fluctuation measurement with a 3.3 mm spatial resolution while maintains a high temporal resolution of1 μs. The optical path, including the reflective collection optics, the high-dispersion spectrometer, and the linear detector array, is carefully optimized to obtain a good image quality and a high throughput. The maximum root mean square radius of the collection optics is 64 μm.The detected photon flux is estimated to be about 10~(11) photons/s/channel.     

基于跨临界CO2热泵的茶叶生产能源系统负荷削减潜力

乡村产业中的化石能源设备逐渐被电能技术替代，引起了乡村负荷波动增大、部分时段产生集中高负荷的问题。为了解决以上问题，将低品位清洁能源应用至乡村的茶叶生产中，针对烘茶全过程的工艺要求提出了跨临界CO₂热泵烘茶技术；并以某茶叶生产乡村为对象，对其代表台区的全年日用电量及产茶日负荷进行了分析，得出采用CO₂热泵烘茶后其负荷得到大幅度削减，整体可降低至原负荷的39.6%~46.8%，峰值负荷与平时负荷的比值由原本的13.6降至5.4~6.2。跨临界CO₂热泵应用至农产品生产中可有效缓解乡村供电压力。     

矢量语音传感器微阵列

人工智能的普及促进了语音交互技术的发展,语音传感器阵列作为智能语音交互的硬件前端,成为语音交互领域的前沿研究方向.矢量语音传声器自有的偶极子指向性、零点深度以及阵列体积小便于集成的特点特别符合语音交互技术对硬件设备的要求.基于此,通过采用两组矢量敏感单元"共点正交"形成矢量微阵列实现声源空间锐化波束指向,其不受瑞利限与空间采样率限制,与传统空间离散分布的声压麦克风阵列有着本质区别,是矢量微阵列的核心优势所在.矢量微阵列传声器弥补了现有双麦阵列的不足,具有更为广阔的应用前景,作为智能语音交互的硬件前端,对推动智能语音交互领域的发展具有重要意义.     

Effect of PyC interface phase on the cyclic ablation resistance and flexural properties of two-dimensional Cf/HfC composites

Composites based on hafnium carbide and reinforced with continuous naked carbon fiber with and without PyC interface were prepared at low temperature by precursor infiltration and pyrolysis and chemical vapor deposition method. The microstructure, mechanical property, cyclic ablation and fiber bundle push-in tests of the composites were investigated. The results show that after three times ablation cycles, the bending strength of samples without PyC interface decreased by 63.6 %; the bending strength of samples with PyC interface only decreased by 37.8 %. The force displacement curve of the samples with PyC interface presented a well pseudoplastic deformation state. The mechanical behavior difference of two kinds of composites was due to crucial function of PyC interface phase including protection of fiber and weakening of fiber/matrix interface.     

“电工学”国家级一流课程建设与实践

根据新时代新工科人才需求特点和电工学课程特点,分析非电专业学生的电类实践需求,提出构建电工学课程为核心的电工电子实践创新能力培养新体系。通过优化教学内容、开展教学模式和考核模式改革、构建教学资源体系和进行教师队伍建设,使我校电工学课程教学质量提升、学生工程实践和创新能力提高、学生满意度增加、一流课程建设成效显著。     

The effect of alkali metal oxide on the properties of borosilicate fireproof glass: Structure,thermal properties,viscosity, chemical stability

The purpose of the current work was to research the effect of alkali metal oxide on the structure, thermal properties, viscosity and chemical stability in the glass system (R₂O–CaO–B₂O₃–SiO₂) systematically. Because the glass would emulsify when Li₂O was added to the glass batch, this article did not discuss Li₂O. The results showed that when the amount of Na₂O was less than 4 mol.%, there was a higher interconnectivity of borate and silicate sub-networks in glass, as more mixed Si–O–B bonds were present in glass. The glass samples exhibited excellent thermal properties and chemical stabilities. As the amount of Na₂O exceeded 4 mol.%, the interconnectivity of borate and silicate sub-networks was weakened. The thermal properties and chemical stabilities of the glass samples were reduced. The connectivity of the silicate sub-network was weakened slightly as the Na/K ratio varied, and the coefficient of thermal expansion (CTE) of the glass samples gradually increased, and the resistance to thermal shock (RTS) value gradually decreased. Moreover, the viscosity of the glass samples decreased with the ratio of Na/Si and Na/K increased.     

成型温度对PBX装药内部质量及性能的影响

针对压制成型的PBX炸药装药，选择CT无损检测、巴西实验和扫描电镜检测等技术，对比研究了室温和加热两种温度下压制成型的炸药装药内部质量、静态力学性能和细观破坏形式。结果表明，加热压制有利于改善炸药装药的内部质量，可避免产生初始损伤，且提高了装药的力学性能。细观尺度上，室温压制成型的装药主要发生界面脱黏破坏，加热压制成型装药的主要破坏形式是穿晶断裂。