离子液体改性花生壳对铬离子的吸附行为与机制

研究了用离子液体改性花生壳,并考察了改性花生壳对Cr(Ⅵ)的吸附行为与机制.结果表明:在改性花生壳用量10 g/L、温度50℃、初始Cr(Ⅵ)质量浓度10 mg/L条件下,改性花生壳对Cr(Ⅵ)的吸附率达99.82％;吸附过程符合Langmuir等温吸附模型,为单分子层吸附,吸附发生在均匀的吸附点位上,理论最大吸附量qm=9.70 mg/g;RL=0.221<1,表明吸附过程为优惠吸附;吸附过程符合准二级动力学模型,动力学常数k2=0.0452 g/(mg·min),理论平衡吸附量qe=1.14 mg/L,表明吸附过程主要为化学吸附.     

锡或锑在无取向电工钢中的研究进展

近年来,在节能减排背景之下,国内外众多研究者对无取向电工钢磁性能的提升做了大量研究。为了探索无取向电工钢磁性能提升的方法,对锡或锑对无取向电工钢磁性能的作用机制(晶粒尺寸和晶体织构的控制)进行分析。基于该作用机制,介绍锡或锑的添加对无取向电工钢磁性能的影响。经研究发现,适量的锡或锑在晶界偏聚,不会阻碍晶界的移动并且致使晶粒尺寸降低;与此同时,锡或锑在晶界偏聚不仅抑制{111}织构在原始晶界处形核及生长,还降低(100)晶粒表面能,促进(100)晶粒生长。因此,适量添加锡或锑,可使无取向电工钢铁损下降、磁感提升。最后结合生产工艺,建议无取向电工钢的研究方向应为稀土含量对高牌号无取向硅钢夹杂物尺寸和数量分布的影响,锡或锑的添加量和常化工艺参数(常化时间、常化温度)对常化晶粒尺寸的影响。     

Preparation and electrochemical performance of nanosized Co3O4 via hydrothermal method

The hydrotalcite-type cobalt compounds were prepared through oxidation of Co（OH）2 gel using NH4OH as precipitating agent and H2O2 as oxidant. These hydrotalcite-type cobalt compounds were transformed into Co3O4 through hydrothermal decomposition with nanostructural deformation. The precursor and product were characterized by Fourier-transform infrared（FT-IR） spectrum, X-ray diffractometry（XRD） and transmission electron microscopy（TEM）. The electrochemical performances of as-prepared nanosized Co3O4 as anode materials in lithium-ion batteries were tested by charge-discharge test in the voltage range of 0-3.0 V. The influence of morphology of Co3O4 particle on the capacity and cycling performance was studied. The results show that the shape and size of the final product can be controlled by altering cobalt sources. The irregular cubic Co3O4 with the average particle size of about 10 nm shows the best electrochemical performance. After 10 charge-discharge cycles, the specific charge capacity retains 555 mA.h/g.     

热处理工艺对BT9合金疲劳和高温持久性能的影响

本文研究了不同的热处理工艺对BT9钛合金的疲劳寿命和高温持久强度的影响,并对其组织、断口进行了光学和电子金相分析。指出了获得良好的综合机械性能的热处理工艺,并讨论了在不同区域内疲劳裂纹扩展的方式。     

瓦楞辊热处理生产工艺简介

瓦楞辊是我厂瓦辊纸板生产线（以下简称瓦线）上的关键部件，而瓦楞辊的热处理硬度又是考核瓦楞辊质量指标的重要参数，其硬度的高低直接影响到瓦楞辊的寿命，影响到瓦线的开停机时间。为此，我厂和机械部北京机电研究所合作，研究出提高瓦楞辊使用寿命和承载能力的热处理工艺。为此，配置了320kw、8000Hz的中频电源及4m淬火机床，选购了180A的十1000×4000mm离子渗氮炉，又配套购置了190kw的1000×4000mm井式炉和台车式回火炉。可对直径小于400mm，长度4000mm以下的瓦楞辊进行离子诊氮-和表面感应淬火的复合热处理，并可对直径小于1000mm…     

Effect of ultrasonic power and bonding force on the bonding strength of copper ball bonds

Copper wire, serving as a cost-saving alternative to gold wire, has been used in many high-end thermosonic ball bonding applications. In this paper, the bond shear force, bond shear strength, and the ball bond diameter are adopted to evaluate the bonding quality. It is concluded that the ef/~cient ultrasonic power is needed to soften the ball to form the copper bonds with high bonding strength. However, excessive ultrasonic power would serve as a fatigue loading to weaken the bonding. Excessive or less bonding force would cause cratering in the silicon.     

ZrB2-SiC基超高温陶瓷（UHTCs）的反应烧结及SHS粉体制备

用普通反应热压方法（RHP）和反应放电等离子体方法（R-SPS）原位反应制备了ZrB2-SiC，ZrB2-SiC—ZrC，ZrB2-SiC-ZrN，以及ZrB2-SiC-AIN4种复合材料。从密度，物相以及显微结构等方面比较了两种烧结方式之间的差别，对于升温速度较慢的普通热压方法，反应分步进行，显微结构不均匀；对于升温速度快的放电等离子体烧结，原料间的自蔓延反应被点着，反应速度快，显微结构均匀。同时以红外灯的热量为点火源，引发了Zr，Si及B4C间在空气气氛下的自蔓延反应，制备了较纯及粒径约为1μm的活性粉体。     

Synthesis of LaF3 superfine powder by microwave heating method

LaF3 superfine powder was synthesized from La(CH3COO)3 and NH4 F by microwave heating method,using ethanol or pure water as dispersants respectively. The results of XRD and SEM indicate that the superfine powder has high purity, regular particle shape and narrow distribution of granularity. The granularity of the best sample is in the range of 100 -200 nm. The influence of different dispersants on the crystal degree and microstructure was discussed. After the superfine powder was formed into a slice at pressure of 25 - 60 MPa, its electrochemical impedance spectroscopy was tested by electrochemical impedance spectroscopy (EIS) measurement. The result shows that the grain refining of LaF3 powder increases its ionic conductivity. Compared with traditional preparation methods of LaF3 powder, the advantages of microwave heating method were summarized.     

34CrNiMo钢齿轮轴开裂原因分析

对34CrNiMo钢齿轮轴的化学成分、金相组织及断口分析表明，其淬火开裂的主要原因是由于锻造温度过高，导致过热缺陷所致。     

美国铝工业空气污染控制法规

引言美国环境保护局(EPA)受权制订若干规范、条例来保护与提高全国的大气质量。其中关于限制原铝和再生铝工厂排放污染物的规范和条例是:新固定污染源的运行标准;协助各州政府制订现有污染源标准和排放指南,以及