Microstructure,mechanical, tribological,and oxidizing properties of AlCrSiN/AlCrVN/AlCrNbN multilayer coatings with different modulated thicknesses

Multilayer structure design is one of the most promising methods for improving the comprehensive performance of AlCrN-based hard coatings applied to cutting tools. In this study, four types of AlCrSiN/AlCrVN/AlCrNbN multilayer coatings, with different modulated thicknesses, were deposited to investigate their microstructure, mechanical, tribological, and oxidizing properties. All multilayer coatings exhibited grain growth along the crystallographic plane of (200) with a NaCl-type face-centered cubic (FCC) structure. The results show that, as the modulation thickness decreases from ～35 nm to ～10 nm, (1) the grain refinement effect is increasingly evident; (2) all multilayer coatings show a hardness of >30 GPa and an elastic modulus of >300 GPa. Both the ability to resist elastic strain to failure and the plastic deformation of multilayer coatings increase. In addition, their resistance to cracking reduces; (3) the wear rates of these multilayer coatings reduce successively from 1.78 × 10^?16 m³ N^?1 m^?1 to 7.7 × 10^?17 m³ N^?1 m^?1. This is attributed to an increase in self-lubricating VO_x and a decrease in adhesives from the counterparts; (4) the best high-temperature oxidation resistance was obtained for the multilayer coating with a modulated thickness of ～15 nm.     

A method of constructing an inspiration library driven by user-perceived preference evaluation data for biologically inspired design

Biologically inspired design (BID) is one of the common methods for product design. To solve the problem of inaccurate acquisition of inspirational creatures due to the lack of user perception preference analysis, a data-driven intelligent service model for BID considering user perception needs is proposed based on Kansei engineering. Firstly, by extracting the perceptual features of creatures from the semantic source elements of products through mapping and encodes them, we proposed a data acquisition method based on intuitionistic fuzzy sets considering different customer preference distributions, bridging the gap caused by the asymmetry between designers and users. Secondly, the functional relationship between biometric features and user-perceived attributes is identified and predicted, and a predictive model of biodata considering user preferences is obtained by multiple linear regression analysis. Finally, based on the data clustering and reorganization theory to understand the organization and dynamics of the database, the construction of a BID library was completed, and the design resources in the library were used as analyzed knowledge for designers to plan design activities. Taking the bionic design of a UAV product as an example, a prototype of a computer-aided design service system was developed based on the theory proposed in the article, and the analyzed knowledge was used to improve the efficiency and science of the design, effectively verifying the usefulness of this study for design. To a certain extent, this study addresses the problem of cognitive limitations of designers and cognitive differences between designers and users, promotes the application of bioinspiration in product design, and improves the marketability of design solutions.     

Effect of mesoporous carbon on oxygen reduction reaction activity as cathode catalyst support for proton exchange membrane fuel cell

In this paper, a new carbon support with a large number of mesoporous-structures is selected to prepare Pt/C catalysts. Transmission electron microscope (TEM) results show that the Pt/3# catalyst presents a sponge-like morphology, Pt particles are not only evenly distributed on the surface of carbon support, but also the smaller Pt particles are deposited in the mesoporous inside the support. The average diameter of Pt particles is only 2.8 nm. The membrane electrode assembly (MEA) based on Pt/3# catalyst also shows excellent performance. In conclusion, the 3# support is an idea carbon support for PEMFC, which helps to improve the oxygen reduction reaction (ORR) activity of the catalyst. Based on the “internal-Pt” structure of the support mesoporous, the efficient three-phase boundaries (TPBs) are construct to avoid the poisoning effect of ionomer on the nano-metal particles, reduce the activation impedance and oxygen mass transfer impedance, and improve the reaction efficiency.     

Activation of LSCF–YSZ interface by cobalt migration during electrolysis operation in solid oxide electrolysis cells

High-temperature water electrolysis through solid oxide electrolysis cells (SOEC) will play a key role in building a hydrogen economy in the future. However, the delamination between the air electrode and the electrolyte remains a critical issue to be addressed. Previously, it was hypothesized that Co migration may improve the catalytic activity of the SrZrO₃ second phase at the LSCF-YSZ interface, eventually leading to the delamination. In this work, the LSCF-YSZ interfaces sintered at different temperatures were examined in detail. The activation behaviors of the LSCF electrodes upon application with electrolysis current were characterized under different conditions. Further, samples containing purposely added SrZrO₃ interlayer with and without cobalt were fabricated and compared. The activation process is less significant for the sample with cobalt-added SrZrO₃ interlayer than the sample with pure SrZrO₃ layer, supporting the hypothesis that Co migration may lead to the activation behavior.     

Improving gelling properties of myofibrillar proteins incorporating with cellulose micro/nanofibres

The effects of cellulose microfibres (CMFs, Average size: 100 ± 5 μm) and cellulose nanofibres (CNFs, Average size: 60 ± 3 nm) on the properties of myofibrillar protein (MP) gels from duck breast meat were studied. The results demonstrated that CMFs and CNFs were mostly connected to MP by non-covalent bonds, the diffusion and cross-linking of MP molecules was promoted, and a denser and more complete gel network was formed. With the increases of CMFs and CNFs concentration (0–10%), the hardness was increased by 13.15% and 19.78% for CMFs10% and CNFs10% gels, respectively, and the elasticity was increased by 40% and 80%, respectively. At the same concentration (0–10%), the increase in gel hardness, viscoelasticity and immobilised water content was greater in the CNFs-MP group than in the CMFs-MP group. The CNFs-MP group had a tighter gel network, and CNFs had a better potential to improve the gelation performance of MP.     

Effects of electron-beam generated X-ray irradiation on the postharvest storage quality of Agaricus bisporus

The objective of this study was to investigate the effects of electron-beam generated X-ray irradiation on the postharvest storage quality and antioxidant capacity of Agaricus bisporus. All mushrooms were treated with different doses of electron-beam generated X-ray irradiation (0, 0.5, 1.0, 1.5 and 2.0 kGy) followed by stored at 4 °C for 21 days. Results showed that when compared with the control group at the end of storage, the firmness of Agaricus bisporus treated with 1.0 kGy was increased by 43.68%, the cell membrane permeability and malondialdehyde (MDA) content were decreased by 14.48% and 32.27% respectively, and the polyphenol oxidase (PPO) activity was reduced by 44.30%. One-kGy treatment was better than the control group to maintain superoxide dismutase (SOD) and catalase (CAT) activity. The finding suggested that the dose of 1.0 kGy generated by electron beam was suitable for keeping the postharvest quality for 21 days of Agaricus bisporus.Industrial relevanceThis study stated that electron-beam generated X-ray pretreatment could be a green and safe technology to improve the overall quality of Agaricus bisporus at 4 °C for 21 days.     

Catalytic behavior in CH4 decomposition of catalysts derived from red mud: Impact of residual Na2O

Catalyst samples for CH₄ decomposition were prepared from red mud (RM) by an acid-leaching neutralization precipitation approach. Water-washing the resultant precipitates multiple times, followed by drying at 105 °C and calcination at 500 °C, resulted in a threshold of residual Na₂O, equivalent to 96% Na₂O removal. Drying the precipitate at a higher temperature of 200 °C, followed by repeated water washing, provided a deeper Na₂O removal of 99% and made the resultant samples more active for the targeted reaction. Subsequently, four catalyst samples with a simulated red mud composition and NaOH contents from 0 to 0.3 wt% were prepared and the catalytic test results revealed that the Na₂O remaining in the RM-derived catalysts did not only inhibit their activation in CH₄ but also lower their maximal activities for CH₄ decomposition. Finally, two catalysts with the same simulated red mud composition and their Na impregnated respectively on Fe₂O₃ and a mixture support of Al₂O₃-SiO₂-TiO₂ were prepared and tested to explore the effect of Na distribution on the activation behavior of RM-derived catalysts for CH₄ decomposition. The activity testing results showed that it was the Na residual dispersed on iron oxides in the RM-derived samples to significantly inhibit the activation of CH₄ decomposition.     

A dotted nanowire arrayed by 5 nm sized palladium and nickel composite nanopaticles showing significant electrocatalytic activity towards ethanol oxidation reaction (EOR)

To the best of our knowledge, this is the first time to report the preparation of a dotted nanowire arrayed by 5 nm sized palladium and nickel composite nanoparticles (denoted as Pd_xNi_y NPs) via a hydrothermal method using NU and PdO·H₂O as the starting materials. The samples prepared at the mass ratio of NU to PdO·H₂O 1:1, 1:2 and 2:1 were, respectively, nominated as catalyst c₁, c₂ and c₃. The chemical compositions of all synthesized catalysts were mainly studied by using X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS), revealing that metallic Ni was one main component of all prepared catalysts. Surprisingly, the main diffraction peaks appearing in the XRD patterns of all prepared catalysts were assigned to the metallic Ni rather than the metallic Pd. Very interestingly, as indicated by the TEM images, a large number of dotted nanowires arrayed by numerous equidistant 5 nm sized nanoparticles were distinctly exhibited in catalyst c₁. More importantly, when being used as electrocatalysts for EOR, all prepared catalysts exhibited an evident electrocatalytic activity towards EOR. In the cyclic voltammetry (CV) test, the peak current density of the forward peak of EOR on catalyst c₁ measured at 50 mV s^?1 was as high as 56.1 mA cm^?2, being almost 9 times higher than that of EOR on catalyst c₃ (6.3 mA cm^?2). Particularly, the polarized current density of EOR on catalyst c₁ at 3600 s, as indicated by the chronoamperometry (CA) experiment, was still maintained to be around 1.47 mA cm^?2, a value higher than the latest reported data of 1.3 mA cm^?2 (measured on the pure Pd/C electrode). Presenting a novel method to prepare dotted nanowires arranged by 5 nm sized nanoparticles and showing the significant eletrocatalytic activities of the newly prepared dotted nanowires towards EOR were the major contributions of this preliminary work.     

盾构隧道施工物料无人运输发展现状及关键技术

盾构隧道施工物料无人运输有助于提升运输效率、降低运输成本、减少运输安全事故率。与公路汽车无人驾驶、港口车辆无人驾驶、轨道交通无人驾驶等逐步成熟的无人驾驶技术不同，在隧道场景下实施施工物料无人运输存在运输物料种类繁多、运输调度困难、地下定位信号拒止、狭窄车道频繁会车、行车路面工况复杂、地上地下联动响应慢等诸多挑战。从实现盾构隧道施工物料无人运输的关键问题分析入手，综述当前盾构隧道施工物料运输方式、运输需求、无人运输发展现状及存在的挑战，提出盾构隧道施工物料无人运输的五大关键技术：多种类物料智能货控能效管理技术，无人化垂直装卸门机控制技术，多传感器融合同步定位与地图构建技术，隧道复杂环境路径规划与自主避障技术，隧-地一体化联动响应的高可靠性无线通信技术。     

Preparation of high-purity SiC ceramics with good plasma corrosion resistance by hot-pressing sintering

High-purity SiC ceramic devices are applied in semiconductor industry owing to their outstanding properties. Nevertheless, it is difficult to densify SiC ceramics without any sintering additive even by HP sintering. In this work, high-purity and dense SiC ceramics were fabricated by HP sintering with very low amounts of sintering aids. Residual B content was only 556 ppm and relative density was more than 99.5%. Furthermore, thermal conductivity of as-prepared SiC ceramics was improved from 155 W m^?1 K^?1 to 167 W m^?1 K^?1 by increasing holding time and their plasma corrosion resistance was promoted in the meantime. The as-prepared high-purity SiC ceramics have broad application prospects in the field of semiconductor industry.