Engineering biphasic hybrid phosphide nanowires as efficient electrocatalyst for hydrogen evolution reaction: Experimental and theoretical insights

Development of highly efficient and cheap electrocatalysts towards the hydrogen evolution reaction (HER) is of great importance for electrochemical water splitting. Herein, hybrid Cu/NiMo-P nanowires on the copper foam were successfully fabricated via a simple two-step method. The hierarchically structured Cu/NiMo-P exhibits large surface areas and rapid electron transfer ability, leading to enhanced catalytic activity. The as-prepared Cu/NiMo-P electrodes need overpotentials of 34 mV and 130 mV to obtain 10 mA cm^?2 for HER in acidic and alkaline solutions, respectively. Density functional theory (DFT) calculations reveal that the Cu/NiMo-P hybrid has a more thermo-neutral hydrogen adsorption free energy and enhanced charge transfer ability as well.     

Role and prospects of green quantum dots in photoelectrochemical hydrogen generation: A review

Eco-friendly quantum dots (QDs) can be termed green QDs which stand as an attractive choice to modify the properties of known semiconductors in the direction of getting efficient photoelectrodes for solar-induced photoelectrochemical (PEC) splitting of water, due to their peculiar properties. Thus, it is of high significance to analyze their merit/demerit as an effective scaffold in PEC cell. QDs are known for their excellent optical properties however, the coupling of green QDs with semiconductor is not only useful in improving absorption characteristics but also promotes charge transfer. This review has undertaken the critical analysis on the worldwide research going on the green QDs modified photoelectrode with respect to their optical, electrical & photoelectrochemical properties, role, usefulness, efficiency, and finally the success in PEC system for hydrogen production. Various methods on the facile synthesis & sensitization techniques of green QDs available in the literature have also been discussed. Further, recent advances on the development of green QDs based photo-electrode, along with major challenges of using green QDs in this field have also been presented.     

基于跨临界CO2热泵的茶叶生产能源系统负荷削减潜力

乡村产业中的化石能源设备逐渐被电能技术替代，引起了乡村负荷波动增大、部分时段产生集中高负荷的问题。为了解决以上问题，将低品位清洁能源应用至乡村的茶叶生产中，针对烘茶全过程的工艺要求提出了跨临界CO₂热泵烘茶技术；并以某茶叶生产乡村为对象，对其代表台区的全年日用电量及产茶日负荷进行了分析，得出采用CO₂热泵烘茶后其负荷得到大幅度削减，整体可降低至原负荷的39.6%~46.8%，峰值负荷与平时负荷的比值由原本的13.6降至5.4~6.2。跨临界CO₂热泵应用至农产品生产中可有效缓解乡村供电压力。     

Design of Ti4+-doped Li3V2(PO4)3/C fibers for lithium energy storage

In this work, we propose a facile approach to fabricate Ti⁴⁺-doped Li₃V₂(PO₄)₃/C (abbreviated as C-LVTP) nanofibers using an electrospinning route followed by a high temperature treatment. In this designed nanocomposite, the ultrafine LVTP dots are homogeneously dispersed into one-dimensional carbon nanofibers and the Ti⁴⁺ doping does not destroy the crystal structure of monoclinic Li₃V₂(PO₄)₃. Compared to the undoped Li₃V₂(PO₄)₃/C (abbreviated as C-LVP), the as-fabricated C-LVTP fibers present higher reversible capacity, superior high-rate capability as well as better cyclic property. Especially, the C-LVT_7%P cathode delivers not only high capacities of 187.2 and 160.3 mAh g^?1 at 0.5 and 10 C respectively, but also stable cyclic property with the reversible capacity of 135.8 mAh g^?1 at 20 C following 500-cycle spans. The good battery characteristics of C-LVT_7%P can be mainly ascribed to Ti⁴⁺ doping, which can increase the electrical conductivity and Li⁺ diffusion coefficient.     

Induced slim ferroelectric hysteresis loops and enhanced energy-storage properties of Mn-doped (Pb0·93La0.07)(Zr0·82Ti0.18)O3 anti-ferroelectric thick films by aerosol deposition

In this study, the high ferroelectric hysteresis loss of (Pb_0·93La_0.07)(Zr_0·82Ti_0.18)O₃ (PLZT 7/82/18) antiferroelectric (AFE) ceramics was reduced by employing a combinatorial approach of Mn acceptor doping followed by thick film fabrication via an aerosol deposition (AD) process. The grains of the as-deposited PLZT 7/82/18 AFE AD thick films were grown by thermal annealing at 550 °C to enhance their electrical properties. Investigation of the electrical properties revealed that Mn-doping results in improved dielectric and ferroelectric properties, increased dielectric breakdown strength (DBS), and energy-storage properties. The Mn-doped PLZT AFE AD films possess a frequency-independent high dielectric constant (ε_r ≈ 660) with low dielectric loss (tan δ ≈ 0.0146), making them suitable candidates for storage capacitor applications. The bipolar and unipolar polarization vs. electric field (P-E) hysteresis loops of PLZT 7/82/18 AFE AD thick films were found to be slimmer than those of their bulk form (double hysteresis) with significantly reduced ferroelectric hysteresis loss, which is attributed to the AD-induced mixed grain structure. The Mn-doped PLZT 7/82/18 AFE AD thick films exhibited a low remnant polarization (P_r ≈ 9.22 μC/cm²) at a high applied electric field (~2750 kV/cm). The energy-storage density and energy efficiency of the Mn-doped PLZT AFE AD thick films were calculated from unipolar P-E hysteresis loops and found to be ~38.33 J/cm³ and ~74%, respectively.     

High energy storage and ultrafast discharge in NaNbO3-based lead-free dielectric capacitors via a relaxor strategy

Dielectric capacitors with decent energy storage and fast charge-discharge performances are essential in advanced pulsed power systems. In this study, novel ceramics (1-x)NaNbO₃-xBi(Ni_2/3Nb_1/3)O₃(xBNN, x = 0.05, 0.1, 0.15 and 0.20) with high energy storage capability, large power density and ultrafast discharge speed were designed and prepared. The impedance analysis proves that the introducing an appropriate amount of Bi(Ni_0·5Nb_0.5)O₃ boosts the insulation ability, thus obtaining a high breakdown strength (E_b) of 440 kV/cm in xBNN ceramics. A high energy storage density (W_total) of 4.09 J/cm³, recoverable energy storage density (W_rec) of 3.31 J/cm³, and efficiency (η) of 80.9% were attained in the 0.15BNN ceramics. Furthermore, frequency and temperature stability (fluctuations of W_rec ≤ 0.4% over 5–100 Hz and W_rec ≤ 12.3% over 20–120 °C) were also observed. The 0.15BNN ceramics exhibited a large power density (19 MW/cm³) and ultrafast discharge time (~37 ns) over the range of ambient temperature to 120 °C. These enhanced performances may be attributed to the improved breakdown strength and relaxor behavior through the incorporation of BNN. In conclusion, these findings indicate that 0.15BNN ceramics may serve as promising materials for pulsed power systems.     

Microwave hybrid fast sintering of red clay ceramics

This work aimed to examine the performance of the hybrid sintering of clay ceramic in a microwave furnace, compared to the sintering process in a conventional furnace. The raw materials were subjected to X-ray fluorescence, loss on ignition (LOI), X-ray diffraction, particle size distribution, real specific mass, and thermogravimetric analyses. The red clay ceramic mass was prepared, extruded, pre-sintered in a conventional furnace at 600°C/60 min, and sintered at temperatures between 700 °C and 1100 °C. The sintering conventional (resistive oven) was carried out for 60 min with a heating rate of 10°C/min. In the microwave furnace, the sintering times were 5, 10, and 15 min, with a heating rate of 50°C/min, with a sintering chamber coated with silicon carbide (susceptor). The sintered specimens were characterized according to linear shrinkage, water absorption, apparent porosity, apparent specific mass, X-ray diffraction, Raman spectroscopy analysis, spectroscopy analysis in the ultraviolet and visible regions, microhardness, and scanning electron microscopy. The results showed that microwave sintering promoted an increase in the microhardness and apparent specific mass, and reduction in water absorption and apparent porosity values, due to greater densification in the microstructure. The best results occurred for specimens sintered at 1100°C.     

新型无机内保温涂层的性能及应用

根据水泥烧成热耗的组成，降低高温设备表面散热是降低水泥烧成热耗的重要途径之一，而减少高温窑炉墙壁的热传导可有效降低设备的表面散热。本文在介绍无机内保温涂层隔热原理的基础上，对保温涂层的应用效果进行了对比研究，通过在传统耐火隔热材料的基础上增加新型无机内保温涂层，可有效降低高温设备外表面温度，减少水泥生产中的散热损失，达到节能降耗的目的。     

新型地锚张弦梁式泥石流格栅坝构件受力的简化计算方法

针对常见泥石流防治结构被冲击破坏的问题，基于“柔性消能”理念，结合张弦梁结构和竖向预应力锚杆技术，提出一种既能改善结构受力性能、增加结构整体抗冲击能力、保证结构安全可靠，又能减小结构构件截面尺寸、节约成本、便于现场施工组装和后期运营维护的新型地锚张弦梁式泥石流格栅坝，并阐述其技术原理。根据泥石流荷载分布和新型地锚张弦梁式泥石流格栅坝的受力特征，给出其简化的内力计算方法；并利用SAP2000建立新结构有限元模型，分析了结构的整体受力，验证了构件简化计算方法的合理性；结合Python语言和Qt De? signer软件开发了相应的设计计算软件，对新型地锚张弦梁式泥石流格栅坝的内力进行求解。结果表明：提出的新结构抗冲击性能好，构件受力均匀；以后设计中应关注竖杆的剪切脆性破坏和立柱偏心受力情况，保证结构安全；变形协调仅使底层张弦梁与竖杆内力偏大，实际工程应用时，应着重验算底层构件，防止其破坏；文中提出的简化计算方法能较准确的反映结构的受力特性，具有一定的合理性，研究可为新型地锚张弦梁式泥石流格栅坝的设计计算和推广应用提供理论依据和技术支持。     

金针菇多糖对微冻大黄鱼及其鱼片品质变化的影响

为研究金针菇多糖（polysaccharide from Flammulina velutipes，FVP）对微冻大黄鱼及鱼片在贮藏期间肌原纤维蛋白性质的变化及水分分布的影响，实验分别选用0.03、0.06、0.09 g/L FVP浸渍处理大黄鱼和鱼片，以无菌水处理为对照组，分析微冻贮藏期间样品的感官指标得分、总挥发性盐基氮含量、总巯基含量、Ca2＋-ATPase活性、蛋白流变学性质以及水分迁移变化规律。结果表明：FVP可有效抑制整鱼总挥发性盐基氮含量上升和感官得分的下降；减缓整鱼及鱼片在微冻过程中总巯基含量、Ca2＋-ATPase活性下降和水分流失；此外FVP还能够延缓大黄鱼因腐败而出现的蛋白凝胶能力减弱。在本实验选取的多糖浓度范围内，0.09 g/L FVP处理组保鲜效果较强。该研究结果可为FVP用于水产品贮运保鲜提供理论参考。