电镀锡机组软熔导电辊脱锡技术研究

粘锡是电镀锡机组软熔导电辊失效的主要原因,应用化学方法脱锡是延长导电辊寿命的重要途径.开发了氢氧化钠(钾)为主要组成,并加入适量亚铅酸钠(钾)和硝酸(亚硝酸)钠配制而成脱锡剂,当脱锡剂温度为40～80℃,导电辊表面温度为40～70℃时,对粘锡导电辊具有很好的脱锡效果.粘锡导电辊脱锡后的表面粗糙度可以恢复到4.0μm以上,导电辊使用寿命提高80%,降低导电辊修复成本90%,并大幅度减少导电辊更换时间,提高电镀锡机组生产作业率.     

A new alloy design concept for austenitic stainless steel with tungsten modification for bipolar plate application in PEMFC

The feasibility of a new alloy design concept utilizing the principle of ‘tungsten bronze effect’ is critically evaluated for the development of metallic bipolar plates for proton exchange membrane fuel cell (PEMFC). An austenitic stainless steel (ASS) is modified with W and La to improve the stability of the passive film in an acidic environment as well as to reduce the contact resistance by the tungsten bronze effect. The experimental ASS containing W and La was evaluated in a simulated PEMFC environment of H₃PO₄ and H₂SO₄ solutions at 80 °C, and the electrical property was evaluated by performing a contact resistance test. The test results show that the ASS modified with W and La has good passive film stability for corrosion resistance and low contact resistance. The X-ray photoelectron spectroscopy (XPS) analysis clearly suggests the possibility of the tungsten bronze effect from the change in valency state of W⁶⁺ to W⁵⁺ in the passive film formed on the modified ASS. The feasibility of a new alloy design concept utilizing the ‘tungsten bronze effect’ is well demonstrated; however, more study is highly required for the development of metallic bipolar plates of PEMFC.     

In对Sn-8Zn-3Bi无铅钎料润湿性的影响

首先采用铺展法测试了Sn-8Zn-3Bi-(0～5)In钎料合金的铺展性.结果表明,少量In的加入提高了钎料的润湿性.当In含量达到0.5%时(质量分数,下同),钎料在铜基底上的铺展面积最大.采用气泡最大压力法对Sn-8Zn-3Bi-(0～1.5)In钎料熔体进行了表面张力测试.加入0.5%的In大大降低了Sn-8Zn-3Bi钎料熔体的表面张力,但进一步增加In的含量导致熔体表面张力增大.最后采用润湿平衡法对上述钎料进行了润湿力测试.结果表明0.5%In的加入使合金的润湿力达到最大,其原因是钎料/铜界面的界面张力减小.     

热处理对制备纳米氧化铟锡(ITO)粉末的影响

以共沸蒸馏工艺辅助的共沉淀法制备了纳米氧化铟-氧化锡（ITO）粉体，研究了不同热处理温度对制备粉体的影响，结果表明，随着热处理温度的提高，粉体发生从四方结构向体心立方结构转变，晶粒出现长大现象，比表面积变化明显，化学组分保持高纯状态，综合比较，在700～800℃进行热处理可以得到尺寸均匀，晶形完整的纳米级粉体。     

PSA与MSA电镀锡产品库存3年后的性能对比

介绍了某电镀锡机组在2016年12月从原PSA(苯酚磺酸)电镀锡工艺切换为MSA(甲基磺酸)电镀锡工艺时,使用同卷基板的前、后半卷分别用2种工艺镀锡,再在相同条件下库存3年后,各项检测数据及印铁涂布内涂料后的性能。结果表明,使用MSA工艺生产的电镀锡产品的各项指标符合标准要求,并在多项检测项目上优于PSA工艺生产的电镀锡产品。     

眼动技术在连弧纹铭带镜设计因子提取中的应用

通过使用眼动仪对连弧纹铭带镜中的设计因子进行提取,达到优化新文创时代下文创产品设计开发的目的。运用眼动实验分析20名被试观看连弧纹铭带镜的视觉热区,依据实验数据对被试在连弧纹铭带镜中的兴趣区域进行划分。结合层次分析法确定被试主要兴趣区域,采用归纳与演绎对其中的显性设计因子和隐形设计因子进行提取。将提取的设计因子应用于文创产品设计当中,并对所设计的产品与其他文创产品进行对比测试。通过实验数据验证眼动仪对于文物中设计因子提取的可行性。     

锡或锑在无取向电工钢中的研究进展

近年来,在节能减排背景之下,国内外众多研究者对无取向电工钢磁性能的提升做了大量研究。为了探索无取向电工钢磁性能提升的方法,对锡或锑对无取向电工钢磁性能的作用机制(晶粒尺寸和晶体织构的控制)进行分析。基于该作用机制,介绍锡或锑的添加对无取向电工钢磁性能的影响。经研究发现,适量的锡或锑在晶界偏聚,不会阻碍晶界的移动并且致使晶粒尺寸降低;与此同时,锡或锑在晶界偏聚不仅抑制{111}织构在原始晶界处形核及生长,还降低(100)晶粒表面能,促进(100)晶粒生长。因此,适量添加锡或锑,可使无取向电工钢铁损下降、磁感提升。最后结合生产工艺,建议无取向电工钢的研究方向应为稀土含量对高牌号无取向硅钢夹杂物尺寸和数量分布的影响,锡或锑的添加量和常化工艺参数(常化时间、常化温度)对常化晶粒尺寸的影响。     

Effect of heat treatment on microstructure and properties of hot-extruded nickel-aluminum bronze

The effect of heat treatment on the microstructure and properties of a hot-extruded nickel-aluminum bronze was investigated. Experimental materials were heat treated through different processes, including quenching, normalizing, aging and annealing, and their microstructure, corrosion resistance and mechanical properties were characterized. It is found that quenching causes all β phase transformed into β phase, however, normalizing causes β phase transformed into β α and κ phases. When the quenched sample is aged, fine phase is precipitated from the as-quenched microstructure of β＇ phase. Annealing causes the transformation of β into a and κ phases. The results of mechanical property tests show that quenching, normalizing and aging improve the tensile strength and hardness of the experimental material, with a corresponding fall in elongation. Annealing raises the elongation but reduces the tensile strength and hardness. Furthermore, corrosion resistance of nickel-aluminum bronze ranks from worse to better in the following order： aged, quenched, normalized, hot-extruded and annealed. However, with the exposure time of corrosion test increasing, the difference of average corrosion rate between those nickel-aluminum bronzes tums small.     

Influence of heat treatment on tribological behaviors of novel wrought aluminum bronze

1　ＩＮＴＲＯＤＵＣＴＩＯＮＡｌｕｍｉｎｕｍｂｒｏｎｚｅｐｏｓｓｅｓｓｅｓｅｘｃｅｌｌｅｎｔｐｈｙｓｉｃａｌ,ｍｅｃｈａｎｉｃａｌａｎｄｔｒｉｂｏｌｏｇｉｃａｌｐｒｏｐｅｒｔｉｅｓ .Ｉｔｉｓａｖａｉｌａｂｌｅｆｏｒｍａｋｉｎｇｗｅａｒ ｒｅｓｉｓｔｉｎｇａｎ