Ti-23Al-17Nb合金激光切割工艺研究

对一种金属间化合物Ti-23Al-17Nb合金的激光切割性进行了初探。试验结果表明只要工艺参数适当，可获得较好质量的切口。切缝质量可以满足随后激光拼焊的要求。     

Effect of cold spray deposition of a titanium coating on fatigue behavior of a titanium alloy

The deposition of titanium on a titanium alloy substrate is being examined for potential use as a surface treatment for medical prostheses. A Ti6Al4V alloy was coated with pure titanium by cold gas dynamic spraying. Coatings were deposited onto samples with two different surface preparation methods (as-received and grit-blasted). The fatigue life of the as-received and grit-blasted materials, both before and after coating, was measured with a rotating-bend fatigue rig. A 15% reduction in fatigue endurance limit was observed after application of the coating to the as-received substrate, but no significant reduction was observed on its application to the grit-blasted substrate. The reduction in fatigue endurance limit has been related to the substrate-coating interface properties, the elastic modulus, and the residual stress states. This article was originally published inBuilding on 100 Years of Success, Proceedings of the 2006 International Thermal Spray Conference, (Seattle, WA), May 15–18, 2006, B.R. Marple, M.M. Hyland, Y.-Ch. Lau, R.S. Lima, and J. Voyer, Ed., ASM International, Materials Park, 2006.     

SiCp/Al复合材料热处理及统计分析

采用四因素多水平组合热处理试验与统计分析相结合的方法研究了粉末冶金制备的12%SiCp/6066Al(体积分数)复合材料的热处理工艺参数与硬度间的关系.结果表明,复合材料与基体合金相比具有峰值提前效应;热处理工艺参数主效应由强到弱依次为时效时间、固溶温度、时效温度、固溶时间;时效时间与时效温度一级交互作用也较重要,其他一级、二级和三级交互作用较小.12%SiCp/6066Al复合材料的优化热处理工艺参数为530℃固溶90min,水淬170℃时效6h.     

AB INITIO CALCULATION OF THE ELASTIC AND OPTICAL PROPERTIES OF Al_3Sc COMPOUND

The ab initio method has been performed to explore the elastic and optical properties of Al3Sc compound, based on a plane wave pseudopotential method. It can be seen that the calculated equilibrium lattice parameter and elastic constants are in reasonable agreement with the previous experimental data. The elastic constants satisfy the requirement for mechanical stability in the cubic structure of the Al3Sc compound. The optical property calculations show that a strong absorptive peak exists from 0-15eV and a relative small absorptive peak exists around 30eV. The form is caused by the optical transitions between high s, p, and d bands, and the latter results from the optical transitions from high s, p, and d bands to the low 2p band.     

Fe/Al金属间化合物光束合金化涂层的组织分层现象

在45钢表面预涂纯Al粉，用光束合金化的方法合成了Fe／Al化合物涂层。使用SEM、EDS、X-ray衍射研究了涂层的组织特点及物相组成。研究结果表明，Fe／Al化合物涂层发生了组织分层现象，表层为FeAl Fe3AlC0.5层，第二层为Fe3Al Fe3AlC0.5层。发生组织分层现象是由合金化过程熔池中Al的含量由表层到底部逐渐减小所引起的。其原因可能与Al的密度较低和熔池搅拌不充分有关。     

利用高频磁场制备自生梯度复合材料的熔体温度选择

研究了通过在熔体凝固过程中的不同温度范围施加高频磁场制备自生梯度复合材料的工艺.对于Al/Mg2Si/Si自生梯度复合材料,近似计算及实验结果表明:Al Mg2Si二元共晶区(555～595C)是施加高频磁场的最佳温度范围,此时处于低粘性熔体中的增强颗粒容易被外加电磁阿基米德力分离.高频磁场施加温度过高或过低,均不易使增强颗粒产生梯度分布效果.     

Fe3Al/Q235异种材料扩散焊界面相结构分析

采用X射线衍射、透射电镜和电子衍射技术对Fe3Al/Q235真空扩散焊界面附近的微观相结构进行了试验研究。试验结果表明，当加热温度1050～1080℃，保温时间60min，压力9.8MPa时，Fe3Al金属间化合物与Q235钢扩散焊界面附近形成了明显的扩散过滤区，该过渡区由Fe3Al相和a-Fe(Al）固深体构成，显微硬度约为480～540HM，不存在含铝校较高的高硬度脆性相。有利于提高Fe3Al/Q235扩散过滤区的韧性，提高扩散焊接头的抗裂纹能力。扩散过滤区中的Fe3Al相与a-Fe(Al）固溶体之间存在着（110）a-Fe(Al)//(011)Fe3Al和[001]a-Fe(Al)//[100]Fe3Al的晶体学取向关系。     

铝元素的添加对锆基合金非晶形成能力影响的电子结构模型

通过构建非晶合金的团簇模型，利用离散变分法从电子层次研究了Al元素对Zr-Cu非晶合金中团簇稳定性的影响。结果表明，Al原子的引入提高了团簇中原子间的亲和力，并且随着Al原子数的增加，亲和力增大，导致新的团簇产生，从而破坏了非晶的团簇结构，Al含量对Zr-Al-Ni非晶合金的稳定性的影响可通过Fermi能级处的态密度大小来反映。     

晶须定向分布SiCw/6A02复合材料的压缩变形行为

通过考察晶须呈定向排列的SiCw/6A02复合材料压缩变形期间的晶须取向和长度的变化，研究了复合材料变形期间的应力应变行为。结果表明，变形期间晶须的转动和折断导致的加工软化和基体合金的加工硬化，共同决定复合材料的压缩应力—应变行为。     

原位生成Al2O3、TiB2和Al3Ti/Al复合材料的热循环行为

本文研究了Al-TiO2-B系原位生成Al2O3、TiB2和Al3Ti/Al颗粒增强铝基复合材料的热循环行为，研究结果表明了纯铝及B／TiO2摩尔比分别为0、1和2的颗粒增强铝基复合材料的热循环行为具有以下结果，纯铝和复合材料热循环后均产生了残余应变和滞后环；Al-TiO2-B系列复合材料热循环应变的各项指标均比纯铝基体大大降低，且具有较小的内耗功和较好的热稳定性，可以预测其具有较高的热疲劳寿命，热循环曲线能很好的评估复合材料在温度循环变化的环境中工作时的热稳定性和热疲劳。