高温预析出对Al-Zn-Mg系铝合金时效硬化和应力腐蚀的影响

研究了高温固溶后降温处理工艺对中强可使预析出LC52和7039铝合金的组织、时效硬化和应力腐蚀的影响。金相观察发现,高温预析出可优先在晶界处产生,并提高随后时效状态下晶界析出相的不连续分布程度,温度降低到一定程度晶内和晶界产生大量析出。合金拉伸性能和应力腐蚀结果表明,预析出在保持强度和塑性的同时,可提高抗应力腐蚀性能。而预析出温度降低,合金强度呈下降趋势。     

Influence of inhibitor addition on the corrosion protection performance of sol–gel coatings on AA2024

Sol–gel films are actively investigated during the last decade as possible candidates for environmentally friendly pre-treatments. However, the important drawback in this case is the lack of active corrosion protection and self-healing ability.     

EIS evaluation of the filiform corrosion of aluminium coated by a cataphoretic paint

Filiform corrosion is mainly considered as a cosmetic attack and is undesirable in most applications. The initiation and propagation of the filaments are related to different parameters such as the presence of defects, the permeability of the coating to water and oxygen, the adherence of the paint system and the presence of salts.

The aim of this work is to study the behaviour of painted aluminium samples towards filiform corrosion or delamination. The 6082 Aluminium alloy was selected and the samples were covered with a cataphoretic epoxy primer without lead (PPG Industries France). Prior to the application of the electrocoat, the samples were pre-treated by a commercial Zr/Ti or chromate conversion treatment or simply etched with a commercial acid etching product.

Filiform corrosion was studied by the normalized test (ISO/DIS 4623): painted and scratched samples were inoculated in HCl and exposed in a constant humidity chamber at 40 °C and 82% RH for 3 weeks. After exposure the samples were subjected to a visual and optical microscopic examination.

Electrochemical impedance spectroscopy was used to study the sensitivity to filiform corrosion. The operating mode of this test is similar to the normalized one. The samples were scratched before inoculation for 1 h in HCl and then exposed to the humidity chamber for a maximum of 4 days. The samples were tested by EIS in an acidified 0.1 M Na₂SO₄ electrolyte solution. The resulting impedance spectra were analyzed with an appropriate equivalent electrical circuit which allows the evaluation of the exposed metallic surface area, directly related to the extent of filiform corrosion or delamination. Different parameters were varied: the exposure time in the humidity chamber; the immersion time in the electrolyte sulphate solution as well as its pH and the coating thickness.     

FeBP非晶态合金超细微粒的合成及其对PH3分解的催化作用

用化学还原法合成了FeBP非晶态合金超细微粒，用电感耦合等离子体光谱（ICP）、X射线粉末衍射（XRD）、透射电子显微镜（TEM）和差热分析（DSC）等手段对其进行了物性表征，并用微型催化反应装置考察了其对PH3分解的催化作用，结果表明，非晶态合金FeBP对PH3的分解具有良好的催化作用，能使PH3的分解温度从800℃以上降到500℃左右。490℃时分解率超过90％，540℃时达100％。     

Influence of nano-scaled dispersed second phase on substructure of deformed dispersion strengthened copper alloy

The deformation behavior of dispersion strengthened copper alloy Cu-Al2O3 was studied by TEM. The results show that nano-scaled dispersed second phase not only increases dislocation density in matrix, but also has an important influence on the dislocation substructure. The presence of fine dispersed Al2 O3 particles results in a uniform and random dislocation distribution in matrix copper and causes the difficulty in formation of dislocation cell structure and the decrease in the amount of cell structure during deformation. Deformation gives rise to much more dislocations and dislocation cells form more difficultly and the decrease in the cell size with the increase of dispersion degree.     

Preparation of Plate Fe_(60)Co_8Zr_(10)Mo_5W_2B_(15) Bulk Amorphous Alloy and Its Fracture Toughness

1Introduction Duwez[1]synthesizedthefoilAu Siamorphousalloyforthefirsttimewithrapidsolidification,whichinitiatedthepreparationofamorphousalloysintheprocessofalloysolidification,andthereaftertheresearchonamorphousal loysdevelopedrapidly.Since1980s,withthec…     

Effects of thermal and mechanical treatments on a titanium-based conversion coating for aluminium alloys

The influence of mechanical deformation and heating on the protective performance of a chromium-free conversion treatment for aluminium alloys has been assessed by polarisation and AC impedance measurements. Protection is unlikely to be seriously compromised by typical production operations.     

RMT1-250转换开关用电接触材料

铜铬锆合金是一种形变热处理材料，兼具了铜铬合金和铜锆合金的各种优良性能，经过时效处理的铜铬锆合金，与铜相比，高温强度有很大的改善，而且具有较高的导电率。所以铜铬锆合金广泛应用于电焊机、低压电器等行业。根据对铜铬锆成分的适当调整，可用作为电焊机电极，低压电器触桥、短路环等各种电接触材料。铜铬锆合金用于RMT1－250转换开关，接近于触桥材料的应用，但使用的条件更苛刻一些，要承受部分电弧的侵蚀和由此产生的高温，因此对材料要求具有良好的导电导热性和更高的高温强度。     

合金钢连铸机生产工艺分析及实践

对新钢特殊钢有限责任公司整个合金钢连铸机的生产工艺进行了分析，提出了提高钢水质量和优化连铸工艺参数的有效措施，使铸坯的质量得到了有效控制和改善。     

Al-Zn-Ce非晶合金的相选择与组织结构演化

本文研究了具有典型分解特征的Al-Zn-Ce非晶合金的形成和晶化过程，探讨了各种相的生成顺序。XRD和DSC测试结果表明强烈的化合物短程序有利于Al-Zn-Ce非晶合金的形成。在Al-Zn-Ce非晶合金的晶化过程中存在复杂的相选择行为，多种相的竞争形核和有限生长使其具有复杂的结构特点。同时，结果也表明冷速对该体系非晶的形成有很大影响。