Surface modification of spherical LiNi1/3Co 1/3 Mn1/3O2 with Al2O3 using heterogeneous nucleation process

To improve the cycle stability at high voltage and high charge/discharge rate, spherical LiNi1/3Co1/3Mn1/3O2 was coated with Al2O3 by using heterogeneous nucleation process, and the physical and electrochemical properties were studied. The SEM images show that there is a uniform coating on the modified spherical LiNi1/3Co1/3Mn1/3O2. The electrochemical tests indicate that the properties of LiNi1/3Co1/3Mn1/3O2 coated with 0.5% aluminum oxide are the best. The initial capacities are 150 and 173 mA.h/g at the rate of I C in the voltage range of 2.7-4.3 V and 2.7-4.6 V, respectively, and the discharge capacities maintain about 99% and 85% after 30 cycles, respectively. While those of the bare LiNi1/3Co1/3Mn1/3O2 are only 90% and 75%, respectively. The CV tests of LiNi1/3Co1/3Mn1/3O2 show that Al203-coating can restrain the oxide-reduction peak currents fading during the charge/discharge course.     

铸造／热压Pr—Fe—B磁体的矫顽力及其与晶粒尺寸关系

研究了铸造/热压 r_(19)Fe_(74.5)B_5Cu_(1.5)永磁体的磁硬化特点.发现磁体反磁化过程受反向畴的形核控制.矫顽力与晶粒尺寸的对数存在线性关系: _iH_c(MA/m)=1.7312—0.4816Ind(μm)根据反向畴形核的随机性和矫顽力的统计特性讨论了该式的物理意义。     

钢中珠光体相变机制的研究进展

简要总结了钢中珠光体相变的机制，特别是珠光体形核的晶体学和长大的动力学。基于形核时的最小形核能和渗碳体与铁素体“合作”生长的要求，珠光体通常在奥氏体晶界形核并只向某一晶粒内生长，因而晶界珠光体与相邻晶粒存在特定取向关系而与生长进入的晶粒无特定取向关系。晶体学研究表明，珠光体形核的领先相与碳浓度及渗碳体与铁素体间的取向关系(分别为Pitsch-Petch、Bagaryatsky或lsaichev)无关。最近的研究发现，具Bl结构的非共格杂质粒子界面是过共析钢中晶内珠光体形核的有效位置，初步的结果表明，晶内珠光体形核的原因在于杂质粒子生长造成的局部区域碳贫化及低能的珠光体，杂质界面取代高能的奥氏体，杂质界面。特定过冷度下的层片间距与正向界面推移速率的关系是珠光体生长动力学的主要问题。基于珠光体与奥氏体间的无序界面假设和稳态扩散方程分别发展了以体扩散控制和以界面扩散控制为主的动力学理论。两种理论均与实验结果符合较好，但后者似更合理。最近的实验在珠光体中发现了生长台阶与结构台阶，表明生长动力学方程需要修正。     

冷却速率对Al-Si-Mg三元合金凝固过程的影响

试验研究了冷却速率对Al-2.06%Si-1.58%Mg三元合金凝固过程的影响.同时通过热力学计算预测了不同冷却条件下Al-2.06%Si-1.58%Mg三元合金的凝固路径和相析出规律.试验及计算结果均表明,改变凝固速率可使Al-2.06%Si-1.58%Mg合金的凝固过程按照不同的路径进行,从而达到控制析出相种类的目的.在低的冷却速率下,相析出规律为:L→L1 Fcc_A1→L1 Fcc_A1 Si→L1 Fcc_A1 Si Mg2Si,而在较高的冷却速率下,相析出规律为:L→L1 Fcc_A1→L1 Fcc_A1 Mg2Si→L1 Fcc_A1 Si Mg2Si.     

低碳微量铌钢形变过程中动态相变的特点

用热模拟变形实验研究了低碳微量铌钢形变中的动态相变以及形变后冷却中的相变行为，透射电镜观察了Nb（CN）的析出及对铁素体晶粒截径和体积转变量的影响。结果表明：含Nb钢动态相变中铁素体形核位置依次为原奥氏体晶界、铁素体，奥氏体的相界前沿直至奥氏体晶内，随着细小的应变诱导Nb（CN）析出在基体上弥散分布，铁素体的转变量大幅增加并且其相变长大趋势得到有效抑制，使得铁素体的长大在时间和空间上均受到限制，是一个以形核为主的过程，相变完成后铁素体晶粒截径约为2舯；而形变后冷却相变工艺中铁素体的形核位置主要为奥氏体晶界以及形变带，而大量弥散分布的Nb（CN）析出对细化铁素体晶粒的作用并不明显，是一个形核长大的过程，最终得到的铁素体晶粒截径约为7μm。     

Dispersion-strengthening effect of Cu-based Mn, Al, and Zn rich alloys

In this systematic study, dispersion-strengthening effect of the Cu–25.91Mn (wt.%), Cu–26.62Mn–8.99Al (wt.%), Cu–22.17Mn–12.32Zn (wt.%) ingot alloys have been investigated. Samples were homogenized at a high fixed temperature in different periods and cooled with different cooling rates. After processes, microanalysis of the samples were interpreted by using scanning electron microscope (SEM) and weight percentages of the elements of the occurrence phases in the samples obtained by using electron dispersion spectroscopy (EDS) technique. Additionally, some characteristic properties of the heat treated samples with different conditions of Cu–Mn, Cu–Mn–Al, Cu–Mn–Zn ingot alloys were also discussed.     

二元包晶合金研究进展

综合评述了二元包晶合金凝固领域的有关理论和实验研究的进展情况.指出,目前研究的内容主要集中在固态方面,而对与凝固过程密切相关的液态二元包晶合金的结构和性质则涉及很少.因而从液态二元包晶合金的结构和性质入手,寻求液态和固态之间的相互关系,是一个值得研究的新课题.     

Al-C和Al-Ti-C中间合金对AZ91合金晶粒的细化

制备出两种用于AZ91合金晶粒细化的Al-C和Al-Ti-C中间合金.结果表明:这两种中间合金对AZ91合金均有良好的晶粒细化作用.向AZ91合金中加入1%的Al-C中间合金可使晶粒由原来的约130μm减小至65μm左右;向AZ91合金中加入1%的Al-TI-C中间合金可使晶粒由原来的约130μm减小至45μm左右.然而,两种中间合金添加量分别大于1%时,晶粒尺寸没有进一步的变化.分析认为:Al-C和Al-Ti-C中间合金起晶粒细化作用的分别是Al4C3相和Al4C3和TiC复合相.     

20钢渗硼过程中硼化物形核和生长的TEM观察及室温形变的影响SCIEI

本文采用单向减薄制样法在透射电镜下直接观察了20钢渗硼初期硼化物的形核和生长特性及室温形变的影响。X射线及电子探针分析结果表明:渗硼初期试样表层仅有Fe_2B形成;表层硼原子浓度与形变量之间具有单调增长的关系;偏聚于位错胞壁之中的硼原子阻碍了形变组织的恢复和再结晶,加速了硼化物的形核和长大。     

液态金属快速结晶的热力学驱动力

采用超高真空无容器悬浮熔炼技术使液态Ｆｅ和Ｎｉ的过冷度分别达２００和２３５Ｋ，借助量热法测定出其比热各为４８．６和４０．５Ｊ·ｍｏｌ~（－１）·Ｋ~（－１）．据此精确计算出深过冷Ｆｅ和Ｎｉ快速结晶的热力学驱动力△Ｇ_（ＬＳ），并与Ｔｕｒｎｂｕｌｌ模型和Ｄｕｂｅｙ－Ｒａｍａｃｈａｎｄｒａｒａｏ模型的近似计算结果相比较，发现这两种近似模型在过冷度超过１００Ｋ时均产生大于１％的偏差．进一步分析发现，△Ｇ_（ＬＳ）的计算偏差对深过冷液态金属中晶体形核率的影响极大，因此快速凝固研究中应尽可能精确计算△Ｇ_（ＬＳ）．