纳米二氧化硅对硅酸盐水泥水化硬化的影响

利用微量热分析、X射线衍射、差热分析、扫描电镜和氮气吸附等手段研究了纳米SiO2对硅酸盐水泥水化硬化的影响.结果表明:纳米SiO2掺量为5%(质量分数)时,其高火山灰反应能大量吸收Ca(OH)2,进而促进水泥水化,提高水化开始时的放热速率,并改善水泥浆体的微观结构,使得水泥石更加均一密实.同时,纳米SiO2的掺入使得标准稠度需水量急剧上升,凝结时间缩短,促进水泥石的中后期强度增长.     

Chemical control of colloidal fouling of reverse osmosis systems

Fouling of membranes by colloidal organic and inorganic particles continues to be documented as the most common and challenging obstacle in attaining stable continuous operation of reverse osmosis (RO) and ultrafiltration (UF) systems. Much current research is being conducted on physical parameters to mitigate such fouling. The focus has been on membrane synthesis and element design; microfiltration and ultrafiltration pretreatment; electromagnetic devices; correlation with physical factors such as Silt Density Index, zeta potential and critical flux; technique of direct observation of fouling process through a membrane; and classification of macromolecular organics for correlation with fouling characteristics. We report initial successes with chemical control of colloidal fouling. Through screening with a large number of observable coagulations of natural colloids, we have developed a group of proprietary anticoagulants and dispersants that would, at less than 10 ppm dosage to the RO feedwater, control various classes of colloidal foulants. Case studies of the control of humic matter, elemental sulfur and colloidal silicate in problematic RO systems that became stabilized are briefly presented. We conclude that a great need and potential exists in economically controlling the myriads of fouling interactions of colloidal particles during concentration within the brine channels of RO membrane elements. Low dosages of antifoulants can in many cases obviate the need for installation and maintenance of pretreatment unit or operations designed to remove such colloidal foulants from the process stream.     

填料对双组分缩合型室温硫化硅橡胶性能的影响

考察了多种补强填料和半补强(或增量)填料如硅藻土、碳酸钙和氧化铝等对室温硫化(RTV)硅橡胶的机械性能和介电性能的影响。结果表明,采用经六甲基二硅氮烷处理的气相法白炭黑或沉淀法白炭黑作填料时,RTV硅橡胶多方面的性能都有所提高;采用补强填料和半补强填料并用的RTV硅橡胶的性能优于使用单一补强填料的RTV硅橡胶;随着填料用量的增加,RTV硅橡胶的机械性能、相对介电常数和介质损耗因数都有一定程度的提高,但体积电阻率有所降低。     

Synthesis and characterization of organic-inorganic hybrid thin films from poly(acrylic) and monodispersed colloidal silica

Hybrid thin films containing nano-sized inorganic domain were synthesized from poly(acrylic) and monodispersed colloidal silica with coupling agent. The 3-(trimethoxysilyl)propyl methacrylate (MSMA) was bonded with colloidal silica first, and then polymerized with acrylic monomer to form a precursor solution. Then, the precursor was spin coated and cured to form the hybrid films. The silica content in the hybrid thin films was varied from 0 to 50 wt%. The experimental results showed that the coverage area of silica particle by the MSMA decreased with increasing silica content and resulted in the aggregation of silica particle in the hybrid films. Thus, the silica domain in the hybrid films was varied from 20 to 35 nm by the different mole ratios of MSMA to silica. The results of scanning electron microscope, transmission electron microscope, and elemental analysis support the above results. The prepared hybrid films from the crosslinked acrylic polymer moiety showed much better film uniformity, thermal stability and mechanical properties than the poly(methyl methacrylate) (PMMA) based hybrid materials. Large pin-holes were found in the PMMA-silica hybrid films probably due to the significant difference on thermal properties between the two moieties or the evaporation of solvent. The refractive index decreased linearly with increasing the silica fraction in the hybrid films. Excellent optical transparence was obtained in the prepared hybrid films. These results show that the hybrid thin films have potential applications as passive films for optical devices.     

界面光催化剂对罗丹明B的吸附及其光催化性能研究

以中空粒子TiO2@@SiO2为载体,通过表面烷基化改性,制备出一种能漂浮于水面的界面光催化剂TiO2@@SiO2-O,并用IR,TG,接触角对其进行表征。结果表明:在无搅拌状态下,与中空粒子TiO2@@SiO2相比,界面光催化剂TiO2@@SiO2-O对罗丹明B的吸附性大大增加,其光催化效率提高了30%。     

虎眼万年青总皂苷中单体皂苷的分离纯化

虎眼万年青总皂苷中含有很多皂苷组分,为了得到虎眼万年青单体皂苷,采用硅胶柱层析法分离虎眼万年青总皂苷,以氯仿-甲醇混合液为流动相进行洗脱,TLC跟踪检测。5 g虎眼万年青总皂苷进行硅胶柱层析分离,TLC检测,得到5种虎眼万年青皂苷的单体组分,得率分别为2.6%、2.6%、3.6%、5.4%、12.6%。超高压液相色谱检测,分离效果相对较好的是D、E组分。结果表明,采用硅胶柱层析的方法可以初步达到分离纯化虎眼万年青皂苷的目的。     

酶解产物人参皂苷Rh_2、Rh_3的二氯甲烷层析分离

人参皂苷Rh2、Rh3具有一定的抗癌作用,而这些稀有皂苷在传统红参中的含量甚微。为了获得纯度较高的人参皂苷单体,将人参二醇类皂苷经酶转化等方法处理,得到以人参皂苷Rh2和Rh3为主的混合物。常压下,用二氯甲烷-甲醇作为洗脱液变换梯度进行硅胶柱分离,分别采用流动相V(二氯甲烷)∶V(甲醇)=7∶0.10、7∶0.13、7∶0.15、7∶0.18、7∶0.2、7∶0.3渐变梯度进行洗脱,当流动相V(二氯甲烷)∶V(甲醇)=7∶0.3时,成功分离出人参皂苷Rh2和Rh3。经高效液相色谱检测,为反式的二十、二十二碳烯Rh3和顺式的二十、二十二碳烯Rh3(即Rk2)混合物,纯度达到95%以上;也得到较纯的Rh2,经高效液相色谱检测为20(S)-Rh2和20(R)-Rh2异构体的混合物,纯度达到85%以上。     

人参皂苷Re的分离提纯

采用硅胶柱层析法分离人参叶三醇皂苷,以氯仿-甲醇为流动相洗脱,得到了纯度较高的人参皂苷Re。结果表明,利用硅胶柱层析柱从35 g叶三醇皂苷中分离得到人参皂苷Re7.36 g,得率为21.03%。采用重结晶法对经硅胶柱分离制备的5 g Re进行提纯,将结晶产品分开收集,第2次结晶效果最好,得产品2.43 g,得率为48.68%,纯度为98.89%。     

含镁羟基磷灰石、磷酸三钙复合生物陶瓷涂层的研究

通过溶胶凝胶法在钛合金基体上合成了含镁羟基磷灰石/β-磷酸三钙陶瓷复合涂层．研究表明,羟基磷灰石相与β-磷酸三钙相共同存在于600℃烧结的复合涂层中．X射线光电子能谱分析显示,镁离子已合成到涂层之中．在模拟体液中,在复合涂层表面沉积出了较为明显的新生类骨层．使用MG63细胞进行培养试验,结果显示涂层具有良好的细胞亲和性．试验结果表明：含镁羟基磷灰石／β-磷酸三钙复合涂层具有良好的生物活性,有望在医疗实践中作为人工骨质材料得到广泛应用．     

多壁碳纳米管负载ZnO纳米复合材料的制备及其光催化性能研究

采用溶胶法,以醋酸锌和硝酸处理过的多壁碳纳米管（MWCNTs）为主要原料,制备了MWCNTs-ZnO光催化复合材料。通过X射线衍射（XRD）、透射电子显微镜（TEM）、扫描电子显微镜（SEM）等手段研究了制得样品的形态结构;通过紫外-可见分光光度计（UV-vis）,在紫外光照射下,分析比较了MWCNTs-ZnO复合材料、MWCNTs和ZnO的混合物以及纯ZnO对甲基橙光催化降解的性能。结果表明：在相同条件下MWCNTs-ZnO复合催化剂对甲基橙光降解有着最高的光催化活性。讨论了复合催化剂用量、重复使用等因素对甲基橙光催化降解效果的影响,并就复合催化剂的抗光腐蚀机制进行了初步的探讨。