Piezoresistive Behavior Study on Finger‐Sensing Silicone Rubber/Graphite Nanosheet Nanocomposites

A novel finger‐sensing nanocomposite with remarkable and reversible piezoresistivity is successfully fabricated by dispersing homogeneously conductive graphite nanosheets (GNs) in a silicone rubber (SR) matrix. Because of the high aspect ratio of the graphite nanosheets, the nanocomposite displays a very low percolation threshold. The SR/GN nanocomposite with a volume fraction of conductive nanosheets closest to that for the percolation threshold presents a sharp positive‐pressure coefficient effect of the resistivity under very low pressure, namely, in the finger‐pressure range (0.3–0.7 MPa), whereby the abrupt transition could be attributed to compressive‐stress‐induced deformation of the conducting network. The super‐sensitive piezoresistive behavior of the nanocomposite is accounted for by an extension of the tunneling conduction theory which provides a good approximation to the piezoresistive effect.     

一种环氧树脂阻尼灌封胶的热氧加速老化研究

研究了某种环氧树脂阻尼灌封胶在热氧老化的作用下分子结构、硬度、断面形貌以及动态力学性能随时间的变化．傅立叶红外光谱图表明，所制备的样品环氧基团反应比较完全，热氧老化后试样表面由仲胺和环氧基团形成的酯键发生了部分断裂和氧化；邵氏硬度的增加、瓦向高温区移动则表明在老化过程中复杂的固化反应仍然继续进行；最大损耗因子（tanδmax）波动较小表明试样老化后分子结构几乎保持不变；SEM图片显示试样的冲击断裂由老化前的韧性转变为老化后的脆性断裂．     

改性生物质作为型煤黏结剂的研究

探讨了用NaOH改性生物质秸秆作为型煤黏结剂的可行性,考察了NaOH溶液浓度对生物质改性的影响以及生物质添加量、无机物(MgO和MgCl2)添加量对型煤机械强度、防水性能和着火温度的影响。研究结果表明,NaOH改性液的质量分数为1.0%~2.0%时,制得的生物质型煤有较高的机械强度;生物质添加量在2%~20%时,随生物质添加量的增加,机械强度增加,着火温度降低,但防水性较差;而在生物质型煤中加入适量无机黏结剂后,型煤有很高的浸水强度,表现出优越的防水性能。     

3Cr-3Mo二次硬化钢的回火组织和力学性能

研究了3cr—3Mo二次硬化钢淬火回火后的组织和力学性能。结果表明：随回火温度的升高，试验钢中先后析出M3c、M2c和M7C3等碳化物，在575℃回火时硬度达到峰值；400一575℃回火后试验钢的抗拉强度约为l600MPa，冲击韧性为30J／cm^2；回火温度高于600℃时，强度和硬度迅速下降，冲击韧性增加；640℃回火时，以M2C型碳化物为主，抗拉强度为1100MPa，冲击韧性增加至55J／cm^2。     

Comment on Greenwood (2007): Solving the puzzle of structure/function relations in the aging brain?

Neuroimaging experiments have shown that prefrontal regions of the brain, which have the most age-related volume loss, are also the regions most likely to be more active in older adults than in younger adults. In an attempt to solve this puzzle, P. M. Greenwood (see record 2007-15625-001) has proposed a cascade that flows from age-related atrophy in the brain to changed processing strategies that result in plastic changes in regions adjacent and contralateral to the atrophic areas, culminating in greater functional activity. This hypothesis should stimulate research into these mechanisms and hopefully will ultimately inform researchers' ability to rehabilitate cognitive disorders in the elderly. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

4%Cr铸钢支承辊热处理工艺

以太钢1549轧机采用的4%Cr铸钢支承辊为依托,研究了该辊子从铸造成形到最终精加工之间的三次热处理工艺。最终达到其技术要求:辊身硬度65~70HS、淬硬层深≥70 mm、辊颈硬度42~48HS。     

Preparation and Properties of Rare Earth Modified Carbon Black/Natural Rubber Composites

The oxides Eu, Ho, Er and Dy were used to prepare the hydroxides of rare earth modified carbon black. Then natural rubber latex （NRL） was added into the reactor. The system reacted at 85 ℃ with stirring for 1 h to prepare powdered HAF-Ln（OH）3/NR composites. The effects of the kind and content of Ln on the particle size distribution of P [ NR/HAF-Ln （OH）3 ] and mechanical properties of its vulcanizate were studied respectively. It is found that rare earth can help to get the powder of the composite, the product particle with a diameter less than 0.9mm will be get when the composites containing the compound of Ho, Er and Dy with dosage of 1.0, 1.0, O. 5 percent, respectively. The adding of Ln can improve the tensile strength and tear strength of the vulcanizate effectively, what＇s more, Er and Dy can decrease the permanent set of vulcanizate significantly. The SEM studies shows that P[ NR/HAF-Dy （OH）3 ] vulcanizate shows superior mechanical properties that depend primarily on the absence of free carbon black, the fine dispersion of carbon black in the rubber matrix and better polymer-filler interaction.     

影响道路沥青低温抗裂性能的因素

用弯曲梁流变仪、直接拉伸试验机对7种国内外油源沥青样品进行了低温抗裂性能的评价，从沥青的四组分、相对分子质量及其分布来分析其对沥青低温抗裂性能的影响，结果表明，沥青的相对分子质量分布宽，对沥青的低温抗裂性能有利。     

Effects of Y and Ce on Microstructures and Properties of Nb-Si System Composites

The effects of yttrium and cerium on microstructures and properties of Nb-Si system composites were investigated by scanning electron microscopy( SEM), energy dispersive spectrum(EDS), X-ray diffraction(XRD) and high temperature oxidation experiments.It is found that the coarse primary silicide phase became finer and more homogeneous with Y and Ce addition.The results of high temperature oxidation experiments show that the oxidation rates of NbSi system composites with an appropriate amount of Y and Ce decrease compared with those of alloys without Y or Ce addition, and oxidation products mainly distribute along the phase boundaries between the Nb solid solution and silicide.     