激光熔覆模压硬质合金粉末层的研究

利用液压机和简易模具直接将硬质合金粉末(25? 15%Co 60% WC)压制在碳钢基体上;采用大功率CO2激光器对预置层进行扫描,在一定工艺参数下得到了表面较为平整、无裂纹、与基体形成良好冶金结合的涂层;利用扫描电镜和显微硬度计对涂层进行成分、形貌和显微硬度分析.结果表明,在相对较软的涂层基体上分布着高硬度的条状碳化物及少量的鱼骨状共晶体.涂层的平均硬度达到56HRC.     

Prevention of steel corrosion in concrete exposed to seawater with submerged sacrificial anodes

This paper presents the results of a study of the effectiveness of submerged sacrificial anodes in preventing the onset of pitting corrosion in the emerged part of marine piles. Experimental tests were carried out on reinforced concrete columns with steel embedded both in chloride free concrete and chloride contaminated concrete in order to compare the effects of sacrificial anodes on passive steel and on corroding steel. Results have shown, at least under the present testing conditions, that sacrificial anodes may be more effective in preventing corrosion initiation (i.e. in providing cathodic prevention) than in controlling ongoing pitting corrosion (i.e. in guaranteeing cathodic protection). Monitoring criteria for this type of prevention are also discussed.     

喷涂与激光重熔技术制备镍基纳米钴包碳化物复合涂层的研究

采用横流2．0kW CO2激光器，在45钢表面制备了表面较平整、较细密、基本消除了裂纹与孔隙并与基体呈冶金结合的镍基纳米WC／Co复合涂层。通过SEM，EDAX，XRD，AFM及Nano Indenter XP分析了熔覆层的显微组织、成分、物相及结合强度。结果表明，涂层的显微组织为涂层中镶嵌着大量与Ni基合金结合良好的WC／C。颗粒，其中在原子力显微镜下可见相当数量的粒度≤100μm的纳米颗粒。涂层的结合强度比传统热喷涂涂层提高了2．1倍。涂层中纳米WC／Co的纳米效应在激光熔覆中起着重要作用。     

激光表面熔凝处理对U-2Nb合金抗腐蚀性能的影响

利用波长1．06μm的激光对U-2Nb合金进行了表面熔化处理。结果表明；U-2Nb合金激光熔化层的显微硬度（HV）由处理前的2900MPa提高到3300MPa；合金基材为双相（α＋γ）珠光体，经激光处理后变成马氏体（α′），激光处理能细化显微组织，使Nb元素实现均匀分布。阳极极化试验与质量法腐蚀试验表明：激光处理能明显提高合金的抗腐蚀能力，在FeCl3·6H2O溶液中激光处理后合金的失重仅为处理前的1／5。     

高速钢激光表面熔凝层的显微结构SCIEI

本文对W_(18)Cr_4V高速钢进行激光表面熔凝处理,采用光学显微镜和透射电镜分析表明,熔凝层组织为极细的树枝晶。部分枝晶中心保留有δ铁素体。枝晶内为孪晶马氏体和少量位错马氏体,孪晶马氏体上沿孪晶面M_(23)C_6碳化物呈薄片状共格析出。枝晶臂间为富W,V和Cr合金元素的奥氏体和M_6C碳化物。     

反射衰减诊断激光光束的应用分析

介绍了普通光学元件反射诊断激光光束的应用,提出了利用平面平晶的平面反射进行光能衰减,详细论述了采用该方法进行光能衰减的可行性,分析了平面平晶反射衰减中反射光S偏振态和P偏振态能量的差异,对激光束诊断的影响和解决方法,结合半导体绿激光器的光束诊断进行了应用分析。实验证明,该方法结构简单、调整方便、误差小,利用普通平面平晶反射衰减即可满足激光强度的匹配要求,实现了待测激光束无失真取样,达到很好的测试效果。     

送粉激光堆焊梯度功能材料

采用同步送粉的方法进行了316L不锈钢和铁基合金粉末的激光堆焊.通过显微组织观察、SEM电镜扫描、拉伸试验、磨损试验和EDAX能谱分析等手段对激光堆焊层组织性能以及成分进行了分析和测试.两种堆焊材料的梯度功能组合使得不同堆焊部位可以满足不同的工艺和性能要求.激光堆焊层和基体呈冶金结合、稀释率小,堆焊组织细小、致密、无裂纹、气孔等缺陷,底层试样抗拉强度和伸长率达到752.4MPa和41.05%,表层材料磨损性能大大超过基体材料.送粉激光堆焊可以实现材料与性能的优化匹配,为金属零件的梯度功能修复和复杂零件的成形提供了一条有效途径.     

Laser melting of Ti-15Al-20Nb alloy

Titanium aluminides have become promising materials for high-temperature applications, but the relatively poor oxidation resistance and elevated- temperature strength of these alloys limit their application to temperatures lower than 1000 °C. Niobium addition improves the properties of titanium aluminide. However, the mechanical, metallurgical, and corrosion properties of Ti- Al- Nb may be improved by treatment with a laser beam. Consequently, the present study examines the properties of Ti- 15Al- 20Nb alloy subjected to the Nd:YAG laser melting process. Hardness in the surface region increases to twice the base material hardness, and corrosion resistance improves considerably after laser treatment.     

表面处理对球墨铸铁接触疲劳性能的影响

本文研究了激光微熔处理和高频感应加热淬火对球墨铸铁表面组织、接触疲劳强度和接触疲劳破坏过程的影响。结果表明,激光处理和高频淬火均可提高球铁的接触疲劳强度,但其接触疲劳破坏过程和形式却不同,前者是由于硬化层与基体间裂纹扩展造成大块深层剥落,后者则是表层裂纹在油楔作用下造成小块浅层脱落。     

浅谈埋地钢质管道阴极保护对3PE涂层的影响

阴极保护和防护涂层的联合应用是埋地钢质管道腐蚀防护普遍采用的一项技术,已在国内数万公里管道上应用,并取得了显著效果。文章介绍了阴极保护的参数、目前采用较先进的3PE防护涂层(三层结构聚乙烯涂层,底层是熔结环氧粉末,面层是聚乙烯)下的阴极保护参数。通过对实例的研究分析,介绍阴极保护对3PE环氧粉末涂层的影响。