基于AlAs氧化法研制的垂直腔面发射激光器

结合垂直腔面发射激光器的制备,研究了AlAs选择性氧化工艺中氧化炉温、氮气流量、水温等条件和AlAs层的横向氧化速率之间的关系,并得到了可精确控制氧化过程的工艺条件,在优化的工艺条件下运用湿氮氧化制备出InGaAs/GaAs垂直腔面发射激光器,实现了器件的室温脉冲激射.     

Examination of the role of oxygen in the photografting of methacrylic acid on a polyethylene film with a mixed solvent consisting of water and organic solvents

The photografting of methacrylic acid (MAA) on a linear low‐density polyethylene film (thickness = 30 μm) under air and nitrogen atmospheres was investigated at 60°C in mixed solvents consisting of water and an organic solvent, with xanthone as a photoinitiator. The organic solvents used were acetone, methanol, tetrahydrofuran, and dioxane. A maximum percentage of grafting occurred at a certain concentration of the organic solvent in the mixed solvent. This was observed for the systems under both air and nitrogen. The grafting reaction under air exhibited an induction period, but the rate of grafting after the period was greater than that under nitrogen. The formation of poly(ethylene peroxide)s by photoirradiation seemed to be a factor for the accelerated photografting under air. On the basis of attenuated total reflection infrared spectroscopy and scanning electron microscopy of the grafted film, the MAA‐grafted chains of the sample prepared under air tended to penetrate more deeply inside the film than those of the sample prepared under nitrogen. The resulting grafted films exhibited a pH‐responsive character: the grafted films shrank in an acidic medium but swelled in alkaline medium. This was evaluated from measurements of dimensional changes in the grafted films. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 992–998, 2003     

苯和甲苯差分吸收光谱方法的实验室测量研究

本文介绍了差分光学吸收光谱法(DOAS)测量大气污染气体浓度的基本原理。DOAS方法就是利用氙灯发出的紫外—可见光，经望远镜准直后再经过一段距离的传输，由望远镜来接收．在传输中，由于各种不同的分子在不同的波段对光有不同的吸收特征，使光谱具有了污染物的特征，再通过与光源发出的光进行比较，反演这些气体在大气中浓度．我们将DOAS方法应用在监测有机物上，在分析光谱的过程中，应用多项式拟合和最小二乘法，从而精确地从测量光谱中来反演出大气中污染气体的浓度．文中用DOAS方法测量了苯和甲苯的样品，并分析了结果，结果和理论吻合．可为环境中有机污染物监测提供可靠的方法。     

EPON:下一代接入网的最佳选择

EPON技术具有大带宽、高性价比、结构简单和一定服务质量保证等特点,被业界普遍看好,成为 下一代接入网的最佳候选技术.本文主要介绍了EPON的工作原理、分层结构、接入控制和组帧方式,最后给出 了实现EPON的关键技术和难点以及EPON的发展近况.     

Effects of cononsolvency on gelation of poly(vinyl alcohol) in mixed solvents of dimethyl sulfoxide and water

We studied the rates of gelation and phase separation of poly(vinyl alcohol) (PVA) solutions in mixtures of dimethyl sulfoxide (DMSO) and water at 25 °C and found that both the rates show a maximum at a volume fraction of DMSO φ_DMSO=0.60 while gelation was not observed either in pure DMSO or pure water, suggesting that water-DMSO is a cononsolvent system for PVA. On the basis of the data by Cowie [Can J Chem 36 (1961) 2240] we concluded that the 1:2 stable complex between one DMSO molecule and two water molecules is the main cause of this cononsolvency.     

溶胶–凝胶法制备ATO-SiO_2抗静电复合薄膜的特性研究

采用两步溶胶–凝胶法制备出 ATO(掺锑氧化锡)-SiO_2复合抗静电薄膜。通过 DTA-TG、XRD、SEM 对 薄膜的结构和形貌进行了表征,结果表明:抗静电复合薄膜表面均匀致密。薄膜中 SiO_2为无定形结构,ATO 的衍射峰 与 SnO_2一致。研究了 SnO_2的含量对薄膜导电性能、结合强度和透过率的影响,发现随 SnO_2含量增加 ?(SnO_2/ SiO_2)从 5 至 12.5,薄膜的表面电阻降低(从 1010ù/□降低到 108ù/□),薄膜的结合强度下降,薄膜的透过率降低(从 89.0%降至 84.2%),结合三方面性能,得出最佳 SnO_2的配比为:?(SnO_2/ SiO_2)=10。     

一种基于DBF的双基地雷达系统的性能分析与实验研究

讨论了一种基于数字波束形成的脉冲追赶式双基地雷达系统的构成和基本工作原理．对该双基地雷达的性能进行了理论分析，并通过实验结果进行了验证。     

Preparation and properties of poly(ethylene oxide) star polymers

Poly(ethylene oxide) (PEO) star polymers were prepared by anionic polymerization of methacryloyl chloride and glyceryl trimethacrylate with sec‐butyllithium in cyclohexane. The ensuing polymers were grafted with poly(ethylene glycol) of molecular weight 400. The final product was washed with methylene chloride and analyzed with infrared spectroscopy, differential scanning calorimetry, and thermogravimetry. Star polymers of PEO were also prepared by anionic polymerization of glycidol with sec‐butyllithium in cyclohexane. The initiator was chosen so as to yield a polymer of 10,000 molecular weight. The resulting polymers were analyzed by nuclear magnetic resonance, infrared spectroscopy, and thermogravimetry. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 87: 322–327, 2003     

TMS320F240串口通信特征及其应用

主要论述了TMS320F240串行外设接口模块的特点，并通过与MCS5l单片机通信，实现液晶显示。     

Aggregate States and Energetic Disorder in Highly Ordered Nanostructures of para‐Sexiphenyl Grown by Hot Wall Epitaxy

We report on photoluminescence (PL) and thermally stimulated luminescence (TSL) in highly ordered nanostructures of para‐sexiphenyl (PSP) grown by hot wall epitaxy (HWE). A low‐energy broad band is observed in the PL spectra that can be attributed to the emission from molecular aggregates. While the intrinsic exciton emission in steady‐state PL dominates at low temperatures, the emission from aggregates increases with elevating temperature and its magnitude depends sensitively on film preparation conditions. Time‐resolved PL measurements showed that the aggregate emission decays with a life‐time of ≈ 4 ns, which is approximately an order of magnitude larger than the lifetime of singlet excitons. TSL data suggests the presence of an energetically disordered distribution of localized states for charge carriers in PSP films, which results from an intrinsic disorder in this material. A low‐temperature TSL peak with the maximum at around 30 K evidences for a weak energy disorder in PSP films, and has been interpreted in terms of a hopping model of TSL in disordered organic materials.