咪唑啉型缓蚀剂的合成及其缓蚀性能研究

以棕榈酸、二乙烯三胺为原料合成咪唑啉，并对其进行水溶性改性制备了咪唑啉型缓蚀剂YG-1，与助剂硫脲复配得到复配缓蚀体系YG-2。应用静态挂片失重法、电化学法评价了该复配缓蚀体系YG-2的缓蚀性能，研究了缓蚀机理，并用扫描电镜分析了腐蚀前后及加入复配缓蚀体系YG-2后A3钢的表面形貌。研究结果表明，在30℃下加入复配缓蚀体系YG-2能有效地抑制饱和CO2的高矿化度盐水对A3钢的腐蚀，其使用浓度为20mg／L时，缓蚀率达到98．5％，腐蚀速率仅为0．009mm／a，远好于我国石油天然气行业标准规定的指标。     

BaTiO3基Au纳米颗粒复合薄膜的制备及其光学性质研究

采用溶胶-凝胶（sol-gel）方法，成功的将高体积面分比的Au纳米颗粒复合到BaTiO3的非晶薄膜中，并对其光学性质进行了研究。用XRD、TEM、椭偏仪、吸收光谱、光克尔效应OKE（Optical Kerr Effcet）方法对薄膜进行了表征和测试。从吸收光谱观察到表面等离子体共振SPR（Surface Plasma Resonance)峰随热处理温度升高而红移的现象。光学非线性测试表明薄膜具有高的三阶非线性极化率Χ^(3)和超快的响应时间。     

Effect of Strain Rate on Discontinuous Flow and Mechanical Characteristics of High-Nitrogenous Steel

Experimental study on the effect of strain rate on discontinuous flow and mechanical characteristics of the high-nitrogenous steel Kh23AG19F has been performed. Within the range of strain rates from 4.62 · 10^-5 to 1.85 · 10 ^-4 s^-1, discontinuous flow, reflected by serration on the tensile diagram, is chiefly determined by intergranular deformation mechanisms. Under strain rates over 1.85 · 10^-2 s^-1, combined deformation modes prevail, which cause a change in the character of discontinuous flow and transform a serrated tensile diagram into a wavy graph, with the yield stress of steel increased significantly.     

改性沥青新型磨耗层在高等级路面上的应用

从材料、适用范围、形成机理、经济分析、施工工艺五个方面，介绍了改性沥青新型磨耗层在高等级路面上的应用，并通过试验路的观察表明，改性沥青新型磨耗层具有快速排水、增加摩阻力、愈合原路面微裂缝和较强抗磨耗的功能，是处置高等级路面上常有的龟裂、网裂、脱皮、露骨、抗磨系数不足、渗水等病害较具推广价值的新型施工工艺。     

不同级配对微表处混和料性能的影响

微表处技术是一种性能优良的路面养护技术。首先检验了微表处用原材料的技术指标,在满足规范的要求下选择了三种不同级配,并对三种不同级配的微表处混和料的使用性能进行了比较。     

汽油烃类族组成测试方法对比

介绍了使用荧光指示剂吸附色谱法、多维气相色谱法的测定影响因素和近红外光谱快速法的分析特点以及三种方法在汽油族组成测定中的应用，并就三种方法对同一试样的测定结果进行了对比，找出各种测定方法容易产生误差的原因及分析对策。     

聚乙烯催化剂表面分形和多重分形特征

应用分形和多重分形理论研究了负载型聚乙烯催化剂(简称催化剂)表面形态。提出一种图片处理和计算过程更加完备的基于扫描电子显微镜照片的分形维数和多重分形谱计算程序,对4种催化剂进行分析计算。探讨了分形维数、多重分形谱相关参数与催化剂表面形态及与聚合活性的对应关系。实验结果表明,催化剂表面形态的复杂程度可以用表面分形维数来表征,聚合活性高的催化剂表面形态更加复杂,有更大的比表面积,对应的分形维数值也越大。催化剂表面分形维数的变化程度可以用多重分形谱来表征,聚合活性高的催化剂表面分形维数的跨度和分散程度更高。提出的分形维数和多重分形谱计算程序为催化剂的评定与设计提供了一种实用的手段。     

Effect of select parameters on the properties of edible film from water-soluble fish proteins in surimi wash-water

Edible film from water-soluble fish proteins were developed by casting film solution on leveled trays and effects of pH (9.5, 10.0 and 10.5), heating temperature (60, 70 and 80 °C), and heating time (10, 20 and 30 min) of the film solution on various film properties were determined using Response Surface Methodology (RSM). The impact of pH and heating temperature of film solution was more significant, overall, on the film's properties than heating time. Contour plots of tensile strength and elongation at break was highest at pH of 10.0 at 70 °C (2.75-3.02 MPa) but low in elongation at break (6.35-9.16%), while water vapor permeability and oxygen permeability were at their lowest (58.55-65.96 g mm/m² d kPa and 351.33-624.18 cm³ μm/m² d kPa). There was a direct correlation between the films’ and proteins’ solubility on one hand, and heating temperature of film solution on the other, which reversed with change in pH of film solution. Film color was darker and more yellowish with increase in the pH of film solution.     

新型高K栅介质ZrO2薄膜材料的制备及表征

采用超高真空电子束蒸发法制备了新型高 K栅介质-非晶 ZrO2薄膜. X射线光电子能谱 (XPS) 中 Zr3d5/2 和 Zr3d3/2 对应的结合能分别为 182.1eV和 184.3eV, Zr元素的主要存在形式为 Zr4+,说明薄膜由完全氧化的 ZrO2组成 ,并且纵向分布均一.扩展电阻法( SRP)显示 ZrO2薄膜的 电阻率在 108Ω@ cm以上,通过高分辨率透射电镜( HR- XTEM)可以观察 ZrO2/Si界面陡直,没有 界面反应产物 ,证明 600℃快速退火后 ZrO2薄膜是非晶结构.原子力显微镜( AFM)表征了薄膜的 表面粗糙度,所有样品表面都很平整,其中 600℃快速退火样品 (RTA)的 RMS为 0.480nm.     

润滑油用纳米TiO2的表面改性及自修复性能研究

采用油酸对纳米TiO2进行表面改性，使其稳定分散于基础油中。利用HQ-1摩擦磨损试验机考察纳米TiO2的自修复性能，并探讨其自修复机理。试验结果表明，经改性后的纳米TiO2粉体作为润滑添加剂具有良好的分散稳定性、减摩抗磨性和自修复性。