Fabrication and thermo stability of the SnO2/Ag/SnO2 tri-layer transparent conductor deposited by magnetic sputtering

Using the magnetic sputtering technique, the SnO₂/Ag/SnO₂ tri-layer transparent films were fabricated on float glasses successfully. Compared with the commercial FTO (F-doped SnO₂) film, the SnO₂/Ag/SnO₂ tri-layer films have higher visible-light transmittance and better conductivity. The total thickness of the SnO₂/Ag/SnO₂ films is one third of the commercial FTO film leading to the high visible-light transmittance. The high carrier concentration of the SnO₂/Ag/SnO₂ films contributes to the tri-layer films’ low resistivity. In addition, to further improve the performance of the SnO₂/Ag/SnO₂ tri-layer films, samples were annealed under different temperatures. The results illustrate that the lowest sheet resistance (5.92 Ω/sq) and the highest visible-light transmittance (87.0%) were obtained after annealing at 200 °C. Furthermore, the thermal stability of the films could be enhanced by a multi-step annealing process due to the recrystallization effect.     

罩式退火温度对高强IF钢组织及性能的影响

为研究不同退火温度下高强IF钢的组织性能及织构的变化规律,采用温箱式电阻炉加热模拟罩式退火工艺,研究了不同退火温度下高强IF钢210P1冷轧板力学性能;对不同退火温度钢板的r90进行了统计并对其进行显微组织观察;采用X射线衍射仪及热场发射扫描电镜对不同退火温度的罩式退火成品板进行了织构分析。结果表明,在高强IF钢210P1冷轧板的罩式退火过程中,提高退火温度将使晶粒明显长大。随着退火温度的升高,屈服强度及抗拉强度下降,伸长率升高,n值略有上升,板材横向r值增加较明显,有利织构{111}取向密度增加,不利织构{100}取向密度降低。     

双层过道布置问题的混合整数非线性规划模型及两阶段改进模拟退火算法

结合实际布局活动中，设施在多层空间布置的实际情况，提出了双层过道布置问题，并构建了该问题的混合整数非线性规划（MINLP）模型。针对问题特征，提出了一种改进模拟退火算法，通过采用两阶段改进策略，对退火过程及抽样过程进行改进。该算法以自适应搜索策略替代马氏链搜索长度，并引入记忆功能、回火操作以提高求解质量，通过设置双阈值来提高求解效率。应用所提算法对24个基准算例进行测试，并将其与原模拟退火算法和GUROBI精确方法作对比，验证了所提算法的有效性。     

航班恢复问题的迭代局部搜索算法

在恶劣天气和机械故障等原因造成航班不能按照原计划执行时，航空公司需要采取相应的措施对航班进行恢复。本文基于经典的资源指派模型，综合考虑了调整时间、换机、联程拉直、取消航班和调机5种恢复策略，提出一种以最小化加权成本为优化目标的航班恢复模型，并设计一种迭代局部搜索算法。首先用构造-修复启发式方法构造可行解，然后从该初始解出发，在飞机路线对的邻域中进行局部搜索。当陷入局部最优后，对解进行扰动，然后从扰动后的解重新出发进行局部搜索。为了提高搜索效率，同时降低陷入局部最优解的概率，局部搜索过程采用模拟退火算法。实例结果表明，本文提出的模型及算法能够在短时间内对受到影响的大规模航班计划进行恢复。     

Effect of the annealing procedure and the molecular weight on the crystalline phase morphology and thermal properties of polylactide

The thermomechanical properties of poly(lactide) (PLA) are strongly related to its semicrystalline microstructure and morphology. Thermal annealing is a strategy to improve the crystallinity of PLA. However, the different techniques and specimen types needed for each kind of characterization could lead to misleading conclusions. In this work, annealed samples of three PLA grades with different molecular weights were studied by DSC, wide angle X‐ray scattering and polarized optical microscopy (POM) and the results are related to their thermomechanical and impact properties. Special focus is put on the POM results obtained by different approaches and the suitability of each of them to be related to the thermomechanical properties. By annealing medium molecular weight PLA specimens at 140 °C an important increase of the heat distortion temperature was obtained, which was not related to the spherulite size but to the combination of high crystallinity degree together with high α/α′ crystal type ratio. However, the impact properties of annealed PLA decreased with increase in the annealing temperature according to an increment in crystallinity and in the α/α′ crystal ratio. © 2019 Society of Chemical Industry     

DP980高强钢连续退火后的组织与性能

研究了不同工艺参数对980 MPa级连续退火双相钢组织及力学性能的影响,利用光学显微镜、透射电镜(TEM)以及拉伸试验对双相钢的微观组织和力学性能进行测试及分析。结果表明:DP980钢的退火组织主要由铁素体、马氏体岛和少量的贝氏体组成,马氏体岛附近的位错密度较高。随着均热温度的升高,DP980钢的抗拉强度呈现先降低后升高的趋势,屈服强度与抗拉强度的趋势一致,伸长率先升高后降低。随着过时效温度的升高,DP980钢的抗拉强度和屈服强度降低,降低幅度较小,伸长率上升,但变化不明显,说明通过调整过时效温度来调控其力学性能的作用较小。     

球化退火工艺对高碳马氏体不锈钢8Cr13MoV组织及性能的影响

为了优化高碳马氏体不锈钢8Cr13MoV的球化热处理工艺,提高其退火后的冷加工性能,采用微观组织分析法以及拉伸力学分析法研究了球化退火过程中奥氏体化保温时间和冷却速率对8Cr13MoV钢的球化效果影响。结果表明, 随着奥氏体保温时间的增加,组织中细颗粒状碳化物数量减少,索氏体数量增多,试样硬度先降低后升高,但断后伸长率持续增加;随冷却速率增加,试样组织中细颗粒状碳化物和索氏体数量、硬度和强度增加,断后伸长率降低。综合对比,奥氏体保温时间ϕ90 min时试样综合力学性能较好,冷却速率应控制在25 ℃·h^-1以内。与奥氏体保温时间相比,冷却速率对力学性能的影响更加显著。     

缓冷出口温度对连续退火SPCC冷轧薄板屈服强度的影响

研究了缓冷出口温度对连续退火SPCC冷轧薄板组织和屈服强度的影响。结果表明:连续退火SPCC冷轧薄板的组织由等轴的铁素体晶粒和晶界处的块状渗碳体及晶粒内的颗粒状渗碳体组成。随着缓冷出口温度从680 ℃提高至700 ℃,平均晶粒尺寸从10.1 μm增加至12.5 μm;此外,提高缓冷出口温度还能够抑制晶界处块状渗碳体的形成,促进晶粒内细小渗碳体更加细小弥散的析出。当缓冷出口温度从680 ℃提高至700 ℃时,冷轧薄板的屈服强度约降低了28 MPa。     

退火工艺对搅拌摩擦加工镁合金微观组织和显微硬度的影响

采用搅拌摩擦加工(Friction stir processing,FSP)技术对AZ31镁合金进行加工,通过采取不同温度及保温时间的退火工艺,研究了FSP镁合金在退火过程中的微观组织演变过程及硬度变化规律。结果表明,FSP成功制备了细晶AZ31镁合金,其平均晶粒尺寸细化程度达54.9%。当退火温度在200～300 ℃时,加工区(SZ)晶粒尺寸较为稳定,且组织发生不同程度的均匀化和细化;当温度超过300 ℃时,加工区晶粒互相吞噬而快速长大。在退火温度较低、短时间保温时热影响区(HAZ)组织变化不明显,而延长保温时间或者升高温度,HAZ区组织会迅速细化、均匀化;当退火温度超过300 ℃时,再结晶会在短时间内完成,随后晶粒继续长大。在300 ℃下保温60 min为最优退火工艺,可使SZ、HAZ组织分别细化10.9%、35.6%。