表面织构形状对牙轮钻头轴承摩擦学性能影响的实验研究

牙轮钻头滑动轴承作为钻头破岩过程中传递载荷的关键部件,在低速重载的钻井过程中易发生黏着磨损失效。为改善牙轮钻头滑动轴承的耐磨性能,利用纳秒激光雕刻技术,在牙轮钻头滑动轴承轴颈表面加工了面积比为10%、深度为20μm的圆形、矩形、三角形及复合织构;基于赫兹相似理论,设计近似模拟钻头轴承工况的环-块配对副单元实验方案,并在UMT摩擦试验机上开展织构形状对钻头滑动轴承摩擦副摩擦因数、磨损量、温升变化和微观形貌影响规律的实验研究。结果表明:仿生织构的形状及布置方式对减摩和耐磨效果影响极大,其中圆形、矩形织构的减摩和耐磨性能最优,其次为三角形织构,而复合织构反而增大了摩擦因数及磨损量;单一织构对试件磨损量及温升的影响不大,而复合织构在增加摩擦的同时温度有明显升高,不利于井下高温环境下延长牙轮钻头寿命。     

Improving weld formability by a novel dual-rotation bobbin tool friction stir welding

A novel dual-rotation bobbin tool friction stir welding (DBT-FSW) was developed, in which the upper shoulder (US) and lower shoulder (LS) have different rotational speeds. This process was tried to weld 3.2 mm thick aluminum-lithium alloy sheets. The metallographic analysis and torque measurement were carried out to characterize the weld formability. Experimental results show that compared to conventional bobbin tool friction stir welding, the DBT-FSW has an excellent process stability, and can produce the defect-free joints in a wider range of welding parameters. These can be attributed to the significant improvement of material flow caused by the formation of a staggered layer structure and the unbalanced force between the US and LS during the DBT-FSW process.     

二维层状Ni/β-Ni(OH)2纳米复合材料的制备及其摩擦学性能研究

采用水热反应制备出β-Ni(OH)2,然后通过水热还原得到Ni/β-Ni(OH)2纳米复合粉体材料,采用X射线衍射仪(XRD)和扫描电子显微镜(SEM)对复合材料的相结构、成分及形貌进行表征分析。采用四球摩擦磨损试验机评价制备的Ni/β-Ni(OH)2作为润滑油添加剂的摩擦学性能,基础油为PAO6。摩擦试验后,采用SEM分析典型试验钢球磨斑的表面形貌,利用能谱仪(EDS)研究磨斑表面化学元素的组成,探讨Ni/β-Ni(OH)2纳米复合润滑添加剂的减摩抗磨机制。结果表明:Ni/β-Ni(OH)2纳米复合材料作为润滑添加剂具有极好的减摩抗磨性能,显著优于基础油PAO6和未负载纳米Ni的二维β-Ni(OH)2层状材料;与基础油相比,添加0.1%质量分数Ni/β-Ni(OH)2添加剂的油样的摩擦因数和磨斑直径分别降低了17.6%和41.5%;Ni/β-Ni(OH)2纳米复合粉体综合了纳米Ni及层状β-Ni(OH)2两部分结构特性,在摩擦过程中,复合材料中的纳米金属粒子Ni与层状结构材料β-Ni(OH)2能够相互增强起到协同润滑作用。     

Heat Transfer Analysis of MHD Power Law Nano Fluid Flow through Annular Sector Duct

Flow and heat transfer analysis of an electrically conducting MHD power law nano fluid is carried out through annular sector duct,under the influence of constant pressure gradient.Two types of nano particles(i.e.Cu and TiO2)are used in power law nano fluid.Strongly implicit procedure,(SIP)is used to simulate the discretized coupled algebraic equations.It has been observed that volume fraction of nano particles,ϕand magnetic field parameter,Ha are favourable for the heat transfer rate,however,both resist the fluid flow.Impact of applied uniform transverse magnetic field exceeds in the case of shear thickening fluids(i.e.n>1)by increasing the value of Ha as compared to that in shear thinning fluids(i.e.n<1).Therefore,enhancement in heat transfer rate is comparably more in shear thickening fluid.Furthermore,comparable limiting case study with published result is also carried out in this research paper.     

Tribological and corrosion behaviors of fluorocarbon coating reinforced with sodium iron titanate platelets and whiskers

A series of sodium iron titanate (NFTO)–fluorocarbon composite coatings have been prepared with the liquid-phase blending method. The effects of two types of NFTO, NFTO platelets, and NFTO whiskers, on the tribological and corrosion behaviors of the composite coatings, are systematically studied. The results show that the addition of NFTO can significantly enhance the friction-reducing and wear resistance performances of the fluorocarbon coating. Under dry sliding, the minimum specific wear rate is 1.67 × 10⁻⁴ mm³/Nm for the platelet-filled composite coatings and 1.15 × 10⁻⁴ mm³/Nm for the whisker-filled composite coatings, respectively, showing a decrease of 83.5 and 88.6% than that of pure coating. Under a simulated seawater environment, the minimum specific wear rate is 5.44 × 10⁻⁵ mm³/Nm for the platelet-filled composite coatings and 0.84 × 10⁻⁵ mm³/Nm for the whisker-filled composite coatings, respectively, showing a decrease of 90.5 and 98.5% than that of pure coating. The morphologies of worn surfaces, wear debris, and transfer films are analyzed, and the corresponding wear resistance mechanisms are discussed. The electrochemical impedance spectroscopy certifies a remarkably improved corrosion resistance of the composite coatings which have been immersed in 3.5 wt % NaCl solution for 30 days. The composite coating reinforced with 7.5 wt % platelets shows the highest resistance of 256.3 × 10⁶ Ω·cm², approximately two orders of magnitude higher than that of pure coating. © 2020 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020 , 137, 48936.     

25CrNi2MoV钢的微动磨损性能

采用微动摩擦磨损试验机在干摩擦条件下对新型高速重载传动轴用25CrNi2MoV钢进行微动磨损试验,研究了不同载荷(50~200N)和频率(15~30Hz)下该钢的微动磨损性能。结果表明:在频率为20Hz条件下,当载荷由50N增至200N时,25CrNi2MoV钢的平均摩擦因数由0.766减至0.661,磨损体积由19.65×10^-3 mm^3增至75.83×10^-3 mm^3;在载荷为30N条件下,当频率由15Hz增至30Hz时,平均摩擦因数由0.790增至0.905,磨损体积由11.43×10^-3 mm^3增至23.88×10^-3 mm^3;在不同试验参数下,25CrNi2MoV钢磨损表面均出现了氧化和犁沟现象,磨损机制包含氧化磨损和磨粒磨损;在频率为20Hz条件下,载荷为50,100N时,25CrNi2MoV钢的磨损机制以黏着磨损为主,载荷为150,200N时,主要磨损机制为疲劳磨损;在载荷为30N条件下,频率为15~25Hz时,磨损机制以磨粒磨损为主,当频率增至30Hz时,磨损机制以疲劳磨损为主。     

一种液压摩擦焊机电液系统研究与试验

针对海上石油平台、海底输送管线维修的需要,提供了一种液压摩擦焊机液压和电器系统设计思路,通过参数计算、电液控制系统设计,研发了一种液压摩擦焊机,通过对DH38钢摩擦叠焊单元成型工艺试验,发现焊接接头拉伸强度达到了母材强度的76%以上,验证了液压摩擦焊机的可靠性能,通过该研究的应用,可对海上石油平台、海底输送管线的维修起到积极作用。     

基于Matlab计算滚动轴承滚滑接触内部应力分布

滚动轴承服役过程中,因滚滑现象和残余应力的存在,使赫兹接触应力不能反映材料真实的受力状态,应力分布与实验现象存在一定的偏差,因此滚滑接触下材料的内部应力计算显得尤为重要。研究一种快速、简单的材料滚滑接触内部应力的计算方法,以替代耗时长的有限元法。以现有公式为基础,通过Matlab编程计算滚滑接触下材料内部的应力场;对比不同摩擦因数下2D、3D滚滑接触内部应力场的差别。结果表明:摩擦因数越大,最大剪切应力越大,位置越接近表面,与滚动方向的夹角越小;切向摩擦力使接触点两侧最大正交切应力大小及位置发生变化;随着摩擦因数增大,一侧应力值上升,位置靠近表面,另一侧反之。提出的计算方法简单、方便,其结果为解析解,便于与残余应力或其他应力结合求出真实应力场。通过实例分析发现,真实应力场能够更好地解释实验现象,对于轴承材料组织演变的研究有重要意义。     

单相硼化物的制备及摩擦磨损性能研究

为了深入研究渗硼层中硼化物的性能，采用真空感应熔炼法制备单相硼化物材料。观察分析制备的硼化物微观组织，测试其力学性能。采用MMU-5G型销-盘式摩擦磨损试验机，在干摩擦条件下，研究了不同载荷下单相硼化物的摩擦学性能，观察其磨损表面形貌特征，探讨其磨损方式。结果表明：制备的硼化物为单一相，试样纯度高，试样的平均显微硬度为HV2065，平均断裂韧性值为1.68 MPa·m1/2；硼化物的断口处没有宏观的塑性变形，断口齐平光亮，表现为脆性断裂特征；干摩擦条件下随着载荷从10 N增加到30 N，硼化物的摩擦因数先降低后增加，20 N载荷时达到最小值，而其磨损量随着载荷的增加不断上升；随着载荷从10 N增加到30 N，磨损表面的粗糙度先逐渐上升后急剧上升； 10~20 N载荷下，硼化物的磨损以磨粒磨损为主，而25~30 N载荷下，硼化物的主要磨损方式从磨粒磨损转变为脆性破损。