High energy Urbach characteristic observed for gallium nitride amorphous surface oxide

We have observed an “above band-gap” Urbach like characteristic for gallium nitride films (at the high energy side of the band-edge). A combination of X-ray diffraction, secondary ion mass spectroscopy and optical transmission measurements were taken for gallium nitride samples of different thickness. From this data we demonstrate that the high energy Urbach like characteristic is related to the presence of an amorphous surface oxide. It is shown to dominate the absorption spectra of thin gallium nitride samples, for which the influence of surface oxidation is strongest.     

亚稳态金属材料抗空蚀性能研究

用旋转圆盘实验机研究了三种金属材料的空蚀。试验结果表明 :Fe -Mn -Si形状记忆合金、Fe -Cr-Ni-Mn不锈钢空蚀中分别诱发产生密排六方晶体结构的马氏体和体心立方晶体结构的马氏体 ,其抗空蚀性能依次为 0Cr13Ni5Mo不锈钢的 7.3倍和 2 .1倍。亚稳态金属材料抗空蚀性能与空蚀过程中动态相变对应力的响应密切相关。空蚀诱发马氏体相变不仅有利于改善材料抗空蚀性能 ,而且马氏体相变及其逆转变引起的能量耗散和伪弹性大大提高了Fe-Mn -Si铁基形状记忆合金的抗空蚀性能     

Cr12MoV钢冷挤压成形模强化工艺的研究

针对Crl2MoV钢冷挤压成形模热处理存在的质量问题，对加热温度和方式进行了大量的试验研究，在此基础上，提出了改进的快速加热工艺。结果表明，经该工艺处理后，模具使用寿命得到显提高。     

调质状态下40Cr钢的焊接

在合理制定焊接工艺的基础上，采用R307珠光体耐热钢焊条成功地进行40Cr钢在调质状态下的焊接，解决了通常采用25—13型奥氏体焊条焊接出现的焊缝强度低、焊接接头性能差的问题。     

Cr∶LiSAF再生放大系统

设计了灯抽运Cr∶LiSAF(Cr∶LiSrAlF6)飞秒再生放大系统 ,对 80fs光脉冲 (展宽后约 10 3ps)进行了再生放大研究 ,获得了再生放大的输出能量与输入能量和放大倍率与放大往返次数间的关系 ,得到了 8× 10 5的放大倍率和 0 4mJ的单脉冲再生放大输出     

Simulation of the Forming Behaviour of a Boron Modified P91 Ferritic Steel

The forming behaviour at high temperature of a modified 9%Cr‐1%Mo (P91) ferritic steel containing B and Ti for elevated temperature service was investigated. The microstructure of the as‐received material is mainly martensite at room temperature, but special etching revealed prior austenite grains of about 25 μm in size. Torsion tests were conducted at temperatures in the range 850 to 1250 °C to simulate the hot rolling process under comparable conditions of temperature, strain rate and strain. The deformation data obtained from these tests were correlated with the Garofalo equation with a stress exponent of 4.6 and an activation energy of 315 kJ/mol. This equation was used to predict the formability behaviour for the rolling process and also to determine the maximum forming efficiency and stability of the steel. A temperature of 1200 °C is recommended to conduct the forming process.     

Cr12型模具钢锻造内部裂纹产生的原因及预防

基于Cr12型钢种的特点，归纳了Cr12钢锻造时内部裂纹的类型，分析了内部裂纹产生的原因并提出了相应的预防措施。     

控制W9Cr3Mo4V低倍碳化物剥落的工艺改进

针对W9Cr3M04V轧制成品材低倍碳化物剥落的形成原因分析，得出一次碳化物颗粒粗大、在1／4D至中心区域聚集是导致低倍热酸浸试验碳化物剥落的主因；由此进行冶炼过程中注速（锭形）、浇注温度选择对比工艺试验，得出在原有冶炼＋轧制的工艺基础上选用2．2t锭、降低浇注温度（1489℃）能有效改善一次碳化物颗粒大小和聚集程度，进而有效降低低倍碳化物剥落倾向。     

氢对2.25Cr-1Mo压力容器用钢力学性能影响

基于试样高温高压釜充氢方法 ,研究了氢对 2 2 5Cr 1Mo压力容器用钢力学性能的影响。对充氢前后的试样进行了拉伸和CVN冲击试验 ,结果表明 ,氢对 2 2 5Cr 1Mo钢的拉伸力学性能和冲击韧性影响不显著。     

ZrO_2与40Cr钢钎焊中的缓冲层

本试验研究了ＺｒＯ２与４０Ｃｒ钢在加入缓冲层前后的钎焊连接，结果表明：插入缓冲层Ｃｕ和Ｔｉ可以提高接头强度。对每一种缓冲层，存在一最佳厚度，对应的钎焊强度最大。此最佳厚度对Ｃｕ为０．４ｍｍ左右，对Ｔｉ为１ｍｍ左右。作者认为这是由缓冲层的力学性能和热膨胀系数对残余应力释放产生的两种相反影响而造成的。钎焊时，缓冲层Ｃｕ和Ｔｉ向钎料中均有程度不同的溶解，但不影响钎料对ＺｒＯ２的浸润和反应结合。ＺｒＯ２－４０Ｃｒ钢连接的所有接头均断在陶瓷的近缝区，其断裂方式有三种。