Superplastic behaviour of Ti-48at.%Al two-phase titanium aluminide compacts made from mechanically alloyed powder

An HIP compact of MA-processed powder having a nominal composition of Ti-48at.% Al was produced. The compact consisted of a large amount of TiAl(λ) and a small amount of Ti₃Al (₂), in a completely ultra-fine equiaxed grain structure. This two-phase compact showed typical superplastic deformation behaviour. A maximum elongation of 550% was obtained. A strain exponent, n = 2, and grain size exponent, p = 2, were determined from the results of a strain-rate-change test and a creep test at constant initial stress using samples having various grain sizes, respectively. The activation energy for creep, Q_c at constant stress was calculated to be 350 kJ/mole. It is concluded that the superplastic deformation mechanism of the material under study is grain boundary sliding controlled by lattice diffusion in the TiAl phase.     

LD钢超塑性压缩变形参数与金相组织

通过对ＬＤ（７Ｃｒ７Ｍｏ３Ｖ２Ｓｉ）模具钢起塑性压缩变形后的金相组织观察研究，分析了变形参数、原始组织对变形后金相组织的影响。     

NiAl超塑性变形的正电子寿命研究

研究了B2型多晶NiAl的晶界结构对缺陷态正电子寿命的影响，并结合正电子谱探讨了热挤压及超塑性变形过程后的晶界结构，热挤压的NiAl合金具有有完全的再结晶组织，而超塑性变形过程中的动态回复和再结晶是一种不完全再结晶过程，所得到的晶界仍属于亚晶界或小角度晶界范畴，再结晶晶界在超塑性变形过程中不产生滑动。     

Stored energy analysis of Zn—5Al eutectic alloy in superplastic deformation

The stored energy and the energy release during SPD(superplastic deformation)of a Zn-5Al alloy were studied.The alloy after rolling process gains more stored energy,and the as-rolled speciment can obtain maximum elongation and minimum flow stress without hot loding treatment before SPD.Experimental results show that stroed energy release process is along with SPD process and is also an impetus to SPD.The as -rolled Zn-5Al alloy has 48J/mol stored energy which was measured with DSC(differential scanning calorimeter)and conforms well to the calcuated value.The as-rolled Zn-5Al alloy after SPD with an elongation of 2500% releases 112J/mol stored energy,Analysis shows that the strain rate is in direct ratio to the rate of stred energy release.     

超塑处理对喷射成形GCr15钢超塑性的影响

研究了超塑处理对喷射成形GCr15钢超塑性的影响，超塑性拉实验结果表明，未经超塑处理的铸态试样，延伸率为119％，经过二次油淬和二次油淬＋高温回火超塑处理的两种试样，延伸率分别为328％和671％，变形温度和应变速率对GCr15钢的超塑性有一定的影响，但材料的微观组织对其超塑性具有决定性作用，超塑处理改变了材料试样的微观组织，导致其超塑性发生变化，经过二次油淬＋高温回火超塑处理后试样具有球化组织，其超塑性最好，未经超塑处理的铸态试样具有珠光体组织，超塑性最差，经过二次油淬超塑处理后试样的组织是马氏体和少量碳体物的混合，其超塑性介于上述两种试样之间，喷射成形工艺使GCr15钢获得均匀细化的稳定组织，这对于细晶超塑性是必要的，超塑处理材料的超塑性得到更大的提高。     

铍青铜(QBe2)超塑性预处理工艺的研究

通过工艺试验发现,供应态的铍青铜(QBe2)经一定的预处理,可获得良好的超塑性。在550℃和ε=1.67×10~(-3)s~(-1)的应变速率拉伸,合金能呈现大于1000％的高延伸率。文中提出的淬火+时效;淬火+冷轧,淬火+时效+冷轧的三种预处理工艺都能使合金获得超塑性的组织状态。分析和讨论了预处理工艺参数和所需的最佳组织条件。     

陶瓷材料的超塑性

虽然陶瓷材料在本质上是一种脆性材料；然而研究已表明细晶陶瓷材料具有超塑性，在高温下能产生很大的拉伸形变．本文综述了超塑性的特征和Y2O3稳定四方ZrO2多晶体这种典型的超塑性陶瓷材料的形变机理，形变特征以及动态晶粒生长、玻璃相和产生孔穴对其超塑性形变的影响，此外，还总结了其他陶瓷材料，包括Al2O3、Al2O3－Y2O3稳定四方ZrO2、纳米陶瓷和玻璃陶瓷的超塑性行为和特征．     

8090 Al-Li合金超塑变形的多重机制

本文研究了8090Al-Li 合金的超塑性变形中的微观组织结构及变形机制。电镜观察表明在8090Al-Li 合金的最佳超塑性变形条件下(T=500℃,(?)_1=3.33×10~(-3)s~(-1)),动态回复和动态再结晶是该合金超塑性变形的多重机制之一,起到了细化晶粒、释放三角晶界处应力集中和消除晶界滑动的障碍的作用。     

温轧态2618A铝合金高应变速率超塑性的研究

对温轧态２６１８Ａ铝合金在不同温度（４７０～５５０℃）和应变速率为１０￣（－３）～１０￣（０）ｓ￣（－１）范围内的超塑性进行了研究，确定了最佳超塑性变形规范：在５００～５３０℃温度范围内，应变速率为２．８×１０￣（－１）ｓ￣（－１）的条件下，可获得大于２３０％的延伸率，表明该合金具有高应变速率超塑性的特性。     

Superplasticity and Diffusion Bonding of Ti_3AI Intermetallic Compounds

The superplasticity of Ti_3Al intermetallic compounds has been investigated in this paper.TheTi-14Al-21Nb ternary alloy showed 477% elongation at the strain rate of 1.49×10~(-5) s~(-1) and950℃.The elongation of Ti-14Al-21 Nb-3Mo-1V quinary alloy approached to 573% at the strainrate of 4.52×10~(-5) s~(-1) and the same temperature,and it was found that the elongation value in-creased to 1096.4%as temperature was raised up to 980℃ at the same strain rate.Ti_3Al base al-loys were bonded by diffusion bonding technology and good joints were created,the simulatedspecimens were performed by SPF/DB process.