 为了探究以铁尾矿为调质剂制备高炉渣基矿渣纤维的可行性及最佳工艺参数，测定了不同铁尾矿添加量时调质高炉熔渣的变温黏度，研究了铁尾矿添加量对调质高炉熔渣黏度、流动度、质点移动活化能及渣系结构的影响。结果表明,随着铁尾矿添加量的增加，调质高炉熔渣的黏度逐渐增大，流动度逐渐减小；渣系质点移动活化能随着铁尾矿添加量的增加呈先增大后减小再增大的趋势；综合考虑矿渣纤维的质量和成纤条件的可行性，调质剂铁尾矿的最佳添加量为20%。     

Effect of nonionic side chain length of polycarboxylate-ether-based high-range water-reducing admixture on properties of cementitious systems

Despite the large variations in the behaviors of water-reducing admixtures upon changes in their structures, most previous reports on the cement-admixture compatibility did not provide sufficient information on the structure of the admixture. Hence, the evaluation and generalization of the reports on the cement-admixture compatibility are challenging. In this study, three different polycarboxylate-ether-based water-reducing admixtures with the same free nonionic content, anionic/nonionic molar ratio, and main chain length and different side chain lengths were produced. The compatibility of these admixtures with a CEM I 42.5R-type cement was investigated. In addition, an analysis of variance was performed on the experiment results to evaluate the contributions of the admixture type, admixture/cement ratio, and elapsing time to the Marsh funnel flow time, mini-slump, slump flow, and compressive strength. The water-reducing admixtures having long or short side chains reduced the initial flow characteristics of the cementitious systems. However, the admixture having the shortest side chain was better with regard to flow retention. The side chain length of the admixture did not have significant effects on the compressive strength and water absorption capacity of the mortar mixtures and mini-slump performances of the cement paste mixtures. Regarding the behaviors of the admixtures in the cementitious systems, an optimal admixture side chain molecular weight is proposed.     

专用聚丙烯树脂PPH-Y35生产及应用研究

针对无纺布的应用特性,对专用聚丙烯树脂PPH-Y35生产工艺、性能进行了优化。利用专用生产聚丙烯树脂PPH-Y35装置,用高效催化剂氢调法、选取复合抗氧化剂生产出高质量的产品。将用PPH-Y35生产的无纺布与同类产品的性能对比,其性能优异,在医疗卫生领域中的应用更有优势。     

水胶比、矿渣掺量对水泥砂浆强度及流动度影响的研究

通过改变矿渣掺量、水胶比试验,研究矿渣水泥砂浆的抗折、抗压强度和流动度变化的规律,找出了矿渣的最优的掺量。     

废弃PET降解产物改性PC复合材料的制备及其性能

为提高聚碳酸酯（PC）材料流动性,以乙二醇（EG）为溶剂降解废弃聚对苯二甲酸乙二醇酯（PET）得到的产物为改性剂,制备PET降解产物改性的PC复合材料,对测试结果进行分析讨论。结果表明,PET降解反应中产物主要BHET及其低聚物,降解产物的加入能够有效提高复合材料熔体质量流动速率,且熔体质量流动速率随着降解产物添加量的增加而增大．综合分析复合材料的力学性能及流动性,确定最佳实验用量为4%,降解体系为m(PET)∶m(EG)为1∶3．      

新型聚羧酸减水剂的研究

以丙烯酸类单体及聚乙二醇单甲醚为主要原料,制得聚乙二醇单甲醚—丙烯酸酯类大分子单体,再与丙烯酸类单体聚合制备了一种新型HPA聚羧酸减水剂。HPA对水泥具有高分散性,其掺量为0.15%、水灰比为0.29时,水泥净浆流动度可达250-290mm。     

原材料质量对萘系高效减水剂性能的影响

近几年，我国相继研制开发了一系列高效减水剂，目前萘系高效减水剂仍是产量最大，应用最广泛的一种高效减水剂。影响萘系高效减水剂性能的因素很多，本文主要探讨了原材料质量对其性能的影响。经过大量试验总结了其主要原料工业萘、硫酸和甲醛的质量对萘系高效减水剂性能的影响规律，以指导生产。     

自密实活性粉末混凝土的研究

试验主要通过调整填充体的颗粒级配使其具有高强和自密实等特性;同时研究了原材料品种、填充体的颗粒级配、养护制度、外加剂性能及配合比对强度的影响;并在未掺钢纤维的情况下,配制出了流动度好,标准养护下抗压强度达120MPa以上的高强混凝土.     

HL-HGM高强无收缩灌浆料性能及其应用实践

HL-HGM高强无收缩灌浆料是一种高强度、无收缩、流动性大的灌浆材料,本文研究了不同水料比对灌浆料的流动度、泌水率、凝结时间、强度等性能的影响,简要介绍了产品在杭州湾跨海大桥50m简支箱梁支座安装中的应用,与环氧树脂砂浆灌浆相比,具有施工工艺简单,施工进度快,工程质量高,节约成本,环保等特点。     

PVC和ACR共混工艺及其性能

为改善ＰＶＣ的流动性，对ＡＣＲ与ＰＶＣ机械共混工艺进行探索。研究发现，以母粒（ＰＶＣ：ＡＣＲ＝１：１组成）和ＰＶＣ共混，能同时提高其流动性和冲击强度。