Accelerating the decarbonization of carbonaceous gold ore by suspension oxidation roasting towards the improvement of gold leaching efficiency

Eliminating the gold preg-robbing effect of carbonaceous matter in carbonaceous gold ores is crucial for gold leaching. In this study, suspension oxidation roasting was proposed to accelerate the decarbonization of carbonaceous gold ore. The characteristics of oxidation reaction process and gas release were analyzed by TG-DTA-FTIR. The phase transformation and microstructure evolution of samples during roasting were analyzed by XRD, SEM and BET. The results show that the gold preg-robbing effect was eliminated after the gasification of carbonaceous matter, and the CaO generated by decomposition of carbonates can effectively capture the SO₂. After roasting for 75 min at 650 °C in a 20% O₂ atmosphere, the total carbon removal rate reached 99.42%, the distribution of exposed gold increased from 28.85% to 77.10% and the gold leaching efficiency increased from 4.55% to 84.83%. In addition, about 70% sulfur was mainly fixed in the roasted products in the form of sulfate. Therefore, the suspension oxidation roasting process is an efficient and clean pretreatment method for carbonaceous gold ores.     

离子型稀土矿山淋洗及尾水富集试验研究

对浸矿后离子型稀土原地浸矿场采用清水进行淋洗，在184天的清水淋洗过程中，尾水氨氮值从最开始的507mg/L，降低至140mg/L，淋洗尾水pH4.52~3.10。淋洗尾水采用两级反渗透膜分离，既回收有价资源稀土，又能使出水氨氮达标。结果表明，产水氨氮浓度稳定低于15mg/L，对稀土的截留率高于98.25%，浓水中稀土离子平均浓度313.4mg/L，可进一步回收稀土资源。     

Evidence of fluid evolution of Baoshan Cu−Pb−Zn polymetallic deposit: Constraints from in-situ sulfur isotope and trace element compositions of pyrite

In-situ LA-ICP-MS and S isotopes of pyrite from the Baoshan Cu polymetallic deposit were conducted to investigate the ore-forming process and the enrichment mechanism of elements. Three generations of pyrite (Py I, Py II, and Py III) in the skarn-type ores and pyrite in the carbonate-hosted sulfide ores from central, western, and northern (C_Py, W_Py, and N_Py) mining districts are selected for comparison. Compared with Py I and Py III, the contents of most elements in Py II are apparently higher. The As and Se contents are high within a wide range and are decoupled in the growth band of the C_Py. The highest As, Se, and Pb contents were found in W_Py and N_Py. These results indicate the drastic changes in the temperature and fluid mixing during the mineralization. The occurrence of fluctuation and change in temperature and f(O₂) was triggered by intermittent pulses of magmatic-hydrothermal fluids, mixing with meteoric water, and water−rock interactions. The sulfur isotopes of all species of pyrite indicated the magmatic source. The change in the f(O₂) conditions caused slight differences in the sulfur isotope compositions. Consequently, a metallogenic model was proposed to explain the ore-forming processes.     

固溶处理对TiB2/6061复合材料硬度及耐磨性的影响

采用氟盐法制备了TiB₂质量分数为3%的原位合成TiB₂/6061复合材料,研究了固溶温度和固溶时间对复合材料硬度和耐磨性能的影响。结果表明:TiB₂颗粒弥散分布在6061铝合金基体中,明显细化6061铝合金基体晶粒。当固溶温度一定时,随固溶时间延长,复合材料的硬度和耐磨性可获得明显提高,但固溶时间在6~10 h时,复合材料的性能变化不显著。当固溶时间一定时,随固溶温度升高,复合材料硬度和耐磨性呈现先上升后下降的趋势。3wt%TiB₂/6061复合材料经530 ℃×10 h固溶处理后,硬度和耐磨性能最佳,相较于铸态硬度值提高了79.5％,磨损量减少了59.1%。固溶处理后复合材料的磨损表面犁沟变细变浅,材料脱落现象减少。     

Migration and distribution of saline ions in bauxite residue during water leaching

Bauxite residue, a highly saline solid waste produced from digestion of bauxite for alumina production, is hazardous to the environment and restricts vegetation establishment in bauxite residue disposal areas. A novel water leaching process proposed here was used to investigate the dynamic migration and vertical distribution of saline ions in bauxite residue. The results show that water leaching significantly reduced the salinity of bauxite residue, leaching both saline cations Na⁺, K⁺, Ca²⁺ and anions CO^2?₃, SO^2?₄, HCO^?₃. Na⁺ and K⁺ migrated from 40–50 to 20–30 cm of the column, presenting a high migration capacity. The migration capacity of Ca²⁺ was lower and accumulated at 30–40 cm of the column. CO^2?₃ initially distributed at 20–30 cm of the column, subsequently transported to 30–40 cm of the column, and finally returned to 20–30 cm of the column along with evaporation. SO^2?₄ was originally distributed at 40–50 cm, but finally migrated to 20–30 cm of the column. Nevertheless, HCO^?₃ remained at the bottom of the column, and its migratory was less affected by evaporation.     

铋精矿加压氧化氨浸高效分离铜、硫和铋

针对湖南柿竹园铋精矿火法冶炼过程中存在的成本高、低浓度SO₂和散烟排放污染环境、有价金属综合回收率低等问题, 以柿竹园铋精矿为原料, 提出了加压氧化氨浸分离铋与铜、硫的新工艺, 研究了氨水加入量、浸出温度、浸出时间、浸出压力及浸出液固比等因素对铜、硫、铋浸出率的影响。在氨水用量1.8 mL/g_铋精矿、液固比4∶1、釜压2.8 MPa、浸出温度160 ℃、浸出时间5 h、搅拌速度600 r/min的优化工艺条件下, 铜、硫浸出率分别达93.57%和92.87%, 铋不浸出并以氧化铋形态全部入渣, 实现了铜、硫与铋的高效分离。     

福建某低品位金矿新型浸金剂浸金试验

福建某斑岩型金矿品位低、规模大,金主要以自然金形式存在,可见金的粒度较粗,为高效利用该低品位金矿,开展新型浸金剂金蝉全泥浸出试验和柱浸试验,结果表明：全泥浸出在磨矿细度为-0.074 mm占80%、矿浆浓度25%、加石灰调pH 值11.0左右、初始金蝉浓度为500 mg/L和过程中控制金蝉浓度不小于300 mg/L条件下浸出20 h,金的浸出率为93.43%,金蝉耗量为1.02 kg/t；柱浸在矿石粒度为-30 mm条件下喷淋浸出23天,金累计浸出率和金蝉累计耗量分别为86.54%和1.22 kg/t。     

湿法炼锌酸浸渣常规干燥实验研究

本文以湿法炼锌酸性浸出渣为研究对象,实验研究干燥温度、物料量、干燥时间对酸浸渣相对脱水率的影响,综合考虑干燥工艺的时效性、经济效益以及工艺效率,控制物料量为50g、干燥温度为90℃、干燥时间为80min时,酸浸渣相对脱水率可达到98.32%。实验研究对促进酸浸渣中有价金属的资源综合利用、改善环境等具有重要的指导意义。     

含煤盆地深层“超饱和”煤层气形成条件

中国深层煤层气资源丰富，但总体勘探和认识程度较低，尚未形成较为系统的深层煤层气地质理论。通过解剖分析准噶尔盆地白家海凸起和鄂尔多斯盆地临兴区块深层"超饱和"煤层气井的试气/生产动态，估算原地游离气的含气量，分析了深层"超饱和"煤层气的形成条件。研究表明：①深层"超饱和"煤层气储层中除吸附气外，还含有原地游离气，用常规试气方法可直接获得气流，煤层气的产出不明显依赖于排水降压；②埋藏超过一定深度，在煤阶和温度的综合作用下，煤的吸附能力将随埋深的继续增加而降低，煤层中吸附气的饱和度有增加的趋势，在达到吸附饱和后，出现原地游离气并形成"超饱和"煤层气，盆地深层具有"超饱和"煤层气形成的优势条件；③由于地温梯度和压力梯度的不同，不同盆地"超饱和"煤层气出现的临界深度不同，异常高压和异常高热流可以降低深层"超饱和"煤层气形成的临界深度；④深层"超饱和"煤层气开发具有大大缩短见气时间、充分利用地层能量和累积产水量低等优势，有望成为未来煤层气勘探开发的一个重要领域。