Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.     

Piezoelectric properties and microstructure of ceramicrete-based piezoelectric composites

Inorganic piezoelectric ceramic composite is the potential sensing element for long-term structural health monitoring due to its excellent durability and compatibility. In this study, a Ceramicrete-based piezoelectric composite is proposed preliminarily, in which the magnesium potassium phosphate cement is used as the matrix and the lead zirconate titanate particle is utilized as the functional phase. Piezoelectric properties test and microstructure analysis are performed to evaluate the testing samples. Results show that the piezoelectric performance of the composite increase with the increase of piezoelectric ceramic particle size. The value of the piezoelectric strain factor (d₃₃) can reach 83.8 pC/N, while the corresponding piezoelectric voltage factor (g₃₃) is 50.1 × 10^-3 V•m/N at the 50th day after polarization. Microstructure analysis illustrates that the interfacial transition zone (ITZ) between the matrix and the particles is dense. Moreover, the influence of aging on the composite is attributed to the continuous hydration after polarization. It indicates that the composites have a higher piezoelectric performance, which can be regarded as a promising sensing element material.     

Impact behavior of aminosilane functionalized nanosilica based shear thickening fluid impregnated Kevlar fabrics

In the present work, two types of shear thickening fluids have been synthesized by using neat and aminosilane functionalized silica nanoparticles and their viscosity curves have been obtained by the rheometer. Based on the values of peak viscosity of synthesized shear thickening fluids, the surface functionalized nanosilica based shear thickening fluid has been chosen as a best candidate due to the high viscosity for impregnation into the neat Kevlar of different layers viz. four (04) and eight (08) layers for velocity impact study. The experimental investigations reveal high energy absorption of shear thickening fluid impregnated Kevlar as compared to the neat Kevlar. The maximum energy absorption 62 J is achieved corresponding to the initial velocity 154 m∙s⁻¹ for 08 layers shear thickening fluid impregnated Kevlar specimen. The data have also been analytically determined and validated with the experimental data. The experimental data have good agreement with the analytical data within the accuracy of around 15 to 20%. The present findings can have significant inferences towards the fabrication of shear thickening fluids using nanomaterials for numerous applications such as soft armors, dampers, nanofinishing and so forth.     

The origin of interfacial delamination in Au/ceramic cofired LTCC structure

The interfacial delamination of electrode/ceramic multilayer structure will seriously damage the reliability of low temperature co-fired ceramic (LTCC) module in practical applications. In this work, three kinds of glasses employed in Au electrode are designed and prepared to study the abnormal expansion and delamination process in the Au/ceramic LTCC multilayer structure. The interfacial delamination in the co-fired structure is found to be attributed to the abnormal expansion of glass in respect to Au electrode at high temperature, which is originated from the enlarged closed pores during the co-firing process. This conclusion is further confirmed by co-firing the sample in a low-pressure condition. The mechanism and elimination of interfacial delamination here provides a feasible solution for the design of novel glasses in Au electrode for LTCC applications.     

Effect of Zr addition on the interfacial reaction of the SiC joint brazed by Inconel 625 powder filler

Ni-based alloys are believed to be the most suitable brazing fillers for SiC ceramic application in a nuclear environment. However, graphite, which severely deteriorates the mechanical property of the joint, is inevitable when Ni reacts with SiC. In this paper, Different amounts of Zr powders are mixed with Inconel 625 powders to braze SiC at 1400 °C. When Zr addition reaches 40 wt%, the brazed seam confirms the absence of graphite. This research proves that Zr can avoid the graphite’s formation by suppressing Ni’s activity. The room-temperature shear strength of the joint with graphite’s absence is tested to be 81.97 MPa, which is almost three times higher than that of the joint with graphite. The interfacial reaction process and mechanism of the SiC joint are investigated and explained in this paper using thermodynamic calculations.     

Evaluation of anticorrosion and contact resistance behavior of poly(orthophenylenediamine)- coated 316L SS bipolar plate for proton exchange membrane fuel cell

The present work was focused on the corrosion properties and contact resistance behavior of poly(orthophenlyenediamine) (PoPD) coating on 316L SS bipolar plates. To reduce the corrosion rate and increase the interfacial conductivity of 316L SS bipolar plates, PoPD coating was deposited using an electropolymerization technique by the various monomer concentration of orthophenlyenediamine (oPD) on its surface. The presence of 1, 2, 4, 5- tetra substituted benzene nuclei of phenazine units in the polymer coating was confirmed by infrared spectroscopy. X-ray photoelectron spectroscopy analysis has confirmed the (%) of chemical composition in PoPD coating. The results of scanning electron microscopy analysis revealed that the uniform and compact coating with complete cover on 316L SS. The corrosion properties were investigated in 0.5 M H₂SO₄ and 2 ppm HF solution at 80 °C. The polarization test results showed that the PoPD coating reduced the corrosion current density both in the PEMFC anode and cathode environments. The charge transfer resistance values were in the order of 316L SS ? 0.02 M PoPD ? 0.06 M PoPD ? 0.04 M PoPD. A very low interfacial contact resistance and good adhesion strength was observed for 0.04 M PoPD coating. The higher contact angle of 0.04 M PoPD coating explained the hydrophobic property and more benefit of water management in the PEMFC environment. The results of the analysis of total metal ion releases clearly explained that the low level of metal ions released for 0.04 M PoPD coating. The overall studies revealed the PoPD coating with optimized 0.04 M oPD concentration showed best performance and provided more anodic protection to 316L SS bipolar plates.     

Morphological study of thin films: Simulation and experimental insights using horizontal visibility graph

We studied the morphological nature of various thin films such as silicon carbide (SiC), diamond (C), germanium (Ge), and gallium nitride (GaN) on silicon substrate Si(100) using the pulsed laser deposition (PLD) method and Monte Carlo simulation. We, for the first time, systematically employed the visibility algorithm graph to meticulously study the morphological features of various PLD grown thin films. These thin-film morphologies are investigated using random distribution, Gaussian distribution, patterned heights, etc. The nature of the interfacial height of individual surfaces is examined by a horizontal visibility graph (HVG). It demonstrates that the continuous interfacial height of the silicon carbide, diamond, germanium, and gallium nitride films are attributed to random distribution and Gaussian distribution in thin films. However, discrete peaks are obtained in the brush and step-like morphology of germanium thin films. Further, we have experimentally verified the morphological nature of simulated silicon carbide, diamond, germanium, and gallium nitride thin films were grown on Si(100) substrate by pulsed laser deposition (PLD) at elevated temperature. Various characterization techniques have been used to study the morphological, and electrical properties which confirmed the different nature of the deposited films on the Silicon substrate. Decent hysteresis behavior has been confirmed by current-voltage (IV) measurement in all the four deposited films. The highest current has been measured for GaN at ～60 nA and the lowest current in SiC at ～30 nA level which is quite low comparing with the expected signal level (μA). The HVG technique is suitable to understand surface features of thin films which are substantially advantageous for the energy devices, detectors, optoelectronic devices operating at high temperatures.     

C-O-Co bond-stabilized CoP on carbon cloth toward hydrogen evolution reaction

Highly active, low-cost, and durable electrocatalysts toward hydrogen evolution reaction (HER) are crucial for electrochemical water splitting. Herein, a green, facial, and effective strategy was proposed to develop CoP on carbon cloth (CoP/o-CC) as efficient self-supported hydrogen evolution electrodes. The designed CoP/o-CC exhibits superior catalytic activity with overpotentials of 118 mV and 95.45 mV to deliver a current density of 10 mA cm^?2 in acidic and alkaline solution, respectively, which is superior to most reported studies. In addition, the designed CoP/o-CC electrode also possesses excellent stability even under a large current density of 100 mA cm^?2. The origin of significantly enhanced stability thereby was further systematically investigated. Experimental study reveals that the oxygenated functional groups on carbon cloth play the role to bind the CoP electrocatalysts, forming C-O-Co bonds. Thus, the enhanced electrochemical and structural stability of CoP/o-CC is predominantly caused by the interfacial interaction of the C-O-Co bonds between the CoP active materials and surface oxygenated functional groups of carbon fiber. Therefore, we believe that this work provides an in-depth insight into the role of interfacial interaction between the substrate and the catalysts and offers a new methodology to design durable and efficient electrocatalysts.     

Facile synthesis of black phosphorus directly grown on carbon paper as an efficient OER Electrocatalyst: Role of Interfacial charge transfer and induced local charge distribution

Black phosphorus (BP), as a new 2D material, is normally synthesized by a high-pressure and high-temperature (HPHT) method from white and red phosphorus, which severely hinders the further development of BP for any potential applications and leads to search for other potential applications of BP with big challenge. Herein, we develop a facile and efficient Thermal-Vaporization-Transformation (TVT) approach to prepare a highly active BP directly grown on carbon paper as the electrode for Oxygen evolution reaction (OER), showing a low onset potential of 1.45 V versus RHE. Simultaneously, the current density of BP-CP illustrates the excellent electro-catalysis stability only decreases by 3.4% after continuous operation for 10000 s. Meanwhile, the density functional theory (DFT) calculations further illustrates the P-doped carbon layer in the upper side of BP layer is actually responsible for its enhanced OER property, and the adjacent carbon atoms of the embedded P atoms are actually the active sites due to the induced local change distribution by intramolecular change transfer. Considering the facile, but efficient and scalable, TVT approach can directly synthesize BP-CP with excellent OER performance, which is promising for BP electrocatalysts used for OER in metal-air batteries, fuel cells, water-splitting devices, even other key renewable energy.