Interface regulation effects on mechanical behavior of heterostructure Ti6Al4V/TiAl-based laminated composite sheets

Design of architectured composites with layered-ordered structure can solve the strength-toughness mismatch problem of structural materials. In the present study, heterostructure Ti6Al4V/TiAl laminated composite sheets with different thicknesses of interface layer and TiAl composite layer were successfully produced by hot-pressing technology. The effects of interface regulation and laminated structure on their mechanical properties, crack propagation, and fracture behavior were studied. The results indicated that compressive strength of the sheets increased with the decrease in interface thickness. Compressive strength of TiAl composite sheet with thicker composite layer reached 1481.55 MPa at the arrester orientation with sintering holding time of 40 min, which was 25.96% higher than that of the sheet obtained at 120 min. Analysis indicated that the interface area transferred stress through slip bands and through-interface cracks. Compressive strength at the divider orientation reached 1443.06 MPa, which was 45.78% higher than that of the sheet obtained at 120 min. In this case, the interface area transferred stress through slip bands and along-interface cracks. For TiAl composite sheets with thinner composite layer, compressive strength was further improved to 1631.01 MPa and 1594.66 MPa at the arrester and divider orientations with sintering holding time of 40 min, respectively. The ductile metal layer exerted a significant toughening effect. Both interface regulation and laminated structure transformation could enhance the hetero-deformation induced (HDI) strengthening and improve the comprehensive mechanical properties of the composite sheets.     

Experimental investigation of different morphology textured ceramic tools by in-situ formed for the dry cutting

Surface texture is considered an important measure to improve the cutting performance of a tool. In this study, we have prepared three types of textured and conventional tools on the rake face by an in-situ formed method. During the experiment, the best parameters of three types of textured tools were selected for dry cutting AISI 1045 steel at different cutting speeds. Cutting forces, cutting temperatures, workpiece surface roughness, and tool wear were measured during the cutting process. The results showed that textured tools have significantly reduced cutting force, cutting temperature, and tool wear, and the roughness of the workpiece was improved compared with the conventional tool. The micro-pit texture tool has less stress contact region than the micro-groove width texture tool, but the micro-groove width texture tool exhibiting the best cutting performance. This investigation clearly showed that the textured tool prepared by the in-situ formed method has improved cutting performance.     

Achieving Rich and Active Alkaline Hydrogen Evolution Heterostructures via Interface Engineering on 2D 1T‐MoS2 Quantum Sheets

Large‐scale production of hydrogen from water‐alkali electrolyzers is impeded by the sluggish kinetics of hydrogen evolution reaction (HER) electrocatalysts. The hybridization of an acid‐active HER catalyst with a cocatalyst at the nanoscale helps boost HER kinetics in alkaline media. Here, it is demonstrated that 1T–MoS₂ nanosheet edges (instead of basal planes) decorated by metal hydroxides form highly active ${\text{edge}}_{{\text{1T‐MoS}}_{\text{2}}}$/ ${\text{edge}}_{\text{Ni}{(\text{OH})}_{\text{2}}}$ heterostructures, which significantly enhance HER performance in alkaline media. Featured with rich ${\text{edge}}_{{\text{1T‐MoS}}_{\text{2}}}$/ ${\text{edge}}_{\text{Ni}{(\text{OH})}_{\text{2}}}$ sites, the fabricated 1T–MoS₂ QS/Ni(OH)₂ hybrid (quantum sized 1T–MoS₂ sheets decorated with Ni(OH)₂ via interface engineering) only requires overpotentials of 57 and 112 mV to drive HER current densities of 10 and 100 mA cm^?2, respectively, and has a low Tafel slope of 30 mV dec^?1 in 1 m KOH. So far, this is the best performance for MoS₂‐based electrocatalysts and the 1T–MoS₂ QS/Ni(OH)₂ hybrid is among the best‐performing non‐Pt alkaline HER electrocatalysts known. The HER process is durable for 100 h at current densities up to 500 mA cm^?2. This work not only provides an active, cost‐effective, and robust alkaline HER electrocatalyst, but also demonstrates a design strategy for preparing high‐performance catalysts based on edge‐rich 2D quantum sheets for other catalytic reactions.     

适应不同重力环境的仿壁虎机器人运动仿真

针对不同重力环境下仿壁虎机器人的运动稳定性、运动高效协调性等问题,基于四足机器人的步态规划现状和仿壁虎机器人自身特定的机械结构,设计了仿壁虎机器人在g、0、-g 3种环境下的足端轨迹和运动步态。在ADAMS仿真软件中研究了机器人的运动学和动力学特性,得到了仿壁虎机器人稳定爬行与脚掌黏附力、足端轨迹和运动步态的关系。探讨了仿真结果的合理性和局限性,为仿壁虎机器人在实际环境中的稳定运动奠定了理论基础。     

不同粒径改性粉煤灰对磷酸根吸附性能的影响

废水排放过量的磷导致水体污染日益严重，将粉煤灰通过化学改性制备成了水化硅酸钙吸附剂，研究了改性吸附剂对磷酸根的吸附效果。利用XRD, SEM及BET比表面积等手段对粒度分级前后的吸附剂进行表征，研究不同粒级吸附剂对磷酸根的吸附性能，并考察其吸附机理。结果表明，不同粒级的吸附剂其化学成分出现了明显的偏析现象，孔隙结构也差异显著。相比其他粒径下的吸附剂颗粒，颗粒粒径在50?75 μm时，吸附剂中钙和硅含量较多，铝、铁和镁含量较低，水化硅酸钙组分含量最高，且伴有含铝的托贝莫来石晶体出现，钙离子的增加使其可以与更多的磷酸根结合形成沉淀。同时此粒径下具有较高的比表面积及孔隙度，疏松多孔的结构为钙离子提供更多活性位点。当使用粒径在50?75 μm的吸附剂吸附磷酸根时，磷的饱和吸附量可达到17.1 mg/g，比未分级的吸附剂高19.58%。     

NSA-500-1型氩弧焊机VD9不同接法对引弧和稳弧的影响

从一起NSA－500－1型氩弧焊机故障，分析其高压脉冲旁路二极管VD9不同接法对引弧、稳弧及设备安全的影响。     

φ1m氨合成塔20钢异径管失效分析

分析了氨合成塔底部副线20钢异径管爆破的原因。结果表明：异径管长期处于200℃以上工作，管内H2与管材中的碳或Fe3发生化学反应，生成CH4致使管内脱碳并产生裂纹，异径管强度降低脆性增加，导致爆破。     

DXDK800自动充填包装机料袋长度的调整

本文主要介绍了在DXDK800自动充填包装机中 ,采用一种新型的齿轮—蜗轮、蜗杆差速器来对膜片的进给速度进行微量的调整。及采用一种新型的可调式偏心链轮来调整横封辊的瞬时线速度 ,使其与料袋膜的进给速度相一致     

TiAl基合金板材制备技术的发展现状

综述了TiAl基合金板材制备技术的发展现状。介绍了的制备TiAl基合金板材三种技术的工艺过程及制得的TiAl基合金板材的显微组织和力学性能。     

The need for style systems in ODA

Many advanced document systems provide a formatting mechanism called ‘style sheets’ Style sheets provide a great deal of flexibility in describing a document's format, and allow easy maintenance of different house styles for a collection of documents. In this paper, we describe the basics of general style sheet systems, argue that successful document interchange must include the exchange of style sheet information, and evaluate ODA's style mechanism against this requirement.