铝上铬磷化工艺及促进剂的研究

选择了铬磷化工艺中适宜的溶液组成，并研究了铬磷化的工艺条件和转化膜层的性质，优选了铬磷化液的促进剂。该促进剂能加速铬磷化的反应速度，细化膜层和提高抗蚀性，已明显地提高了转化膜的质量。另外，还对铬磷化过程的电位－时间曲线进行了探讨。     

锌－镍合金钝化膜的组成和结构对耐蚀性的影响

采用俄歇电子能谱（ＡＥＳ）和Ｘ射线光电子能谱（ＸＰＳ）等方法测定了锌－镍合金铬酸盐纯化膜的组成和结构，并对Ｚｎ－Ｎｉ合金钝化膜的耐蚀性进行了研究。     

Corrosion resistance of electroplated Zn-Co alloy coating

By the NSS test and the test in SO2 gas atmosphere and detecting the φcorr-t curves, Rp-t curves and the cyclic voltammogram curves, the corrosion resistance of the electroplated Zn-Co alloy coating was studied. The corrosion resistance of the electroplated Zn-Co alloy coating is three times higher than that of the galvanized coating. Because the corrosion resistance of the Zn-Co alloy coating is especially remarkable in SO2 gas atmosphere, it is particularly fit to be used as a protective coating in industrial atmosphere. The reason why the Zn-Co alloy coating has such a high corrosion resistance is that its corrosive product has a comparatively great role in depressing the corrosive process.     

化学镀钴-磷基多元合金的研究现状

由于钴－磷基合金膜具有优异的磁性能和较高的耐蚀性，能有效的用于数字存储装置，已引起人们的极大关注。     

脉冲电流对锌酸盐镀锌层的影响

研究了在锌酸盐镀锌体系中采用脉冲电流时，脉冲频率，脉冲的占空比、反向电流对镀层外观，耐蚀性的影响，发现在最佳脉冲条件下得到的镀锌层比直流电镀得到的镀层光亮，结晶细致，耐蚀性能有很大的提高。     

高耐蚀性Zn—Co合金镀层钝化工艺的研究

研究了电镀Zn-Co合金镀层的钝化液的组成及工艺条件，溶液各成分及工艺条件对钝化膜质量的影响，通过几种腐蚀试验方法，测量了钝化膜的耐蚀性，结果表明，研究的钝化工艺可以得到耐蚀性良好的钝化膜。     

铸钢件黑色磷化工艺的研究

通过对黑色磷化各种工艺因素的研究,确定了铸钢件锰系中温黑色耐磨磷化工艺的最佳方案.采用体视显微镜研究了磷化膜表面微观形貌;采用X射线荧光光谱法(XRF)对磷化膜的厚度和成分进行了测定;采用点蚀法对磷化膜的耐蚀性进行了研究.结果表明,磷化膜性能好,磷化液污染小,便于维护和调整;温度适中,节约能源.本文还对磷化液中各成分作用进行了理论分析.     

测量镀层厚度时值得注意的一个问题

一、问题的提出镀层的厚度以及镀层厚度在基体表面的分布均匀性,是评定镀层性能的一个很重要的物理性能参数,它直接影响着镀件的外观、抗蚀性能、孔隙率、耐磨性等镀层质量,也关系到节约金属材料,节约能源和提高生产效率。而且在电镀工艺研究中,经常是以相同的镀层厚度为基准,去研究和比较镀层的其它一些性能和质量参数,从而评定各种工艺的优劣。因此电镀工作者非常重视镀层厚度的测量。     

锌酸盐电沉积锌镍合金工艺研究

本文重点研究了锌酸盐电沉积锌镍合金的镀液组成及工艺条件；各因素对镀层合金成分的影响，并测试了镀液和镀层性能；最后得到了比较理想的电镀镍合金工艺。     

高耐蚀性锡锌合金镀层钝化工艺研究

本文重点研究了锡锌合金镀层(含锌25％左右)的铬酸盐钝化液中活化剂和硬化剂的作用,以及钝化工艺条件的影响。研制了比较理想的钝化液的组成和工艺条件,得到了彩虹色钝化膜,并具有良好的耐蚀性。