Fine powder of TiC was prepared by self-propagating high-temperature synthesis(SHS)method with re-duction stage.The influence of diluent and relative density of the sample on both combustion rate and combus-tion temperature has been studied.The combustion reaction in the system of TiO_2-Mg-C begins at the meltingof Mg.The propagation of combustion wave is related to the gasifying of Mg.The activation energy of theprocess has an approximate linear dependence on the porosity of the sample. 相似文献
3.
4.
只含铵钨青铜(ATB)和W_(20)O_(53)两相的兰钨在一定的工艺条件下被还原成钨粉。兰钨中ATB(或W_(20)O_(53))的含量对钨粉粒度有明显的影响。兰钨中ATB含量越多,所得到的钨粉越粗。 相似文献
5.
钼对钨-镍-铁高比重合金性能和组织的影响 总被引:1,自引:0,他引:1
在95wt%W-3.5wt%Ni-1.5wt%Fe粉末混合料中加入纯钼粉,经成型烧结后,发现当钼的加入量超过1wt%时,能提高合金的强度,而合金的延伸率、截面收缩率及密度降低,合金的钨晶粒细化;钼溶解在基体相及钨相中,有固溶强化的作用。 相似文献
6.
本文用孔隙体积收缩法对γ-Fe 烧结机理进行了初步的探讨,得出γ-Fe致密化速度常数和温度的关系如下:D=17.68e■,并求出了不同温度下的致密化速度常数 D(cm~2/sec):1000℃—2.06×10~(-7);1100℃—7.8×10~(-7);1200℃—2.46×10~(-6);1250℃—4.142×10~(-6)。求出了γ-Fe 烧结时的活化能为 H=46200卡/克原子,与已知γ-Fe 烧结时体扩散激活动能67900卡/克原子~74200卡/克原子和晶介扩散激活能30000卡/克原子相比较,从而得出γ-Fe 的烧结机理为混合扩散机理,体积扩散、表面扩散、晶界扩散都起着重要作用。 相似文献
7.
通过对立方氮化硼(CBN)烧结体的显微结构的观察,讨论其烧结机理。采用离子腐蚀技术显露多晶体晶界,采用离子减薄法制备薄膜试样;在显微镜和透射电镜下观察到CBN的晶粒长大、MgO夹杂、挛晶、位错和裂纹等现象;CBN多晶体中裂纹的途径基本上是穿晶断裂,断口形貌具有准解理断裂的特征。纯CBN粉末体的烧结过程符合在压力下单元系固相烧结的一般规律。粉体通过再结晶和晶粒长大变成原子结合的多晶体;通过以塑性流动为主的物质迁移变成致密体。加有少量Ni等金属的CBN粉体,在烧结过程中出现液相,但不具备液相烧结过程的一般特征。 相似文献
8.
9.
利用表面分析技术、俄歇能谱仪(AES)和光电子化学分析仪(ESCA)研究了水雾化奥氏体不锈钢粉末在不同露点分解氨气氛中烧结时的表面反应。结果发现:烧结气氛的露点影响着颗粒之间的界面反应。与-25℃露点条件相比较,-41℃露点条件烧结可加速颗粒表面的还原反应,清除氧化物及其夹杂,非金属元素在颗粒界面的富集程度下降,增强颗粒之间的金属结合强度,提高了烧结材料的力学性能。 相似文献
10.
在恒体积条件下给出了多种扩散机制耦合作用两球单元烧结模型的推导过程,编制了相应的计算软件,计算了铜在不同的粒度、温度、时间条件下的颈长方程和对心收缩方程。结果表明:在相同条件下,多机制综合作用颈长方程略高于表面扩散机制单独起作用的颈长方程;多机制综合作用的对心收缩小于只考虑晶界扩散和体积扩散的对心收缩。颈长方程的时间指数随时间的增加而变小。在不同烧结条件下各种机制对颈部物质的贡献存在很大差别。加热速率影响颗粒的对心收缩,在相同烧结时间内,加热速率越低,烧结收缩量越大。压密度越高,在烧结初期颗粒的颈长速率和收缩速率越低。 相似文献