Process Intensification of Living Cationic Polymerization of Isobutylene by a Flow Reaction System

Increasing the reaction temperature of the living cationic polymerization of isobutylene is crucial for industrial production due to the cost of refrigeration. The reaction temperature increase was achieved with an accelerated reaction rate using a flow reaction system. The polymerization conditions, including the flow reactor design, were based on the results of kinetic studies. Utilizing a milli‐scale flow reactor, polyisobutylene, which has a narrow molecular weight distribution, was obtained within a considerably short residence time at a high temperature. Furthermore, it was confirmed that the value of M_w/M_n correlates with the product of the Reynolds number and the angle of collision.     

Combustion synthesis of AlN doped with carbon and oxygen

Carbon-and-oxygen-doped AlN specimens were prepared by combustion synthesis using Al, graphite, and AlN. Graphite addition changed the product color from white to blue. By XRD, the lattice constant increased slightly with increasing carbon content. Blue AlN powder was synthesized with a molar ratio of the diluent AlN of 0.2-0.5 with a fixed graphite content of 0.05. At an AlN molar ratio exceeding 0.6, carbon was not successfully incorporated due to the lower reaction temperature. Calcination at 800°C in air removed residual graphite without changing the crystal structure or product color. Oxygen, nitrogen, and carbon analyses revealed that blue AlN powders contained 0.45-0.54 mass% carbon and 1.4-1.6 mass% oxygen, while the undoped AlN contained 0.021 mass% carbon and 0.94 mass% oxygen. The origin of the white-to-blue color change was investigated via reflection measurements. Blue AlN exhibits an absorption peak at 634 nm (1.96 eV). From first-principles electronic structure calculations, the C-doped AlN and carbon-and-oxygen-doped AlN with a 1:1 ratio could be classified as p-type, whereas the O-doped AlN and 1:3 carbon-and-oxygen-doped AlN were n-type. One reason for the absorption peak at 634 nm may be a transition from the conduction band to an upper unoccupied state. These results suggest the possible control of optical and electronic properties of AlN via carbon-and-oxygen doping.     

Fine-tuned,molecular-composite,organosilica membranes for highly efficient propylene/propane separation via suitable pore size

Fine-tuned, molecular-composite, organosilica membranes were fabricated via the co-condensation of organosilica precursors bis(triethoxysilyl)acetylene (BTESA) and bis(triethoxysilyl)benzene (BTESB). Fourier transform infrared and UV–vis spectra confirmed the co-condensation behaviors of BTESA and BTESB. The evolution of the network structure indicated that the incorporated BTESB decreased the membrane pore size, which was determined by a modified gas translation model according to the steric effect of the phenyl groups. The incorporation of BTESB to BTESA finely tuned the membrane structure and endowed the resultant composite membrane with improved separation properties. The BTESAB 9:1 membrane (molar ratio of BTESA/BTESB was 9:1) exhibited high C₃H₆ permeance at 4.5 × 10⁻⁸ mol m⁻² s⁻¹ Pa⁻¹ and a C₃H₆/C₃H₈ permeance ratio of 33 at 50°C. One of the most important developments of this study involved clearly defining the relationship between membrane pore size and C₃H₆/C₃H₈ separation performance for organosilica membranes in single and binary separation systems.     

Crosslinked acrylic pressure‐sensitive adhesives. II. Effect of humidity on the crosslinking reaction

The effect of humidity during storage on the crosslinking reactions of isocyanate groups was investigated with attenuated total reflectance Fourier transform infrared spectroscopy with pressure‐sensitive adhesives composed of poly[ethyl acrylate‐co‐(2‐ethylhexyl acrylate)‐co‐(2‐hydroxyethyl methacrylate)] as a base resin and polyisocyanate as a crosslinker. A peak‐resolving analysis of the amide II region revealed four bands. According to an analysis of the Fourier transform infrared spectra of the model compounds, these four bands were assigned to free urethane linkages, hydrogen‐bonded urethane linkages, free urea linkages, and hydrogen‐bonded urea linkages. As expected, storage under humid conditions led to the formation of free and hydrogen‐bonded urea linkages corresponding to the promotion of isocyanate consumption. Peak resolution of the amide II region was found to be a reasonable way of monitoring urethane and urea linkages during crosslinking reactions. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 3039–3045, 2003     

A Bayesian propensity score adjustment for latent variable modeling and MCMC algorithm

The estimation of the differences among groups in observational studies is frequently inaccurate owing to a bias caused by differences in the distributions of covariates. In order to estimate the average treatment effects when the treatment variable is binary, Rosenbaum and Rubin [1983. The central role of the propensity score in observational studies for causal effects. Biometrika 70, 41-55] proposed an adjustment method for pre-treatment variables using propensity scores. Imbens [2000. The role of the propensity score in estimating dose-response functions. Biometrika 87, 706-710] extended the propensity score methodology for estimation of average treatment effects with multivalued treatments.However, these studies focused only on estimating the marginal mean structure. In many substantive sciences such as the biological and social sciences, a general estimation method is required to deal with more complex analyses other than regression, such as testing group differences on latent variables. For latent variable models, the EM algorithm or the traditional Monte Carlo methods are necessary. However, in propensity score adjustment, these methods cannot be used because the full distribution is not specified.In this paper, we propose a quasi-Bayesian estimation method for general parametric models that integrate out the distributions of covariates using propensity scores. Although the proposed Bayes estimates are shown to be consistent, they can be calculated by existing Markov chain Monte Carlo methods such as Gibbs sampler. The proposed method is useful to estimate parameters in latent variable models, while the previous methods were unable to provide valid estimates for complex models such as latent variable models.We also illustrated the procedure using the data obtained from the US National Longitudinal Survey of Children and Youth (NLSY1979-2002) for estimating the effect of maternal smoking during pregnancy on the development of the child's cognitive functioning.     

Comparison of activities in selective catalytic reduction of NOx by C3H8 over Co/MFI, Fe/MFI, and H/MFI zeolite catalysts

The Co/MFI(SiO₂/Al₂O₃ = 30) were prepared by a precipitation method with NaOCl in alkali solutions exhibited high activities to N₂ at 250 °C for the selective catalytic reduction (SCR) of NO_x. These catalysts showed two UV–vis bands at 700 and 400 nm, indicating the presence of octahedral Co(III) as well as tetrahedral Co(II). The high SCR activity over such Co(III, II)/MFI(30) seems to come from Co(III)---O moieties. The Co(II)MFI(30) catalysts prepared from Co(II)Cl₂ exhibited low SCR activities due to the presence of tetrahedral Co(II) ions in MFI. Less CO formation occurred over Co/MFI catalysts. The Fe/MFI(30) catalyst exhibited high activity due to the presence of some Fe---O species in MFI but more amount of CO were produced during SCR. H/MFI(30) catalyst exhibited a good SCR activity. However, more amount of carbonaceous deposits were produced on it. The correlation between acid concentration and SCR activity was discussed over H/MFIs.     

Fabrication of a poly-Si thin-film transistor with storage capacitor

The fabrication process of a low-temperature poly-Si thin-film transistor (TFT) with a storage capacitor was studied. The atmospheric-pressure chemical-vapour deposited SiO₂ protected the buried indium tin oxide (ITO) from reduction by a pure H₂ plasma treatment that was essential for the effective improvement of the poly-Si TFT characteristics. Thus, a storage capacitor with an ITO (picture electrode)-SiO₂-ITO (buried common electrode) structure was successfully fabricated. The poly-Si TFT with a channel width/length W/L ratio of 5 drove a 3 pF storage capacitor in 2 μs, and it showed superior driverability for LCD use. The TFT also had good hold characteristics under illumination for the realization of grey-scale representation.     

InxGa1−xAs ohmic contacts to n-type GaAs with a tungsten nitride barrier

Significant reduction of the contact resistance of In_0.7Ga_0.3As/Ni/W contacts (which were previously developed by sputtering in our laboratory) was achieved by depositing a W₂N barrier layer between the Ni layer and W layer. The In_0.7Ga_0.3 As/Ni/W₂N/W contact prepared by the radio-frequency sputtering technique showed the lowest contact resistance of 0.2 Ωmm after annealing at 550°C for 10 s. This contact also provided a smooth surface, good reproducibility, and excellent thermal stability at 400°C. The polycrystalline W₂N layer was found to suppress the In diffusion to the contact surface, leading to improvement of the surface morphology and an increase in the total area of the In_xGa−As between metal and the GaAs substrate. These improvements are believed to reduce the contact resistance.