GaN自支撑衬底的化学机械抛光研究

Chemical mechanical polishing （CMP） has been used to produce smooth and scratch-free surfaces for GaN. In the aqueous solution of KOH, GaN is subjected to etching. At the same time, all surface irregularities, including etch pyramids, roughness after mechanical polishing and so on will be removed by a polishing pad. The experiments had been performed under the condition of different abrasive particle sizes of the polishing pad. Also the polishing results for different polishing times are analyzed, and chemical mechanical polishing resulted in an average root mean square （RMS） surface roughness of 0.565 nm, as measured by atomic force microscopy.     

Chemical mechanical polishing of freestanding GaN substrates

Chemical mechanical polishing (CMP) has been used to produce smooth and scratch-free surfaces for GaN. In the aqueous solution of KOH, GaN is subjected to etching. At the same time, all surface irregularities, including etch pyramids, roughness after mechanical polishing and so on will be removed by a polishing pad. The experiments had been performed under the condition of different abrasive particle sizes of the polishing pad. Also the polishing results for different polishing times are analyzed, and chemical mechanical polishing resulted in an average root mean square (RMS) surface roughness of 0.565 nm, as measured by atomic force microscopy.     

Si(111)衬底上HVPE GaN厚膜生长

在Si(111)衬底上,以MOCVD方法高温外延生长的AIN为缓冲层,使用氮化物气相外延(HVPE)方法外延生长了15Km的c面GaN厚膜.并利用X射线衍射(XRD)、光致发光谱(PL)、拉曼光谱(Raman)等技术研究了GaN厚膜的结构和光学性质.分析结果表明,GaN厚膜具有六方纤锌矿结构,外延层中存在的张应力较小,...