该文基于掺钪AlN薄膜制备了高次谐波体声波谐振器(HBAR),研究了钪(Sc)掺杂浓度对AlN压电薄膜材料特性及器件性能的影响。研究表明,当掺入Sc的摩尔分数从0增加到25%时,压电应力系数e₃₃增加、刚度 下降,导致Al₁-_xSc_xN压电薄膜的机电耦合系数 从5.6%提升至15.8%,从而使HBAR器件的有效机电耦合系数 提升了3倍。同时,当Sc掺杂摩尔分数达25%时,Al₁-_xSc_xN(x为Sc掺杂摩尔分数)压电薄膜的声速下降13%,声学损耗提高,导致HBAR器件的谐振频率和品质因数降低。     

甲玛地区角岩矿微生物浸出的试验研究

介绍了西藏华泰龙矿业开发有限公司角岩的矿石性质,针对该低品位铜矿石进行了详细的微生物浸出试验研究,在原矿铜品位仅为0.12%、SiO_2含量高达69.12%的情况下,用接种量为10%的浸矿菌液,浸出1 d时,铜浸出率即为34.44%,浸出11 d时,浸出率达到70.02%,此时较无菌条件下的浸出率高出17.46个百分点。     

超低排放改造后烟气余热利用设备存在问题及防治措施

随着火电厂超低排放改造的普遍应用，低温省煤器等烟气余热利用设备获得了广泛应用。本文针对烟气余热利用设备在实际工程应用中所存在的低温腐蚀、磨损、积灰堵塞以及振动等问题，分析了形成原因及主要影响因素，提出了选用耐低温腐蚀性能优异的材料制造换热器，合理设计受热面结构型式，控制烟气流速和受热面金属壁温，加装吹灰设备以及导流板和防振隔板等防治对策，有效地解决了烟气余热利用设备所存在的低温腐蚀、磨损、积灰堵塞以及振动等问题。     

Technological and sensorial properties of liquid nitrogen ice cream enriched with protein from brewing waste (trub)

Debittered trub (brewing waste) is an important source of protein source (70.26%). Trub and whey protein were used for 5% protein enrichment of ice cream frozen by liquid nitrogen. Three formulations were elaborated: ice cream standard (ICS), ice cream with whey protein (ICW) and ice cream with trub (ICT). Chemical composition, rheological properties, texture, overrun, melting rate, scanning electron microscopy and a sensorial test were performed. Results showed that ICT presented a higher viscosity, obtained on the upward curve up to 6.76 Pa s⁻¹, consistency index (22.96 (Pa s⁻¹)ⁿ), hysteresis area (140.40 mPa s⁻¹) and hardness (31113.33 g) but a lower melting rate (0.38 g min⁻¹), overrun (13.92%) and sensorial acceptability than the other formulations. The addition of trub debittered for protein enrichment improved ice cream properties and demonstrated that it could be used as a food ingredient.     

Adaptive backstepping repetitive learning control design for nonlinear discrete‐time systems with periodic uncertainties

This paper addresses a tracking problem for uncertain nonlinear discrete‐time systems in which the uncertainties, including parametric uncertainty and external disturbance, are periodic with known periodicity. Repetitive learning control (RLC) is an effective tool to deal with periodic unknown components. By using the backstepping procedures, an adaptive RLC law with periodic parameter estimation is designed. The overparameterization problem is overcome by postponing the parameter estimation to the last backstepping step, which could not be easily solved in robust adaptive control. It is shown that the proposed adaptive RLC law without overparameterization can guarantee the perfect tracking and boundedness of the states of the whole closed‐loop systems in presence of periodic uncertainties. In addition, the effectiveness of the developed controller is demonstrated by an implementation example on a single‐link flexible‐joint robot. Copyright © 2014 John Wiley & Sons, Ltd.     

Correlation between instrumental texture and colour quality attributes with sensory analysis of selected cheeses as affected by fat contents

This study evaluated several physical and sensory parameters of different types of cheese available in the Polish market. The measurements of textural properties were conducted in an Instron universal testing machine, while the colour properties of cheeses were measured using a Minolta chromameter. The chemical composition was determined by means of the near‐infrared spectroscopy (NIRs). Moreover, a trained sensory panel was invited to assess the cheese texture‐related properties. Generally, cheeses with reduced fat content were characterised by higher hardness, adhesiveness, cohesiveness and elasticity. Texture‐related parameters of cheese with canola oil were comparable to that of most of full‐fat cheeses. The correlation analysis between physical and sensory attributes related to cheese textural properties indicated the potential applications of TPA, shear and penetration tests (r = 0.766, r = 0.75 and r = 0.765, respectively) for the evaluation of sensory properties related to the hardness. Meanwhile, the elasticity of cheese obtained from sensory evaluation was strongly correlated with the elasticity determined from the shear test (r = 0.722) and moderately correlated with the elasticity from penetration test (r = 0.588), indicating a need to refine the method of penetration test. In addition, cheeses exhibited higher meltability during convection heating at 230 °C than microwave heating. The values of meltability for cheese with reduced fat content were lower than those of full‐fat cheese.     

Properties and applications of β‐glycosidase from Bacteroides thetaiotaomicron that specifically hydrolyses isoflavone glycosides

To modify the glycan part of glycosides, the gene encoding β‐glycosidase was cloned from Bacteroides thetaiotaomicron VPI‐5482. The cloned gene, bt_1780, was expressed in Escherichia coli MC1061 and the expressed enzyme was purified using Ni‐NTA affinity chromatography. The purified enzyme, BTBG, showed optimal activity at 50 °C and pH 5.5. Interestingly, this enzyme did not have any hydrolysing activity on ordinary β‐linkage–containing substrates such as xylobiose, lactose and cello‐oligosaccharide, but specifically hydrolysed isoflavone glycosides such as daidzin, genistin and glycitin. Compared to a commercial beta glucosidase, BTBG selectively hydrolysed isoflavone glycosides in soybean extract mixture solution. These results suggest that BTBG may be a specialized enzyme for the hydrolysis of glycosides and that the substrate specificity of BTBG is applicable for the bioconversion of isoflavone glycosides in the food industry.     

Catalytic Hydrocracking of a Bitumen‐Derived Asphaltene over NiMo/γ‐Al2O3 at Various Temperatures

Hydrocracking of a bitumen‐derived asphaltene over NiMo/γ‐Al₂O₃ was investigated in a microbatch reactor at varying temperatures. The molar kinetics of asphaltene cracking reaction was examined by fitting the experimental data. Below a defined temperature, the molar reaction showed the first‐order kinetic feature while at higher temperatures secondary reactions such as coke formation became significant, causing deviation of the reaction behavior from the proposed first‐order kinetic model. Selectivity analysis proved that dominant products varied from gases to liquids to gases with increasing temperature, shifting the dominant reaction from C–S bonds cleavage to C–C bonds cleavage.