Relationships of tensile strength with crosslink density for the high-carbon black-filled EPDM compounds with various softeners

Equilibrium swelling and rheological tests were adopted to systematically investigate the effects of softener type and dosage on the crosslink densities. The results turned out that the chemical crosslink density could be distinguished from the physical crosslink density by comparing the results of equilibrium swelling and rheological tests. The liquid butadiene (LB) as a softener leads to the greatest reduction in crosslink density, followed by polyethylene wax (PW) and paraffinic oil (PO). The tensile strength decreases with increasing PO content while shows peak values with increase of LB and PW contents. The dependencies of chemical crosslink density on the aging time under 150°C are quite different for the three softeners, which can be expected from the double crosslinking networks consisting of small softener and large main crosslinking networks. Further investigation has been performed to correlate the tensile strength with chemical crosslink density of ethylene propylene diene monomer elastomer vulcanizates. Three different linear relationships can be obtained for the softeners independent of the aging time. It can now be expected from this study that the role of some new softeners in rubber compounds is not only confined to plasticization but also forms crosslinking networks in the peroxide-cured rubbers.     

Novel TiC-based composites with enhanced mechanical properties

Novel TiC-based composites were synthesized by reactive hot-pressing at 1800 °C for 1 h with ZrB₂ addition as a sintering aid for the first time. The effects of ZrB₂ contents on the phase composition, microstructure evolution, and mechanical properties were reported. Based on the reaction and solid solution coupling effects between ZrB₂ and TiC, the product ZrC may be partially or completely dissolved into the TiC matrix, and then phase separation within the miscibility gap is observed to form lamellar nanostructured ZrC-rich (Zr, Ti)C. The TiC-10 mol.% ZrB₂ (starting batch composition) exhibits good comprehensive mechanical properties of hardness 27.7 ± 1.3 GPa, flexural strength 659 ± 48 MPa, and fracture toughness of 6.5 ± 0.6 MPa m^1/2, respectively, which reach or exceed most TiC-based composites using ceramics as sintering aids in the previous reports.     

Core–shell NTC materials with low thermal constant and high resistivity for wide-temperature thermistor ceramics

Core–shell structures have been proposed to improve the electrical properties of negative-temperature coefficient (NTC) thermistor ceramics. In this work, Al₂O₃-modified Co_1.5Mn_1.2Ni_0.3O₄ NTC thermistor ceramics with adjustable electrical properties were prepared through citrate-chelation followed by conventional sintering. Co_1.5Mn_1.2Ni_0.3O₄ powder was coated with a thin Al₂O₃ shell layer to form a core–shell structure. Resistivity (ρ) increased rapidly with increasing thickness of the Al₂O₃ layer, and the thermal constant (B) varied moderately between 3706 and 3846 K. In particular, Co_1.5Mn_1.2Ni_0.3O₄@Al₂O₃ ceramic with 0.08 wt% Al₂O₃ showed the increase of ρ double, and the change in its B was less than 140 K. The Co_1.5Mn_1.2Ni_0.3O₄@Al₂O₃ NTC ceramics showed high stability, and their grain size was relatively uniform due to the protection offered by the shell. The aging coefficient of the ceramic was less than 0.2% after aging for 500 hours at 125°C. Taken together, the results indicate that as-prepared Co_1.5Mn_1.2Ni_0.3O₄@Al₂O₃ NTC ceramics with a core–shell structure may be promising candidates for application as wide-temperature NTC thermistor ceramics.     

In situ Raman spectroscopic study towards the growth and excellent HER catalysis of Ni/Ni(OH)2 heterostructure

The electrochemical water splitting to produce H₂ in high efficiency with earth-abundant-metal catalysts remains a challenge. Here, we describe a simple “cyclic voltammetry + ageing” protocol at room temperature to activate Ni electrode (AC-Ni/NF) for hydrogen evolution reaction (HER), by which Ni/Ni(OH)₂ heterostructure is formed at the surface. In situ Raman spectroscopy reveals the gradual growth of Ni/Ni(OH)₂ heterostructure during the first 30 min of the aging treatment and combined with polarization measurements, it suggests a positive relation between the Ni/Ni(OH)₂ amount and HER performance of the electrode. The obtained AC-Ni/NF catalyst, with plentiful Ni–Ni(OH)₂ interfaces, exhibits remarkable performance towards HER, with the low overpotential of only 30 mV at a H₂-evolving current density of 10 mA/cm² and 153 mV at 100 mA/cm², as well as a small Tafel slope of 46.8 mV/dec in 1 M KOH electrolyte at ambient temperature. The excellent HER performance of the AC-Ni/NF could be maintained for at least 24 h without obvious decay. Ex situ experiments and in situ electrochemical-Raman spectroscopy along with density functional theory (DFT) calculations reveal that Ni/Ni(OH)₂ heterostructure, although partially reduced, can still persist during HER catalysis and it is the Ni–Ni(OH)₂ interface reducing the energy barrier of H1 adsorption thus promoting the HER performance.     

Se doped nickel-molybdenum bimetal sulfide with enhanced electrochemical activity for hydrogen evolution reaction

In this work, we synthesized Se doped MoS₂@Ni₃S₂ with nanosheets coated nanorods structure supported on Ni foam (MoNiSeS). Firstly, MoS₂@Ni₃S₂ (MoNiS) nanorods was synthesized by hydrothermal method. After selenization treatment, MoSe₂ successfully formed on the edge of MoS₂ nanosheets and particle Ni₃S₂ transformed into NiSe, in which MoSe₂ and NiSe acted as new phase in MoNiSeS. The obtained MoNiSeS only needs a low overpotential of 68 mV to reach the current density of 10 mA cm^?2, and has a low Tafel plots of 72.77 mV dec^?1 and good electrochemical durability, whose electrochemical activity is much better than that of MoNiS and NiSeS, implying the introduction of Mo and Se is beneficial to improve the electrocatalytic performance of NiS for HER. In addition, the proper amount of Mo source, which has an effect on the morphology of product, has also been investigated. For MoNiSeS, the typical nanosheets coated nanarods expose more active sites and the synergic effects is good to the improvement of the catalytic activity. Meanwhile, WNiSeS has also been prepared using the same method and the corresponding results show that the electrochemical activity of WNiSeS is much better than that of NiSeS, proving the universality of this strategy.     

Novel thermal-sensitive properties of NBT-BZT composite ceramics for high-temperature NTC thermistors

We found for the first time that (1 − x) Na_0.5Bi_0.5TiO₃-xBiZn_0.5Ti_0.5O₃ (NBT–BZT) composite ceramics showed negative temperature coefficient (NTC) at a high temperature. The NBT–BZT nanopowders were successfully prepared by Pechini method. Their ceramics were sintered at 1100°C. The NBT–BZT ceramic exhibited a good linear relationship between logarithm of electrical resistivity (Inρ) and reciprocal of absolute temperature (1000/T) at 250°C–1050°C. The obtained ρ₆₀₀, ρ₉₀₀, and B_600/900 constants of the NBT–ZBT NTC thermistors are approximately 5.92 × 10⁶ to 3.01 × 10⁴ Ω cm, 7.03 × 10³ to 7.60 × 10² Ω cm and 2.3 × 10⁴-1.3 × 10⁴ K, respectively. The electrical characteristics can be tuned to the desired value by changing the Na_0.5Bi_0.5TiO₃ content in the compound. The electrical conductivity in these compounds is due to the electron jumps between Ti³⁺ and Ti⁴⁺ and oxygen-ion conductivity. Results demonstrate a tremendous potential of the studied system for perovskite materials with NTC performance.     

负载型复合载体及其镍基催化剂的性能

采用溶胶-凝胶法制备了负载型ZrO_2/Al_2O_3和ZrO_2/Al_2O_3-SiO_2复合载体,研究了不同复合载体对Ni基催化剂CO_2重整甲烷反应和性能的影响,并用XRD、IR、TPR、TPD和BET等方法对复合载体及催化剂进行了表征。结果表明,ZrO_2负载在基载体后比表面积、碱性、活性组分Ni的分散度和Ni与ZrO_2的相互作用增大。NiO在复合载体表面的分散容量与ZrO_2的负载量有关,ZrO_2的负载量为37．5%时NiO的分散容量达最高值(24．0%)。与Ni/ZrO_2相比,Ni/ZrO_2/Al_2O_3-SiO_2和Ni/ZrO_2/Al_2O_3催化剂对CO_2的吸附能力增大,CO_2吸附量增加,酸强度降低,CO_2重整CH_4反应活性提高,其中以Ni/ZrO_2/Al_2O_3催化剂的活性最好。     

热声制冷机及其改进实验研究

热声制冷作为一种很有前途的制冷方法，在国内外相关领域引起了极大兴趣。热声制冷机由声发生器、共振管、板叠及高、低温换热器等部分组成。对声驱动器的振动膜及其冷却系统、气体弹簧系统、高、低温换热器进行了初步改进，使制冷机冷端温降从原来的12℃提高到27℃左右，这是目前国内报道的最大温降。     

类胡萝卜素的命名

本根据国际理论与应用化学协会(IUPAC)所制定的命名规则和国际上认可的习惯名称，对类胡萝卜素的命名进行了详细的说明。