磁力可控电磁超声换能器设计及特性

电磁超声换能器一般采用具有超强磁力的稀土永磁制作,在实际检测中由于磁力不可控,存在偏置磁场不够强导致换能效率过低和磁力过强造成操作不方便等问题.提出一种偏置磁场磁力可控的电磁超声换能器,采用电磁铁与永磁铁相结合的方式,达到偏置磁场磁力可控的目的.通过有限元仿真和试验得出,提出的偏置磁场磁力可控的电磁超声换能器,在电磁铁处于关闭模式下,永磁铁能够提供基础磁场;采用增强模式或减弱模式,无被测物时,换能器下表面平均垂直磁通最大分别增强78.58％和减弱19.36％,而提离2 mm检测钢板时,换能器下方钢板表面平均垂直磁通最大分别增强52.99％和减弱38.02％;得出3种模式下,探头磁力随着提离距离缩小而增强的试验曲线;通过增强模式对铝板和钢板进行测厚试验,将检测信号幅值分别提高46.91％和62.01％.所设计的磁力可控电磁超声换能器不仅具有磁力可控的功能,还能够提高检测信号幅值.     

BS960E高强钢激光-电弧复合焊接头氢脆行为研究

氢脆具有很强的微观组织敏感性,威胁着各类高强结构材料的安全服役.采用激光-电弧复合焊工艺对BS960E型高强钢进行焊接,并对接头在原位电化学充氢的条件下进行慢应变速率(10-5s-1)拉伸试验,结合微观组织和断裂特征进行分析并对接头的氢脆行为进行研究.结果 表明,焊接热循环所形成的富马氏体中的细晶区可以使接头表现出一定的氢脆敏感性,马氏体较大的氢扩散系数和较低的氢溶解度以及氢在晶界上的快速扩散是引起接头对氢脆敏感的主要原因,通过控制焊接工艺参数可抑制焊接热循环所引起的马氏体转变量,能够降低BS960E型高强钢激光-电弧复合焊接头的氢脆敏感性.     

Effects of Different Short-Term UV-B Radiation Intensities on Metabolic Characteristics of Porphyra haitanensis

The effects of ultraviolet (UV) radiation, particularly UV-B on algae, have become an important issue as human-caused depletion of the protecting ozone layer has been reported. In this study, the effects of different short-term UV-B radiation on the growth, physiology, and metabolism of Porphyra haitanensis were examined. The growth of P. haitanensis decreased, and the bleaching phenomenon occurred in the thalli. The contents of total amino acids, soluble sugar, total protein, and mycosporine-like amino acids (MAAs) increased under different UV-B radiation intensities. The metabolic profiles of P. haitanensis differed between the control and UV-B radiation-treated groups. Most of the differential metabolites in P. haitanensis were significantly upregulated under UV-B exposure. Short-term enhanced UV-B irradiation significantly affected amino acid metabolism, carbohydrate metabolism, glutathione metabolism, and phenylpropane biosynthesis. The contents of phenylalanine, tyrosine, threonine, and serine were increased, suggesting that amino acid metabolism can promote the synthesis of UV-absorbing substances (such as phenols and MAAs) by providing precursor substances. The contents of sucrose, D-glucose-6-phosphate, and beta-D-fructose-6-phosphate were increased, suggesting that carbohydrate metabolism contributes to maintain energy supply for metabolic activity in response to UV-B exposure. Meanwhile, dehydroascorbic acid (DHA) was also significantly upregulated, denoting effective activation of the antioxidant system. To some extent, these results provide metabolic insights into the adaptive response mechanism of P. haitanensis to short-term enhanced UV-B radiation.     

Mechanical properties and wear behavior of Tin+1(Al,A)Cn (A = Ga,In, Sn,n = 1, 2) via quasi-high-entropy of single atomic thick A layer

The strengthening method of multi-element M-site solid solution is a common approach to improve mechanical properties of MAX phase ceramic. However, the research on capability of multi-element A-site solid solution to improve mechanical properties has rarely been reported. Thereupon, quasi-high-entropy MAX phase ceramic bulks of Ti₂(Al_1?xA_x)C and Ti₃(Al_1?xA_x)C₂ (A = Ga, In, Sn, x = 0.2, 0.3, 0.4) were successfully synthesized by in situ vacuum hot pressing via multi-elements solid solution. The multi-elements solid solution in single-atom thick A layer was confirmed by X-ray diffraction and X-ray photoelectron spectroscopy as well as by energy dispersive X-ray spectroscopy mappings. Effects of doped multi-elements contents on the phase, microstructure, mechanical properties, and high temperature tribological behaviors were studied. Results demonstrated that the Vickers hardness, anisotropic flexural strength, fracture toughness, and tribological properties of Ti–Al–C based MAX ceramics could be remarkably improved by constitution of quasi-high-entropy MAX phase in A layers. Moreover, the strengthening and wear mechanisms were also discussed in detail. This method of multi-element solid solution at A-site provides new way to enhance mechanical properties of other MAX phase ceramics.     

Contribution of Invariant Natural Killer T Cells to the Clearance of Pseudomonas aeruginosa from Skin Wounds

Chronic infections are considered one of the most severe problems in skin wounds, and bacteria are present in over 90% of chronic wounds. Pseudomonas aeruginosa is frequently isolated from chronic wounds and is thought to be a cause of delayed wound healing. Invariant natural killer T (iNKT) cells, unique lymphocytes with a potent regulatory ability in various inflammatory responses, accelerate the wound healing process. In the present study, we investigated the contribution of iNKT cells in the host defense against P. aeruginosa inoculation at the wound sites. We analyzed the re-epithelialization, bacterial load, accumulation of leukocytes, and production of cytokines and antimicrobial peptides. In iNKT cell–deficient (Jα18KO) mice, re-epithelialization was significantly decreased, and the number of live colonies was significantly increased, when compared with those in wild-type (WT) mice on day 7. IL-17A, and IL-22 production was significantly lower in Jα18KO mice than in WT mice on day 5. Furthermore, the administration of α-galactosylceramide (α-GalCer), a specific activator of iNKT cells, led to enhanced host protection, as shown by reduced bacterial load, and to increased production of IL-22, IL-23, and S100A9 compared that of with WT mice. These results suggest that iNKT cells promote P. aeruginosa clearance during skin wound healing.     

基于电沉积法回收废水中铝离子的最佳工艺参数分析

基于电沉积法,针对某铝箔生产企业所产生的高含铝离子废水,通过不同峰值电流密度下形成的电沉积试样的相关电化学曲线测试结果和镀层中的Al质量分数分析,确定所采用电沉积法的最佳峰值电流密度为9 A·dm-2,此时沉积层中铝质量分数为33.21％,原子数量占比为24.69％.     

Methods and mechanisms for uniformly refining deformed mixed and coarse grains inside a solution-treated Ni-based superalloy by two-stage heat treatment

The uniform refinement mechanisms and methods of deformed mixed and coarse grains inside a solution-treatment Ni-based superalloy during two-stage annealing treatment have been investigated.The two-stage heat treatment experiments include an aging annealing treatment(AT)and a subsequent recrystallization annealing treatment(RT).The object of AT is to precipitate some δ phases and consume part of storage energy to inhibit the grain growth during RT,while the RT is to refine mixed and coarse grains by recrystallization.It can be found that the recrystallization grains will quickly grow up to a large size when the AT time is too low or the RT temperature is too high,while the deformed coarse grains cannot be eliminated when the AT time is too long or the RT temperature is too low.In addition,the mixed microstructure composed of some abnormal coarse recrystallization grains(ACRGs)and a large number of fine grains can be observed in the annealed specimen when the AT time is 3 h and RT tem-perature is 980℃.The phenomenon attributes to the uneven distribution of δ phase resulted from the heterogeneous deformation energy when the AT time is too short.In the regions with a large number of δ phases,the recrystallization nucleation rate is promoted and the growth of grains is limited,which results in fine grains.However,in the regions with few δ phases,the recrystallization grains around grain boundaries can easily grow up,and the new recrystallization nucleus is difficult to form inside grain,which leads to ACRGs.Thus,in order to obtain uniform and fine annealed microstructure,it is a prereq-uisite to precipitate even-distributed δ phase by choosing a suitable AT time,such as 12 h.Moreover,a relative high RT temperature is also needed to promote the recrystallization nucleation around δ phase.The optimal annealing parameters range for uniformly refining mixed crystal can be summarized as:900℃×12 h+990℃×(40-60 min)and 900℃×12 h+1000℃×(10-15 min).     

气藏平均地层压力跟踪计算新方法

平均地层压力是产能评价和动态分析的基础，准确、快速获取平均地层压力对高效开发气藏意义重大。基于地层压力随时间变化的规律，分析了平均地层压力的变化规律。研究结果表明：平均地层压力等效点仅随时间发生改变，平均地层压力的下降速率等于或者近似等于井底流压的下降速率。从封闭弹性驱动气藏的物质平衡方程出发，考虑偏差系数和井底流压随平均地层压力的变化，推导建立了平均地层压力跟踪计算新方法，根据生产数据可迭代计算平均地层压力。方法验证结果显示，采气速度和采出程度共同影响模型的计算结果。应用实例表明，跟踪计算法与压力恢复试井和物质平衡法之间的相对误差均较小，满足工程计算精度要求，且跟踪计算法不需依托生产测试数据，节约了测试费用，避免了测试占产。     

Dealloying corrosion of anodic and nanometric Mg41Nd5 in solid solution-treated Mg-3Nd-1Li-0.2Zn alloy

The microstructure and chemical compositions of the solid solution-treated Mg-3Nd-1Li-0.2Zn alloy were characterized using optical microscope,scanning electron microscope(SEM),transmission electron microscope(TEM),electron probe micro-analyzer(EPMA)and X-ray photoelectron spectroscopy(XPS).The corrosion behaviour of the alloy was investigated via electrochemical polarization,electrochemical impedance spectroscopy(EIS),hydrogen evolution test and scanning Kelvin probe(SKP).The results showed that the microstructure of the as-extruded Mg-3Nd-1Li-0.2Zn alloy contained α-Mg matrix and nanometric second phase Mg41 Nd5.The grain size of the alloy increased significantly with the increase in the heat-treatment duration,whereas the volume fraction of the second phase decreased after the solid solution treatment.The surface film was composed of oxides(Nd2O3,MgO,Li2O and ZnO)and carbonates(MgCO3 and Li2CO3),in addition to Nd.The as-extruded alloy exhibited the best corrosion resistance after an initial soaking of 10 min,whereas the alloy with 4h-solution-treatment possessed the lowest corrosion rate after a longer immersion(1 h).This can be attributed to the formation of Nd-containing oxide film on the alloys and a dense corrosion product layer.The dealloying corrosion of the second phase was related to the anodic Mg41Nd5 with a more negative Volta potential relative to α-Mg phase.The preferential corrosion of Mg41Nd5 is proven by in-situ observation and SEM.The solid solution treatment of Mg-3Nd-1Li-0.2Zn alloy led to a shift in corrosion type from pitting corrosion to uniform corrosion under long-term exposure.