Optimization of room-temperature TCR of polycrystalline La0.9-xSrxK0.1MnO3 ceramics by Sr adjustment

High-density La_0.9-xSr_xK_0.1MnO₃ ceramics (LSKMO, A-site = La, Sr and K, 0 ≤ x ≤ 0.25) are successfully fabricated by using facile sol-gel method. Electrical properties are performed by using combination of phenomenological percolation (PP) model, double exchange (DE) mechanism, and Jahn-Teller (JT) effect. Moreover, X-ray diffraction and scanning electron microscopy are employed to analyze the structure and morphology of LSKMO ceramics. Valence states and ionic stoichiometry are assessed by using X-ray photoemission spectrometry. Results reveal that Sr²⁺ ions, substituting La³⁺ ions, significantly influenced DE mechanism and JT effect. In addition, Sr-doping plays essential role in improving electrical properties of LSKMO ceramics. At optimal doping content of x = 0.09, peak temperature coefficient of resistance (TCR) of the resistivity is found to be 11.56% K^?1 at 297.15 K, which is optimal TCR for A-site K-occupied perovskite manganese oxides. These results confirm that polycrystalline LSKMO ceramics render high room-temperature TCR values due to Sr-doping.     

One step method of structure engineering porous graphitic carbon nitride for efficient visible-light photocatalytic reduction of Cr(Ⅵ)

Porous g-C3N4 nanosheets (PCN) were prepared by the nickel-assisted one-step thermal polymerization method.Hydrogen (H2) which was produced by the reaction between nickel (Ni) foam and ammonia (NH3) defined the structure and properties of PCN.During the formation of PCN,the participation of H2 not only enhanced the spacing between layers but also boosted the specific surface area that more active sites were exposed.Additionally,H2 promoted pores formation in the nanosheets,which was beneficial to the transfer of photons through lamellar structure and improved the absorption efficiency of visible light.Remarkably,the obtained PCN possessed better Cr(Ⅵ) photocatalytic reduction efficiency than pure g-C3N4.The reaction rate constant (k) of PCN (0.013 min-1) was approximately twice that of bare g-C3N4 (0.007 min-1).Furthermore,the effects of original pH and concentration of Cr(Ⅵ)-containing solution on removal efficiency of Cr(Ⅵ) were explored.A possible photocatalytic mechanism was proposed based on the experiments of radical scavengers and photoelectrochemical characterizations.     

Cu掺杂对有序Sr3YCo4-xCuxO10.5+δ多晶的结构与物理性能的影响

采用固相反应法制备了四方Sr3YCo4-xCuxO10.5+δ(x=0~1.0)多晶。用热重-差示扫描量热分析,X射线衍射研究了多晶的有序化相变及结构。在固溶范围内(x=0~0.4),观察到有序峰(103)和(215),说明四方Sr3YCo4-xCuxO10.5+δ多晶为超结构,这是由于合成时在1000℃以上发生了吸氧(δ)有序化相变；当x=0.6~1.0时,978℃时在晶界处形成了单斜杂相,破坏了Sr3YCo4-xCuxO10.5+δ多晶的有序。当x=0~0.4时,多晶呈半导体输运行为。随着Cu掺杂量的增加,Co4+提供的空穴载流子浓度增大,电阻率明显下降；由于Cu的固溶,自旋熵增加,载流子浓度和自旋熵的共同作用使x=0~0.2多晶的热电势不变,x=0.4的热电势降低。并且Cu掺杂导致的晶格畸变使Co3+离子由高自旋态转变为高/低自旋混合态,磁化强度和铁磁转变温度(Tc)降低,磁结构由G-型反铁磁转变为铁磁。在进行二次烧结后,300K时电阻率明显降低,热电势为一次烧结的2倍,可能是二次烧结使多晶的有序化程度增大,提高了铁磁有序排列。     

Investigating the effect of water-mixing nitrogen atmospheric pressure plasma jet on polyether-ether-ketone and time stability under different conditions

Possessing excellent properties including good biocompatibility, high strength, and stiffness, polyether-ether-ketone (PEEK) has significant application values in medical and industrial fields. However, the relatively poor wettability and low adhesion limit its further applications. Atmospheric pressure plasma jet (APPJ) has been utilized for adjusting PEEK properties, but better hydrophilization effect and time stability after treatment are still urgently needed. In this paper, we employ a water-mixing nitrogen (N₂ H₂O) APPJ to process PEEK, and surface wettability can be effectively improved (contact angle ~18° within 2 min, distance between sample and nozzle outlet: 10 mm) without inducing obvious microstructure damages. Additionally, after storing for 40 days, the sample treated by N₂ H₂O APPJ also possessed better wettability (~54°) compared with that treated by N₂ APPJ (~65°). On the basis of this low-damage and high-efficient modification method, we perform aging experiments under different conditions (different temperatures 25, −10°C; and low vacuum condition: 50 kPa) to determine a relatively optimum storing condition for this method. The experiment results indicate that low temperature and vacuum are conducive to retaining the plasma-induced wettability (~34°). The treatment method and storing conditions for PEEK presented here may facilitate the application of PEEK in various fields.     

LaCr0.7Fe0.3O3-NiMn2O4 supported NTC composite ceramics with a sandwich-like structure

A novel sandwich-like structure was first proposed to adjust the electrical properties of NTC thermistors. The LaCr_0.7Fe_0.3O₃-NiMn₂O₄ supported composite ceramics with sandwich-like structure were initially fabricated via traditional solid-state reaction and uniaxial pressing methods, which allowed for the advantages of each component to be integrated into one material. X-Ray diffraction analysis indicates the ceramics mainly consisting of orthorhombic perovskite LaCr_0.7Fe_0.3O₃ and cubic spinel NiMn₂O₄ phases. SEM images manifest that the three layers adhered well to each other and exhibited high density. For electrical properties, the ρ_25°C was expanded to a wide range of 1182–110,233 Ω?cm and could be adjusted to the desired values by tuning the volume ratio of two basic layers, the B value was enhanced from 3358 K to 4167 K by NiMn₂O₄, and the thermal stability was improved by LaCr_0.7Fe_0.3O₃ with a resistance shift less than 0.55 % after annealing at 150 °C for 1500 h.     

The effect of alkali metal oxide on the properties of borosilicate fireproof glass: Structure,thermal properties,viscosity, chemical stability

The purpose of the current work was to research the effect of alkali metal oxide on the structure, thermal properties, viscosity and chemical stability in the glass system (R₂O–CaO–B₂O₃–SiO₂) systematically. Because the glass would emulsify when Li₂O was added to the glass batch, this article did not discuss Li₂O. The results showed that when the amount of Na₂O was less than 4 mol.%, there was a higher interconnectivity of borate and silicate sub-networks in glass, as more mixed Si–O–B bonds were present in glass. The glass samples exhibited excellent thermal properties and chemical stabilities. As the amount of Na₂O exceeded 4 mol.%, the interconnectivity of borate and silicate sub-networks was weakened. The thermal properties and chemical stabilities of the glass samples were reduced. The connectivity of the silicate sub-network was weakened slightly as the Na/K ratio varied, and the coefficient of thermal expansion (CTE) of the glass samples gradually increased, and the resistance to thermal shock (RTS) value gradually decreased. Moreover, the viscosity of the glass samples decreased with the ratio of Na/Si and Na/K increased.