国内外钎焊标准化现状及发展

综述了ISO,CEN,ANSI,JISC,SAC等标准化机构发布的钎焊标准,从术语标准、符号标准、过程标准、产品标准和试验标准等方面分析了国内外钎焊标准化现状,提出了发展我国钎焊标准化工作的几点建议.     

凝固方式对Sn-Bi钎料组织和性能的影响

采用炉冷、空冷、水冷和液氮冷却方式以及外加磁场的方法研究不同的凝固方式对Sn-Bi钎料的冲击韧性和显微组织的影响.研究结果表明,快速冷却与旋转磁场均能细化钎料合金的微观组织,抑制粗大树枝晶的生长,但快速冷却会造成Bi的偏析,旋转磁场会造成组织不均.同时快速冷却与旋转磁场都会破坏含Ge合金的塑性改善机制,造成含Ag合金中Ag3Sn相粗大,而旋转磁场的离心力作用还会造成Ag3Sn相和Bi相的宏观偏析.在组织细化以及成分偏析的共同作用下,Sn-57Bi共晶钎料的冲击韧性随冷却速率的增大呈现先增加后减少的趋势.     

Analysis of microstructure and performance of temper bead welded joints for SA508-3steel by Quenching and Tempering mode

The HAZ microstructure and performance of Quenching and Tempering mode temper bead welding and general welded joints which were made on SA508-3 steel of 60 mm thickness were compared in this article.The result shows that tempering sorbite which has excellent overall performance was obtained in both modes.The microstructure of Quenching and Tempering mode welded joints got more fine grain.Even though the hardness of tempering bead welded joints is higher than the general one,it still meets the standards which is lower than 350 HV.The impact absorbing energy of each district of tempering bead welded joints HAZ reached 170 J, which is equal to general one.     

试样尺寸对SA508-3钢焊接接头断裂韧度的影响

针对大型核容器SA508-3钢焊接接头断裂韧度进行了研究.结果表明,在大试样条件下,母材、焊缝金属及热影响区的断裂韧度存在差异,焊缝金属的断裂韧度优于热影响区,母材的断裂韧度最低.试样几何尺寸直接影响裂纹尖端的应力状态,小试样时裂纹尖端处于平面应力状态,母材、焊缝金属及热影响区全部呈韧窝断裂,表现出良好的塑性;大试样时裂纹尖端处于平面应变状态,母材断口特征转变为准解理与解理混合断裂,热影响区为典型的准解理断裂,焊缝为韧窝断裂.     

高速列车6005A-T6铝合金焊接接头软化分析

测试了6005A-T6铝合金双丝MIG焊和激光-双丝MIG复合焊的焊接热循环曲线,并利用热处理方法进行了焊接软化的热模拟试验,探讨了6005A-T6铝合金焊接接头的软化问题.结果表明,焊接热循环峰值温度超过260℃时热影响区开始软化,当峰值温度达到350℃左右时软化最为严重,晶内的非稳态强化相β"相及β'相转变为平衡态的β相(Mg₂Si)并聚集长大是造成软化的根本原因;受热温度在260~500℃的热影响区,焊后经简单的时效处理后,硬度无法恢复至原始状态;复合焊的焊接热循环曲线在260℃以上的高温停留时间相对较短,这是造成复合焊接头软化程度低于常规MIG焊的直接原因.     

45CrNiMoVA钢动态断裂韧度的测定

通过对45CrNiMoVA钢在静态下直至K=3.3×10~6MPam~(1/2)/s下的动态断裂韧度K_(Id)和J=1.8～2.5×10~4N·mm~(-1)/s 下的J_(Id)测定,探讨了采用闭环回路电液伺服试验机测定动态断裂韧度的方法。在动态J_(Id)测试中采用了J_R阻力曲线法,在国内尚未见报导。试验结果还表明:加载速率K(J)对K_(Id)(J_(Id))的影响趋势与一般报导的Cr-Mo-V系钢是相似的。用此法测得结果对于加载速率低于4毫米的冲击加载可提供安全分析的断裂韧度指标K_(Id)和J_(Id)值。     

时效处理对ER347不锈钢熔敷金属微观组织和力学性能的影响

研究了ER347熔敷金属在750?℃长期时效过程中σ相的析出行为及其对力学性能的影响.结果显示,ER347熔敷金属的铁素体含量、硬度及冲击韧性与时效时间存在密切关联.ER347熔敷金属在750?℃时效时,随时效时间的延长,σ相析出增多,硬度增大,铁素体含量和韧性则降低.ER347熔敷金属焊态冲击韧性良好,时效处理后,韧性下降,其脆化的根本原因在于δ-铁素体分解形成了硬脆σ相,显著降低了ER347熔敷金属韧性.(σ+γ2)结构内部存在大量的高能σ/γ2和δ/σ/γ2非共格界面,且σ相自身硬脆,易作为潜在裂纹源,在高应变速率下,发生脆性开裂并迅速扩展,导致熔敷金属韧性降低.     

Novel approach of LY12 alloy brazing

The LY12 Al alloy was brazed with the adoption of the improved KF-CsF-AlF3 flux matching Ag-Al-Cu-Zn filler metal. The shear strength of brazed joint could reach 80% of that of the substrate and the tensile strength of butt brazed joint will be 70% of that of the substrate. This was the great progress against the traditional claim that Al alloy reinforced by heat treatment could not be brazed. The experimental results and theoretical analysis had proved that it was the key issue to remove the MgO oxide film below 503℃. The addition of rare earth La was the effective way to obtain better mechanical properties of the filler metal as well as brazed joints.     

Al/Cu管异种材料火焰钎焊连接

采用火焰钎焊技术，实现了Al/Cu管异种材料的中温钎焊连接。所采用的改进型的CsF-AlF3钎剂Si粉含量在1％时，钎焊接头的抗裂性能最好。本试验所采用的钎剂具有熔点低、免清洗、无腐蚀、钎剂活性佳和接头抗裂性能好等优点，该技术达到了国内领先水平。     

Sn-Ag-Cu-Ce无铅钎料合金体系的热力学计算及预测

利用周模型对Sn—Ag—Cu—Ce无铅钎料合金体系进行了热力学计算预测。热力学计算结果表明，Ag、Cu含量(质量分数)分别为0．5％-4．5％时，当Ce的含量(质量分数)超过0．05％时，体系达到化学平衡状态；当Ce的含量(质量分数)达到0．6％左右时，Sn、Ag、Cu分别都出现了“等活度系数”现象。这一研究结果可为无铅钎料合金的成分设计提供理论指导。