Ultraviolet-shielding and conductive double functional films coated on glass substrates by sol-gel process

Ultraviolet-shielding and conductive double functional films were composed of CeO2-TiO2 film and SnO2:Sb film deposited on glass substrates using sol-gel process.Ce(NO3)3·6H2O and Ti(C4H9O4),SnCl4 and SbCl3 were used as precursors of the two different functional films respectively.The CeO2-TiO2 films were deposited on glass substrates by sol-gel dip coating method,and then the SnO2:Sb films with different thickness were deposited on the pre-coated CeO2-TiO2 thin film glass substrates,finally,the substrates coated with double functional films were annealed at different temperatures.The optical and electrical properties of the CeO2-TiO2 films and the double films were measured by UV-Vis spectrometer and four probe resistance measuring instrument.The crystal structures and surface morphology of the films were characterized using XRD and optical microscope,respectively.The obtained results show that the ultraviolet-shielding rate of the glass substrates with CeO2-TiO2 films is not less than 90%,and transmittance in visible lights can reach 65%.With the thickness of the SnO2:Sb film increasing,its conductivity became better,and the surface resistance is about 260 Ω/ when the SnO2:Sb films were deposited 11 cycles of the dip on the pre-coated CeO2-TiO2 glass.The ultraviolet-shielding rate of the glass substrates with double functional films is higher than 97%,and the peak transmittance in the visible lights is 72%.Additionally,with increasing the heat treatment time,the Na+ of the glass substrates diffuses into the films,resulting in the particle size of SnO2 crystal smaller.     

减反射可见光与反射近红外线双功能镀膜玻璃

采用溶胶-凝胶工艺,用提拉法在光伏玻璃上制备了玻璃/TiO2-SiO2/SnO2∶F/SiO2减反射可见光与反射近红外双功能膜。用拟合方法研究了TiO2掺量对TiO2-SiO2膜层折射率的影响、以及溶胶中水含量对SiO2膜层折射率的影响;研究了快速热处理温度对SnO2∶F膜结构和方块电阻的影响,用紫外-可见光谱(UV-Vis)测试了膜层的透射率,用扫描电镜(SEM)观察了膜层的表面形貌。结果表明,TiO2掺量可以使TiO2-SiO2膜层的折射率在1.49~1.97之间变化,SiO2溶胶中的水含量能够在膜面上形成微孔,降低SiO2膜层的折射率。通过优化工艺,制备出了在可见光范围平均透过率约为96%、1120nm波长近红外起始反射的双功能复合膜。对得到的结果进行了讨论。     

工作人员辐射防护监测的一般原则——ICRP35号出版物(译文续)

(62)对于很多类型的操作,把污染水平保持在远低于推定限值以下是不困难的,而且应用调查水平的概念通常也是方便的。例如,在很少发生污染的区域,测量仪器本底计数率的少许增加就应引起足够的重视,进行简单的调查以便查明新的污染源,这一行动被认为是正当的。而在污染较为普遍的区域,测量结果的趋势可能给出操作过程恶化