Effects of phosphorus content on generation and growth of cracks in nickel–phosphorus platings owing to thermal cycling

We observed crack generation and structural changes in electroless nickel–phosphorus (Ni–P) plating layers formed on copper-metalized silicon nitride substrates both during thermal cycling from ? 40 to 250 °C and during storage (not cycling) at 250 °C in order to investigate the effect of the phosphorus contents on crack generation and growth in the Ni–P platings. The used platings contained phosphorus at three different contents: 2.1 wt% [Ni–P(low)], 6.5 wt% [Ni–P(med)], and 10.9 wt% [Ni–P(high)]. The generation time and the amount of cracks were strongly dependent on their phosphorus contents. More cracks appeared after thermal cycling than after storage at 250 °C. In Ni–P(low), cracks were generated after 200 thermal cycles, whereas no cracks were observed even after 250 h of storage at 250 °C. In Ni–P(med) and Ni–P(high), both during thermal cycling and storage at 250 °C, cracks formed during or after crystallization of the amorphous layers. These results suggest that the primary factors affecting the generation of cracks in electroless Ni–P platings are crystallization of the Ni–P platings and repeated changes in thermal stress.     

Fabrication of BSCF-based mixed oxide ionic-electronic conducting multi-layered membrane by sequential electrophoretic deposition process

The Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3-δ (BSCF)-based multi-layered oxygen separation membrane was fabricated by the sequential electrophoretic deposition (EPD) process. A thin porous/dense bi-layer of BSCF was formed on a thick porous support of BSCF. The porous support prepared by a sacrificial template method using BSCF powder mixed with wheat starch (30 wt%) as a pore-forming agent, followed by uniaxial pressing and low-temperature sintering, was directly used as an EPD electrode. A thin BSCF layer was first formed on the porous support, and then a thin BSCF + PMMA (polymethyl methacrylate) layer was sequentially formed on the thin BSCF layer using a bimodal suspension of BSCF and PMMA. A 30-μm thin porous/dense bi-layer of BSCF of which the total thickness was obtained by optimizing the processes of EPD and subsequent co-sintering. The oxygen separation performance of 3.7 ml (STP) min^?1 cm^?2 at 860 °C was achieved for the BSCF-based multi-layered oxygen separation membrane.     

Anti‐Sway Crane Control Considering Wind Disturbance and Container Mass

A method for estimating the sway angle using an observer has already been proposed. The state observer estimates the sway angle accurately and must use the detected sway angle value. However, the estimated sway angle has an error owing to rope length error, friction force, and wind. Moreover, the container mass cannot be determined, and therefore the observer parameter is not suitable. We already proposed robust antisway control for overcoming rope length error without adding a new sensor. Further, we designed a friction disturbance observer to cancel out the influence of the friction force. In this paper, we first propose a container mass estimation method when a crane system performs rolling up control. The observer parameter can be selected using the estimated mass value. Second, in crane parallel shift control, we propose a robust antisway control even when there is a wind disturbance. We design a wind disturbance observer and propose a wind disturbance estimator to separate the friction observer output from the wind disturbance observer output. We confirm through experiments that the proposed method can reduce vibration.     

A wind-tunnel study on exhaust gas dispersion from road vehicles—Part I: Velocity and concentration fields behind single vehicles

By a reduced-scale model in a wind tunnel, we investigate the dispersion behavior of exhaust gas from automobiles. Two types of vehicles are considered, a passenger car and a small-size truck. Tracer gas experiments show that the exhaust gas dispersion is enhanced significantly by the vehicle wake compared to the case when the vehicle body is absent. The passenger car and the truck promote dispersion in the horizontal and the vertical direction, respectively. The wake field is analyzed by particle image velocimetry (PIV), and the distribution of the mean and the fluctuation fields is found to conform to the concentration field of the exhaust gas. The buoyancy of the exhaust gas has minor effect except on the vertical spread behind the truck whose wake flow amplifies the vertical displacement generated near the pipe exit.     

Fracture Resistance Behavior of High‐Thermal‐Conductivity Silicon Nitride Ceramics

Silicon nitride ceramics were prepared from a high‐purity silicon powder doped with 2 mol% Y₂O₃ and 5 mol% MgO as sintering additives via a route of sintering of reaction‐bonded silicon nitride (SRBSN). The materials sintered at 1900°C for 3, 6, 12, and 24 h had thermal conductivities of 109, 125, 146, and 154 W/m/K, and four‐point bending strengths of 786, 676, 608, and 505 MPa, respectively. The fracture toughness values, determined by the single‐edge‐precracked‐beam (SEPB) method, were 8.4, 8.6, 9.7, and 10.7 MPa m^1/2 for the materials sintered for 3, 6, 12, and 24 h, respectively, which were similar to the results measured by the chevron‐notched‐beam (CNB) test method. The materials sintered for longer times (12 and 24 h) showed stronger R‐curve behaviors over longer range of crack extension, in comparison with the materials sintered for shorter times (3 and 6 h).     

Effect of Calcium Maltobionate on the Glass Transition Temperature of Model and Hand-made Hard Candies

Glass transition temperature (T_g) is an important parameter for the physical quality control of hard candies. In order to understand the applicability of calcium maltobionate to hard candy, effect of calcium maltobionate addition on the T_g of model and hand-made hard candies was investigated. Freeze-dried calcium maltobionate-sugar (sucrose containing a small amount of glucose-fructose mixture) and calcium maltobionate-reduced isomaltulose mixtures were prepared as model candies, and their anhydrous T_g was evaluated using a differential scanning calorimetry. The anhydrous T_g increased linearly with the molar fraction of calcium maltobionate. From these results, it was expected that calcium maltobionate can improve the physical stability of normal and sugarless candies. For comparison, various commercial candies were employed, and their T_g was evaluated using a thermal rheological analysis. The T_g values were in the range of 28–49 °C. The T_g values were higher than 25 °C, which is significant with respect to the physical stability of the candies. Calcium maltobionate-sugar and calcium maltobionate-reduced isomaltulose candies were prepared as hand-made candies. The calcium maltobionate-reduced isomaltulose candies had higher T_g than the calcium maltobionate-sugar candies at each calcium maltobionate content, although reduced isomaltulose has a lower T_g than sugar. At a high calcium maltobionate content, calcium maltobionate-reduced isomaltulose candy had an equivalent T_g to the commercial sugarless candies, and thus practically acceptable stability was expected. In the case of calcium maltobionate-sugar candies, there was a possibility that the hydrolysis of sugar reduced their T_g. Vacuum-concentration will be useful to improve the T_g of the candies.     

Present Status of the Nd:YAG Thomson Scattering System Development for Time Evolution Measurement of Plasma Profile on Heliotron J

A new high repetition rate Nd:YAG Thomson scattering system is developed for the Heliotron J helical device.A main purpose of installing the new system is the temporal evolution measurement of a plasma profile for improved confinement physics such as the edge transport barrier (H-mode) or the internal transport barrier of the helical plasma.The system has 25 spatial points with ～10mm resolution.Two high repetition Nd:YAG lasers (>550mJ@ 50Hz) realize the measurement of the time evolution of the plasma profile with ～10ms time intervals.Scattered light is collected by a large concave mirror (D=800 mm,f/2.25) with a solid angle of ～100 mstr and transferred to interference filter polychromators by optical fiber bundles in a staircase form.The signal is amplified by newly designed fast preamplifiers with DC and AC output,which reduces the low frequency background noise.The signals are digitized with a multi-event QDC,fast gated integrators.The data acquisition is performed by a VME-based system operated by the CINOS.     

Capillary rise properties of porous mullite ceramics prepared by an extrusion method with various diameters of fiber pore formers

Porous mullite ceramics with unidirectionally oriented pores were prepared by an extrusion method using rayon fibers as the pore formers. Rayon fibers of 8.1, 9.6, 16.8, and 37.6 μm in diameter were used as the pore formers and were kneaded with alumina powder, kaolin clay, China earthen clay, and water to form pastes. These pastes were extruded into cylindrical tubes, dried, and fired at 1500 °C for 4 h. The apparent porosities ranged from 45.7 to 48.2 %. The pore size distributions showed a sharp peak at 9.4, 10.0, 15.6, and 30 μm with increasing fiber diameters. The height of the capillary rise was 1780, 1670, 1320, and 950 mm with increasing fiber diameter. The maximum capillary rise is much higher than previously reported. The contact angle and effective pore radius that determine the capillary rise ability were calculated by fitting the capillary rise curves using the Fries and Dreyer’s equation.     

The Function of Sialidase Revealed by Sialidase Activity Imaging Probe

Sialidase cleaves sialic acid residues from glycans such as glycoproteins and glycolipids. In the brain, desorption of the sialic acid by sialidase is essential for synaptic plasticity, learning and memory and synaptic transmission. BTP3-Neu5Ac has been developed for sensitive imaging of sialidase enzyme activity in mammalian tissues. Sialidase activity in the rat hippocampus detected with BTP3-Neu5Ac increases rapidly by neuronal depolarization. It is presumed that an increased sialidase activity in conjunction with neural excitation is involved in the formation of the neural circuit for memory. Since sialidase inhibits the exocytosis of the excitatory neurotransmitter glutamate, the increased sialidase activity by neural excitation might play a role in the negative feedback mechanism against the glutamate release. Mammalian tissues other than the brain have also been stained with BTP3-Neu5Ac. On the basis of information on the sialidase activity imaging in the pancreas, it was found that sialidase inhibitor can be used as an anti-diabetic drug that can avoid hypoglycemia, a serious side effect of insulin secretagogues. In this review, we discuss the role of sialidase in the brain as well as in the pancreas and skin, as revealed by using a sialidase activity imaging probe. We also present the detection of influenza virus with BTP3-Neu5Ac and modification of BTP3-Neu5Ac.