Graded evolution of anisotropic microstructure during sintering from crystal-oriented powder compact

Anisotropic sintering, including shrinkage and grain growth, was examined for c-axis-oriented (Sr,Ca)₂NaNb₅O₁₅ (SCNN) ceramics, which were prepared by colloidal processing under a magnetic field. In the c-axis-oriented SCNN powder compact, shrinkage and grain growth along the c-axis were higher than those along the a-axis. The anisotropic microstructural development was clearly associated with anisotropic sintering shrinkage. X-ray diffraction, scanning electron microscopy, and energy back scattering diffraction showed that the grain growth of oriented particles by including random grains contribute to the development of the oriented microstructure. Finally, the highly crystal-oriented SCNN ceramics with a densified microstructure were obtained through anisotropic sintering. These results clearly showed the potential to develop a well-defined anisotropic microstructure during sintering by designing and controlling the particle packing structure in a powder compact.     

Vapor absorption by LiBr aqueous solution in vertical smooth tubes

Heat and mass transfer in a falling film vertical in-tube absorber was studied experimentally with LiBr aqueous solution. The presented results include the effect of solution flow rate, solution subcooling and cooling water temperature on the absorption in a smooth copper tube 16.05 mm I.D. and 400 mm long. The experimental data in the previous report for a 1200-mm-long tube was also re-examined and compared. It was demonstrated by the observation of the flow in the tube that the break down of the liquid film into rivulets leads to deterioration of heat and mass transfer at lower film Reynolds number or in longer tubes. An attempt to evaluate physically acceptable heat and mass transfer coefficients that are defined with estimated temperature and concentration at the vapor–liquid interface was also presented.     

Preparation of pyrochlores. A1−xHxTaO3·nH2O (A=Na,K)

Pyrochlores of A_1?xH_xTaO₃·nH₂O (A=Na,K) were prepared under the hydrothermal conditions. The values of x for these compounds were increased from 0.3 to 0.5 for A=Na and from 0.2 to 0.5 for A=K by treatment with the distilled water. The compounds with x<0.5 were decomposed to a mixture of NaTaO₃ and Na₂Ta₄O₁₁ for A=Na, or to a mixture of KTaO₃ and a tetragonal tungsten bronze phase, and those with x=0.5 to a single phase of A₂Ta₄O₁₁ at elevated temperatures. Below the decomposition temperatures, defect pyrochlores with oxygen vacancies, $\text{A}{}_{\mathrm{<mtext>1?</mtext><mtext>x</mtext>}}\text{TaO}{}_{\mathrm{<mtext>3?</mtext><mtext>x</mtext><mtext>2</mtext>}}$, were produced. They were hygroscopic, and in the case of A=K and x=0.5 the original phase was recovered by leaving in air for several hours.     

66/77-kV C-GIS using composite insulation in SF6 gas

A second-generation model of cubicletype gas-insulated switchgear (C-GIS) with composite insulation incorporating SF₆ gas has been developed. The design does not require a gas process in field assembly; it has high reliability and its installation is more rapid; and a further reduction in size is achieved. The design principles are described in detail.     

FDTD analysis of switching characteristics in magnetooptic functional devices using magnetostatic surface waves

Collinear magnetooptic interaction with magnetostatic surface waves (MSSW) can be used for wavelength‐selective switches, wavelength filters, and frequency shifters in wavelength‐division‐multiplexed (WDM) photonic networks and optical processing systems. The switching efficiency can be improved with a multilayer waveguide structure. To investigate the dynamic switching characteristics, the FDTD method was employed. The mode conversion between TE and TM mode was successfully demonstrated with FDTD simulation. The filtering characteristics were also evaluated. The FDTD results were compared with the result from the coupled mode theory, and good agreement was obtained. Switching of an optical pulse was also demonstrated by the FDTD method. © 2007 Wiley Periodicals, Inc. Electr Eng Jpn, 162(1): 40–47, 2008; Published online in Wiley InterScience ( www.interscience.wiley.com ). DOI 10.1002/eej.20501     

Twin-Related Tetragonal Variants in Yttria Partially Stabilized Zirconia

Crystals of yttria partially stabilized zirconia were grown by the arc-image floating-zone technique and studied by transmission electron microscopy. Crystals annealed at 1700°C consist of tetragonal precipitates and a cubic matrix. The platelike domains in a precipitate are twin-related tetragonal variants stacked alternately parallel to the (011) twin plane. The axial relations between the tetragonal precipitate and the cubic matrix are [100]_tetragonal|[100]_cubic, [011]_tetragonal|[011]_cubic.     

Electrical resistivity and Seebeck coefficient of La1−x M x MnO3 (M = Ca,Sr) single crystals

The temperature dependence of the electrical resistivity and Seebeck coefficient was measured on single crystals of La_1–x Ca _x MnO₃(0 <x 0.3) and La_1–x Sr _x MnO 3 (0 <x 0.4) grown by the arc-image floating zone method. The electrical conduction for La_1–x crystals withx 0.2 was of the activation type aboveT _c and of the degenerate type belowT _c, while that for the crystal withx = 0.1 was of the activation type over the whole measured temperature range between –170 and 400°C. The conduction behaviour of La_{1– x} Sr _x MnO₃ was essentially the same as that of La_1–x Ca _x MnO₃ except that the conduction of the crystals withx = 0.3 and 0.4 was of the degenerate type aboveT _c. A distinct difference in Seebeck data was observed between the calcium and the strontium compounds.     

X-ray CDF study on the behaviour of the amorphous chain under extension

The behaviour of the amorphous chain in vulcanized natural rubber (NR) and styrene-butadiene rubber (SBR) under extension is studied by means of the cylindrical distribution function (CDF) derived from wide angle X-ray scattering (WAXS). In the case of the highly stretched vulcanized NR where the orientation-induced crystallization took place, the observed WAXS intensity was separated into a crystalline peak component and a broad amorphous one from which the CDF was obtained. The CDF calculated from the broad component shows that some of the amorphous segments of the highly stretched vulcanized NR are extended as fully as the crystalline chains and that the fraction of the segments increases with increasing extension. In the case of SBR, such fully stretched segments as in the case of the vulcanized NR show higher degree of an interchain packing order than those in the vulcanized NR.     

Residual Stress in Siliceous Glass Between Mullite Crystals

A birefringence of siliceous glass, which is coexisting with mullite crystals, was studied by an optical polarizing microscope. The cause of the birefringence was assumed to be the residual stress induced by a large contraction difference between the mullite and glass on cooling. The stress has been evaluated to be as high as—0.3 GPa, and to correspond to the elastic one which began to develop at the glass transition point.     

Synthesis of terpene alcohols from isoprene oligomers

Various terpene alcohols were prepared from isoprene oligomers via two steps: epoxidation with peracetic acid and isomerisation with aluminium triisopropoxide. For example, 2-methylene-6-methyl-7-octene-1-o1 was prepared from 2,6-dimethyl-1,7-octadiene. From 2,6-dimethyl-2,7-octadiene, 3,3,6-trimethyl-1,5-heptadiene, 2,7-dimethyl-2,6-octadiene, 2,6-dimethyl-1,3,6-octatriene, 1-methyl-4-isopropenyl-1-cyclohexene, and 1,5-dimethyl-1,5-cyclooctadiene, the corresponding alcohols were obtained, respectively.