非离子型聚氨酯预聚体可聚合乳化剂的合成及性能

采用甲苯二异氰酸酯 (TDI) ,聚乙二醇 10 0 0 (PEG -10 0 0 ) ,丙烯酸为原料 ,通过分子设计合成了带有双键的非离子型可聚合乳化剂。并对其CMC值、流变行为及乳化力进行了表征。结果显示 :此乳化剂的CMC值在 6.0 %左右、浊点为 (54± 1)℃、HLB值为 16.1可以取代OP -10的乳化能力 ;该乳化剂可以与丙烯酸酯类单体进行乳液共聚 ,得到性能优异的共聚乳液     

环氧树脂改性聚氨酯-丙烯酸酯乳液的合成

聚氨酯-丙烯酸酯复合乳液虽然较单一乳液的性能有很大改善,但是其涂膜的硬度、耐水性、耐化学品性还难以满足高档水性木器涂料的要求。在聚氨酯-丙烯酸酯复合乳液中以不同方式加入环氧树脂,分别制备了物理共混和化学共聚的聚氨酯-丙烯酸酯-环氧树脂复合乳液,研究了环氧树脂加入方式、用量等对乳液及涂膜性能的影响。研究发现环氧树脂对于涂膜的硬度、耐水性、耐化学品性等有明显改进。环氧树脂的质量分数在3%～4%为宜。     

影响环氧改性水性PUA乳液稳定性和耐水性的因素

以甲苯二异氰酸酯（TDI-80）、聚醚二醇（N220）、二羟甲基丙酸（（DMPA）、1，4-丁二醇（BDO）、环氧树脂E-20和丙烯酸羟丙酯（HPA）为主要原料，用三乙胺（（TEA）作中和剂、乙二胺（EDA）为扩链剂制备了环氧改性的水性聚氨酯-丙烯酸酯乳液，讨论了NCO／OH总摩尔比、DMPA含量、HPA含量、环氧树脂含量和中和度对乳液稳定性和耐水性的影响。结果表明，PUA乳液的耐水性随着NCO／OH总摩尔比和环氧树脂用量的增加明显增强，随中和度的增大而减弱；随着DMPA含量和中和度的增大，PUA乳液的外观和稳定性变好；当NCO／OH的总摩尔比为1．1～1．2，DMPA的含量为6％，环氧树脂的用量为4％～8％，以及中和度为90％～95％时，所得PUA乳液具有较好的稳定性和耐水性。     

室温自交联水性含氟聚氨酯-聚丙烯酸酯复合乳液的制备

采用原位无皂乳液聚合工艺,以丙烯酸单体为溶剂,双丙酮丙烯酰胺（DAAM)和己二酰肼（ADH)为交联体系得到室温自交联水性含氟聚氨酯-聚丙烯酸酯（WFPUA)。通过红外光谱（FT-IR)、透射电镜（TEM)和原子力显微镜（AFM)对聚合物结构进行了表征。同时,研究了含氟量,酮肼交联比例对WFPUA胶膜的性能影响。结果显示,当含氟量为8%、酮肼摩尔比为1：1时,接触角能达到110.5?,吸水率下降至8.8%,抗拉强度从18.12MPa提高至28.55MPa。热重分析表明,酮肼交联的引入有效提高了乳胶膜的热稳定性。     

阳离子含氟PUA表面施胶剂的制备及应用

为制备一种能够明显提高纸张施胶效果和印刷性能的聚合物表面施胶剂,以2,2,3,4,4,4-六氟丁醇甲基丙烯酸酯(FA)、苯乙烯(St)、丙烯酸丁酯(BA)为单体,在交联聚氨酯溶液(PU)中通过溶液聚合相转化法制得阳离子含氟聚氨酯-丙烯酸酯复合乳液(FPUA)表面施胶剂.用FT-IR、TEM和纸张物理性能检测的手段对聚合物结构、乳胶粒子形态以及应用性能进行了表征.实验结果表明,以质量分数为1.0%的FPUA进行表面施胶时,可使纸张的施胶度和拉毛速率分别达到9.50 s和2.80 m/s以上,油墨吸收率为26.0%～29.0%;乳胶粒子呈球形,其粒径约为230nm.     

聚氨酯-丙烯酸酯复合乳液的合成条件研究

研究了聚氨酯-丙烯酸酯（PUA）复合乳液的合成条件：引发剂的种类和用量、丙烯酸（AA）、软硬单体比例、乳化剂以及反应温度的影响，得出：用K2S2O8做引发剂能得到稳定的PUA乳液，适量的AA有利于涂膜的附着力，硬单体的比例增大有利于涂膜的耐水性；乳液聚合只用少量的、适当比例的乳化剂就能得到稳定的复合乳液；聚合温度控制在80-85℃为宜。     

The utilization of carbon nitride to reinforce the mechanical and thermal properties of UV-curable waterborne polyurethane acrylate coatings

The waterborne polyurethane-acrylate (WPUA and Wsi-PUA) oligomers were prepared by anionic self-emulsifying method, using isophorone diisocyanate (IPDI), polyethylene glycol (PEG), dimethylol propionic acid (DMPA), vinyl hydroxyl silicone oil (VHSO) and hydroxyethyl methyl acrylate (HEMA) as raw materials. Then, a series of UV-curable waterborne Wsi-PUA–C₃N₄ composites containing different content of g-C₃N₄ were obtained with oligomer and photoinitiator Darocur 1173. FTIR, XRD, TEM, SEM, and TGA were employed to investigate the structure, morphology and thermal property of the Wsi-PUA–C₃N₄ composite films. The effect of g-C₃N₄ content on the performance was also investigated. The mechanical performance, water resistance and gel content of UV-PUA films were measured. It was found that with g-C₃N₄ particle was introduced into Wsi-PUA oligomer, the hardness, tensile strength, gel content, water resistance and thermal stability of composite films were significantly augmented. Moreover, when the content of g-C₃N₄ was 1.0 wt.%, the UV-curable film had the best mechanical property. The obtained composite is promising for a number of applications, e.g., for protecting the surfaces of metal and wood.     

聚氨酯-丙烯酸酯复合乳液的合成与性能

采用甲基丙烯酸甲酯(MMA)与水性聚氨酯乳液共聚反应制备聚氨酯-丙烯酸酯(PUA)复合乳液,研究了MMA添加量、引发剂种类和聚合温度对PUA复合乳液及涂膜性能的影响,确定了PUA复合乳液合成的工艺参数。用傅立叶红外光谱(FTIR)测定反应产物的结构。研究发现油溶性引发剂比水溶性引发剂更适合PUA体系的乳液聚合。随着MMA添加量的增大,PUA复合乳液胶粒粒径增大,黏度减小,涂膜光泽度下降,机械性能增强,耐水性增加。     

聚氨酯／丙烯酸酯复合弹性乳液的研究

通过粒径、热性能和力学性能的测定,研究了非共聚型及共聚型水性聚氨酯/丙烯酸酯(PUA)弹性树脂的结构和性能。发现PUA具有核/壳结构特征;共聚型PUA比非共聚型PUA具有更好的聚丙烯酸酯(PA)、聚氨酯(PU)之间的混溶性;PA复合PU后,不仅提高了乳液的固含量,而且体现出较好的弹性,适合于弹性建筑涂料等方面的应用。     

胶粘剂用聚氨酯-丙烯酸酯复合乳液的合成与表征

提出了合成PUA复合乳液的新的原位乳液聚合工艺,通过多次实验得出了最佳配比为:NCO/OH(总)为1.1￣1.2,DMPA的质量百分含量为2.1%￣2.2%,MMA占固体分的20%左右。激光散射法测定的乳液胶粒粒径及其分布表明,MMA含量较高时胶粒按几个粒子融合机理增大,较低时胶粒按单个粒子长大机理增大。