Effect of heat treatment and zircon addition on the properties of low-cement castables based on recycled alumina grog

In this investigation, low-cement castables were prepared using 70% alumina grog aggregates obtained from crushed alumina brick waste. The aggregates were thermally treated at 1550 °C for 3 h. Four types of low-cement castables were prepared with various types of aggregates (alumina grog with or without thermal treatment) and fillers (with or without zircon addition), and they were evaluated in terms of their physical, thermal, and chemical properties. Microstructural analysis via scanning electron microscopy (SEM) was performed on the castables before and after slag attack. Compared to the other fabricated castables, the thermally treated alumina grog castables with zircon showed better physical properties, such as a higher bulk density, cold crushing strength, and modulus of rupture and a lower apparent porosity and water absorption. In addition, they had a higher positive linear thermal expansion, refractoriness under load, permanent linear change, and hot modulus of rupture. The results of the SEM with energy dispersive X-ray analysis of the prepared castables confirmed that the mullite and anorthite phases were predominant when zircon was not added and the zircon–mullite phase additionally appeared upon the incorporation of zircon. A quantitative elemental analysis via X-ray fluorescence spectroscopy was employed to determine the composition of the castables. X-ray diffraction analysis showed that the alumina grog castables had a high mullite and low anorthite content, and the thermally treated alumina grog had a high anorthite, low mullite, and high zircon content. The improvement in the mechanical and thermo-mechanical properties of the castables with thermally treated alumina grog and added zircon can be attributed to the formation of the zircon–mullite phase with a low mullite phase content.     

Influence of α′‐/α‐crystal polymorphism on properties of poly(l‐lactic acid)

Poly(l ‐lactic acid) (PLLA) is a biodegradable and biocompatible thermoplastic polyester produced from renewable sources, widely used for biomedical devices, in food packaging and in agriculture. It is a semicrystalline polymer, and as such its properties are strongly affected by the developed semicrystalline morphology. As a function of the crystallization temperature, PLLA can form different crystal modifications, namely α′‐crystals below about 120 °C and α‐crystals at higher temperatures. The α′ modification is therefore of special importance as it may be the preferred polymorph developing at processing‐relevant conditions. It is a metastable modification which typically transforms into the more stable α‐crystals on annealing at elevated temperature. The structure, kinetics of formation and thermodynamics of α′‐ and α‐crystals of PLLA are reviewed in this contribution, together with the effect of α′‐/α‐crystal polymorphism on the properties of PLLA. © 2018 Society of Chemical Industry     

Nanotechnology‐based wastewater treatment

Water contamination is a global challenge impacting both the environment and human health with significant economic and social costs. The growing scarcity of usable water resources requires effective treatment of wastewater. In this context, developing cheaper, safer and more efficient wastewater treatment technologies are the need of the hour. One promising approach that several studies have reported success has been the usage of nanomaterials in water and waste water management. The rapid progress of research in nanomaterial sciences has shown their growing potential; however, there has not been a great amount of information available on their implementation. This review focuses on developments in nanotechnology that hold strong potential for wastewater treatment. The review covers key techniques in nanomaterial‐based water treatments including adsorption, filtration and photocatalysis with recent examples showing how to improve their properties and efficiencies according to the need.     

Effects of upholstery materials on the burning behavior of real‐scale residential upholstered furniture mock‐ups

Fire spread and growth on real‐scale four cushion mock‐ups of residential upholstered furniture (RUF) were investigated with the goal of identifying whether changes in five classes of materials (barrier, flexible polyurethane foam, polyester fiber wrap, upholstery fabric, and sewing thread), referred to as factors, resulted in statistically significant changes in burning behavior. A fractional factorial experimental design plus practical considerations yielded a test matrix with 20 material combinations. Experiments were repeated a minimum of two times. Measurements included fire spread rates derived from video recordings and heat release rates (HRRs). A total of 13 experimental parameters (3 based on the videos and 10 on the HRR results), referred to as responses, characterized the measurements. Statistical analyses based on Main Effects Plots (main effects) and Block Plots (main effects and factor interactions) were used. The results showed that three of the factors resulted in statistically significant effects on varying numbers of the 13 responses. The Barrier and Fabric factors had the strongest main effects with roughly comparable magnitudes. Foam was statistically significant for fewer of the responses and its overall strength was weaker than for Barrier and Fabric. No statistically significant main effects were identified for Wrap or Thread. Multiple two‐term interactions between factors were identified as being statistically significant. The Barrier*Fabric interaction resulted in the highest number of and strongest statistically significant effects. The existence of two‐term interactions means that it will be necessary to consider their effects in approaches designed to predict the burning behavior of RUF.     

Continuous Flow Fabrication of Block Copolymer–Grafted Silica Micro‐Particles in Environmentally Friendly Water/Ethanol Media

Polymer‐grafted inorganic particles (PGIPs) are attractive building blocks for numerous chemical and material applications. Surface‐initiated controlled radical polymerization (SI‐CRP) is the most feasible method to fabricate PGIPs. However, a conventional in‐batch reaction still suffers from several disadvantages, including time‐consuming purification processes, low grafting efficiency, and possible gelation problems. Herein, a facile method is demonstrated to synthesize block copolymer–grafted inorganic particles, that is, poly(poly(ethylene glycol) methyl ether methacrylate) (PPEGMEMA)‐b‐poly(N‐isopropylacrylamide) (PNIPAM)–grafted silica micro‐particles using continuous flow chemistry in an environmentally friendly aqueous media. Immobilizing the chain transfer agent and subsequent SI‐CRP can be accomplished sequentially in a continuous flow system, avoiding multi‐step purification processes in between. The chain length (MW) of the grafted polymers is tunable by adjusting the flow time or monomer concentration, and the narrower molar mass dispersity (Р< 1.4) of the grafted polymers reveals the uniform polymer chains on the particles. Moreover, compared with the in‐batch reaction at the same condition, the continuous system also suppresses possible gelation problems.     

Off‐grid DoA estimation method of wideband signals

In this paper, an off‐grid direction of arrival (DoA) estimation method is proposed for wideband signals. This method is based on the sparse representation (SR) of the array covariance matrix. Similar to the time domain DoA estimation methods, the correlation function of the sources was assumed to be the same and known. A new measurement vector is obtained using the lower‐left triangular elements of the covariance matrix. The DoAs are estimated by quantizing the entire range of continuous angle space into discrete grid points. However, the exact DoAs may be located between two grid points; therefore, this estimation has errors. The accuracy of DoA estimation is improved by the minimization of the difference between the new measurement vector and its estimated values. Simulation results revealed that the proposed method can enhance the DoA estimation accuracy of wideband signals.