Influence of metal-support interactions on reaction pathways over Ni/CeZrOx–Al2O3 catalysts for ethanol steam reforming

This work investigates selective Ni locations over Ni/CeZrO_x–Al₂O₃ catalysts at different Ni loading contents and their influences on reaction pathways in ethanol steam reforming (ESR). Depending on the Ni loading contents, the added Ni selectively interacts with CeZrO_x–Al₂O₃, resulting in the stepwise locations of Ni over CeZrO_x–Al₂O₃. This behavior induces a remarkable difference in hydrogen production and coke formation in ESR. The selective interaction between Ni and CeZrO_x for 10-wt.% Ni generates more oxygen vacancies in the CeZrO_x lattice. The Ni sites near the oxygen vacancies enhance reforming via steam activation, resulting in the highest hydrogen production rate of 1863.0 μmol/g_cat·min. In contrast, for 15 and 20-wt.% Ni, excessive Ni is additionally deposited on Al₂O₃ after the saturation of Ni–CeZrO_x interactions. These Ni sites on Al₂O₃ accelerate coking from the ethylene produced on the acidic sites, resulting in a high coke amount of 19.1 mg_c/g_cat·h (20Ni/CZ-Al).     

Analysis and proposition of limiting current density measurement protocol

Limiting current density at different temperatures, backpressures, and balance gases can be used to separate molecular diffusion resistance, Knudsen diffusion resistance and local transport resistance of membrane electrode assembly (MEA). However, the measurement of limiting current density has no unified protocol. The diverse choices in the literature, either in the control of current or voltage or in the atmosphere like relative humidity and O₂ concentrations, make it difficult to compare the results and identify the true bottleneck hindering the mass transport. In this work, the current-voltage curves obtained by current scanning/stepping and voltage scanning/stepping methods under dilute O₂ of different concentrations and a wide range of relative humidity were measured and analyzed systematically. It is found that the voltage stepping method is superior to the other three ways of control for the reliable determination of the limiting current density. Aided with simultaneous electrochemical impedance spectroscopy measurement, the limiting current density can be determined with pinpoint accuracy. When the limiting current density is just used to qualitatively evaluate different MEA, the voltage scanning method can be used instead for its high time efficiency. The selection of the atmosphere also plays an important role in suppressing the distortion from excessive water and reducing the spurious contribution from proton conduction resistance. It is found that O₂ concentrations at 0.5 vol% and relative humidity at 90% can give the best estimation of O₂ transport resistance in membrane electrode assembly.     

No-Reference Video Quality Assessment using novel hybrid features and two-stage hybrid regression for score level fusion

This paper presents a novel No-Reference Video Quality Assessment (NR-VQA) model that utilizes proposed 3D steerable wavelet transform-based Natural Video Statistics (NVS) features as well as human perceptual features. Additionally, we proposed a novel two-stage regression scheme that significantly improves the overall performance of quality estimation. In the first stage, transform-based NVS and human perceptual features are separately passed through the proposed hybrid regression scheme: Support Vector Regression (SVR) followed by Polynomial curve fitting. The two visual quality scores predicted from the first stage are then used as features for the similar second stage. This predicts the final quality scores of distorted videos by achieving score level fusion. Extensive experiments were conducted using five authentic and four synthetic distortion databases. Experimental results demonstrate that the proposed method outperforms other published state-of-the-art benchmark methods on synthetic distortion databases and is among the top performers on authentic distortion databases. The source code is available at https://github.com/anishVNIT/two-stage-vqa.     

Preparation of high-activity coal char-based catalysts from high metals containing coal gangue and lignite for catalytic decomposition of biomass tar

The potential of using high metals containing coal gangue and lignite to prepare high-activity coal char-based catalysts is investigated for effective biomass tar decomposition. Loose structure and rough surface are formed for these char-based catalysts with heterogeneous distribution of a large number of inorganic particles. In the biomass tar decomposition, the performance of the coal char-based catalysts is significantly influenced by the content of the metals in the raw materials and coal gangue char (GC) with the ash content as high as 50.80% exhibits the highest activity in this work. A high biomass tar conversion efficiency of 93.5% is achieved at 800 °C along with a significant increase in the fuel gas product. During the five-time consecutive tests, the catalytic performance of GC increases a little at the second or third times reuse and remains relatively stable, showing the remarkable stability of the catalyst in biomass tar decomposition applications.     

Phase composition,microstructure, and properties of Al4O4C–(Al2OC)1-x(AlN)x –Zr2Al3C4–Al2O3 refractories prepared at high temperatures in nitrogen

The novel Al₄O₄C–(Al₂OC)_1-x(AlN)_x–Zr₂Al₃C₄–Al₂O₃ refractories with ultra-low carbon content have been successfully prepared by constructing the core-shell structure of aluminum at 1300–1700°C in nitrogen. The phase composition, microstructure, and properties of the novel refractories are deeply investigated. The cracking temperature on the core-shell structure of aluminum is further explored and the reaction mechanism of Zr₂Al₃C₄ has also added explanation. The results show that the novel refractories have excellent physical properties and cannot be corroded by molten iron. There exist two different Al₂OC solid solutions in the novel refractories, Al₂OC-rich (Al₂OC)_1-x(AlN)_x and AlN-rich (Al₂OC)_1-x(AlN)_x. The temperatures affect their relative content. When temperatures are less than 1600°C, the relative content of Al₂OC-rich (Al₂OC)_1-x(AlN)_x is more than that of AlN-rich (Al₂OC)_1-x(AlN)_x. When temperatures are above 1700°C, the relative content of AlN-rich (Al₂OC)_1-x(AlN)_x is more than that of Al₂OC-rich (Al₂OC)_1-x(AlN)_x. The core-shell structure of aluminum fully ruptures at about 1200°C. Zr₂Al₃C₄ begins to form at about 1000°C and generates in large at 1200°C.     

Investigation on thermal conductivity and mechanical properties of Si3N4 ceramics via one-step sintering

High thermal conductivity Si₃N₄ ceramics were fabricated using a one-step method consisting of reaction-bonded Si₃N₄ (RBSN) and post-sintering. The influence of Si content on nitridation rate, β/(α+β) phase rate, thermal conductivity and mechanical properties was investigated in this work. It is of special interest to note that the thermal conductivity showed a tendency to increase first and then decrease with increasing Si content. This experimental result shows that the optimal thermal conductivity and fracture toughness were obtained to be 66 W (m K)^-1 and 12.0 MPa m^1/2, respectively. As a comparison, the nitridation rate and β/(α+β) phase rate in a static pressure nitriding system, i.e., 97% (MS10), 97% (MS15), 97% (MS20) and 8.3% (MS10), 8.3% (MS15), 8.9% (MS20), respectively, have obvious advantages over those in a flowing nitriding system, i.e., 91% (MS10), 91% (MS15), 93% (MS20) and 3.1% (MS10), 3.3% (MS15), 3.3% (MS20), respectively. Moreover, high lattice integrity of the β-Si₃N₄ phase was observed, which can effectively confine O atoms into the β-Si₃N₄ lattice using MgO as a sintering additive. This result indicates that one-step sintering can provide a new route to prepare Si₃N₄ ceramics with a good combination of thermal conductivity and mechanical properties.     

微波辅助孵育法富集麦胚多肽的工艺优化

目的 麦胚孵育过程中蛋白酶将蛋白质水解成肽和氨基酸，多肽具有明确的生理活性和营养调节作用。本研究以麦胚为试验原料，采用微波辅助预处理的方法，研究孵育的温度、时间、pH及料液比4种因素对孵育后的蛋白酶活力及多肽含量的影响。 方法 通过单因素和响应曲面试验进行工艺条件优化。 结果 与未进行微波辅助预处理的样品相比，微波辅助处理（600 W, 10 s）能显著提高孵育后样品中的蛋白酶酶活力（约9.4倍）和肽含量（约3.1倍）。经过微波辅助处理后，孵育温度为51.5℃、pH为4.0、时间为6.33 h、料液比为1:7时，蛋白酶活力达最高为3826.24 U/g；孵育温度为45.0 ℃、pH为4.8、时间为8 h、料液比为1:7时，肽含量达最高为262.63 mg/g。 结论 微波辅助处理能有效的激活麦胚孵育液中的内源性蛋白酶活性，促进蛋白水解反应，显著提高孵育后的肽含量。该研究结果为麦胚多肽的制备新工艺开发提供了研究基础。     

广州市郊填埋场附近蔬菜重金属检测与讨论

蔬菜是人们餐桌上必不可少的食物,重金属在受污染的自然环境中又无处不在,而蔬菜中的重金属含量尤其令人担忧。本文使用原子吸收分光光度法(石墨炉)和原子荧光分光光度法检测了广州市郊某垃圾填埋场附近所种植蔬菜中重金属含量。结果:抽样由2013年10月至2014年9月共持续一年,共抽样检测12次,按平均每个月一次的频率,检测结果并未发现有蔬菜超出国家规定的限量值。