为解决电镀砂轮磨削加工中容屑空间不足的问题，采用点胶微粘接的方法制备了磨料有序排布的电镀砂轮，分析了磨料粘接效果和镀层力学性能。通过SEM分析了磨料/镀层/导电胶的结合界面，并进行了干磨削试验。研究结果表明，直径约为磨料粒径40%的胶点可粘接住磨料，单个胶点上粘接多颗磨料的占比小于6%；双脉冲电镀工艺制备的镀层显微硬度大于500HV，表层残余应力小于100MPa，磨料/镀层/导电胶之间的界面贴合紧密，无明显缺陷；砂轮在磨削时没有出现磨料脱落现象。     

Effect of spheroidized microstructure on the impact toughness and electrochemical performance of a high-carbon steel

The influence of cementite spheroidization on the impact toughness and electrochemical properties of a high-carbon steel has been thoroughly investigated in this study. Heavy warm rolling, followed by 2 h of annealing, has resulted in near-complete spheroidization, leading to a microstructure consisting of nano-cementite globules dispersed in the ultrafine-grained ferritic matrix. The Charpy impact test exhibited superior impact toughness with increased spheroidization. It is validated by the presence of abundant dimples in the fractographs of spheroidized specimens, in contrast to the as-received one that experienced a brittle failure due to its lamellar pearlitic structure. Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) carried out in a 3.5% NaCl solution revealed that the corrosion resistance of the alloy gets improved with the increase in the degree of spheroidization. This is attributed to the lower susceptibility of the spheroidized specimen to microgalvanic corrosion owing to the minimum area of contact between nano-spheroidized cementite and ferrite, as elucidated with the help of EIS results aided by equivalent electrical circuit model.     

Fire safe,sustainable loose furnishing

The aim of this exploratory study has been to investigate the fire properties and environmental aspects of different upholstery material combinations, mainly for domestic applications. An analysis of the sustainability and circularity of selected textiles, along with lifecycle assessment, is used to qualitatively evaluate materials from an environmental perspective. The cone calorimeter was the primary tool used to screen 20 different material combinations from a fire performance perspective. It was found that textile covers of conventional fibres such as wool, cotton and polyester, can be improved by blending them with fire resistant speciality fibres. A new three‐dimensional web structure has been examined as an alternative padding material, showing preliminary promising fire properties with regard to ignition time, heat release rates and smoke production.     

机械合金化FeS/Cu复合材料的摩擦磨损性能

以FeS和CuSn8Ni1粉末为原料，利用机械合金化技术和粉末冶金技术制备了FeS/Cu复合材料，探讨了不同载荷情况下所制备的FeS/Cu复合材料的摩擦学性能及润滑膜与转移膜特征。结果表明：机械合金化提高了FeS与铜合金基体界面结合性能，进而提高了材料减摩耐磨性能；当载荷较小时，摩擦副表面接触不稳定，复合转移膜不连续，摩擦因数波动大；载荷较大时，复合转移膜易破损，材料的减摩耐磨性能变差；当载荷为150 N时，载荷适宜，材料表面软化，复合转移膜更加完整，摩擦因数较小。     

Characterizations of friction welding joint interface for AISI 316

Because of heat amount is different from peripheral to central of friction welding interface, which is leaded to vary the characterizations along that interface. Current study, respectively, focused on the effect of different friction pressure on micro-structural and mechanical properties of that friction welding joint interface. Presently, these friction pressures are 110, 130, 150 and 170 MPa while kept all other conditions constant. The effects of different friction pressure on welding interface characterization were investigated by EDX, SEM, tensile, compression, impact and hardness tests. The tensile tests carried out on the standardized test piece with diameter 6 mm and 8 mm, thus, compression tests were extracted from the positions of 0°, 45° 90° with test specimen of 4 mm diameter and 6.5 mm length at weld center. Whereas, the impact test pieces were picked up in two positions, the first one is symmetrical, which it obtained to the respect of the rotation axis and the interface, on the other hand, the second one is non-symmetrical with the axis of rotation and symmetrical to the interface, for making the notch head coincide with the center of the welded joint, The obtained results showed that with reducing of friction pressure will present lack of bonding increasing from peripheral toward the welding center, which will responsible on reducing of the mechanical properties such as tensile, compression and impact strength.     

基于材料力学性能的最低设计金属温度曲线分析

铁素体钢在低温条件下存在明显的韧脆转变现象。为防止脆断事故的发生,需要确定铁素体钢制压力容器的最低使用温度。针对ASME中的A^D四条冲击豁免曲线,对应地选取了4种材料,基于材料实际的屈服强度和参考温度,按照ASME中豁免曲线的计算方法,计算得到4种材料的最低设计金属温度曲线,并与对应的A^D曲线对比,定量地分析ASME中豁免曲线的保守性。结果表明,ASME中的豁免曲线相对于材料自身的最低设计金属温度曲线保守性较大;韧性相近的材料被划分到不同的豁免曲线,使得韧性富裕量差异较大,对于某些材料,其断裂韧性被低估。     

转载溜槽衬板磨损预测的DEM仿真方法

针对EDEM自动划分网格较稀疏问题,采用Hypermesh划分仿真模型网格,利用Herz-Mindlin接触理论的Archard磨损模型对转载溜槽磨损问题进行仿真,在网格单元上提取出漏斗和溜管衬板的接触能量和磨损量,分析了磨损量与接触能量的关系。假设转载溜槽衬板磨损深度为物料与溜槽衬板的使用时间为线性函数,根据现场衬板磨损量的测量值,将衬板的磨损系数关系的看作隐式的单变量方程,应用EDEM软件的仿真结果求解出磨损系数的标定值。分析了漏斗和溜管的磨损机理。该方法可用于转载溜槽的磨损预测。     

森林抚育对森林生态系统的影响

伴随着我国社会经济的稳固发展,人们的生活质量逐渐有了明显改善,而在生态问题趋于严重使人们的环境保护意识显著提高的过程中,森林抚育对于森林生态系统的作用和价值愈发凸显。对此,文章针对森林抚育,从提高森林利用率、维持森林动植物生态平衡、增加可利用水资源等多个方面就其对森林生态系统的影响进行了分析,旨在给予相关森林保护工作者可行的帮助,并以此促进我国森林开发工作的可持续发展。     

飞机撞击下高温气冷堆乏燃料厂房损伤研究

本文针对典型高温气冷堆乏燃料厂房在双发商用飞机撞击载荷下的响应及结构完整性开展研究，并探讨结构特性对撞击损伤的影响。对乏燃料厂房及飞机分别建立有限元模型，通过弹体-目标相互作用分析模拟了飞机撞击过程，综合IAEA与NRC的评价准则对乏燃料厂房在飞机撞击下的损伤程度进行评估。数值结果表明：厂房上对应于机身及发动机的撞击位置发生可接受的局部损伤；乏燃料贮存井墙体对于提高构筑物抗飞机撞击能力有重要作用。此外，构筑物外形对损伤有很大影响，圆柱形壳体的抗飞机撞击能力显著强于方形厂房，是核电厂厂房设计的优化方向之一。