Self-construction of pea-like Cu/Cu2S Mott-Schottky electrocatalyst for the oxygen evolution reaction

The speed of the oxygen evolution reaction seriously affects the hydrogen production efficiency of water electrolysis. Hence it is crucial to develop efficient and durable OER electrocatalysts. Construction of heterojunction catalysts is also one of the strategies to develop efficient catalysts. In this paper, a pea-like Cu/Cu₂S–C3 Mott?Schottky electrocatalyst was self-constructed by vapor deposition, while CF (copper foam) was used as substrate material and copper source, and thiourea was served as sulfur source. The built-in electric field is formed at the metal-semiconductor interface, which endows it with promising electrocatalytic performance. As the working electrode, the overpotentials of Cu/Cu₂S–C3 required to reach the current density of 10 and 50 mA cm^?2 were about 170 and 335 mV. The impact of the Mott-Schottky structure on the catalyst was also reflected in stability. The i-t tests of the sample Cu/Cu₂S–C3 were carried out under 10 and 60 mA cm^?2 and performed well.     

Activation of LSCF–YSZ interface by cobalt migration during electrolysis operation in solid oxide electrolysis cells

High-temperature water electrolysis through solid oxide electrolysis cells (SOEC) will play a key role in building a hydrogen economy in the future. However, the delamination between the air electrode and the electrolyte remains a critical issue to be addressed. Previously, it was hypothesized that Co migration may improve the catalytic activity of the SrZrO₃ second phase at the LSCF-YSZ interface, eventually leading to the delamination. In this work, the LSCF-YSZ interfaces sintered at different temperatures were examined in detail. The activation behaviors of the LSCF electrodes upon application with electrolysis current were characterized under different conditions. Further, samples containing purposely added SrZrO₃ interlayer with and without cobalt were fabricated and compared. The activation process is less significant for the sample with cobalt-added SrZrO₃ interlayer than the sample with pure SrZrO₃ layer, supporting the hypothesis that Co migration may lead to the activation behavior.     

基于VMD和BSA-KELM的高陡边坡位移预测模型研究

边坡位移的时间序列曲线存在复杂的非线性特性,传统的预测模型精度不足以满足预测要求。为此提出了基于变分模态分解的鸟群优化-核极限学习机的预测模型,并用于河北省某水泥厂的边坡位移预测。该方法首先采用VMD把边坡位移序列分解为一系列的有限带宽的子序列,再对各子序列分别采用相空间重构并用核极限学习机预测,采用鸟群算法优化相空间重构的嵌入维度和KELM中惩罚系数和核参数三个数值,以取得最优预测模型。最后将各个子序列预测值叠加,得到边坡位移的最终预测值。结果表明：和KELM、BSA-KELM、EEMD-BSA-KELM模型相比,基于VMD的BSA-KELM预测精度更高,为边坡位移的预测提供一种有效的方法。     

Double emulsion (W/O/W) gel stabilised by polyglycerol polyricinoleate and calcium caseinate as mangiferin carrier: insights on formulation and stability properties

Mangiferin (MGF) is a phenolic compound isolated from mango, but its poor solubility significantly limits its use. In this study, MGF was embedded into the inner aqueous phase of W₁/O/W₂ emulsions. Firstly, the dissolution method of MGF was determined. MGF remained stable in solution with pH 13 at 30 min, and its solubility reached 10 mg mL⁻¹. When the pH of MGF solutions was adjusted from pH 13 to pH 6, MGF did not immediately crystallise, providing sufficient time to construct the MGF-loaded W₁/O/W₂ emulsions. Subsequently, the MGF-loaded W₁/O/W₂ emulsions were constructed using polyglycerol polyricinoleate (PGPR) and calcium caseinate (CAS). The formation and stability of the W₁/O/W₂ emulsions were investigated. The MGF-loaded W₁/O/W₂ emulsions stabilised with 1% PGPR and 1% – 3% CAS exhibited a low viscosity, limited loading capacity, and poor stability. Conversely, the MGF-loaded W₁/O/W₂ emulsions stabilised by 3%PGPR–3%CAS exhibited optimal loading capacity (encapsulation efficiency = 95.31% and loading efficiency = 0.91%) and stability, which was attributed to the fact that high viscosity and gel state retarded the migration of inner aqueous phase. These results indicated that the W₁/O/W₂ emulsions stabilised by PGPR and CAS may be a potential alternative for encapsulating mangiferin.     

Pristine and cobalt doped copper sulfide microsphere particles for seawater splitting

In this work, copper sulfide particles are synthesized with different Co doping concentrations such as 0, 1 and 5% at 80 °C by optimizing synthesis times from 1 to 3 h. Copper sulfide particles possess two structural phases of covellite CuS and digenite Cu₉S₅. The increase in synthesis time from 1 to 3 h increases the Cu₉S₅ phase growth and changes the morphology from flower to microsphere. The CuS synthesized with 0, 1 and 5% Co dopant concentrations demonstrate flower consisting of agglomerated nanosheets, microsphere and flower like microsphere. The elemental investigation substantiates Co ions presence in CuS microspheres. The A_1g (LO) mode intensity is decreased with increase in Co dopant concentration confirming Co incorporation into CuS microsphere. The CuS synthesized with 0, 1, 5% Co dopants exhibit 322 mV, 305 mV and 289 mV to attain 100 mA/cm² in 1 M KOH seawater. The CuS synthesized with 5% Co dopant demonstrates higher double layer capacitance (C_dl) of 173.9 mFcm^?2 and lower charge transfer resistance (R_ct) of 6.07 Ω with 78.84% retention after 10 h continuous stability than that of the other pristine (118.3 mFcm^?2, 13.72 Ω) and 1% Co doped CuS microsphere (165.7 mFcm^?2, 8.55 Ω) indicating more surface active site and rapid charge carrier transport, respectively.     

Numerical simulation of water and heat transport in the cathode channel of a PEM fuel cell

Cathode channel of a PEM fuel cell is the critical domain for the transport of water and heat. In this study, a mathematical model of water and heat transport in the cathode channel is established by considering two-phase flow of water and air as well as the phase change between water and vapor. The transport process of the species of air is governed by the convection-diffusion equation. The VOSET (coupled volume-of-fluid and level set method) method is used to track the interface between air and water, and the phase equilibrium method of water and vapor is employed to calculate the mass transfer rate on the two-phase interface. The present model is validated against the results in the literature, then applied to investigate the characteristics of two-phase flow and heat transfer in the cathode channel. The results indicate that in the inlet section, water droplets experience three evolution stages: the growing stage, the coalescence stage and the generation stage of dispersed water drops. However, in the middle and outlet sections of the channel, there are only two stages: the growth of water droplets, and the formation of a water film. The mass transfer rate of phase change in the inlet section of the channel varies over time, exhibiting an initial increase, a decrease followed, and a stabilization finally, with the maximum and stable values of 1.78 × 10^?4 kg/s and 1.52 × 10^?4 kg/s for Part 1, respectively. In the middle and outlet sections, the mass transfer rate increase firstly and then keeps stable gradually. Furthermore, regarding the distribution of the temperature and vapor mass fraction in the channel, near the upper surface of the channel, the temperature and vapor mass fraction first change slightly (x < 0.03 m) and then rapidly decrease with fluctuations (x > 0.03 m). In the middle of the channel, the temperature and vapor mass fraction slowly decrease with fluctuation.     

A dotted nanowire arrayed by 5 nm sized palladium and nickel composite nanopaticles showing significant electrocatalytic activity towards ethanol oxidation reaction (EOR)

To the best of our knowledge, this is the first time to report the preparation of a dotted nanowire arrayed by 5 nm sized palladium and nickel composite nanoparticles (denoted as Pd_xNi_y NPs) via a hydrothermal method using NU and PdO·H₂O as the starting materials. The samples prepared at the mass ratio of NU to PdO·H₂O 1:1, 1:2 and 2:1 were, respectively, nominated as catalyst c₁, c₂ and c₃. The chemical compositions of all synthesized catalysts were mainly studied by using X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS), revealing that metallic Ni was one main component of all prepared catalysts. Surprisingly, the main diffraction peaks appearing in the XRD patterns of all prepared catalysts were assigned to the metallic Ni rather than the metallic Pd. Very interestingly, as indicated by the TEM images, a large number of dotted nanowires arrayed by numerous equidistant 5 nm sized nanoparticles were distinctly exhibited in catalyst c₁. More importantly, when being used as electrocatalysts for EOR, all prepared catalysts exhibited an evident electrocatalytic activity towards EOR. In the cyclic voltammetry (CV) test, the peak current density of the forward peak of EOR on catalyst c₁ measured at 50 mV s^?1 was as high as 56.1 mA cm^?2, being almost 9 times higher than that of EOR on catalyst c₃ (6.3 mA cm^?2). Particularly, the polarized current density of EOR on catalyst c₁ at 3600 s, as indicated by the chronoamperometry (CA) experiment, was still maintained to be around 1.47 mA cm^?2, a value higher than the latest reported data of 1.3 mA cm^?2 (measured on the pure Pd/C electrode). Presenting a novel method to prepare dotted nanowires arranged by 5 nm sized nanoparticles and showing the significant eletrocatalytic activities of the newly prepared dotted nanowires towards EOR were the major contributions of this preliminary work.     

CNT-interconnected iron-doped NiP2/Ni2P heterostructural nanoflowers as high-efficiency electrocatalyst for oxygen evolution reaction

Oxygen evolution reaction (OER) plays a decisive role in electrolytic water splitting. However, it is still challengeable to develop low-cost and efficient OER electrocatalysts. Herein, we present a combination strategy via heteroatom doping, hetero-interface engineering and introducing conductive skeleton to synthesize a hybrid OER catalyst of CNT-interconnected iron-doped NiP₂/Ni₂P (Fe-(NiP₂/Ni₂P)@CNT) heterostructural nanoflowers by a simple hydrothermal reaction and subsequent phosphorization process. The optimized Fe-(NiP₂/Ni₂P)@CNT catalyst delivers an ultralow Tafel slope of 46.1 mV dec^?1 and overpotential of 254 mV to obtain 10 mA cm^?2, which are even better than those of commercial OER catalyst RuO₂. The excellent OER performance is mainly attributed to its unique nanoarchitecture and the synergistic effects: the nanoflowers constructed by a 2D-like nanosheets guarantee large specific area and abundant active sites; the highly conductive CNT skeleton and the electronic modulation by the heterostructural NiP₂/Ni₂P interface and the hetero-atom doping can improve the catalytic activity; porous nanostructure benefits electrolyte penetration and gas release; most importantly, the rough surface and rich defects caused by phosphorization process can further enhance the OER performance. This work provides a deep insight to boost catalytic performance by heteroatom doping and interface engineering for water splitting.     

Theoretical study the component and facet dependence of HER performance on nickel phosphides surfaces

Energy depletion and environmental pollution are still serious challenges for human beings. The application of hydrogen energy should be a promising strategy to address this issue. However, the hydrogen production should be one shortcoming for hydrogen energy. The hydrogen evolution reaction (HER) based on electrocatalysis is an effective way to enhance the hydrogen generation with small energy consumption under ambient conditions. Many works have been devoted to develop high performance catalysts to satisfy the HER processes. Nevertheless, the mechanism about facet-dependence and composition-dependence influence is still need to deeply study. Hereon, based on density functional theory calculations, the [100], [110], and [111] facets of Ni_xP_y (Ni₃P, Ni₂P, NiP, NiP₂, NiP₃) systems were created and their HER catalytic activity were used to reveal the underline mechanism. By analyzing the variation of Gibbs free energy, it was found that the structural composition has a greater effect on HER than the facet. Significantly, the Ni₂P(111) surface with Ni/P-termination has the best HER performance for all samples in present work. Through exploring the electron transfer of H with surrounding atoms during the HER process, the H adsorption mechanism as well as its reaction mechanism has been revealed. The deep insights in this work provide an important fundamental that the contents of non-metal for compounds catalysts can heavily influence the performance of HER, which should give more guidance for designing new catalysts.     

Trimetallic NiFeCr-LDH/MoS2composites as novel electrocatalyst for OER

The development of efficient and stable oxygen evolution reaction (OER) catalysts is an ongoing challenge. In order to solve the problem of low oxygen evolution efficiency of the current OER catalysts, a novel material was synthesized by the incorporation of NiFeCr-LDH and MoS₂, and its structural and electrochemical properties were also investigated. The introduction of MoS₂ improves the electrochemical performance of NiFeCr-LDH. The polarization curve shows that the potential of composite material is only 1.50 V at a current density of 10 mA cm^?2, which is far superior to commercial precious metal catalysts. In addition, the stability experiment shows that the composite material has excellent stability, and the current density has little change after 500 cycles. Furthermore, we found that some metal ions, such as Ni, Cr and Mo, exist in the form of high valence on the surface of NiFeCr-LDH@MoS₂, which is also conducive to the occurrence of oxygen evolution reaction.