Transient liquid phase sintering of high-purity mullite for high-temperature structural ceramics

High-purity mullite ceramics, promising engineering ceramics for high-temperature applications, were fabricated using transient liquid phase sintering to improve their high-temperature mechanical properties. Small amounts of ultrafine alumina or silica powders were uniformly mixed with the mullite precursor depending on the silica-alumina ratio of the resulting ceramics to allow for the formation of a transient liquid phase during sintering, thus, enhancing densification at the early stage of sintering and mullite formation by the reaction between additional alumina and the residual glassy phase (mullitization) at the final stage of sintering. The addition of alumina powder to the silica-rich mullite precursor resulted in a reaction between the glassy silica and alumina phases during sintering, thereby forming a mullite phase without inhibiting densification. The addition of fine silica powder to the mullite single-phase precursor led to densification with an abnormal grain growth of mullite, whereas some of the added silica remained as a glassy phase after sintering. The resulting mullite ceramics prepared using different powder compositions showed different sintering behaviors, depending on the amount of alumina added. Upon selecting an optimum process and the amount of alumina to be added, the pure mullite ceramics obtained via transient liquid phase sintering exhibited high density (approximately 99%) and excellent high-temperature flexural strength (approximately 320 MPa) at 1500 °C in air. These results clearly demonstrate that pure mullite ceramics fabricated via transient liquid phase sintering with compositions close to those of stoichiometric mullite could be a promising process for the fabrication of high-temperature structural ceramics used in an ambient atmosphere. The transient liquid phase sintering process proposed in this study could be a powerful processing tool that allows for the preparation of superior high-temperature structural ceramics used in the ambient processing atmosphere.     

YOLSO: You Only Look Small Object

Small object detection is challenging and far from satisfactory. Most general object detectors suffer from two critical issues with small objects: (1) Feature extractor based on classification network cannot express the characteristics of small objects reasonably due to insufficient appearance information of targets and a large amount of background interference around them. (2) The detector requires a much higher location accuracy for small objects than for general objects. This paper proposes an effective and efficient small object detector YOLSO to address the above problems. For feature representation, we analyze the drawbacks in previous backbones and present a Half-Space Shortcut(HSSC) module to build a background-aware backbone. Furthermore, a coarse-to-fine Feature Pyramid Enhancement(FPE) module is introduced for layer-wise aggregation at a granular level to enhance the semantic discriminability. For loss function, we propose an exponential L1 loss to promote the convergence of regression, and a focal IOU loss to focus on prime samples with high classification confidence and high IOU. Both of them significantly improves the location accuracy of small objects. The proposed YOLSO sets state-of-the-art results on two typical small object datasets, MOCOD and VeDAI, at a speed of over 200 FPS. In the meantime, it also outperforms the baseline YOLOv3 by a wide margin on the common COCO dataset.     

Optimization of hydrogen enrichment via palladium membrane in vacuum environments using Taguchi method and normalized regression analysis

In this study, the separation of hydrogen from gas mixtures using a palladium membrane coupled with a vacuum environment on the permeate side was studied experimentally. The gas mixtures composed of H₂, N₂, and CO₂ were used as the feed. Hydrogen permeation fluxes were measured with membrane operating temperature in the range of 320–380 °C, pressures on the retentate side in the range of 2–5 atm, and vacuum pressures on the permeate side in the range of 15–51 kPa. The Taguchi method was used to design the operating conditions for the experiments based on an orthogonal array. Using the measured H₂ permeation fluxes from the Taguchi approach, the stepwise regression analysis was also employed for establishing the prediction models of H₂ permeation flux, followed by the analysis of variance (ANOVA) to identify the significance and suitability of operating conditions. Based on both the Taguchi approach and ANOVA, the H₂ permeation flux was mostly affected by the gas mixture composition, followed by the retentate side pressure, the vacuum degree, and the membrane temperature. The predicted optimal operating conditions were the gas mixture with 75% H₂ and 25% N₂, the membrane temperature of 320 °C, the retentate side pressure of 5 atm, and the vacuum degree of 51 kPa. Under these conditions, the H₂ permeation flux was 0.185 mol s^?1 m^?2. A second-order normalized regression model with a relative error of less than 7% was obtained based on the measured H₂ permeation flux.     

“自动控制系统工程设计”课程思政教学实践

学习不仅仅是自然科学知识的学习，更是社会科学、民族文化、正确人生观和价值观的形成过程，“课程思政”无疑正是实现该目标的捷径，它是当前高等院校思想政治教育的新模式。如何提升学生解决“复杂工程问题”的能力成为高校开展工程教育和“新工科”的难点和重点，而课程思政正是培养学生解决“复杂工程问题”中所需要的非技术因素的重要途径。“自动控制系统工程设计”是自动化专业高年级学生的一门专业课，当前关于“课程思政”的论述是指导思想居多、实施经验以及案例设计较少，针对该问题以“自动控制系统工程设计”为例，详细给出了“课程思政”教学案例的具体实施过程，对同类课程提供参考。     

Co2FeO4@rGO composite: Towards trifunctional water splitting in alkaline media

Development of efficient, low cost and multifunctional electrocatalysts for water splitting to harvest hydrogen fuels is a challenging task, but the combination of carbon materials with transition metal-based compounds is providing a unique and attractive strategy. Herein, composite systems based on cobalt ferrite oxide-reduced graphene oxide (Co₂FeO₄) @(rGO) using simultaneous hydrothermal and chemical reduction methods have been prepared. The proposed study eliminates one step associated with the conversion of GO into rGO as it uses direct GO during the synthesis of cobalt ferrite oxide, consequently rGO based hybrid system is achieved in-situ significantly, the optimized Co₂FeO₄@rGO composite has revealed an outstanding multifunctional applications related to both oxygen evolution reaction (OER) and hydrogen counterpart (HER). Various metal oxidation states and oxygen vacancies at the surface of Co₂FeO₄@rGO composites guided the multifunctional surface properties. The optimized Co₂FeO₄@rGO composite presents excellent multifunctional properties with onset potential of 0.60 V for ORR, an overpotential of 240 mV at a 20 mAcm^?2 for OER and 320 mV at a 10 mAcm^?2 for HER respectively. Results revealed that these multifunctional properties of the optimized Co₂FeO₄@ rGO composite are associated with high electrical conductivity, high density of active sites, crystal defects, oxygen vacancies, and favorable electronic structure arisinng from the substitution of Fe for Co atoms in binary spinel oxide phase. These surface features synergistically uplifted the electrocatalytic properties of Co₂FeO₄@rGO composites. The multifunctional properties of the Co₂FeO₄@ rGO composite could be of high interest for its use in a wide range of applications in sustainable and renewable energy fields.     

Effect of micro-cracks on the in-plane electronic conductivity of proton exchange membrane fuel cell catalyst layers based on lattice Boltzmann method

Micro-cracks commonly occur on the catalyst layers (CLs) during the manufacturing of catalyst coated membranes (CCMs). However, the crack shape parameters effect on CLs in-plane (IP) electronic conductivity λ_s is not clear. In this work, the relationship between crack parameters and the λ_s is obtained based on the two-dimensional (2D) multiple-relaxation time (MRT) lattice Boltzmann method (LBM). The LBM numerical model is validated by the normalized λ_s experiment applied on three different home-made cracked CLs, and the parameter study focus on crack width, length, quantity and phase angle are carried out. The results show that the decrease of λ_s has different sensitivity |k| to the parameters above. The crack width has little effect on λ_s decrease, and the |k_w| is 0.038. However, crack arm length and quantity show more significant impact, which |k_l| and |k_N| are 0.753 and 0.725, respectively. The CLs with different crack propagation directions show significant anisotropy on λ_s, and a 53.53% decrease in λ_s is observed between 0° and 90° crack phase angle change. To manufacture a high electronic conductivity CL, crack initiation and migration mitigation are highly encouraged.     

Magnetic properties,phase evolution,hollow structure and biomedical application of hematite (α-Fe2O3) and QUAIPH

We investigate synthesis, phase evolution, hollow and porous structure and magnetic properties of quasi-amorphous intermediate phase (QUAIPH) and hematite (α-Fe₂O₃) nanostructure synthesized by annealing of akaganeite (β-FeOOH) nanorods. It is found that the annealing temperature determines the phase composition of the products, the crystal structure/size dictates the magnetic properties whereas the final nanorod morphology is determined by the starting material. Annealing of β-FeOOH at ～300 °C resulted in the formation of hollow QUAIPH nanorods. The synthesized material shows low-cytotoxicity, superparamagnetism and good transverse relaxivity, which is rarely reported for QUAIPH. The QUAIPH nanorods started to transform to porous hematite nanostructures at ～350 °C and phase transformation was completed at 600 °C. During the annealing, the crystal structure changed from monoclinic (akaganeite) to quasi-amorphous and rhombohedral (hematite). Unusually, the crystallite size first decreased (akaganeite → QUAIPH) and then increased (QUAIPH → hematite) during annealing whereas the nanorods retained particle shape. The magnetic properties of the samples changed from antiferromagnetic (akaganeite) to superparamagnetic with blocking temperature T_B = 84 K (QUAIPH) and finally to weak-ferromagnetic with the Morin transition at T_M = 244 K and high coercivity H_C = 1652 Oe (hematite). The low-cytotoxicity and MRI relaxivity (r₂ = 5.80 mM^?1 s^?1 (akaganeite), r₂ = 4.31 mM^?1 s^?1 (QUAIPH) and r₂ = 5.17 mM^?1 s^?1 (hematite)) reveal potential for biomedical applications.     

Electrodeposition of the manganese-doped nickel-phosphorus catalyst with enhanced hydrogen evolution reaction activity and durability

Hydrogen technology is widely considered a novel clean energy source, and electrolysis is an effective method for hydrogen evolution. Therefore, efficient hydrogen evolution reaction (HER) catalysts are urgently needed to replace precious metal catalysts and meet ecological and environmental protection standards. Herein, Ni–Mn–P electrocatalysts are synthesized using facile electrodeposition technology. The influence of the Mn addition on the catalytic behavior is studied by the comprehensive analysis of catalytic performance and morphology of the catalysts. Among them, the Ni–Mn–P0.01 catalyst exhibits small coral-like structures, greatly improving the adsorption and desorption of hydrogen ions and reducing the overpotential hydrogen evolution. Consequently, overpotential at 10 mA cm^?2 electric current density is 113 mV, and the value of the Tafel slope achieves 74 mV/dec. Furthermore, the Ni–Mn–P catalyst shows long-time (20 h) stability at current densities of 10 and 60 mA/cm². The results confirm that the synergistic effect of Ni, Mn, and P accelerates the electrochemical reaction. Meanwhile, the addition of manganese element can change the micromorphology of the catalyst, thereby exposing more active sites to participate in the reaction, enhancing water ionization, improving the catalytic performance. This study opens a new way toward improving the activity of the catalyst by adjusting Mn concentration during the electrodeposition process.     

Machine fault diagnosis with small sample based on variational information constrained generative adversarial network

In actual engineering scenarios, limited fault data leads to insufficient model training and over-fitting, which negatively affects the diagnostic performance of intelligent diagnostic models. To solve the problem, this paper proposes a variational information constrained generative adversarial network (VICGAN) for effective machine fault diagnosis. Firstly, by incorporating the encoder into the discriminator to map the deep features, an improved generative adversarial network with stronger data synthesis capability is established. Secondly, to promote the stable training of the model and guarantee better convergence, a variational information constraint technique is utilized, which constrains the input signals and deep features of the discriminator using the information bottleneck method. In addition, a representation matching module is added to impose restrictions on the generator, avoiding the mode collapse problem and boosting the sample diversity. Two rolling bearing datasets are utilized to verify the effectiveness and stability of the presented network, which demonstrates that the presented network has an admirable ability in processing fault diagnosis with few samples, and performs better than state-of-the-art approaches.     

Silver-substituted (Ag1-xCux)2ZnSnS4 solar cells from aprotic molecular inks

To battle the high open-circuit voltage deficit (V_OC,def) in kesterite (Cu₂ZnSnS₄ or CZTS) solar cells, a current field of research relates to point defect engineering by cation substitution. For example, by partly replacing Cu with an element of a larger ionic radius, such as Ag, the degree of Cu/Zn disorder decreases, and likewise does the associated band tailing. In this paper, solution-processed (Ag_1-xCu_x)₂ZnSnS₄ (ACZTS) samples are prepared through the aprotic molecular ink approach using DMSO as the solvent. The successful incorporation of silver into the CZTS lattice is demonstrated with relatively high silver concentrations, namely Ag/(Ag+Cu) ratios of 13% and 26%. The best device was made with 13% Ag/(Ag+Cu) and had an efficiency of 4.9%. The samples are compared to the pure CZTS sample in terms of microstructure, phase distribution, photoluminescence, and device performance. In the XRD patterns, a decrease in the lattice parameter c/a ratio is observed for ACZTS, as well as significant peak splitting with Ag addition for several of the characteristic kesterite XRD reflections. In addition to the improvement in efficiency, other advantageous effects of Ag-incorporation include enhanced grain growth and an increased band gap. A too high concentration of Ag leads to the formation of secondary phases such as SnS and Ag₂S as detected by XRD.