提出一种适用于聚羧酸减水剂的复合矿物混凝土激发剂,研究了在不同养护条件、不同掺量下,激发剂对混凝土工作性能及各龄期强度的影响,结合XRD,SEM物相检测探讨了激发剂作用机理,并在连江可门港口泊位工程中试用,测试了掺激发剂混凝土的耐久性能.宏观测试结果表明所研激发剂I型对混凝土工作性能影响不大,能够提高混凝土早期强度,且对后期强度及长期耐久性能无不良影响;微观分析表明激发剂I型的掺入加速了C2S,C3S等矿物的水化,并激发了粉煤灰、矿粉的二次水化反应,混凝土强度发展拐点提前出现.     

超塑化剂“CSP”对水泥水化及水泥石微观结构的影响

分别对掺与不掺超塑化剂“ＣＳＰ”的水泥试样进行测试分析，探讨了ＧＳＰ对水泥水化过程及水泥石微观结构的影响。传导量热法、结合水测定分析结果表明．ＣＳＰ使水泥水化的诱导期延长．对初期水化的抑制作用可延缓混凝土坍落度经时损失，而早期和后期水化加快，因此具有早强增器作用．ＴＧ—ＤＴＡ、ＸＲＤ、ＳＥＭ、ＭＩＰ等测试分析结果表明，ＣＳＰ使水泥石中凝胶农产物增多，有害孔减、无害孔增多，因而具有增强和提高混凝土耐久性的作用．     

Effect of lightweight aggregate pre-wetting on microstructure and permeability of mixed aggregate concrete

The influence of lightweight aggregate (LWA) pre-wetting on the chemical bound water and pore structure of the paste around aggregate as well as concrete permeability were investigated. The results show that, in early age the dry LWA has significant effect on the formation of dense paste around it and improving the concrete impermeability. However the prewetted LWA has strong water-releasing effect in later age, which increases the hydration degree of the paste around it, and makes the adjacent paste develop a structure with low porosity and finer aperture, furthermore the concrete impermeability can be improved. It is suggested that, as for concrete with low durability requirement, the LWA without pre-wetting treatment can be used as long as meet the workability requirement of fresh concrete, the good impermeability of concrete can be gained as well. As for concrete with high durability requirement, the prewetted LWA should be used, and the pre-wetting time should be extended as long as possible, in order to optimize the concrete structure in long term, and improve the concrete durability.     

普通强度等级增钙灰混凝土耐久性研究

研究了用增钙灰作普通强度等级混凝土掺合料，所配制的增钙灰混凝土的力学性能，以及抗冻性、抗渗性、收缩、水化热、钢筋锈蚀、凝结时间等性能，为增钙灰在混凝土工程中的应用提供了数据。     

超缓凝剂对硅酸盐水泥砂浆性能的影响

目的为配制一种新型有机复合超缓凝剂，研究不同掺量及养护条件下其缓凝效果和硬化机理．使之可有效地应用于大体积混凝土及缓黏接预应力混凝土工程中．方法利用XRD和SEM等微观手段，对掺入超缓凝剂水泥砂浆的缓凝性能进行了测试和表征．结果超缓凝剂在不同养护条件下，可使水泥水化“休眠”20～40d，“休眠”结束后能迅速水化而结构不发生变化．XRD图谱表明并未发现异常水化物产生；SEM图像表明，掺超缓凝剂的水泥硬化结构更加致密．结论在标准养护条件下，掺量0．035％的超缓凝剂可使水泥水化“休眠”34d，“休眠”结束后59d可达空白试件28d强度．随养护温度增加和超缓凝剂掺量的降低，水化“休眠”期降低．超缓凝剂并未使水化产物发生本质变化，其耐久性应是可靠的．     

粉煤灰-脱硫石膏水泥基材料水化活性及微结构

采用DTA—TG、XRD、SEM以及宏观水化收缩和强度试验等手段研究了粉煤灰一脱硫石膏一水泥三元复合胶凝体系的水化过程、活性效应及微观结构等,根据试验结果总结了复合胶凝材料的水化动力学过程。结果表明,粉煤灰一脱硫石膏水泥石的钙矾石吸热峰强于基准样;在各组分相互活性激发和外掺激发剂作用下,粉煤灰一脱硫石膏水泥石中2次水化效应明显;SEM、XRD表明水泥石早期有明显的钙矾石生成,同时粉煤灰颗粒的表面侵蚀现象明显,进一步说明复合胶凝体系的早期活性得到有效激发,硬化后综合性能得到有效保证。且宏观收缩及强度试验也从侧面印证了微观试验结果。粉煤灰一脱硫石膏水泥基复合胶凝材料体系的研发可大量消耗燃煤电厂的工业废渣,具有显著的“绿色”效应。     

Damage Evolution of Concrete under the Actions of Stray Current and Sulphate

Based on the mechanism of stray current generation in underground structures,the concrete durability test device for stray current and sulphate in typical soil environment was designed to study the damage of concrete under the action of stray current and sulphate.The deterioration law of concrete under the action of stray current and sulphate was studied by microscopic techniques such as scanning electron microscopy (SEM) and X-ray diffraction (XRD).The microstructure of corroded concrete was observed to determine the phase composition of erosion products.The damage performances such as quality,strength,and dynamic elastic mode of corroded concrete were performed.The experimental results show that,under the action of stray current,the products of sulfate-eroded concrete are mainly gypsum,ettringite,and thaumasite;the stray current accelerates the hydration process of cement and the erosion of concrete by sulfate;when the concrete pores are filled with the erosion product,there is an increase of approximately 10% in the concrete compressive strength and dynamic elastic modulus;and the concrete compressive strength is more sensitive to the stray current electrification period than the current intensity.     

JM-Ⅱ外加剂在某高层建筑施工中的应用

在高层钢筋混凝土结构工程中，混凝土性能的优异是确保工程质量的前提。混凝土外加剂用量虽少，但其对混凝土性能影响较大。结合JM—Ⅱ外加剂在某高层建筑施工中的实例，通过试验，研究JM—Ⅱ外加剂的不同掺量对混凝土的和易性、抗压强度、含气量、坍落度损失、凝结时间、泌水率、水化热等性能的影响，同时研究JM—Ⅱ外加剂在不同水灰比情况下，对混凝土的抗渗、抗冻等耐久性的影响。结果表明，JM—Ⅱ外加剂能使混凝土便于浇灌且提高强度，降低水化热，显著提高混凝土的抗渗、抗冻等耐久性能。     

Characterization of Pozzolanic Reaction and Its Effect on the C-S-H Gel in Fly Ash-cement Paste

High resolution solid-state 29Si MAS NMR,combined with XRD,SEM and FTIR were used to characterize the pozzolanic activity of FA,type of main pozzolanic reaction products,and the effect of pozzolanic reaction on the C-S-H microstructure in fly ash-cement (FC) paste.The experimental results indicate that in the hydrated FC paste with 30% dosage of FA at 3 d,FA partially participated in the pozzolanic reaction,while,at 120 d,FA largely reacts.During the hydration of FC paste at laboratory temperature,the pozzolanic reaction products are C-S-H gel rather than zeolitic gel.Moreover,after the covalent bonds of Si-O-Si,Si-O-Al and Al-O-Al in the structure of FA are broken,monosilicates Si-OH and Al-OH groups form,these chemical species can connect C-S-H dimers,thus producing more Al-free C-S-H and aluminous C-S-H than in the plain cement paste.The increased content of Al for Si substitution in the bridging tetrahedra of C-S-H may decrease the stability of C-S-H,which results in a rather obvious loss in the mechanical strength of hardened FC paste.     

电化学除氯处理后的混凝土微观结构研究

为了研究电化学除氯对混凝土中离子分布和微观结构的影响规律,采用压汞法、SEM电子显微镜分析等方法对电化学除氯后不同水灰比混凝土试件中钢筋附近和表面层的氯离子和钾钠离子含量、孔隙结构、显微结构进行对比分析.结果显示,电化学除氯后,钢筋附近混凝土与外层混凝土相比,氯离子含量约为1/2,钾离子含量约为5～10倍,钠离子含量约为8～18倍,水化物颗粒间结合不连续、部分水化产物分解.钢筋附近区域混凝土中的氯离子含量明显低于外表层混凝土,钾、钠离子在钢筋阴极附近大量聚集.经过电化学处理后的混凝土试件钢筋附近区域的孔隙率和大孔含量增多,结构疏松;而外表层混凝土结构致密,孔隙细化,水化产物成网络状结合良好.     

混凝土桥梁耐久性2020年度研究进展

近年来,混凝土桥梁的耐久性引起广泛关注,混凝土桥梁的耐久性直接影响到长期服役桥梁的安全性和使用寿命,是桥梁研究的热点之一。目前,混凝土桥梁耐久性的研究主要分为两个方面：一是从材料的损伤机理层面入手,研究桥梁构件材料的破坏方式和影响因素,分析混凝土桥梁材料的耐久性影响作用机理;二是从桥梁结构的整体出发,研究桥梁耐久性能的设计、评估以及桥梁的养护方案等,探究提高混凝土桥梁结构耐久性的措施。为全面掌握混凝土桥梁耐久性的研究动态,从混凝土桥梁的设计、桥梁混凝土材料的耐久性研究、混凝土桥梁的钢筋锈蚀研究、混凝土桥梁的耐久性提升技术、不同服役环境对桥梁耐久性的影响、长期服役性能评估及寿命预测等方面对2020年关于混凝土桥梁耐久性的论文进行梳理,探讨未来混凝土桥梁耐久性的研究重点和发展方向。     

考虑温度历程的早龄期大坝混凝土自生体积变形分离方法现场试验

混凝土在水化过程中会产生自生体积变形和温度应变等现象,与混凝土的耐久性有着密切联系,为工程建设各方所关注。对此,在西南某混凝土特高拱坝混凝土浇筑现场,采用无应力计对冷却水管周围两处不同位置处早龄期混凝土的应变进行现场监测,运用成熟度理论考虑混凝土的温度历程对混凝土水化进程的影响,采取一种新方法将总应变计算式解耦,从而摆脱对早龄期混凝土的热膨胀系数为定值的依赖,得出混凝土热膨胀系数在等效龄期下的历程,最终从无应力计变形监测值中分离出温度应变和自生体积变形。试验结果表明:这种方法能考虑混凝土温度因素,精确便捷地对早龄期混凝土的热膨胀系数以及自生体积变形进行分离,给现场混凝土的养护以及防裂施工提供指导。     

锰渣掺合料对海工混凝土耐久性的影响

研究了锰渣的组成、结构等基本性能及其对海工混凝土耐久性的影响.所用水淬锰渣碱度系数1.09、质量系数1.71,具有潜在水硬活性.含α′-C2S胶凝矿物,其玻璃体含量和活性指数均约为80％.从水胶比、浆集比、水泥用量等配合比设计参数优化出发,使用锰渣掺合料和萘磺酸甲醛高效减水剂配制了力学性能良好的C40海工混凝土.用5倍正常海水浓度的模拟海水溶液对掺锰渣混凝土进行了侵蚀试验,以考察其耐海水腐蚀性.研究发现,掺锰渣混凝土在人工海水侵蚀及50次冻融循环后质量损失、强度损失均较小,抗渗性有所改善.由于所用水淬锰渣对改善混凝土耐久性有重要作用,其可作为矿物掺合料应用于近海及海洋环境混凝土工程.     

大流动性轻集料混凝土研究

研究了粉煤灰、矿渣、硅灰掺合料对大流动性轻集料混凝土性能的影响。试验结果表明，掺合料单掺效果不及复掺；用堆积密度为503kg/m^3，筒压强度为3．08MPa的页岩陶粒，复合掺入20％的磨细粉煤灰和20％的磨细矿渣，可配制出塌落度267mm、扩展度650mm,28d强度为28．8MPa，表观密度为1804kg/m^3的免振捣大流动性轻集料混凝土；轻集料的物理力学对大流动性轻集料混凝土的性能有重要影响。     

FRP筋的耐久性能研究现状

钢筋锈蚀是混凝土结构面临的主要问题,纤维增强聚合物(FRP)筋代替钢筋增强混凝土构件解决锈蚀问题已成为研究的热点.但FRP筋的耐久性能与材料的组成、性质和筋与混凝土间的相互作用等均有关系,其耐久性腐蚀机理较复杂.综述了FRP筋在温度、水分、酸碱环境以及紫外线作用下的耐久性能研究进展和相关研究成果,为以后FRP筋性能的研究提供参考.     

大体积混凝土施工温度裂缝的预防措施

在大体积混凝土施工中,由于水泥水化热等多种因素产生的混凝土结构裂缝将影响混凝土的耐久性能和力学性能．针对这一问题,从设计、原材料、施工、温控等方面入手,对大体积混凝土施工中应采取的预防措施进行了探讨．     

The chloride permeability of persulphated phosphogypsum-slag cement concrete

The chloride permeability and microstructure of persulphated phosphogypsum-slag cement concrete (PPSCC), the Portland slag cement concrete (PSCC) and ordinary Portland cement concrete (OPCC) were investigated comparatively. Some test methods were used to evaluate the chloride permeability and explain the relationship between the permeability and microstructure of concrete. The results show that the resistance to chloride penetration in PPSCC is significantly better than that in OPCC, the reasons are as follows: 1) the slag in PPSCC is activated by clinker (alkali activation) and phosphogypsum (sulfate activation), forming more low Ca/Si C-S-H gel and gel pores below 10 nm than OPCC, improving the resistance to chloride penetration; 2) the hydration products of PPSCC have a much stronger binding capacity for chloride ions; and 3) in the same mix proportion, PPSCC has a better workability without large crystals calcium hydroxide in the hydration products, the interfacial transition zone (ITZ) is smoother and denser, which can cut off the communicating pores between the pastes and aggregates.     

高性能混凝土微观结构特征及开发应用

从材料的微观结构层次上设计和制备新材料是２１世纪材料科学技术一个重要课题．分析了高性能混凝土研究现状及实施的要点,探索高性能混凝土微观结构及特征,并开拓配制高性能混凝土的新途径、新技术     

寒冷地区机场道面混凝土破坏机理研究

寒冷地区机场混凝土道面常常发生非荷载引起的破坏-耐久性破坏，严重影响飞机的安全起降。必须尽快予以解决，解决混凝土耐久性破坏问题必须首先弄清楚破坏原因，为此，以北方寒冷地区某国际机场为研究对象，从不同角度分析混凝土的破坏机理，排除了碱骨料反应破坏的可能，在宏观性能研究和显微结构分析的基础上，提出寒区机场道面混凝土耐久性破坏的根本原因是混凝土抗渗性差，水分及腐蚀性介质渗入混凝土内部孔隙中，导致混凝土抗冻融性及耐腐蚀性劣化。     

复杂侵蚀环境下透水混凝土耐久性能试验研究

为适应海绵城市建设对高耐久性透水混凝土的需求,配置了低品质活性矿物掺合料透水混凝土和聚丙烯仿钢纤维（PPTF）透水混凝土两个系列。前期已进行了基本性能研究,在此基础上,继续开展复杂多因素侵蚀环境下耐久性能研究。试验采用侵蚀溶液全浸泡方式,共持续300 d,宏观上测试了抗压强度和抗折强度随侵蚀时间的劣化规律,微观上用SEM观测了胶结层的微观结构、用EDS观测了胶结层的化学组成。复杂侵蚀环境下,透水混凝土微观结构变化规律与其宏观力学性能变化规律基本相符。综合基本性能和耐久性能,择优推荐复掺低品质硅灰和低品质粉煤灰透水混凝土和掺3 kg/m³锯齿形PPTF透水混凝土。这两种透水混凝土基本性能均满足城市既有住区道路、人行道、城市广场、体育场、户外停车场、园林景观道路等轻交通路面的使用要求,同时,又表现出了良好的耐久性能。