固硫灰免蒸压加气混凝土性能影响因素的研究

利用循环流化床燃煤固硫灰制备了免蒸压无水泥加气混凝土,并对影响其性能的因素进行了研究。讨论了石灰掺量、激发剂掺量、料浆初始温度、养护制度、固硫灰细度、铝粉掺量等因素对无水泥固硫灰免蒸压加气混凝土性能的影响;并使用SEM和XRD等手段对制品的水化产物进行了形貌和矿物成分分析。研究结果表明:激发剂掺量是影响加气混凝土性能的主要因素;在生石灰掺量为12%,激发剂掺量为2.1%和60℃蒸汽养护1d的条件下,可以制备出容重为705kg/m3,强度达5.44MPa的无水泥固硫灰免蒸压加气混凝土。     

基于内养护原理的功能集料制备及在混凝土中的应用

以陶砂为内养护介质吸附激发剂溶液制备功能集料,并与SAP内养护材料吸附激发剂溶液进行对比,固定内养护引入水量,水灰比及激发剂掺量,研究内养护技术对大掺量粉煤灰混凝土抗压强度,干燥收缩,水化热及微观结构的影响。水化热测试及微观形貌测试表明,内养护与激发剂相结合可同时促进水泥及粉煤灰的水化。抗压强度测试及干燥收缩测试表明,混凝土的60 d抗压强度提高16.5%,60 d干燥收缩降低21%,较好地改善了大掺量粉煤灰混凝土早期强度低,养护依赖性大的问题。     

RSD速凝剂增强作用机理分析

RSD是一种性能优良的喷射混凝土速凝剂，在试验室中掺加RSD后的混凝土强度对比测试表明，该速凝刑不仅能显著提高水泥胶砂的早期强度，而且不降低水泥胶砂的后期强度，并能提高水泥胶砂的耐久性能．通过扫描电镜对掺加RSD逮凝剂的水泥浆进行了观察，分析了水泥石各龄期的水化产物．分析结果表明，RSD速凝剂在水泥浆早期水化过程中能加速C3S的水化和钙矾石的生成，RSD促使C—S—H（Ⅰ）凝胶向C—S—H（Ⅲ）和C—S—H（Ⅳ）转化，增强水泥石的强度．最后对RSD速凝剂的增强作用进行了机理分析．     

昆钢钢渣微粉在混凝土中的应用研究

钢渣作为活性掺合料用于混凝土是实现其资源化利用的有效途径。文章基于昆钢钢渣粉具有的潜在活性及与水泥熟料相似的矿物组成,以钢渣粉取代矿渣粉制备C15、C20、C30和C40混凝土,分析了钢渣粉掺入对混凝土性能的影响,针对混凝土的工作性能、力学性能和水化产物,利用扫描电镜(SEM)和X射线衍射(XRD)等手段对掺钢渣粉混凝土的流动性、塌落度损失、泌水率、抗压强度、抗拉强度以及净浆水化产物等进行研究。结果表明:钢渣粉与矿渣粉复掺有利于提高混凝土的流动性、延缓了塌落度损失,降低了混凝土的滞后泌水,并满足了力学强度的设计要求;钢渣粉的掺入,水化产物种类没有改变,钢渣粉早期水化速度较慢,后期水化程度逐渐提高。     

活性稻壳灰对混凝土强度和耐久性能的影响

研究了高火山灰活性稻壳灰对混凝土强度和耐久性能的影响。结果表明：混凝土中掺加稻壳灰后强度提高，且高水胶比时强度提高率更大；同时，混凝土的抗盐酸溶液的侵蚀能力、抗碳化和抗渗性能也得到改善。其主要原因可归结为：稻壳灰的掺入降低了混凝土的实际水胶比，促进了水泥的水化，使混凝土中有更多的C—S—H凝胶生成，并减少了混凝土中羟钙石的数量，降低了混凝土细孔的平均尺寸，使得混凝土的结构更加密实。     

复掺矿物掺合料对C50海工混凝土性能影响

研究了复掺技术对C50海工混凝土力学性能、工作性能和耐久性能的影响规律。试验结果表明,粉煤灰和矿粉复掺能增强混凝土的抗压和抗折强度,改善新拌浆体的工作性能,硅灰尽管降低了混凝土工作性,却极大提高了它的强度和耐久性。     

石膏掺量对高贝利特-硫铝酸盐水泥性能的影响

利用循环流化床(CFBC)固硫灰代替部分铝矾土、石膏等原料制备高贝利特-硫铝酸盐水泥,并采用XRD、SEM等方法研究了石膏掺量对该水泥凝结时间、抗压强度、水化产物和微观结构的影响。结果表明,利用固硫灰等原料制备的水泥熟料的矿物组成主要有C2S、C4A3S、铁相等;掺入石膏会缩短水泥的凝结时间,最佳石膏掺量为9%;水泥3d、28d净浆强度可以达到39.00MPa和82.59MPa;掺入适量石膏能促进C4A3S和C2S水化,掺量不足会使AFt向AFm转化,掺量过大反而会阻碍C4A3S的水化,进而影响水泥强度;不同石膏掺量下的水泥水化产物主要为AFt、AFm、C-S-H凝胶和铝胶等。     

混合材对高铝水泥强度影响的试验研究

研究了石灰石、粉煤灰 ,矿渣三种矿物混合材不同掺量对高铝水泥强度的影响 .分析了它们在高铝水泥水化过程中的作用和水化产物的微观形貌 ,以及对高铝水泥水化产物晶型转变的影响 .研究表明 :对于高铝水泥净浆试件 ,掺适量的石灰石能够抑制高铝水泥水化产物的晶型转变 ,并能够生成单碳型水化碳铝酸钙 (C3 A·CaCO3 ·11H2 O) .但掺合粉煤灰和矿渣的作用效果不明显 ,对于高铝水泥胶砂试件 ,掺加适量的三种混合材都有利于高铝水泥强度的稳定 ,其中石灰石的作用效果较为明显 .     

硅酸盐-硫铝酸盐水泥混合体系的试验研究

研究了不同比例的硅酸盐、硫铝酸盐水泥混合体系的凝结时间、水泥砂浆的强度性能,并对一定混合比例的OPC-SAC水泥进行了XRD、SEM和水化量热测试。结果表明,硅酸盐水泥与硫铝酸盐水泥混合,SAC中的C4A3-S矿物与OPC中的C3S矿物在共同水化过程中有相互促进的作用,会使混合水泥水化和凝结加速;混合水泥的强度性能与两种水泥的混合比例有关。本研究可对硅酸盐-硫铝酸盐水泥混合体系的应用提供借鉴。     

硬石膏对熟料激发矿渣水化反应的影响

以不同硬石膏掺量的熟料激发矿渣胶凝材料为研究对象,通过对胶结体强度、水化产物的种类及非蒸发水含量等的分析检测,探讨了石膏对熟料激发矿渣的胶凝性能和水化产物的影响.结果表明:适量硬石膏的掺加能够显著提高熟料激发矿渣胶凝材料的早期胶结强度,最佳石膏掺量下,胶凝材料净浆的3d胶结强度可提高95%,细粒尾矿砂浆的3d胶结强度可提高388%.石膏的加入显著促进了钙矾石(AFt)和低钙硅比水化硅酸钙(CSH)在水化早期的优先生成,加快了Ca(OH)2的消耗、抑制了水化铝酸钙(C4AH13)的生成,使3d水化产物中非蒸发水的质量分数由9.23%提高到14.35%.     

Preparation of High Performance Non-dispersible Concrete

A new-type underwater non-dispersible concrete admixture NDA was prepared, its function mechanism was analyzed, and C40 high performance non-dispersible underwater concrete was manufactured by applying NDA.The results indicate that NDA has a suitable workabilhy, low strength loss, and excellent anti-dispersion; the fresh non-dispersible undenvater concrete with NDA has high anti-dispersion, excellent workabilhy such as selfcompacting and not bleeding; hardened non-dispersible underwater concrete with NDA has a high strength, high durability such as high anti-abrasion, impermeability and anticorrosion.     

高性能水下不分散混凝土研究

研制出性能优良的新型水下不分散剂NDA，并利用NDA配制出C40高性能水下不分散混凝土，分析了其作用机理．研究结果表明，NDA具有工作性好、强度损失低、抗分散性能好等优点；掺加NDA的新拌水下不分散混凝土抗分散性能好，能自流平、自密实，无泌水；硬化水下不分散混凝土强度高、抗分散，抗冲磨、抗渗、抗蚀等耐入性能良好．     

混杂纤维(钢/聚丙烯)高性能混凝土正交试验研究

通过正交试验反映了低掺量情况下混杂纤维混凝土各组分对混凝土性能的影响及影响程度,找出了混杂纤维低掺量情况下混凝土在满足强度、工作性(施工性能)、耐久性各方面优越性能时的较优配比.     

Effect of lightweight aggregate pre-wetting on microstructure and permeability of mixed aggregate concrete

The influence of lightweight aggregate (LWA) pre-wetting on the chemical bound water and pore structure of the paste around aggregate as well as concrete permeability were investigated. The results show that, in early age the dry LWA has significant effect on the formation of dense paste around it and improving the concrete impermeability. However the prewetted LWA has strong water-releasing effect in later age, which increases the hydration degree of the paste around it, and makes the adjacent paste develop a structure with low porosity and finer aperture, furthermore the concrete impermeability can be improved. It is suggested that, as for concrete with low durability requirement, the LWA without pre-wetting treatment can be used as long as meet the workability requirement of fresh concrete, the good impermeability of concrete can be gained as well. As for concrete with high durability requirement, the prewetted LWA should be used, and the pre-wetting time should be extended as long as possible, in order to optimize the concrete structure in long term, and improve the concrete durability.     

橡胶粒子改性水泥混凝土的耐久性能

研究了橡胶粒子改性水泥混凝土的工作性能和耐久性能,探讨了橡胶粒子掺量对混凝土性能的影响。试验结果表明,掺加橡胶粒子可明显改善混凝土的工作性能、干缩性及抗冻性能,同时会降低混凝土的抗折、抗压强度和抗碳化性能。橡胶粒子对混凝土早期(3 d)抗折、抗压强度影响较小,但对混凝土28 d抗折、抗压强度的负面影响较大。随着橡胶粒子掺量的增大,混凝土抗冻性能逐渐降低,混凝土的干缩值也有逐渐增大的趋势,但其抗冻性及干缩性仍要优于普通混凝土。     

Effects of the Lithologic Character of Manufactured Sand on Properties of Concrete

Six representative parent rocks of sand, including limestone, quartzite, gneisses, granite, Basalt and Marble were selected to conduct a systematical research on the effects of various lithologies of manufactured sand on the workability, mechanism properties, volume stability and durability of manufacturedsand concrete. The experimental results show that the strength of manufactured-sand concrete is slightly higher than that of natural-sand concrete. Furthermore, substituting 15% cement of the concrete mixture with equal quantity of the six different lithology stone powder respectively, the data indicated that they can improve the concrete's workability, postpone the plastic cracking time, enhance the anti-cracking grade, and have no obvious effect on the properties of antifreeze and sulfate attack resistance but reduce the capability to resist chloride ion penetration. Moreover, the differences in concrete's workability, mechanism properties, volume stability and durability caused by various lithologies of manufactured sand and stone powder were not significant and the influence of lithology variety on the macro properties of concrete could be neglected eventually.     

粉煤灰与粉煤灰混凝土性能

通过实验和理论分析，研究了粉煤灰活化措施、基本效应以及粉煤灰混凝土的工作性、力学特性和耐久性，为粉煤灰混凝土的应用和研究提供参考．研究认为机械活化措施中细磨加工优于分选加工，细磨加工能提高粉煤灰的活性和利用率；强碱激发剂的掺量要适量，引入硫酸盐复合激发剂是必要的，也是有效的，水泥是粉煤灰最有效、最经济的活性激发剂；粉煤灰的作用机理主要有取代效应、火山灰效应、形态效应和微集料效应等；粉煤灰使混凝土的工作性得到改善，早期强度低，后期强度增长快，抗拉强度明显提高，抗裂性、抗渗性、抗冻性、耐蚀性、抗碳化性和对钢筋的保护能力提高，水化热降低，能消除或减轻碱骨料反应的危害。     

混凝土强度对CFRP加固钢筋混凝土梁耐久性影响试验

对长期在氯离子环境下工作的6根不同强度等级的碳纤维加固的钢筋混凝土梁进行耐久性模拟试验,分析了混凝土强度变化对试件耐久性产生影响的机理及效果。结果表明：随着混凝土强度的提高,构件抗氯离子侵蚀的能力显著提高,从而使得构件的耐久性得以改善;在高强混凝土构件中加入用来改善混凝土和易性的粉煤灰,提高了梁的密实度,增强了抗侵蚀性能。     

C30再生粗骨料混凝土和易性和抗压强度研究

以砖混结构建筑拆卸下来的混凝土块为原材料制备C30再生粗骨料混凝土,利用正交设计方法,研究了再生粗骨料取代率、水灰比、砂率对再生混凝土28d抗压强度及和易性的影响。结果表明再生粗骨料取代率是影响混凝土28d抗压强度及和易性的最主要因素;随着再生粗骨料取代率的增加,强度与和易性均下降;使再生粗骨料取代率为60％,水灰比为0．5,砂率为36％,通过合理的配合比可以配制出28d强度达到46．3MPa的混凝土。