09CrCuSb钢连铸坯的高温力学性能

采用Gleeble-3500热模拟试验机对09CrCuSb钢连铸坯的高温力学性能进行测试,得到其在650～1 300℃的应力—应变曲线、高温强度、热塑性和塑性模量的变化规律。结果表明:应力—应变曲线中,应力峰值随测试温度升高而减小,当测试温度高于700℃时,应力—应变曲线中出现应力平台现象;连铸坯试样的高温强度较差,随温度升高,其高温强度整体呈下降趋势;在2.4×10~(-3) s~(-1)应变速率下,存在两个明显的脆性温度区间,第一脆性温度区间为1 200℃～熔点,第三脆性温度区间为700～800℃,在825～1 250℃时09CrCuSb钢连铸坯热塑性较好,断面收缩率均大于80%;连铸坯试样的高温塑性模量在675～1 300℃时小于660.099 MPa。     

Q460C连铸板坯的高温塑性

 在Gleeble 1500热模拟机上测定了Q460C连铸坯的热塑性,深入分析了钢Q460C的高温脆化机理,确定了连铸坯的最佳矫直温度。结果表明,钢Q460C高温脆化受变形速率的影响较大,在第Ⅲ脆性区变形速率越低脆化越严重,实验用钢Q460C的低塑性区确定在660~985 ℃,连铸坯顶弯、矫直温度应高于985 ℃,有利于提高塑性,避免连铸坯表面裂纹的产生。     

含铌微合金高强度钢Q345C连铸坯的热塑性

 通过Gleeble-2000 试验机研究了Q345C钢连铸坯的高温热塑性。利用扫描电镜、金相显微镜、透射电镜观察了第Ⅰ、Ⅲ脆性温度区内拉伸试样断口部位的显微组织及形貌,分析了动态再结晶、相变、析出物等对微合金化钢高温延塑性的影响。结果表明：在1×10-3/s应变速率下, Q345C钢存在两个脆性温度区,即第Ⅰ脆性区（1200～1300℃）和第Ⅲ脆性区（600～875℃）,无第Ⅱ脆性区出现;最高塑性出现在1050℃左右,断面收缩率（Z）达到85.8%;在第Ⅲ脆性区,沿奥氏体晶界析出膜状铁素体抗拉能力较低,晶界处存在夹杂物以及微合金元素的析出物,是钢的热塑性降低的主要原因。     

Q345C连铸坯高温热塑性的研究

在Gleeble-2000热模拟机上,针对Q345C钢连铸坯,进行了高温热塑性测试.分析了Q345C钢试样的断口性质及显微组织与塑性的关系.研究了第Ⅲ脆性区的脆化原因.实验结果表明:在1 300～600℃区间存在两个脆性温度区,其中第Ⅲ脆性温度域为600～850℃,其断面收缩率RA范围是60.23%～29.61%;指出了该钢种在实际生产条件下适宜的铸坯矫直温度.     

低碳钢Q345B大方坯热塑性研究

采用Gleeble 1500热模拟机对Q345B钢在1×10-4s-1和1×10-3s-1应变速率下的热塑性进行了研究。研究表明:在1×10-4s-1的应变速率下,试样在600～TL℃的温度范围内存在两个脆性区,即高温脆性区,为1 217～TL℃,低温脆性区,为600～930℃;在1×10-3s-1的应变速率下,试样在600～TL℃的温度范围内不存在高温脆性区,仅存在低温脆性区,为600～915℃。影响Q345B钢热塑性的主要因素是S偏析、应变速率、铁素体的析出以及细小的AlN粒子的析出。     

微合金Q345B板坯连铸的高温塑性

为了研究含V、Ti、Nb微合金Q345B结构钢的高温塑性,利用Gleeble-1500D热模拟试验机对其进行热拉伸试验,分析了在应变速率为1.5×10-3s-1、变形温度700～1 300℃(Δt=100℃)变形条件下的断裂强度和断面收缩率随温度的变化情况。确定Q345B结构钢存在两个脆性区间,即第Ⅰ脆性温度区间为熔点温度1 300℃,第Ⅲ脆性温度区间为850～740℃。通过扫描电镜和光学显微镜对断口形貌及其组织进行了观察,明确了断裂原因,为连铸生产提供一定的理论指导。     

温度和变形参数对Q345C钢连铸坯热塑性的影响

用Gleeble-2000热模拟机研究了Q345C钢250 mm×1 300 mm连铸坯热履历-连铸坯冷却过程和冷坯加热过程(300～1 320℃)的温度变化,应变速度(3～3×10-4 s-1)和降温速率(1～20℃/s)对热塑性的影响。结果表明,Q345C钢从1320℃冷却到钢的第Ⅲ脆性区,冷却速度越高,钢在第Ⅲ脆性区塑性越差;在600～850℃,连铸坯冷装加热后的热塑性要好于从液态直接冷却到这个温度区间的热塑性;在钢的第Ⅲ脆性区内,钢的热塑性随变形速率增大而变好。     

Cr17铁素体不锈钢的应变速率脆性

研究了Cr17铁素体不锈钢在高温拉伸试验过程中应变速率对合金断面收缩率的影响,并对其发生机制进行了分析。合金在500℃下以不同应变速率(1.43×10-6~1.33s-1)拉伸至断裂,测试断面收缩率,并利用电子探针对晶界成分进行了观察测试。结果表明:应变速率从1.43×10-6 s-1升高至1.43×10-2 s-1,断面收缩率降低,约在1.43×10-2 s-1时达到最低值。然后,随着应变速率增加至1.33s-1,断面收缩率升高。经电子探针测试证实,断面收缩率达到最低值的样品,硫在晶界上偏聚,其他应变速率拉伸的样品没有观察到硫的晶界偏聚。基于多晶金属弹性变形的微观理论,分析这些试验结果,证实了此合金在拉伸试验中具有应变速率脆性的基本特征——临界应变速率。     

2205双相不锈钢连铸坯的高温组织和高温力学性能

对2205双相不锈钢连铸坯进行高温短时拉伸试验,分析了抗拉强度、断面收缩率随温度的变化情况。观察了试验温度为1 300、1 050、950、850℃下试样的高温组织及断口形貌。结果表明,在1 150～1 350℃温度范围内,双相不锈钢试样具有很好的塑性;在1 000～1 100℃时,较高的应变速率抑制了软化作用的进行,使双相不锈钢出现第Ⅱ脆性温度区,同时试样中存在的疏松和细小析出物进一步加剧了裂纹的发展。第Ⅲ脆性区产生的原因是由于在奥氏体晶界上析出了氮化物、碳氮化物等细小析出物造成晶界脆化。     

Nb-Ti-V微合金化船板钢的高温力学性能研究

采用Gleeble-3500热模拟试验机研究D36船板钢连铸板坯的高温力学性能,用扫描电镜观察断口形貌,并分析脆化机理。结果表明:不含钒的铸坯第Ⅰ脆性温度区大于1 350℃;其在1 350～950℃时断面收缩率大于80%,具有良好的高温塑性;第Ⅲ脆性温度区为950～600℃,此时试样断面收缩率处于41.7%～64%。含钒的铸坯第Ⅰ脆性温度区为熔点至1 250℃;在1 250～950℃范围内,塑性较好;其第Ⅲ脆性温度区为950～600℃,此时断面收缩率在34%～73%。为预防铸坯矫直过程裂纹产生,要控制矫直温度在950℃以上。     

Effect of strain rate on high temperature mechanical properties of Q460 continuous cast slab

Gleeble 3500 thermal simulation testing machine and metallographic method were used to test the high temperature mechanical properties of construction steel Q460 continuous cast slab at different strain rates, and the high temperature strength, hot ductility and final room temperature microstructure of Q460 continuous cast slab at different strain rates in the range of 600℃ to 1200℃ were obtained. The results show that when Q460 continuous cast slab is performed at a higher strain rate (10s-1), the reduction of area increases with the increase of the tensile temperature without obvious high temperature brittle zone. But when the strain rate is (10-3s-1), the curves of the reduction of area has two brittle regions. The first one is located at 1100℃ to the melting point temperature, and the second is near 700℃. In general, the reduction of area of this steel grade is greater than 65%, indicating that construction steel Q460 continuous cast slab has good high temperature hot ductility. In addition, under the same strain rate, the tensile strength of Q460 continuous cast slab decreases with the increase of tensile temperature, while the elongation increases with the increase of tensile temperature.     

Q235B 薄板坯高温塑性的研究

根据Gleeble1500热/应变模拟试验机测试的CSP薄板坯连铸工艺生产的成分(%)为0.16~0.20C,0.020~0.060Al_t Q235B钢的70 mm ×1 500 mm薄板坯600~1400℃热塑性曲线,得出连铸坯第Ⅲ脆性区为700~900℃,如在此温度范围矫直,铸坯易产生裂纹。通过扫描电镜分析断口形貌和电子探针的成分分析,得出形变诱导铁素体呈网状析出和奥氏体在低温区域析出氮化物(AlN)导致铸坯脆化。     

含钒低合金钢铸坯高温延塑性研究

采用Gleeble-1500热模拟试验机测试了含钒低合金钢铸坯的高温延塑性,利用扫描电镜、金相显微镜对断口形貌及金相组织进行分析。低合金钢的第Ⅰ脆性温度区在Ts~1 370℃之间,第Ⅲ脆性温度区在915~710℃之间。第Ⅲ脆性区间由奥氏体低温域晶界滑移楔形裂纹造成的沿晶脆性断裂和奥氏体晶界先共析铁素体薄膜造成的沿晶韧性断裂两部分组成。钢中的V对钢的第Ⅲ脆性凹槽的影响比较大,脆化向低温区域延伸。     

Fe--22Mn--0.7CTWIP钢的热塑性与断裂机制

基于Gleeble-1500热力模拟试验机测定了Fe-22Mn-0.7C TWIP钢和Q235钢700~1300℃范围内的静态拉伸行为.采用光学显微镜、扫描电子显微镜、能谱仪、电子探针微区分析等技术表征两钢种不同温度下的变形特征和断口形貌.通过分析基体化学成分、相体积分数、晶粒尺寸、凝固缺陷等因素探讨TWIP钢铸态热塑性的变化规律及其影响机制.研究结果表明,Fe-22Mn-0.7C TWIP钢700~1250℃范围内的铸态抗拉强度高于Q235,而其断面收缩率低于40%,且断口均以沿枝晶间断裂方式为主.晶粒细化和控制溶质显微偏析有利于提高TWIP钢热塑性,与基体均质性改善有关.此外,增加应变速率TWIP钢拉伸强度和断面收缩率同时增大.      

460MPa级海洋平台用钢的高温塑性研究

通过Gleeble-1500D热模拟机来进行EQ47(460 MPa)钢的高温塑性研究,以1×10-3/s的变形速率,在600~1 350℃的温度区间内以每50℃取一间隔做一组高温塑性试验.结果表明:在907~1 270℃之间,断面收缩率均高于60%,钢的高温塑性良好,温度高于1 270℃时,断面收缩率急剧下降,第Ⅲ脆性区在667~907℃之间,在此温度区间内存在明显的塑性低谷,断面收缩率最低值为29.44%.     

ER70S-6连铸坯高温塑性研究

通过在GLEEBLE-1500热模拟实验机上进行的高温拉伸试验,测试了ER70S-6连铸坯的高温塑性,并通过金相、扫描电镜等方法对拉断后试样的断口及组织形貌进行了分析检验。结果表明：对于ER70S-6钢,在1 300～960℃范围内,其断面收缩率均大于60%,具有良好的塑性。断面收缩率小于60%第Ⅲ脆性温度范围为960～720℃,从而在制定连铸和热轧工艺制度时可避开该温度区,或尽量在该区域少停留。