快速热处理对PZT薄膜的微结构及电性能的影响

采用改进的溶胶一凝胶技术,在Ｐｔ／Ｔｉ／ＴｉＯ２／ＳｉＯ２／Ｓｉ（１００）基片上制备了太电ＰＺＴ薄膜,用ＸＲＤ和ＡＦＭ技术分析了不同热处理工艺条件下ＰＺＴ薄膜的微观形貌变化及相结构演化,系统测试了ＰＺＴ薄膜的铁电性能。工艺－结构－性能研究结果表明：快速热处理工艺（ＲＴＡ）有利于ＰＺＴ薄膜保持较低的漏电流密度,热处理温度是影响晶粒大小的主要因素,而保温时间则对ＰＺＴ薄膜的致密性、晶粒均匀度和晶界结合     

非晶态铁电薄膜的铁电相转变

用ＡｒＦ脉冲激光在Ｐｔ／Ｔｉ／ＳｉＯ２／Ｓｉ衬底上合成了非晶态ＳｒＢｉ２Ｔａ２Ｏ９铁电薄膜,研究了铁电相转变。采用常规热退火、激光诱导和低温高压水热法使非晶态ＳＢＴ薄膜发生铁电相转变。     

Pb1—xLaxTiO3薄膜的制备及介电特性研究

用溶胶－凝胶法在Ｐｔ／Ｔｉ／ＳｉＯ２／Ｓｉ（１００）基底上制备Ｐｂ１－ｘＬａｘＴｉＯ３（ＰＬＴ,ｘ〈０．２）薄膜,研究薄膜的结构及其介电、铁电性能。在６００℃下退火１小时的ＰＬＴ薄膜表现出单一的钙钛矿结构,（１００）择优取向明显,在室温下ＰＬＴ薄膜有典型的电滞回线。在ｘ〈０．２（摩尔比）的范围内,ＰＬＴ薄膜相对介电常数则随着Ｌａ的增加而增加。     

溶胶—凝胶技术制备Bi4Ti3O12铁电薄膜的研究

采用溶胶－凝胶技术在Ｓｉ单晶基片上制备了具有层状钙钛矿型结构的Ｂｉ４Ｔｉ３Ｏ１２ｘ铁电薄膜，讨论了回火温度与时间对薄膜结构的影响，Ｘ射线衍射分析表明，经７００℃和７００℃以上温度回火的薄膜为具有层状钙矿型结构的Ｂｉ４Ｔｉ３Ｏ１２多晶薄膜，该薄膜的电滞回线测试呈出剩余极化强度Ｐｒ＝５μＣ／ｃｍ＾２，矫顽场Ｅｃ＝１３０ｋＶ／ｃｍ。     

常压MOCVD制备MgO薄膜的研究

本文首次报道用常压金属有机化学气相沉积（ＡＰ－ＭＯＣＶＤ）在Ｓｉ（１００），ＳｉＯ２／Ｓｉ（１００）和Ｐｔ／Ｓｉ（１００）衬底上外延高质量的ＭｇＯ薄膜。研究了衬底温度与薄膜的取向性关系和ＭｇＯ薄膜的潮解特性。高纯ｍａｇｎｅｓｉｕｍａｃｅｔｙｌａｃｅｔｏｎａｔｅ［ｂｉｓ（２，４－ｐｅｎｔａｎｅｔａｎｅ－ｄｉｏｎｏ）ｍａｇｎｅｓｉｕｍ］［Ｍｇ（ＣＨ２ＣＯＣＨ２ＣＯＣＨ３）２］作为金属有机源，扫描电镜（ＳＥＭ），透射电镜（ＴＥＭ）和Ｘ－ＲＡＹ衍射实验显示，在较低的衬底温度（～４８０℃）下一次淀积成单晶膜。薄膜均匀，致密，结晶性和取向性很好，衬底温度（Ｔｓ）在４００℃到６８０℃之间，在Ｓｉ（１００）衬底上生长的ＭｇＯ薄膜都具有［１００］取向，在Ｓｉ（１００）、ＳｉＯ２／Ｓｉ（１００）和Ｐｔ／Ｓｉ（１００）衬底上生长的ＭｇＯ薄膜也都具有［１００］取向。     

医用NiTi合金表面溶胶-凝胶法制备TiO2-SiO2薄膜

采用溶胶－凝胶法在ＮｉＴｉ形状记忆合金表面制备了ＴｉＯ_２－ＳｉＯ_２复合薄膜,在提高医用ＮｉＴｉ合金的抗腐蚀性方面,收到了显著的效果．运用电化学方法对不同组成的ＴｉＯ_２－ＳｉＯ_２薄膜在模拟体液中的腐蚀行为进行了研究,结果表明,随薄膜中 Ｔｉ／Ｓｉ比的增加,ＴｉＯ_２－ＳｉＯ_２薄膜的抗腐蚀性增强．划痕试验表明 ＴｉＯ_２－ＳｉＯ_２（Ｔｉ／Ｓｉ＝４：１）膜与ＮｉＴｉ合金基体具有较高的界面结合强度．用原子力显微镜（ＡＦＭ）对ＴｉＯ_２－ＳｉＯ_２薄膜的表面形貌及表面粗糙度进行观察和分析,解释并讨论了ＴｉＯ_２－ＳｉＯ_２薄膜的配方组成与其抗腐蚀性的关系,ＳｉＯ_２含量较少时,薄膜结构致密,膜层均匀平滑,且膜基结合力好,作为医用ＮｉＴｉ合金的表面保护层,可以使其耐腐蚀性有显著提高．     

溅射工艺参数对PZT铁电薄膜相变过程的影响

采用射频磁控溅射工艺,在（１１１）Ｐｔ／Ｔｉ／ＳｉＯ２／Ｓｉ衬底上用ＰＺＴ（５３／４７）陶瓷靶制备铁电薄膜。用快速光热退火炉对原位沉积的薄膜进行ＲＴＡ处理。     

PZT—NiTi铁电—铁弹多层膜的制备及表征

用溶胶－凝胶法制备了ＰＺＴ压电薄膜,研制了Ａｕ／ＰＺＴ／ＰＴ／ＴｉＯ２／ＮｉＴｉ／Ｓｉ（１００）多层膜结构,用ＸＲＤ,ＡＦＭ,ＴＥＭ－ＥＤＸ和ＳＡＤ技术考察了薄膜的表面形貌,相结构演化,以及面的元素分布特性。结果表明：ＰＺＴ膜与ＮｉＴｉ合金膜的结合良好,稳定;ＰＴ层的引入,使无定型ＰＺＴ薄膜在５５０℃退火后,转变为钙钛矿结构,降低了晶化温度,并有效地抑制焦碌石相的形成;ＮｉＴｉ薄膜结晶良好;ＴｉＯ     

溶胶—凝胶制备TiO2／SiO2复合薄膜的FT—IR表征

ＦＴ－ＩＲ吸收谱用来研究具有多孔结构的ＴｉＯ２／ＳｉＯ２复合薄膜；薄膜在１２００ｃｍ＾－１有一较强的肩峰，其强度与峰位随热处理温度度而生变化。在９５５ｃｍ＾－１的吸收峰是由于Ｓｉ－Ｏ－Ｔｉ和Ｓｉ－ＯＨ的结果，并随着热处理 度的提高其吸收峰完全是Ｓｉ－Ｏ－Ｔｉ振动所引起的，其峰位随着ＴｉＯ２的增加，向低频区域移动。     

改进溶胶-凝胶法制备PZT50/50铁电薄膜

采用改进的溶胶凝胶法在Ｐｔ／Ｔｉ／ＳｉＯ２／Ｓｉ衬底上制备了ＰＺＴ５０／５０铁电薄膜，用Ｘ射线衍射表征了薄膜的物相，用原子力显微镜（ＡＦＭ）表征薄膜的微观形貌，用ＲＴ６６Ａ测量了薄膜的铁电特性，获得了具有优良的铁电性能的晶粒尺寸为１００ｎｍ的ＰＺＴ５０／５０铁电薄膜，在２０Ｖ电压下，Ｐｒ＝３１．８３μＣ／ｃｍ２。     

Microstructure and optical properties of plasmapolymer thin films with embedded silver nanoparticles

Plasmapolymer thin films with embedded silver nanoparticles were deposited by simultaneous plasma polymerization and metal evaporation. The particle size and shape were determined by transmission electron microscopy (TEM) and analysed by optical image processing. The optical properties in the UV/ VIS/NIR spectral region were determined by the plasma resonance absorption of the silver particles. Transmittance spectra were calculated with the Bergman effective medium theory and compared with experimental spectra.     

Dielectric and pyroelectric properties of Ba-modified lead lanthanum zirconate stannate titanate ceramics

(Pb_0.97−xLa_0.02Ba_x)(Zr_0.75Sn_0.12Ti_0.13)O₃ ceramics in the composition range 0.1 ≤ x ≤ 0.16 were prepared by conventional solid state reaction process. On increasing Ba content from 0.1 to 0.16 mol, the specimens underwent phase transition from the first order to the second order and the Curie temperature decreased from 85 to 35 °C. With x = 0.16, the specimen showed good pyroelectric properties for practical applications. When a 500 V/mm dc bias field was applied, the specimen showed the maximum pyroelectric coefficient of 5800 μC/m² K and figure of merit of 58 × 10⁻⁵ Pa^−0.5 at Curie temperature.     

Engineering properties of concrete containing natural zeolite as supplementary cementitious material: Strength,toughness, durability,and hygrothermal performance

A complex analysis of engineering properties of concrete containing natural zeolite as supplementary cementitious material in the blended Portland-cement based binder in an amount of up to 60% by mass is presented. The studied parameters include basic physical characteristics, mechanical and fracture–mechanics properties, durability characteristics, and hygric and thermal properties. Experimental results show that 20% zeolite content in the blended binder is the most suitable option. For this cement replacement level the compressive strength, bending strength, effective fracture toughness, effective toughness, and specific fracture energy are only slightly worse than for the reference Portland-cement concrete. The frost resistance, de-icing salt resistance, and chemical resistance to MgCl₂, NH₄Cl, Na₂SO₄, and HCl are improved. The hygrothermal performance of hardened mixes containing 20% natural zeolite, as assessed using the measured values of water absorption coefficient, water vapor diffusion coefficient, water vapor sorption isotherms, thermal conductivity, and specific heat capacity, is satisfactory.     

Facile preparation of poly(vinyl alcohol) nanocomposites with pristine layered double hydroxides

In this paper, nano-sized Mg–Al layered double hydroxide (LDH) was synthesized by a fast nucleation and slow aging method. The structures of LDH were characterized by transmission electron microscopy (TEM), atomic force microscopy (AFM) and photon correlation spectroscopy (PCS). Poly(vinyl alcohol) (PVA) nanocomposites with different LDH loadings were prepared by water solution casting method. TEM observations show that the LDH nanoplatelets are uniformly dispersed in the PVA matrix. Tensile tests indicate that the elastic modulus and the tensile strength of PVA are improved by about 15% and 54%, respectively, when incorporating with 2 wt% LDH. The improvement of mechanical properties of PVA can be attributed to fine dispersion of LDH, good compatibility and strong interaction between PVA and LDH. In addition, the presence of LDH decreases the decomposition rates at the second stage and improves the amount of residues of PVA. Meanwhile, the transparency of the nanocomposite films is maintained compared with neat PVA.     

Properties of high performance concrete containing fine-ground ceramics as supplementary cementitious material

This paper presents experimental work regarding the basic physical characteristics, mechanical and fracture-mechanics properties, durability characteristics, hydric and thermal properties of high performance concrete (HPC) with up to 60% of Portland cement replaced by fine-ground ceramics. Experimental results show that the amount of the ceramics in the mix is limited mainly by the resistance against de-icing salts which is found satisfactory only up to the cement replacement level of 10%. The mechanical and water transport properties are not significantly impaired by ceramic additions of up to 20%, whereas the effective fracture toughness, specific fracture energy, and chemical resistance (to MgCl₂, NH₄Cl, Na₂SO₄, HCl) are effectively maintained up to 40%. The frost resistance, water vapor transport and storage parameters and thermal properties are not significantly impaired even up to a 60% replacement level.     

Mechanochemical synthesis,structural, magnetic,optical and electrooptical properties of CuFeS2 nanoparticles

The rapid mechanochemical synthesis of nanocrystalline CuFeS₂ particles prepared by high-energy milling for 60?min in a planetary mill from copper, iron and sulphur elements is reported. The CuFeS₂ nanoparticles crystallize in tetragonal structure with mean crystallite size of about 38?±?1?nm determined by XRD analysis. HRTEM study also revealed the presence of nanocrystals with the size of 5–30?nm with the tendency to form agglomerates. The Raman spectrum confirms the chalcopyrite structure. Low temperature magnetic data for CuFeS₂ support the coexistence of antiferromagnetic and paramagnetic spin structure. Moreover, the hysteresis loops taken at temperatures from 5?K to 300?K revealed a presence of very small amount of ferromagnetic phase, which seems to be associated with the non-consumed elemental Fe in as-prepared nanoparticles. The optical band gap of CuFeS₂ nanoparticles has been detected to be 1.05?eV, larger than band gap of the bulk material. The wider gap possibly resulted from the nano-size effect. Photoresponses of CuFeS₂ nanoparticles were confirmed by I-V measurements under dark and light illumination. It was demonstrated that mechanochemical synthesis can be successfully employed in the one step preparation of nanocrystalline CuFeS₂ with good structural, magnetic, optical and electrooptical properties.     

基于第一性原理研究Heusler合金Fe2CuGa的结构和性能

采用基于密度泛函理论的第一性原理,系统研究了Heusler合金Fe2CuGa的结构、磁性、弹性性能和电子性质.计算结果表明:立方相的基态结构是铁磁态的Hg2CuTi结构.立方到四方的相变几乎是体积不变的,这是形状记忆合金的特性.奥氏体和马氏体的磁矩分别是4.48和4.56μB/f.u..另外,预测了Fe2CuGa的弹性系数.Fe2CuGa的立方结构在力学上是不稳定的而四方结构是稳定的.根据体模量和剪切模量的比值,发现Fe2CuGa在本质上是可延展的.利用态密度的方法解释了Fe2CuGa马氏体相变的来源.     

Preparation and characterization of organic pigments and their fluorescence properties depending on bulk structure

Fluorescent pigments, based on the optical or electrooptical properties of dyes, are the main component in fluorescent coatings and inks. In this study, three kinds of dyes (Rhodamine B, Light Green SF Yellowish, Coumarin) with four different ratios (2.5 wt%, 3 wt%, 3.5 wt%, 4 wt%) were employed as luminophor, and the melamine-formaldehyde (MF) resin was used as curing resin to prepare fluorescent pigments in different color. Fourier transform infrared spectroscopy and X-ray diffractometry were carried out to analyze the structure of the fluorescent pigments. Scanning electron microscopy and particle size distribution were used to present the morphology of fluorescent pigments. UV–vis and fluorescence spectrum were used to demonstrate the optical properties. It can be concluded that, coumarin pigments possessed consecutive structure in MF resin while rhodamine B might be the best for the preparation of printing inks among the three kinds of dyes from the view of particle size. The TG results presented that all the pigments showed good thermal stability, which might possess potential application in high speed printing industry.     

X-cor夹层结构的力学性能试验研究

X-cor夹层结构比强度高,比刚度大,有望取代传统蜂窝夹层结构作为航空航天器的主承力结构材料。采用真空固化成型工艺,通过改变Z-pin的植入参数制备了X-cor夹层结构,研究了Z-pin植入角度、植入间距和直径对其平压、剪切和拉伸性能的影响。研究结果表明,Z-pin的植入参数对X-cor夹层结构的力学性能影响显著。随Z-pin植入角度的增加X-cor夹层结构的平压性能降低,剪切性能增强,拉伸模量减小,拉伸强度先增加后减小。随Z-pin植入间距和直径增加,X-cor夹层结构力学性能均增加。与泡沫夹层结构相比,X-cor夹层结构压缩、剪切和拉伸模量的测试值分别提高了1.26～5.15倍、2.50～13.56倍和1.90～2.71倍,压缩、剪切和拉伸测试值分别提高了1.63～9.20倍、1.28～2.03倍和1.01～2.30倍。