Ultrahigh‐Strength Ultrahigh Molecular Weight Polyethylene (UHMWPE)‐Based Fiber Electrode for High Performance Flexible Supercapacitors

Flexible fiber‐based supercapacitor (FSC) with excellent electrochemical performance and high tensile strength and modulus is strongly desired for some special circumstances, such as load‐bearing, abrasion resistant, and anticutting fabrics. Here, a series of ultrahigh‐strength fiber electrodes are prepared for flexible FSCs based on ultrahigh molecular weight polyethylene fibers, on which the polydopamine, Ag, and poly (3,4‐ethylene dioxythiophene): poly(styrenesulfonate) are deposited in sequence. The modified fiber‐based electrode exhibits superhigh strength up to 3.72 GPa, which is the highest among fiber‐based electrodes reported to date. In addition, FSCs fabricated with the optimized fiber electrode shows a specific areal capacity as high as 563 mF cm^?2 at 0.17 mA cm^?2, which corresponds to a high areal energy density of ≈50.1 µWh cm^?2 at a power density of ≈124 µW cm^?2. The specific areal capacity only decrease 8% after 1000 times bending test, indicating the outstanding bending performance of this composite fiber electrode. Furthermore, several FSCs can be connected in series or in parallel to get higher working voltage or higher capacity respectively, which demonstrates its potential for broad applications in flexible devices.     

Scalable Production of Graphene Inks via Wet‐Jet Milling Exfoliation for Screen‐Printed Micro‐Supercapacitors

The miniaturization of energy storage units is pivotal for the development of next‐generation portable electronic devices. Micro‐supercapacitors (MSCs) hold great potential to work as on‐chip micro‐power sources and energy storage units complementing batteries and energy harvester systems. Scalable production of supercapacitor materials with cost‐effective and high‐throughput processing methods is crucial for the widespread application of MSCs. Here, wet‐jet milling exfoliation of graphite is reported to scale up the production of graphene as a supercapacitor material. The formulation of aqueous/alcohol‐based graphene inks allows metal‐free, flexible MSCs to be screen‐printed. These MSCs exhibit areal capacitance (C_areal) values up to 1.324 mF cm^?2 (5.296 mF cm^?2 for a single electrode), corresponding to an outstanding volumetric capacitance (C_vol) of 0.490 F cm^?3 (1.961 F cm^?3 for a single electrode). The screen‐printed MSCs can operate up to a power density above 20 mW cm^?2 at an energy density of 0.064 µWh cm^?2. The devices exhibit excellent cycling stability over charge–discharge cycling (10 000 cycles), bending cycling (100 cycles at a bending radius of 1 cm) and folding (up to angles of 180°). Moreover, ethylene vinyl acetate‐encapsulated MSCs retain their electrochemical properties after a home‐laundry cycle, providing waterproof and washable properties for prospective application in wearable electronics.     

Layered Silicon‐Based Nanosheets as Electrode for 4 V High‐Performance Supercapacitor

Silicon‐based materials have shown great potential and been widely studied in various fields. Unlike its unparalleled theoretical capacity as anodes for batteries, few investigations have been reported on silicon‐based materials for applications in supercapacitors. Here, an electrode composed of layered silicon‐based nanosheets, obtained through oxidation and exfoliation, for a supercapacitor operated up to 4 V is reported. These silicon‐based nanosheets show an areal specific capacitance of 4.43 mF cm^?2 at 10 mV s^?1 while still retaining a specific capacitance of 834 µF cm^?2 even at an ultrahigh scan rate of 50 000 mV s^?1. The volumetric energy and power density of the supercapacitor are 7.65 mWh cm^?3 and 9312 mW cm^?3, respectively, and the electrode can operate for 12000 cycles in a potential window of 4 V at 2 A g^?1, while retaining 90.6% capacitance. These results indicate that the silicon‐based nanosheets can be a competitive candidate as the supercapacitor electrode material.     

Engineering 3D Ion Transport Channels for Flexible MXene Films with Superior Capacitive Performance

2D MXene materials are of considerable interest for future energy storage. A MXene film could be used as an effective flexible supercapacitor electrode due to its flexibility and, more importantly, its high specific capacitance. However, although it has excellent electronic conductivity, sluggish ionic kinetics within the MXene film becomes a fundamental limitation to the electrochemical performance. To compensate for the relative deficiency, MXene films are frequently reduced to several micrometer dimensions with low mass loading (<1 mg cm^?2), to the point of detriment of areal performance and commercial value. Herein, for the first time, the design of a 3D porous MXene/bacterial cellulose (BC) self‐supporting film is reported for ultrahigh capacitance performance (416 F g^?1, 2084 mF cm^?2) with outstanding mechanical properties and high flexibility, even when the MXene loading reaches 5 mg cm^?2. The highly interconnected MXene/BC network enables both excellent electron and ion transport channel. Additionally, a maximum energy density of 252 µWh cm^?2 is achieved in an asymmetric supercapacitor, higher than that of all ever‐reported MXene‐based supercapacitors. This work exploits a simple route for assembling 2D MXene materials into 3D porous films as state‐of‐the‐art electrodes for high performance energy storage devices.     

Substrate‐Free and Shapeless Planar Micro‐Supercapacitors

Micro‐supercapacitors (MSCs), albeit powerful, are unable to broaden their potential applications primarily because they are not as flexible and morphable as electronics. To address this problem, a universal strategy to fabricate substrate‐free, ultrathin, shapeless planar‐MSCs with high‐performance tenability under serious deformation is put forward. These represent a new class of “all‐inside‐one” film supercapacitors, achieved by encapsulating two‐dimensional interdigital microelectrodes within chemically cross‐linked polyvinyl‐alcohol‐based hydrogel electrolyte containing graphene oxide (GO). GO nanosheets significantly improve ionic conductivity, enhance the capacitance, and boost robustness of hydrogel electrolyte. Consequently, the entire MSC, while being only 37 µm thick, can be crumpled and its shape can self‐adjust through fluid channel ten times smaller than its original size without any damage, demonstrating shapelessness. Using MXene as active material, high single‐cell areal capacitance of 40.8 mF cm^?2 is achieved from microelectrodes as thin as 5 µm. Furthermore, to demonstrate wide applicability of this protocol, screen‐printed graphene‐based highly integrated MSCs connecting nine cells in series are fabricated to stably output a high voltage of 7.2 V while crumpling them from 0.11 to 0.01 cm^?3, manifesting superior performance uniformity. This protocol allows the coexistence of high performance with incredible flexibility that may greatly diversify MSCs' applications.     

Sputtered Titanium Carbide Thick Film for High Areal Energy on Chip Carbon‐Based Micro‐Supercapacitors

The areal energy density of on‐chip micro‐supercapacitors should be improved in order to obtain autonomous smart miniaturized sensors. To reach this goal, high surface capacitance electrode (>100 mF cm^?2) has to be produced while keeping low the footprint area. For carbide‐derived carbon (CDC) micro‐supercapacitors, the properties of the metal carbide precursor have to be fine‐tuned to fabricate thick electrodes. The ad‐atoms diffusion process and atomic peening effect occurring during the titanium carbide sputtering process are shown to be the key parameters to produce low stress, highly conductive, and thick TiC films. The sputtered TiC at 10^?3 mbar exhibits a high stress level, limiting the thickness of the TiC‐CDC electrode to 1.5 µm with an areal capacitance that is less than 55 mF cm^?2 in aqueous electrolyte. The pressure increase up to 10^?2 mbar induces a clear reduction of the stress level while the layer thickness increases without any degradation of the TiC electronic conductivity. The volumetric capacitance of the TiC‐CDC electrodes is equal to 350 F cm^?3 regardless of the level of pressure. High values of areal capacitance (>100 mF cm^?2) are achieved, whereas the TiC layer is relatively thick, which paves the way toward high‐performance micro‐supercapacitors.     

A Low‐Cost,Self‐Standing NiCo2O4@CNT/CNT Multilayer Electrode for Flexible Asymmetric Solid‐State Supercapacitors

The demand for a new generation of flexible, portable, and high‐capacity power sources increases rapidly with the development of advanced wearable electronic devices. Here we report a simple process for large‐scale fabrication of self‐standing composite film electrodes composed of NiCo₂O₄@carbon nanotube (CNT) for supercapacitors. Among all composite electrodes prepared, the one fired in air displays the best electrochemical behavior, achieving a specific capacitance of 1,590 F g^?1 at 0.5 A g^?1 while maintaining excellent stability. The NiCo₂O₄@CNT/CNT film electrodes are fabricated via stacking NiCo₂O₄@CNT and CNT alternately through vacuum filtration. Lightweight, flexible, and self‐standing film electrodes (≈24.3 µm thick) exhibit high volumetric capacitance of 873 F cm^?3 (with an areal mass of 2.5 mg cm^?2) at 0.5 A g^?1. An all‐solid‐state asymmetric supercapacitor consists of a composite film electrode and a treated carbon cloth electrode has not only high energy density (≈27.6 Wh kg^?1) at 0.55 kW kg^?1 (including the weight of the two electrodes) but also excellent cycling stability (retaining ≈95% of the initial capacitance after 5000 cycles), demonstrating the potential for practical application in wearable devices.     

High‐Performance,Low‐Cost,and Dense‐Structure Electrodes with High Mass Loading for Lithium‐Ion Batteries

Lithium‐ion batteries have undergone a remarkable development in the past 30 years. However, conventional electrodes are insufficient for the ever‐increasing demand of high‐energy batteries. Here, reported is a thick electrode with a dense structure, as an alternative to the commonly recognized porous framework. A low‐temperature sintering technology with the aid of aqueous solvent, high pressure, and an ion‐conductive additive is originally developed for preparing the LiCoO₂ (LCO)/Li₄Ti₅O₁₂ (LTO) dense‐structure electrode as the representative cathode/anode material. The 400 µm thick cathode with 110 mg cm^?2 mass loading achieves a high specific capacity of 131.2 mAh g^?1 with a good capacity retention of 96% over 150 cycles, far exceeding the commercial counterpart (≈40 µm) of 54.1 mAh g^?1 with 39%. The ultrathick electrode of 1300 µm thickness presents a remarkable area capacity of 28.6 mAh cm^?2 that is 16 times that of the commercial electrode. The full cell based on the dense electrodes delivers an extremely high areal capacity of 14.4 mAh cm^?2. The ion‐diffusion coefficients of the densely sintered electrodes increase by nearly three orders of magnitude. This design opens up a new avenue for scalable and sustainable material manufacturing towards various practical applications.     

Rationally Engineered Electrodes for a High‐Performance Solid‐State Cable‐Type Supercapacitor

Wire‐shaped electrodes for solid‐state cable‐type supercapacitors (SSCTS) with high device capacitance and ultrahigh rate capability are prepared by depositing poly(3,4‐ethylenedioxythiophene) onto self‐doped TiO₂ nanotubes (D‐TiO₂) aligned on Ti wire via a well‐controlled electrochemical process. The large surface area, short ion diffusion path, and high electrical conductivity of these rationally engineered electrodes all contribute to the energy storage performance of SSCTS. The cyclic voltammetric studies show the good energy storage ability of the SSCTS even at an ultrahigh scan rate of 1000 V s^?1, which reveals the excellent instantaneous power characteristics of the device. The capacitance of 1.1 V SSCTS obtained from the charge–discharge measurements is 208.36 µF cm^?1 at a discharge current of 100 µA cm^?1 and 152.36 µF cm^?1 at a discharge current of 2000 µA cm^?1, respectively, indicating the ultrahigh rate capability. Furthermore, the SSCTS shows superior cyclic stability during long‐term (20 000 cycles) cycling, and also maintains excellent performance when it is subjected to bending and succeeding straightening process.     

A Self‐Branched Lamination of Hierarchical Patronite Nanoarchitectures on Carbon Fiber Cloth as Novel Electrode for Ionic Liquid Electrolyte‐Based High Energy Density Supercapacitors

The developments of rationally designed binder‐free metal chalcogenides decorated flexible electrodes are of paramount importance for advanced energy storage devices. Herein, binder‐free patronite (VS₄) flower‐like nanostructures are facilely fabricated on a carbon cloth (CC) using a facile hydrothermal method for high‐performance supercapacitors. The growth density and morphology of VS₄ nanostructures on CC are also controlled by varying the concentrations of vanadium and sulfur sources along with the complexing agent in the growth solution. The optimal electrode with an appropriate growth concentration (VS₄‐CC@VS‐3) demonstrates a considerable pseudocapacitance performance in the ionic liquid (IL) electrolyte (1‐ethyl‐3‐methylimidazolium trifluoromethanesulfonate), with a high operating potential of 2 V. Utilizing VS₄‐CC@VS‐3 as both positive and negative electrodes, the IL‐based symmetric supercapacitor is assembled, which demonstrates a high areal capacitance of 536 mF cm^?2 (206 F g^?1) and excellent cycling durability (93%) with superior energy and power densities of 74.4 µWh cm^?2 (28.6 Wh kg^?1) and 10154 µW cm^?2 (9340 W kg^?1), respectively. As for the high energy storage performance, the device stably energizes various portable electronic applications for a long time, which make the fabricated composite material open up news for the fabrication of fabrics supported binder‐free chalcogenides for high‐performance energy storage devices.     

High Electroactive Material Loading on a Carbon Nanotube@3D Graphene Aerogel for High‐Performance Flexible All‐Solid‐State Asymmetric Supercapacitors

Freestanding carbon‐based hybrids, specifically carbon nanotube@3D graphene (CNTs@3DG) hybrid, are of great interest in electrochemical energy storage. However, the large holes (about 400 µm) in the commonly used 3D graphene foams (3DGF) constitute as high as 90% of the electrode volume, resulting in a very low loading of electroactive materials that is electrically connected to the carbon, which makes it difficult for flexible supercapacitors to achieve high gravimetric and volumetric energy density. Here, a hierarchically porous carbon hybrid is fabricated by growing 1D CNTs on 3D graphene aerogel (CNTs@3DGA) using a facile one‐step chemical vapor deposition process. In this architecture, the 3DGA with ample interconnected micrometer‐sized pores (about 5 µm) dramatically enhances mass loading of electroactive materials comparing with 3DGF. An optimized all‐solid‐state asymmetric supercapacitor (AASC) based on MnO₂@CNTs@3DGA and Ppy@CNTs@3DGA electrodes exhibits high volumetric energy density of 3.85 mW h cm^?3 and superior long‐term cycle stability with 84.6% retention after 20 000 cycles, which are among the best reported for AASCs with both electrodes made of pseudocapacitive electroactive materials.     

High‐Energy Asymmetric Supercapacitor Yarns for Self‐Charging Power Textiles

Rapid growth of electronic textile increases the demand for textile‐based power sources, which should have comparable lightweight, flexibility, and comfort. In this work, a self‐charging power textile interwoven by all‐yarn‐based energy‐harvesting triboelectric nanogenerators (TENG) and energy‐storing yarn‐type asymmetric supercapacitors (Y‐ASC) is reported. Common polyester yarns with conformal Ni/Cu coating are utilized as 1D current collectors in Y‐ASCs and electrodes in TENGs. The solid‐state Y‐ASC achieves high areal energy density (≈78.1 µWh cm^?2), high power density (14 mW cm^?2), stable cycling performance (82.7% for 5000 cycles), and excellent flexibility (1000 cycles bending for 180°). The TENG yarn can be woven into common fabrics with desired stylish designs to harvest energy from human daily motions at high output (≈60 V open‐circuit voltage and ≈3 µA short‐circuit current). The integrated self‐charging power textile is demonstrated to power an electronic watch without extra recharging by other power sources, suggesting its promising applications in electronic textiles and wearable electronics.     

Multilayer‐Folded Graphene Ribbon Film with Ultrahigh Areal Capacitance and High Rate Performance for Compressible Supercapacitors

Limited by 2D geometric morphology and low bulk packing density, developing graphene‐based flexible/compressible supercapacitors with high specific capacitances (gravimetric/volumetric/areal), especially at high rates, is an outstanding challenge. Here, a strategy for the synthesis of free‐standing graphene ribbon films (GRFs) for high‐performance flexible and compressible supercapacitors through blade‐coating of interconnected graphene oxide ribbons and a subsequent thermal treatment process is reported. With an ultrahigh mass loading of 21 mg cm^?2, large ion‐accessible surface area, efficient electron and ion transport pathways as well as high packing density, the compressed multilayer‐folded GRF films (F‐GRF) exhibit ultrahigh areal capacitance of 6.7 F cm^?2 at 5 mA cm^?2, high gravimetric/volumetric capacitances (318 F g^?1, 293 F cm^?3), and high rate performance (3.9 F cm^?2 at 105 mA cm^?2), as well as excellent cycling stability (109% of capacitance retention after 40 000 cycles). Furthermore, the assembled F‐GRF symmetric supercapacitor with compressible and flexible characteristics, can deliver an ultrahigh areal energy density of 0.52 mWh cm^?2 in aqueous electrolyte, almost two times higher than the values obtained from symmetric supercapacitors with comparable dimensions.     

Oxygen‐Deficient Bismuth Oxide/Graphene of Ultrahigh Capacitance as Advanced Flexible Anode for Asymmetric Supercapacitors

Oxygen‐deficient bismuth oxide (r‐Bi₂O₃)/graphene (GN) is designed, fabricated, and demonstrated via a facile solvothermal and subsequent solution reduction method. The ultrafine network bacterial cellulose (BC) as substrate for r‐Bi₂O₃/GN exhibits high flexibility, remarkable tensile strength (55.1 MPa), and large mass loading of 9.8 mg cm^?2. The flexible r‐Bi₂O₃/GN/BC anode delivers appreciable areal capacitance (6675 mF cm^?2 at 1 mA cm^?2) coupled with good rate capability (3750 mF cm^?2 at 50 mA cm^?2). In addition, oxygen vacancies have great influence on the capacitive performance of Bi₂O₃, delivering significantly improved capacitive values than the untreated Bi₂O₃ flexible electrode, and ultrahigh gravimetric capacitance of 1137 F g^?1 (based on the mass of r‐Bi₂O₃) can be obtained, achieving 83% of the theoretical value (1370 F g^?1). Flexible asymmetric supercapacitor is fabricated with r‐Bi₂O₃/GN/BC and Co₃O₄/GN/BC paper as the negative and positive electrodes, respectively. The operation voltage is expanded to 1.6 V, revealing a maximum areal energy density of 0.449 mWh cm^?2 (7.74 mWh cm^?3) and an areal power density of 40 mW cm^?2 (690 mW cm^?3). Therefore, this flexible anode with excellent electrochemical performance and high mechanical properties shows great potential in the field of flexible energy storage devices.     

A High Energy Density Asymmetric Supercapacitor from Nano‐architectured Ni(OH)2/Carbon Nanotube Electrodes

The demand for advanced energy storage devices such as supercapacitors and lithium‐ion batteries has been increasing to meet the application requirements of hybrid vehicles and renewable energy systems. A major limitation of state‐of‐art supercapacitors lies in their relatively low energy density compared with lithium batteries although they have superior power density and cycle life. Here, we report an additive‐free, nano‐architectured nickel hydroxide/carbon nanotube (Ni(OH)₂/CNT) electrode for high energy density supercapacitors prepared by a facile two‐step fabrication method. This Ni(OH)₂/CNT electrode consists of a thick layer of conformable Ni(OH)₂ nano‐flakes on CNT bundles directly grown on Ni foams (NFs) with a very high areal mass loading of 4.85 mg cm^?2 for Ni(OH)₂. Our Ni(OH)₂/CNT/NF electrode demonstrates the highest specific capacitance of 3300 F g^?1 and highest areal capacitance of 16 F cm^?2, to the best of our knowledge. An asymmetric supercapacitor using the Ni(OH)₂/CNT/NF electrode as the anode assembled with an activated carbon (AC) cathode can achieve a high cell voltage of 1.8 V and an energy density up to 50.6 Wh/kg, over 10 times higher than that of traditional electrochemical double‐layer capacitors (EDLCs).     

Efficient Lightweight Supercapacitor with Compression Stability

This paper reports the fabrication of an electrochemical supercapacitor (ES) with high gravimetric and areal capacitances, achieved at a high mass ratio of active material to current collector. The active material, polypyrrole, is in situ polymerized in an aerogel‐based current collector composed of crosslinked cellulose nanocrystals (CNCs) and multiwalled carbon nanotubes (MWCNTs). Mechanical robustness, flexibility, and low impedance of the current collectors are achieved by the chemical crosslinking of CNC aerogels and efficient dispersion of MWCNTs through the use of bile acid as a dispersant. Furthermore, the advanced electrode design results in low contact resistance. A single‐electrode areal capacitance of 2.1 F cm^?2 is obtained at an active mass loading of 17.8 mg cm^?2 and an active material to current collector mass ratio of 0.57. Large area ES electrodes and devices show flexibility, excellent compression stability at 80% compression, and electrochemical cyclic stability over 5000 cycles. Moreover, good retention of capacitive properties is achieved at high charge–discharge rates and during compression cycling. The results of this investigation pave the way for the fabrication of advanced lightweight ES, which can be used for energy storage in wearable electronic devices and other applications.     

A Flexible 3D Multifunctional MgO‐Decorated Carbon Foam@CNTs Hybrid as Self‐Supported Cathode for High‐Performance Lithium‐Sulfur Batteries

One of the critical challenges to develop advanced lithium‐sulfur (Li‐S) batteries lies in exploring a high efficient stable sulfur cathode with robust conductive framework and high sulfur loading. Herein, a 3D flexible multifunctional hybrid is rationally constructed consisting of nitrogen‐doped carbon foam@CNTs decorated with ultrafine MgO nanoparticles for the use as advanced current collector. The dense carbon nanotubes uniformly wrapped on the carbon foam skeletons enhance the flexibility and build an interconnected conductive network for rapid ionic/electronic transport. In particular, a synergistic action of MgO nanoparticles and in situ N‐doping significantly suppresses the shuttling effect via enhanced chemisorption of lithium polysulfides. Owing to these merits, the as‐built electrode with an ultrahigh sulfur loading of 14.4 mg cm^?2 manifests a high initial areal capacity of 10.4 mAh cm^?2, still retains 8.8 mAh cm^?2 (612 mAh g^?1 in gravimetric capacity) over 50 cycles. The best cycling performance is achieved upon 800 cycles with an extremely low decay rate of 0.06% at 2 C. Furthermore, a flexible soft‐packaged Li‐S battery is readily assembled, which highlights stable electrochemical characteristics under bending and even folding. This cathode structural design may open up a potential avenue for practical application of high‐sulfur‐loading Li‐S batteries toward flexible energy‐storage devices.     

Direct Conversion of Fe2O3 to 3D Nanofibrillar PEDOT Microsupercapacitors

Microsupercapacitors (µSCs) are attractive electrochemical energy storage devices serving as alternatives to batteries in miniaturized portable electronics owing to high‐power density and extended cycling stability. Current state‐of‐the‐art microfabrication strategies are limited by costly steps producing materials with structural defects that lead to low energy density. This paper introduces an electrode engineering platform that combines conventional microfabrication and polymerization from the vapor phase producing 3D µSCs of the conducting polymer poly(3,4‐ethylenedioxythiophene) (PEDOT). A sputtered Fe₂O₃ precursor layer enables deposition of a 250 nm thick polymer coating comprised of a high packing density of vertically aligned PEDOT nanofibers possessing exceptional electrical conductivity (3580 S cm^?1). The 3D µSCs exhibit state‐of‐the‐art volumetric energy density (16.1 mWh cm^?3) as well as areal (21.3 mF cm^?2) and volumetric (400 F cm^?3) capacitances in 1 m H₂SO₄ aqueous electrolyte. These figures of merit represent the highest values among conducting polymer‐based µSCs. Electrochemical performance is controlled by investigating coating thickness, gap distance, fractal geometry, and gel electrolyte (1 m H₂SO₄/polyvinyl alcohol). The quasisolid‐state µSCs exhibit extended rate capability (50 V s^?1), retain 94% of original capacitance after 10 000 cycles and remain thermally stable up to 60 °C.     

Hierarchical Free‐Standing Carbon‐Nanotube Paper Electrodes with Ultrahigh Sulfur‐Loading for Lithium–Sulfur Batteries

The rational combination of conductive nanocarbon with sulfur leads to the formation of composite cathodes that can take full advantage of each building block; this is an effective way to construct cathode materials for lithium–sulfur (Li–S) batteries with high energy density. Generally, the areal sulfur‐loading amount is less than 2.0 mg cm^?2, resulting in a low areal capacity far below the acceptable value for practical applications. In this contribution, a hierarchical free‐standing carbon nanotube (CNT)‐S paper electrode with an ultrahigh sulfur‐loading of 6.3 mg cm^?2 is fabricated using a facile bottom–up strategy. In the CNT–S paper electrode, short multi‐walled CNTs are employed as the short‐range electrical conductive framework for sulfur accommodation, while the super‐long CNTs serve as both the long‐range conductive network and the intercrossed mechanical scaffold. An initial discharge capacity of 6.2 mA·h cm^?2 (995 mA·h g^?1), a 60% utilization of sulfur, and a slow cyclic fading rate of 0.20%/cycle within the initial 150 cycles at a low current density of 0.05 C are achieved. The areal capacity can be further increased to 15.1 mA·h cm^?2 by stacking three CNT–S paper electrodes—resulting in an areal sulfur‐loading of 17.3 mg cm^?2—for the cathode of a Li–S cell. The as‐obtained free‐standing paper electrode are of low cost and provide high energy density, making them promising for flexible electronic devices based on Li–S batteries.     

Hierarchical Ni–Co Hydroxide Petals on Mechanically Robust Graphene Petal Foam for High‐Energy Asymmetric Supercapacitors

A hierarchical structure consisting of Ni–Co hydroxide nanopetals (NCHPs) grown on a thin free‐standing graphene petal foam (GPF) has been designed and fabricated by a two‐step process for pseudocapacitive electrode applications. The mechanical behavior of GPFs has been, for the first time to our knowledge, quantitatively measured from in situ scanning electron microscope characterization of the petal foams during in‐plane compression and bending processes. The Young's modulus of a typical GPF is 3.42 GPa, indicating its outstanding mechanical robustness as a nanotemplate. The GPF/NCHP electrodes exhibit volumetric capacitances as high as 765 F cm^?3, equivalent to an areal capacitance of 15.3 F cm^?2 and high rate capability. To assess practical functionality, two‐terminal asymmetric solid‐state supercapacitors with 3D GPF/NCHPs as positive electrodes are fabricated and shown to exhibit outstanding energy and power densities, with maximum average energy density of ≈10 mWh cm^?3 and maximum power density of ≈3 W cm^?3, high rate capability (a capacitance retention of ≈60% at 100 mA cm^?2), and excellent long‐term cyclic stability (full capacitance retention over 15 000 cycles).